Caracterização de compósitos Nb-20%cu obtidos por moagem de alta energia e sinterizados por fase líquida

In this work, was studied the formation of a composite of the refractory metal niobium with copper, through the process of high-energy milling and liquid phase sintering. The HEM can be used to synthesize composite powders with high homogeneity and fine size particle distribution. It may also produce the solid solubility in immiscible systems such as Nb-Cu, or extend the solubility of systems with limited solubility. Therefore, in the immiscible system Cu-Nb, the high-energy milling was successfully used to obtain the composite powder particles. Initially, the formation of composite particles during the HEM and the effect of preparation technique on the microstructure of the material was evaluated. Four loads of Nb and Cu powders containing 20%wt Cu were synthesized by MAE in a planetary type ball mill under different periods of grinding. The influence of grinding time on the metal particles is evaluated during the process by the withdrawal of samples at intermediate times of milling. After compaction under different forces, the samples were sintered in a vacuum furnace. The liquid phase sintering of these samples prepared by HEM produced a homogeneous and fine grained. The composite particles forming the sintered samples are the addition of a hard phase (Nb) with a high melting point, and a ductile phase (Cu) with low melting point and high thermal and electrical conductivities. Based on these properties, the Nb-Cu system is a potential material for many applications, such as electrical contacts, welding electrodes, coils for generating high magnetic fields, heat sinks and microwave absorbers, which are coupled to electronic devices. The characterization techniques used in this study, were laser granulometry, used to evaluate the homogeneity and particle size, and the X-ray diffraction, in the phase identification and to analyze the crystalline structure of the powders during milling. The morphology and dispersion of the phases in the composite powder particles, as well the microstructures of the sintered samples, were observed by scanning electron microscopy (SEM). Subsequently, the sintered samples are evaluated for density and densification. And finally, they were characterized by techniques of measuring the electrical conductivity and microhardness, whose properties are analyzed as a function of the parameters for obtaining the composite

Obtenção de pós de Nb a partir da redução aluminotérmica com ignição por plasma

The aluminothermic reduction consists in an exothermic reaction between a metallic oxide and aluminum to produce the metal and the scum. The extracted melted metal of that reaction usually comes mixed with particles of Al2O3 resulting of the reduction, needing of subsequent refine to eliminate the residual impure as well as to eliminate porosities. Seeking to obtain a product in powder form with nanometric size or even submicrometric, the conventional heat source of the reaction aluminothermic , where a resistor is used (ignitor) as ignition source was substituted, for the plasma, that acts more efficient way in each particle of the sample. In that work it was used as metallic oxide the niobium pentoxide (Nb2O5) for the exothermal reaction Nb2O5 + Al. Amounts stoichiometric, substoichiometric and superestoichiometric of aluminum were used. The Nb2O5 powder was mixed with aluminum powder and milled in planetarium of high energy for a period of 6 hours. Those powders were immerged in plasm that acts in a punctual way in each particle, transfering heat, so that the reaction can be initiate and spread integrally for the whole volume of the particle. The mixture of Nb2O5 + Al was characterized through the particle size analysis by laser and X-ray diffraction (DRX) and the obtained product of reaction was characterized using the electronic microscopy of sweeping (MEV) and the formed phases were analyzed by DRX. Niobium powders with inferior sizes to 1 mm were obtained by that method. It is noticed, through the analysis of the obtained results, that is possible to accomplish the aluminothermic reduction process by plasma ignition with final particles with inferior sizes to the original oxide

Produção de estrutura com gradiente de porosidade a partir da sinterização por plasma da mistura de pós Ti-Nb-Sn

Porous structures are being widely investigated for use in biomedical implants, aiming to mechanically integrate and functionally the implant inside the bone tissue. Moreover, this structure is also important for drugs that can be stored and can induce and accelerate the process of osseointegration. With the purpose to investigate this effect, Ti, Nb and Sn metal powders, were sintered by plasma using a hollow cathode discharge. Sintering was performed in argon plasma set at 4 mbar pressure and temperatures of 500 ° C, 600 ° C and 700 ° C. Samples were also sintered in the electrical resistance furnace at 1200 ° C in order to compare plasma sintering with the conventional method. It was observed that plasma samples sintered with the hollow cathode configuration showed a gradient in porosity, while the samples sintered in the resistive furnace did not. Furthermore, differences in the microstructure of the samples were found, were a surface with higher porosity and ales porous core were obtained at different temperatures. The percolation profile of distilled water and the chemical compositions of the porous layers of the plasma treated samples were the main results obtained. Based on these results, we can conclude that this structure is particularly important for application in the biomedical field such as scaffolds for drug delivery and implants

Estudo de um compósito Nb-15%pCu obtidos por moagem de alta energia e sinterizados por fase líquida

