Comportamento magnético de compósitos de matriz polimérica com adição de ferritas

Polymer matrix composites offer advantages for many applications due their combination of properties, which includes low density, high specific strength and modulus of elasticity and corrosion resistance. However, the application of non-destructive techniques using magnetic sensors for the evaluation these materials is not possible since the materials are non-magnetizable. Ferrites are materials with excellent magnetic properties, chemical stability and corrosion resistance. Due to these properties, these materials are promising for the development of polymer composites with magnetic properties. In this work, glass fiber / epoxy circular plates were produced with 10 wt% of cobalt or barium ferrite particles. The cobalt ferrite was synthesized by the Pechini method. The commercial barium ferrite was subjected to a milling process to study the effect of particle size on the magnetic properties of the material. The characterization of the ferrites was carried out by x-ray diffraction (XRD), field emission gun scanning electron microscopy (FEG-SEM) and vibrating sample magnetometry (VSM). Circular notches of 1, 5 and 10 mm diameter were introduced in the composite plates using a drill bit for the non-destructive evaluation by the technique of magnetic flux leakage (MFL). The results indicated that the magnetic signals measured in plates with barium ferrite without milling and cobalt ferrite showed good correlation with the presence of notches. The milling process for 12 h and 20 h did not contribute to improve the identification of smaller size notches (1 mm). However, the smaller particle size produced smoother magnetic curves, with fewer discontinuities and improved signal-to-noise ratio. In summary, the results suggest that the proposed approach has great potential for the detection of damage in polymer composites structures

Síntese e caracterização de ferrita ni-zn pelo método dos precursores poliméricos calcinada por energia de microondas

Magnetic ceramics have been widely investigated, especially with respect to intrinsic and extrinsic characteristics of these materials. Among the magnetic ceramic materials of technological interest, there are the ferrites. On the other hand, the thermal treatment of ceramic materials by microwave energy has offered various advantages such as: optimization of production processes, high heat control, low consumption of time and energy among others. In this work were synthesized powders of Ni-Zn ferrite with compositions Ni1- xZnxFe2O4 (0.25 ≤ x ≤ 0.75 mols) by the polymeric precursor route in two heat treatment conditions, conventional oven and microwave energy at 500, 650, 800 and 950°C and its structural, and morphological imaging. The materials were characterized by thermal analysis (TG/ DSC), X-ray diffraction (XRD), absorption spectroscopy in the infrared (FTIR), scanning electron microscopy (SEM), X-ray spectroscopy and energy dispersive (EDS) and vibrating sample magnetometry (VSM). The results of X-ray diffraction confirmed the formation of ferrite with spinel-type cubic structure. The extrinsic characteristics of the powders obtained by microwave calcination and influence significantly the magnetic behavior of ferrites, showing particles ferrimagnéticas characterized as soft magnetic materials (soft), is of great technological interest. The results obtained led the potential application of microwave energy for calcining powders of Ni-Zn ferrite

Estudo da síntese e propriedade magnética de ferritas de manganês/cobalto dopadas com níquel

For the chemical method of synthesis of co-precipitation were produced ferrite powders manganese-cobalt equal stoichiometric formula Mn (1-x) Co (x) Fe2O4, for 0 < x < 1, first reagent element using as the hydroxide ammonium and second time using sodium hydroxide. The obtained powders were calcined at 400 ° C, 650 ° C, 900 ° C and 1150 ° C in a conventional oven type furnace with an air atmosphere for a period of 240 minutes. Other samples were calcined at a temperature of 900 ° C in a controlled atmosphere of argon, to evaluate the possible influence of the atmosphere on the final results the structure and morphology. The samples were also calcined in a microwave oven at 400 ° C and 650 ° C for a period of 45 minutes possible to evaluate the performance of this type of heat treatment furnace. It was successfully tested the ability of this group include isomorphic ferrite with the inclusion of nickel cations in order to evaluate the occurrence of disorder in the crystalline structures and their changes in magnetic characteristics.To identify the structural, morphological, chemical composition and proportions, as well as their magnetic characteristics were performed characterization tests of X-ray diffraction (XRD), scanning electron microscopy (SEM), transmission electron microscopy (TEM), energy dispersive spectroscopy (EDX), thermogravimetric (TG), vibrating sample magnetometry (MAV) and Mössbauer spectroscopy. These tests revealed the occurrence of distortion in the crystal lattice, changes in magnetic response, occurrence of nanosized particles and superparamagnetism

Efeito Kerr magneto-óptico; Ressonância ferromagnética; Acoplamento bilinear; Acoplamento biquadrático

