Estudo da oxidação superficial de ligas odontológicas de Ni-Cr em plasma pulsado para uso em restaurações metalocerâmicas

Metal ceramic restorations matches aesthetic and strength, and in your making occurs an interface oxide layer, wetting resulting and atomic and ionic interactions resulting between metal, oxide and porcelain. However, frequent clinical fails occurs in this restoration type, because lost homogeneous deposition oxide layer and lost interface bond. Thus, in this study, thought depositate homogeneous oxide films above Ni-Cr samples surfaces polite previously, at plasma oxide environment. Six samples was oxided at 300 and 400ºC at one hour, and two samples was oxided in a comum chamber at 900ºC, and then were characterized: optical microscopic, electronic microscopic, micro hardness, and X ray difratometry. Colors stripes were observed at six samples plasma oxided and a grey surface those comum oxided, thus like: hardness increase, and several oxides from basic metals (Ni-Cr)

Obtenção e Caracterização Físico-Química do Sistema Compósito PEG-TiO2

Hybrid systems formed from polymers and transition metals have now their physical and chemical properties extensively investigated for use in electronic devices. In this work, Titanium Dioxide (TiO2) from the precursor of titanium tetrabutoxide and the composite system Poly(Ethylene Glycol)-Titanium Dioxide (TiO2-PEG) were synthesized by sol-gel method. The PEG as acquired and TiO2 and composites powders were analyzed by X-Ray Diffraction (XRD), Spectroscopy in the Infrared region with Fourier transform (IRFT), Thermogravimetric Analysis (TGA), Scanning Electron Microscopy (SEM) and Electrochemical Impedance Spectroscopy (EIS). In the XRD analysis were observed in the TiO2 crystal faces of one of its polymorphs - anatase phase, crystal planes in Poly (Ethylene Glycol) with considerable intensity and in the composite systems the mixture of crystal faces of their precursors isolated and reduction of crystallinity. The TG / DTG suggested increasing the thermal instability of PEG in the composite powders as TiO2 is incorporated into the system. Spectral analysis presented in the infrared overlapping bands for the polymer and metal oxide, reducing the intensity of symmetric stretching of ligand groups in the main chain polymer and angular deformations; were observed using SEM micrographs of the morphological changes suffered by composite systems with the variation of the oxide concentration. Analyses by impedance spectroscopy indicated that the increased conductivity in composite occurs in line with the addition of the metal oxide concentration in the composite system

Otimização de parâmetros mecânicos e microestruturais dos moldes em areia de sílica ligados quimicamente pelo processo de cura a frio em fundição de aço

Surface defects on steel parts borne costs of smelting industries due to the need of rework. Sand molds are frequently used in foundry industries and largely responsible for providing surface defects. This study aims to optimize the levels of the molding process variables to minimize the occurrence of surface defects in steel castings in silica sand molds chemically linked by cold cure process. The methodology used the experimental design with split plot, being considered in the study the resin percentage factors in the mold formulation, addition of iron oxide, type of paint, the paint application method, amount of ink layers, use of hot air along the lines and waiting time of the mold before casting. They were analyzed as response variables erosion defects, sand inclusion, penetration, porosity and surface finish. Tensile strength tests were performed to evaluate the influence of factors on mechanical parameters and the microstructural parameters were carried out the analysis of X-ray diffraction, scanning electron microscopy (SEM) and thermal analysis (TG / DSC / dilatometry). The results elucidate that for the faulty erosion, the only significant factor with a 95% confidence level was the type of ink and the ink alumina-based superior results obtained. For the sand inclusion of defect, there were three significant factors, with best results obtained with alumina-based paint and spray applied using hot air in the mold before casting the metal. For the defect penetration, there were four significant factors, the best results being achieved with 0.8% of resin and addition of iron oxide in the molding formulation, the paint being applied by brush and standby time of 24 hours before leak. For the defect porosity with a 95% confidence level, no significant factors. For the defect surface finish, the best results were achieved with the 0.8% formulation of the resin in the mold and application of the paint brush. To obtain the levels of the factors that optimize all defects simultaneously, we performed a weighted average of the results of each type of fault, concluding that the best levels of the factors were: 0.8% resin and addition of iron oxide in the formulation of the template, application of two coats of paint applied with a brush or spray, using hot air in the mold before casting and 24 hours of waiting ready the mold before casting. These levels of the optimized factors were used in an experiment to confirm that ratified the results, helping to reduce rework and consequently reducing costs of cast steel parts.