Otimização da síntese de nanoferritas de nizn dopada com cobre e cobalto

Different compositions of Ni0,5-xCuxZn0,5Fe2O4 and Ni0,5-xCoxZn0,5Fe2O4 0 ≤ x ≤ 0.3 were synthesized ferrite y the citrate precursor method. The stoichiometric compositions were calcined in air at 350°C and then pressed into pellets and toroids. The pressed samples were sintered at temperatures of 1000, 1050 and 1100°C/3h in air control at the speed of heating and cooling. The calcined powders were characterized by XRD, TGA / DTG, FTIR, SEM and vibrating sample magnetometry (VSM) and the sintered samples by XRD, SEM, MAV, density and measurements of permeability and magnetic losses. There was pure phase formation ferrimagnetism applied at all temperatures except for A-I composition at all sintering temperatures and A-II only at a temperature of 1100°C. Crystallite sizes were obtained by Rietveld analysis, nanometer size from 11 to 20 nm for the calcined powders. For SEM, the sintered samples showed grain size between 1 and 10 micrometers. Bulk density (ρ) of sintered material presented to the Families almost linear behavior with increasing temperature and a tendency to decrease with increasing concentration of copper, different behavior of the B Family, where the increase in temperature decreased the density. The magnetic measurements revealed the powder characteristics of a soft ferrimagnetic material. Two processes of magnetization were considered, the superparamagnetism at low temperatures (350°C) and the formation of magnetic domains at higher temperatures. Obtaining the best parameters for P and B-II magnetic ferrites at high temperatures. The sintered material at 1000°C showed a relative permeability (μ) from 50 to 800 for the A Family and from 10 to 600 for the B Family. The samples sintered at 1100°C, B Family showed a variation from 10 to 1000 and the magnetic loss (tan δ) of A and B Families, around of 1. The frequency response of the toroidal core is in the range of 0.3 kHz. Several factors contribute to the behavior of microstructure considering the quantities μ and tan δ, such as the grain size, inter-and intragranular porosity, amount of grain boundary and the aspects of the dynamics of domain walls at high frequencies.

Desenvolvimento de sistema magnético polimérico contendo antimicrobianos para tratamento de infecções por Helicobacter pylori

Helicobacter pylori is the main cause of gastritis, gastroduodenal ulcer disease and gastric cancer. The most recommended treatment for eradication of this bacteria often leads to side effects and patient poor compliance, which induce treatment failure. Magnetic drug targeting is a very efficient method that overcomes these drawbacks through association of the drug with a magnetic compound. Such approach may allow such systems to be placed slowed down to a specific target area by an external magnetic field. This work reports a study of the synthesis and characterization of polymeric magnetic particles loaded with the currently used antimicrobial agents for the treatment of Helicobacter pylori infections, aiming the production of magnetic drug delivery system by oral route. Optical microscopy, scanning electron microscopy, transmission electron microscopy, x-ray powder diffraction, nitrogen adsorption/desorption isotherms and vibrating sample magnetometry revealed that the magnetite particles, produced by the co-precipitation method, consisted of a large number of aggregated nanometer-size crystallites (about 6 nm), creating superparamagnetic micrometer with high magnetic susceptibility particles with an average diameter of 6.8 ± 0.2 μm. Also, the polymeric magnetic particles produced by spray drying had a core-shell structure based on magnetite microparticles, amoxicillin and clarithromycin and coated with Eudragit® S100. The system presented an average diameter of 14.2 ± 0.2 μm. The amount of magnetite present in the system may be tailored by suitably controlling the suspension used to feed the spray dryer. In the present work it was 2.9% (w/w). The magnetic system produced may prove to be very promising for eradication of Helicobacter pylori infections

Síntese e caracterização de pigmentos nanométricos encapsulados pelos métodos dos precursores poliméricos, hidrotermal de microondas e co-precipitação associado à química sol-gel convencional

The demand for materials with high consistency obtained at relatively low temperatures has been leveraging the search for chemical processes substituents of the conventional ceramic method. This paper aims to obtain nanosized pigments encapsulated (core-shell) the basis of TiO2 doped with transition metals (Fe, Co, Ni, Al) through three (3) methods of synthesis: polymeric precursors (Pechini); hydrothermal microwave, and co-precipitation associated with the sol-gel chemistry. The study was motivated by the simplicity, speed and low power consumption characteristic of these methods. Systems costs are affordable because they allow achieving good control of microstructure, combined with high purity, controlled stoichiometric phases and allowing to obtain particles of nanometer size. The physical, chemical, morphological, structural and optical properties of the materials obtained were analyzed using different techniques for materials characterization. The powder pigments were tested in discoloration and degradation using a photoreactor through the solution of Remazol yellow dye gold (NNI), such as filtration, resulting in a separation of solution and the filter pigments available for further UV-Vis measurements . Different calcination temperatures taken after obtaining the post, the different methods were: 400 º C and 1000 º C. Using a fixed concentration of 10% (Fe, Al, Ni, Co) mass relative to the mass of titanium technologically and economically enabling the study. By transmission electron microscopy (TEM) technique was possible to analyze and confirm the structural formation nanosized particles of encapsulated pigment, TiO2 having the diameter of 20 nm to 100 nm, and thickness of coated layer of Fe, Ni and Co between 2 nm and 10 nm. The method of synthesis more efficient has been studied in the work co-precipitation associated with sol-gel chemistry, in which the best results were achieved without the need for the obtainment of powders the calcination process