Estudos comparativos do ciclo de regeneração de diferentes tipos de silicoaluminofosfatos

Different types of heterogeneous catalysts of the silicoaluminophosphate type, (SAPO-5, SAPO-11, SAPO-31, SAPO-34 and SAPO-41), molecular sieves with a: AFI, AEL, ATO, CHA and AFO structure, respectively, were synthesized through the hydrothermal method. Using sources such as hydrated alumina (pseudobohemita), phosphoric acid, silica gel, water, as well as, different types of organic structural templates, such as: cetyltrimethylammonium bromide (CTMABr), di-isopropylamine (DIPA), di-n- propylamine (DNPA) and tetraethylammonium hydroxide (TEOS), for the respective samples. During the preparation of the silicoaluminophosphates, the crystallization process of the samples occurred at a temperature of approximately 200 ° C, ranging through periods of 18-72 h, when it was possible to obtain pure phases for the SAPOs. The materials were furthermore washed with deionized water, dried and calcined to remove the molecules of the templates. Subsequently the samples were characterized by X-ray diffraction (XRD), scanning electron microscopy (SEM), absorption spectroscopy in the infrared region (FT-IR), specific surface area and thermal analysis via TG/DTG. The acidic properties were determined using adsorption of n-butylamine followed by programmed termodessorption. These methods revealed that the SAPO samples showed a typically weak to moderate acidity. However, a small amount of strong acid sites was also detected. The deactivation of the catalysts was conducted by artificially coking the samples, followed by n-hexane cracking reactions in a fixed bed with a continuous flow micro-reactor coupled on line to a gas chromatograph. The main products obtained were: ethane, propane, isobutene, n-butane, n-pentane and isopentane. The Vyazovkin (model-free) kinetics method was used to determine the catalysts regeneration and removal of the coke

Efeitos do tratamento superficial da sílica ativa com soluções de ácidos nítrico e fosfórico em propriedades do concreto

The addition of active silica potentially improves the quality of concrete due to its high reactivity and pore refinement effect. The reactivity of silica is likely related to its charge density. Variations in surface charge alter the reactivity of the material consequently affecting the properties of concrete. The present study aimed at investigating variations in the charge density of silica as a function of acid treatments using nitric or phosphoric acid and different pH values (2.0, 4.0 and 6.0). Effects on concrete properties including slump, mechanical strength, permeability and chloride corrosion were evaluated. To that end, a statistical analysis was carried out and empirical models that correlate studied parameters (pH, acid and cement) with concrete properties were established. The quality of the models was tested by variance analysis. The results revealed that the addition of silica was efficiency in improving the properties of concrete, especially the electrochemical parameters. The addition of silica treated using nitric acid at pH = 4.0 displayed the best cement performance including highest strength, reduced permeability and lowest corrosion current

Efeito de variáveis de processo no tempo de fermentação e na concentração das dicetonas vicinais totais

