A Comparati ve Study of Mechanical and Tribological Properties of AISI-304 and AISI-316 Submitted to Glow Discharge Nitriding

Mechanical and tribological properties of AISI 304 and AISI 316 stainless steels submitted to glow discharge ion nitriding are reported. The atmosphere was 20:80 - N2:H2 with substrate temperatures ranging from 300 to 500 °C. Treatment at 300 °C produced expanded austenite (γN) in both steels. Increasing the temperature, the phases γ′-Fe4N and ε- Fe2+xN were present and the latter is the major phase for AISI 304. At 500 °C, the CrN phase was also identified in both steels. Hardnesses of about 13-14 GPa at near surface regions were obtained in both steels. Moreover, AISI 316 nitrided at 500 °C has the deepest hard layer. Tribological tests showed that wear can be reduced by up to a factor of six after the nitriding processes, even for a working temperature of 300 °C. The profiles during and after nanoscratch tests did not reveal significant differences after nitriding processes in both steels.

A Comparative Study of Mechanical and Tribological Properties of AISI-304 and AISI-316 Submitted to Glow Discharge Nitriding

Mechanical and tribological properties of AISI 304 and AISI 316 stainless steels submitted to glow discharge ion nitriding are reported. The atmosphere was 20:80 - N2:H2 with substrate temperatures ranging from 300 to 500 °C. Treatment at 300 °C produced expanded austenite (γN) in both steels. Increasing the temperature, the phases γ′-Fe4N and ε- Fe2+xN were present and the latter is the major phase for AISI 304. At 500 °C, the CrN phase was also identified in both steels. Hardnesses of about 13-14 GPa at near surface regions were obtained in both steels. Moreover, AISI 316 nitrided at 500 °C has the deepest hard layer. Tribological tests showed that wear can be reduced by up to a factor of six after the nitriding processes, even for a working temperature of 300 °C. The profiles during and after nanoscratch tests did not reveal significant differences after nitriding processes in both steels.

Um estudo das condições de percolação e estabilidade em barragens de terra mediante métodos geofísicos: caso do dique de Sant Llorenç de Montgai - Espanha

The monitoring of Earth dam makes use of visual inspection and instrumentation to identify and characterize the deterioration that compromises the security of earth dams and associated structures. The visual inspection is subjective and can lead to misinterpretation or omission of important information and, some problems are detected too late. The instrumentation are efficient but certain technical or operational issues can cause restrictions. Thereby, visual inspections and instrumentation can lead to a lack of information. Geophysics offers consolidated, low-cost methods that are non-invasive, non-destructive and low cost. They have a strong potential and can be used assisting instrumentation. In the case that a visual inspection and strumentation does not provide all the necessary information, geophysical methods would provide more complete and relevant information. In order to test these theories, geophysical acquisitions were performed using Georadar (GPR), Electric resistivity, Seismic refraction, and Refraction Microtremor (ReMi) on the dike of the dam in Sant Llorenç de Montgai, located in the province of Lleida, 145 km from Barcelona, Catalonia. The results confirmed that the geophysical methods used each responded satisfactorily to the conditions of the earth dike, the anomalies present and the geological features found, such as alluvium and carbonate and evaporite rocks. It has also been confirmed that these methods, when used in an integrated manner, are able to reduce the ambiguities in individual interpretations. They facilitate improved imaging of the interior dikes and of major geological features, thus inspecting the massif and its foundation. Consequently, the results obtained in this study demonstrated that these geophysical methods are sufficiently effective for inspecting earth dams and they are an important tool in the instrumentation and visual inspection of the security of the dams

Estudos sedimentológicos e o contexto estrutural da formação Serra do Martins, nos platôs de Portalegre, Martins e Santana/RN

