Adição de subprodutos da cinza da casca de café (coffea canephora) em massa cerâmica para porcelanato

To produce porcelain tiles fluxing agents are used in order to obtain a liquid phase during firing. This liquid phase fills the pores decreasing porosity, water absorption and contributes to material densification. In the porcelain tiles industry, feldspar is the main flux material used, with quantities ranging between 35 and 50%. Studies focus on the discovery of materials with flux characteristics that can reduce the consumption of feldspar by porcelain tiles industry. In this context, the coffee husk ashes, a residue obtained when coffee husks are burned to produce heat for the dryers during the processing of the green fruit, have as main chemical constituents potassium, calcium and magnesium, giving them characteristics of fluxing material. Brazil is the largest coffee producer in the world and is responsible for over 30% of the world s production. In this work a physical treatment of coffee husk ash was carried out in order to eliminate the organic matter and, after this, two by-products were obtained: residual wastes R1 and R2. Both residues were added separately as single fluxes and also in association with feldspar in mixtures with raw materials collected in a porcelain industry located in Dias d Ávila-Ba. The addition of these residues aimed to contribute to the reduction of the consumption of feldspar in the production of porcelain tiles. Specimens were produced with dimensions of 60 mm x 20 mm x 6 mm in an uniaxial die with compacting pressure of 45 MPa. The samples were heated to a temperature of 1200 °C, for 8 minutes. Tests were performed to characterize the raw materials by XRF, XRD, particle size analysis, DTA and TGA and, additionally, the results of the physical properties of water absorption, apparent porosity, linear shrinkage, density, dilatometry, flexural strength and SEM of sintered body were analyzed. Additions of less than 8% of the residue R1 contributed to the decrease of porosity, but the mechanical strength of the samples was not satisfactory. Additions of 5% the R2 residue contributed significantly to decrease the water absorption and apparent porosity, and also to increase the mechanical strength. Samples with addition of feldspar associated with the R2 residue, in proportions of 6.7% of R2 and 6.7% of feldspar, led to results of water absorption of 0.12% and mechanical strength of 46 MPa, having parameters normalized to the manufacture of porcelain stoneware tiles

Incorporação de cinzas da casca de café na produção de placas cerâmicas para revestimento

Brazil is the world s leading coffee producer. In 2008, 45.99 million of 60 kg bags of benefited coffee were produced. In the process of improvement 50% is grain and 50% is husk, thus, 1.38 million tons of coffee husk are produced annually. The husk is used as combustible in the drying and improvement ovens in the coffee farms, generating ash as residue. These ashes contain a high concentration of alkaline metals and earth metals, mainly K2O and CaO. This work studies the use of this residue in the ceramic tiles industry, as fluxing agents in substitution to the feldspar. Ten mixtures with equal ratios of clay and kaolin, proceeding from Bahia and the residue (varying from 30 to 5%) were defined and produced in uniaxial tool die of 60x20mm with approximately 5 mm of thickness and 45MPa compacting pressure. The samples were fired in four different temperatures: 1100 °C, 1150 °C, 1185 °C and 1200 °C during 60 minutes and characterized by means of X-ray fluorescence, X-ray diffraction, gravimetric thermal analysis and differential thermal analysis. The results of water absorption, apparent porosity, linear shrinkage, XRD, dilatometry, flexural strength and SEM were also analysed. The test specimen with addition of 10% of ash fired in 1200 °C resulted in 0.18% water absorption and 40.77 MPa flexural strength, being classified as porcelain stoneware tiles according to ABNT, UNI and ISO norms

Uso da cinza do bagaço da cana-de-açúcar como matéria-prima na substituição dos fundentes para aplicações em porcelanato