There is great difficulty in forming a composite refractory metal niobium with copper. This is due to the fact that Nb-Cu system is almost mutually immiscible and may be neglected solubility between them. These properties hinder or prevent obtaining homogeneous and high-density structures, conventionally prepared. This study aims to analyze the use of high-energy milling process (MAE) to implement these natural difficulties, with regard to the densification of the sintered bodies. The MAE and the press were used in the preparation of powders, to obtain a fine and homogeneous distribution of the grain size. Four loads Nb and Cu powders containing 15% by weight of Cu were then milled for MAE in a planetary type ball mill under various milling times and speeds. The results obtained by MAE were analyzed by scanning electron microscopy (SEM), according to the parameters of time and grinding speed. The samples were compacted under pressure of 200 MPa, were then sintered in liquid phase in a vacuum furnace at temperatures of 1100 ° C / 60 min and 1200 ° C / 60 min. Then it was used to characterize diffraction of X-rays to identify the phases. The microstructures of the sintered samples were observed and evaluated using scanning electron microscopy (SEM). Vickers Microhardness tests were performed, obtaining higher values for the sintered bodies in the largest of the post milling times and the larger grinding speeds. It was found that the liquid phase sintering of the samples that were processed by MAE produced at the end of a homogeneous and densified structure in 77,4% relative to the value of the theoretical density of the composite

Estudo de duas pseudoligas de Nb-Cu obtidas pela rota da metalurgia do pó

The Nb-Cu pseudoalloys present themselves as potential substitutes for the alloys from a well known system and already commercially applied, as the W-Cu alloys, used in applications such as heat sinks, electrical contacts and coils for the generation of high magnetic fields. Because it is an immiscible system, where there is mutual insolubility and low wettability of the liquid Cu on the Nb surface, the processing route used in this work was the Powder Metallurgy. Two Nb alloys were used, with additions of 10% and 20% in weight of Cu, and times of 20, 30 and 40 hours for the high energy milling of the starting powders. The milling evolution of the powders is presented through the characterization techniques, such as the LASER diffraction for particle size, XRD, SEM, EDS, DSC, dilatometry, TEM and chemical analysis. After the milling, portions of the loads were submitted to the annealing heat treatment. The process used for the samples consolidation was the hot pressing, which has been applied both on some milled powders samples, as on the annealed powders. Subsequent heat treatments were performed in the samples at temperatures of 1000ºC (solid phase) and 1100ºC (in the Cu liquid phase). All sets of consolidated samples, and also the two sets of the heat treated, were analyzed by XRD, SEM, EDS, density and Vickers microhardness. Moreover, other Nb powder samples with 10% and 20% in weight of Cu obtained by simple mechanical mixing, were consolidated, thermally treated and characterized with the same techniques applied to the others, and the results were compared among themselves. Despite the difficulty of consolidation and densification of the two pseudoalloys of the Nb-Cu system of this study, on the route that passes through the HEM, samples were obtained with densities around 90% of the theoretical density. And, on the processing route of which were only mixed, the values reached up to 97%. Therefore, in this work are also emphasized the processes that made possible these results.

Caracterização de compósitos Nb-20%cu obtidos por moagem de alta energia e sinterizados por fase líquida

In this work, was studied the formation of a composite of the refractory metal niobium with copper, through the process of high-energy milling and liquid phase sintering. The HEM can be used to synthesize composite powders with high homogeneity and fine size particle distribution. It may also produce the solid solubility in immiscible systems such as Nb-Cu, or extend the solubility of systems with limited solubility. Therefore, in the immiscible system Cu-Nb, the high-energy milling was successfully used to obtain the composite powder particles. Initially, the formation of composite particles during the HEM and the effect of preparation technique on the microstructure of the material was evaluated. Four loads of Nb and Cu powders containing 20%wt Cu were synthesized by MAE in a planetary type ball mill under different periods of grinding. The influence of grinding time on the metal particles is evaluated during the process by the withdrawal of samples at intermediate times of milling. After compaction under different forces, the samples were sintered in a vacuum furnace. The liquid phase sintering of these samples prepared by HEM produced a homogeneous and fine grained. The composite particles forming the sintered samples are the addition of a hard phase (Nb) with a high melting point, and a ductile phase (Cu) with low melting point and high thermal and electrical conductivities. Based on these properties, the Nb-Cu system is a potential material for many applications, such as electrical contacts, welding electrodes, coils for generating high magnetic fields, heat sinks and microwave absorbers, which are coupled to electronic devices. The characterization techniques used in this study, were laser granulometry, used to evaluate the homogeneity and particle size, and the X-ray diffraction, in the phase identification and to analyze the crystalline structure of the powders during milling. The morphology and dispersion of the phases in the composite powder particles, as well the microstructures of the sintered samples, were observed by scanning electron microscopy (SEM). Subsequently, the sintered samples are evaluated for density and densification. And finally, they were characterized by techniques of measuring the electrical conductivity and microhardness, whose properties are analyzed as a function of the parameters for obtaining the composite