This dissertation deals with sedimentological and structural framework of the siliciclastic rock of the Serra do Martins Formation (FSM) in the Portalegre, Martins and Santana plateau, located to the south of Potiguar Basin, in the southwest and central Rio Grande do Norte state. This formation, regarded as of Oligo-Miocene age based on intrusive relations of the Miocene Macau volcanics, has a still disputable age due to the lack of appropriate bio and/or chronostratigraphic markers. The FSSM deposits crop out along 650 to 750 m high plateau, as a remanescent sedimentary cover directly overlying topographically uplifted pre-cambrian crystalline rocks. During the last decades, these deposits were interpreted according to a Tertiary paleoclimatic evolutionary model, associated to pedogenetic processes. The sedimentological characterization of the FSM was done through a detailed study of its facies, petrography and diagenetic features. The facies study was based on description of field relations, textures and structures, the piling up of the strata and their lateral variations. The FSM was deposited by an anastomosing to coarse-meandering fluvial system, including deposits of lag, cannel-fill, ouver-bank and flood plain. The petrographic composition of the sediments, coupled to their facies and paleocurrent directions, suggest a rather distal sourcearea, to the south of the present plateau. The diagenetic study identified an incipient grain mechanical compaction, pronounced dissolution of the framework, matrix and/or cement components, intense precipitation of kaolinite, silic and, eventually, iron oxides, besides mechanical infiltration of the clays. Most of these events, regarded in the literature as associated to near-surface conditions (eo or telodiagenesis), indicate the FSM sediments were never deeply buried. Topographic relations along longitudinal and transversal sections reaching the Potiguar Basin to the north identified regional dips that allow to discuss stratigraphic correlations between the FSM and the basin formations. The sedimentological features of the different units and the intrusive relations of the Macau volcanics were also considered in these correlations,which support the Oligo-Miocene age previously accepted for the FSM. Concerning the tectonic framework of the FSM, this work investigated the pre-cambrian to cretaceous heritage and the cenozoic deformation, allowing the recognition of pre-, sin and post-FSM structures. The crystalline basement, belonging to the Seridó Belt, displays NE and WNW foliation trends related to the Brasiliano-age ductile shear zones. In this terrain, brittle-ductile and brittle NE- and NW-trending structures, associated with extensional joints filled with pegmatites and quartz veins, are related to an E-W compression by the end of Brasiliano Cycle. The E-W joints and NE-trending fractures were reactivated by N-S to N-S to NW extension during late Jurassic to Cretaceous times, controlling the emplacement of the Rio Ceará-Mirim basic dyke swarm and the opening of the Potiguar rift basin

A Comparati ve Study of Mechanical and Tribological Properties of AISI-304 and AISI-316 Submitted to Glow Discharge Nitriding

Mechanical and tribological properties of AISI 304 and AISI 316 stainless steels submitted to glow discharge ion nitriding are reported. The atmosphere was 20:80 - N2:H2 with substrate temperatures ranging from 300 to 500 °C. Treatment at 300 °C produced expanded austenite (γN) in both steels. Increasing the temperature, the phases γ′-Fe4N and ε- Fe2+xN were present and the latter is the major phase for AISI 304. At 500 °C, the CrN phase was also identified in both steels. Hardnesses of about 13-14 GPa at near surface regions were obtained in both steels. Moreover, AISI 316 nitrided at 500 °C has the deepest hard layer. Tribological tests showed that wear can be reduced by up to a factor of six after the nitriding processes, even for a working temperature of 300 °C. The profiles during and after nanoscratch tests did not reveal significant differences after nitriding processes in both steels.

A Comparative Study of Mechanical and Tribological Properties of AISI-304 and AISI-316 Submitted to Glow Discharge Nitriding

Mechanical and tribological properties of AISI 304 and AISI 316 stainless steels submitted to glow discharge ion nitriding are reported. The atmosphere was 20:80 - N2:H2 with substrate temperatures ranging from 300 to 500 °C. Treatment at 300 °C produced expanded austenite (γN) in both steels. Increasing the temperature, the phases γ′-Fe4N and ε- Fe2+xN were present and the latter is the major phase for AISI 304. At 500 °C, the CrN phase was also identified in both steels. Hardnesses of about 13-14 GPa at near surface regions were obtained in both steels. Moreover, AISI 316 nitrided at 500 °C has the deepest hard layer. Tribological tests showed that wear can be reduced by up to a factor of six after the nitriding processes, even for a working temperature of 300 °C. The profiles during and after nanoscratch tests did not reveal significant differences after nitriding processes in both steels.