Among the main challenges in the beer industrial production is the market supply at the lowest cost and high quality, in order to ensure the expectations of customers and. consumers The beer fermentation stage represents approximately 70% of the whole time necessary to its production, having a obligatoriness of strict process controls to avoid becoming bottleneck in beer production. This stage is responsible for the formation of a series of subproducts, which are responsible for the composition of aroma/bouquet existing in beer and some of these subproducts, if produced in larger quantities, they will confer unpleasant taste and odor to the final product. Among the subproducts formed during the fermentation stage, total vicinal diketones is the main component, since it is limiting for product transfusion to the subsequent steps, besides having a low perception threshold by the consumer and giving undesirable taste and odor. Due to the instability of main raw materials quality and also process controls during fermentation, the development of alternative forms of beer production without impacting on total fermentation time and final product quality is a great challenge to breweries. In this work, a prior acidification of the pasty yeast was carried out, utilizing for that phosphoric acid, food grade, reducing yeast pH of about 5.30 to 2.20 and altering its characteristic from flocculent to pulverulent during beer fermentation. An increase of six times was observed in amount of yeast cells in suspension in the second fermentation stage regarding to fermentations by yeast with no prior acidification. With alteration on two input variables, temperature curve and cell multiplication, which goal was to minimize the maximum values for diketones detected in the fermenter tank, a reduction was obtained from peak of formed diacetyl and consequently contributed to reduction in fermentation time and total process time. Several experiments were performed with those process changes in order to verify the influence on the total fermentation time and total vicinal diketones concentration at the end of fermentation. This experiment reached as the best production result a total fermentation time of 151 hours and total vicinal diketone concentration of 0.08 ppm. The mass of yeast in suspension in the second phase of fermentation increased from 2.45 x 106 to 16.38 x 106 cells/mL of yeast, which fact is key to a greater efficiency in reducing total vicinal diketones existing in the medium, confirming that the prior yeast acidification, as well as the control of temperature and yeast cell multiplication in fermentative process enhances the performance of diketones reduction and consequently reduce the total fermentation time with diketones concentration below the expected value (Max: 0.10 ppm)

Estudos comparativos do ciclo de regeneração de diferentes tipos de silicoaluminofosfatos

Different types of heterogeneous catalysts of the silicoaluminophosphate type, (SAPO-5, SAPO-11, SAPO-31, SAPO-34 and SAPO-41), molecular sieves with a: AFI, AEL, ATO, CHA and AFO structure, respectively, were synthesized through the hydrothermal method. Using sources such as hydrated alumina (pseudobohemita), phosphoric acid, silica gel, water, as well as, different types of organic structural templates, such as: cetyltrimethylammonium bromide (CTMABr), di-isopropylamine (DIPA), di-n- propylamine (DNPA) and tetraethylammonium hydroxide (TEOS), for the respective samples. During the preparation of the silicoaluminophosphates, the crystallization process of the samples occurred at a temperature of approximately 200 ° C, ranging through periods of 18-72 h, when it was possible to obtain pure phases for the SAPOs. The materials were furthermore washed with deionized water, dried and calcined to remove the molecules of the templates. Subsequently the samples were characterized by X-ray diffraction (XRD), scanning electron microscopy (SEM), absorption spectroscopy in the infrared region (FT-IR), specific surface area and thermal analysis via TG/DTG. The acidic properties were determined using adsorption of n-butylamine followed by programmed termodessorption. These methods revealed that the SAPO samples showed a typically weak to moderate acidity. However, a small amount of strong acid sites was also detected. The deactivation of the catalysts was conducted by artificially coking the samples, followed by n-hexane cracking reactions in a fixed bed with a continuous flow micro-reactor coupled on line to a gas chromatograph. The main products obtained were: ethane, propane, isobutene, n-butane, n-pentane and isopentane. The Vyazovkin (model-free) kinetics method was used to determine the catalysts regeneration and removal of the coke

Efeitos do tratamento superficial da sílica ativa com soluções de ácidos nítrico e fosfórico em propriedades do concreto

The addition of active silica potentially improves the quality of concrete due to its high reactivity and pore refinement effect. The reactivity of silica is likely related to its charge density. Variations in surface charge alter the reactivity of the material consequently affecting the properties of concrete. The present study aimed at investigating variations in the charge density of silica as a function of acid treatments using nitric or phosphoric acid and different pH values (2.0, 4.0 and 6.0). Effects on concrete properties including slump, mechanical strength, permeability and chloride corrosion were evaluated. To that end, a statistical analysis was carried out and empirical models that correlate studied parameters (pH, acid and cement) with concrete properties were established. The quality of the models was tested by variance analysis. The results revealed that the addition of silica was efficiency in improving the properties of concrete, especially the electrochemical parameters. The addition of silica treated using nitric acid at pH = 4.0 displayed the best cement performance including highest strength, reduced permeability and lowest corrosion current