The present study aims to evaluate the potential use of bagasse ash from sugar cane (CBC) as a flux, replacing phyllite and/or feldspar in standard industrial mass production of enameled porcelain, verifying the possibility of the CBC contribute to the overall reduction of the coefficient of thermal expansion of the ceramic mass. To this end, as a result of the research, we characterized the raw material components of the standard mass (clay, phyllite, kaolin, feldspar, quartz and talc) and the residue of BCC, by testing by XRF, XRD, AG, DTA and ATG. Specimens (CDP) were manufactured in the dimensions of 100 mm x 50 mm x 8 mm in uniaxial matrix under compaction pressure of 33 MPa, assembled in batches of 3 units subsequently sintered at temperatures of 1150°C to 1210°C by varying the Rating Scale at 10°C, heating and cooling ramp of 50°C/min and 25°C/min, with levels of 1 min, 3 min, 5 min, 8 min, 10 min, 15 min, 30 min and 60 min. analyzing the results of the physical properties of water absorption (WA), linear firing shrinkage (LFS), dilatometric analysis (DTA), flexural strain (SFT) and SEM of the sintered bodies in order to verify the adequacy of CDP to ISO 13006, ISO 10545, NBR 13816 standards; NBR 13817 and NBR 13818. The study showed that the formulations that best suit the requirements of the standards are:. G4 - which was applied in 10% of replacing the CBC phyllite, sintering temperature 1210 ° C for 10 min and porch, and F3 - with application of 7.5% of CBC to replace the feldspar in the sintering temperatures of 1190°C, 1200��C and 1210°C for 10 min and porch. These formulations showed better performance regarding the formation of primary and secondary mullite, with considerable reduction of cracks and pores, meeting the prerequisites of standards for glazed porcelain. The results shows that the use of the CBC as a flux in the preparation of porcelain mass meets standard parameters for the manufacture of the product, and thereby can reduce environmental impact and the cost of production. Therefore, it is recommended to use this residue in the ceramics industry, due to its industrial, commercial and collaborative viability for sustainability.

Adição de subprodutos da cinza da casca de café (coffea canephora) em massa cerâmica para porcelanato

To produce porcelain tiles fluxing agents are used in order to obtain a liquid phase during firing. This liquid phase fills the pores decreasing porosity, water absorption and contributes to material densification. In the porcelain tiles industry, feldspar is the main flux material used, with quantities ranging between 35 and 50%. Studies focus on the discovery of materials with flux characteristics that can reduce the consumption of feldspar by porcelain tiles industry. In this context, the coffee husk ashes, a residue obtained when coffee husks are burned to produce heat for the dryers during the processing of the green fruit, have as main chemical constituents potassium, calcium and magnesium, giving them characteristics of fluxing material. Brazil is the largest coffee producer in the world and is responsible for over 30% of the world s production. In this work a physical treatment of coffee husk ash was carried out in order to eliminate the organic matter and, after this, two by-products were obtained: residual wastes R1 and R2. Both residues were added separately as single fluxes and also in association with feldspar in mixtures with raw materials collected in a porcelain industry located in Dias d Ávila-Ba. The addition of these residues aimed to contribute to the reduction of the consumption of feldspar in the production of porcelain tiles. Specimens were produced with dimensions of 60 mm x 20 mm x 6 mm in an uniaxial die with compacting pressure of 45 MPa. The samples were heated to a temperature of 1200 °C, for 8 minutes. Tests were performed to characterize the raw materials by XRF, XRD, particle size analysis, DTA and TGA and, additionally, the results of the physical properties of water absorption, apparent porosity, linear shrinkage, density, dilatometry, flexural strength and SEM of sintered body were analyzed. Additions of less than 8% of the residue R1 contributed to the decrease of porosity, but the mechanical strength of the samples was not satisfactory. Additions of 5% the R2 residue contributed significantly to decrease the water absorption and apparent porosity, and also to increase the mechanical strength. Samples with addition of feldspar associated with the R2 residue, in proportions of 6.7% of R2 and 6.7% of feldspar, led to results of water absorption of 0.12% and mechanical strength of 46 MPa, having parameters normalized to the manufacture of porcelain stoneware tiles