In this work, we investigated the magnetic properties of a monocrystalline Fe thin film and of Fe(80 Å)/Cr(t)/Fe(80 Å) tri-layers, with the nonmagnetic metallic Cr spacer layer thickness varying between 9 Å < t < 40 Å. The samples were deposited by the DC Sputtering on Magnesium Oxide (MgO) substrates, with (100) crystal orientation. For this investigation, experimental magneto-optical Kerr effect (MOKE) magnetometry and ferromagnetic resonance (FMR) techniques were employeed. In this case, these techniques allowed us to study the static and dynamical magnetization properties of our tri-layers. The experimental results were interpreted based on the phenomenological model that takes into account the relevant energy terms to the magnetic free energy to describe the system behavior. In the case of the monocrystalline Fe film, we performed an analytical discussion on the magnetization curves and developed a numerical simulation based on the Stoner-Wohlfarth model, that enables the numerical adjustment of the experimental magnetization curves and obtainment of the anisotropy field values. On the other hand, for the tri-layers, we analyzed the existence of bilinear and biquadratic couplings between the magnetizations of adjacent ferromagnetic layers from measurements of magnetization curves. With the FMR fields and line width angular dependencies, information on the anisotropy in three layers was obtained and the effects of different magnetic relaxation mechanisms were evidenced. It was also possible to observe the dependence of the epitaxy of the multilayers with growth and sputtering parameters. Additionally it was developed the technique of AC magnetic susceptibility in order to obtain further information during the investigation of magnetic thin films

Anisotropia magnética (110) em Nanofilmes de Permalloy sobre MgO(100)

The study and fabrication of nanostructured systems composed of magnetic materials has been an area of great scientific and technological interest. Soft magnetic materials, in particular, have had great importance in the development of magnetic devices. Among such materials we highlight the use of alloys of Ni and Fe, known as Permalloy. We present measurement results of structural characterization and magnetic films in Permalloy (Ni81Fe19), known to be a material with high magnetic permeability, low coercivity and small magneto- crystalline anisotropy, deposited on MgO (100) substrates. The Magnetron Sputtering technique was used to obtain the samples with thicknesses varying between 9 150 nm. The techniques of X- ray Diffraction at high and low angle were employed to confirm the crystallographic orientation and thickness of the films. In order to investigate the magnetic properties of the films the techniques of Vibrant Sample Magnetometry (VSM), Ferromagnetic Resonance (FMR) and Magnetoimpedance were used. The magnetization curves revealed the presence of anisotropy for the films of Py/MgO (100), where it was found that there are three distinct axis - an easy-axis for θH = 0°, a hard-axis for θH = 45° and an intermediate for θH = 90°. The results of the FMR and Magnetoimpedance techniques confirm that there are three distinct axes, that is, there is a type C2 symmetry. Then we propose, for these results, the interpretation of the magnetic anisotropy of Py/MgO ( 100 ) is of type simple C2, ie a cubic magnetic anisotropy type ( 110 )

Otimização da síntese de nanoferritas de nizn dopada com cobre e cobalto

Different compositions of Ni0,5-xCuxZn0,5Fe2O4 and Ni0,5-xCoxZn0,5Fe2O4 0 ≤ x ≤ 0.3 were synthesized ferrite y the citrate precursor method. The stoichiometric compositions were calcined in air at 350°C and then pressed into pellets and toroids. The pressed samples were sintered at temperatures of 1000, 1050 and 1100°C/3h in air control at the speed of heating and cooling. The calcined powders were characterized by XRD, TGA / DTG, FTIR, SEM and vibrating sample magnetometry (VSM) and the sintered samples by XRD, SEM, MAV, density and measurements of permeability and magnetic losses. There was pure phase formation ferrimagnetism applied at all temperatures except for A-I composition at all sintering temperatures and A-II only at a temperature of 1100°C. Crystallite sizes were obtained by Rietveld analysis, nanometer size from 11 to 20 nm for the calcined powders. For SEM, the sintered samples showed grain size between 1 and 10 micrometers. Bulk density (ρ) of sintered material presented to the Families almost linear behavior with increasing temperature and a tendency to decrease with increasing concentration of copper, different behavior of the B Family, where the increase in temperature decreased the density. The magnetic measurements revealed the powder characteristics of a soft ferrimagnetic material. Two processes of magnetization were considered, the superparamagnetism at low temperatures (350°C) and the formation of magnetic domains at higher temperatures. Obtaining the best parameters for P and B-II magnetic ferrites at high temperatures. The sintered material at 1000°C showed a relative permeability (μ) from 50 to 800 for the A Family and from 10 to 600 for the B Family. The samples sintered at 1100°C, B Family showed a variation from 10 to 1000 and the magnetic loss (tan δ) of A and B Families, around of 1. The frequency response of the toroidal core is in the range of 0.3 kHz. Several factors contribute to the behavior of microstructure considering the quantities μ and tan δ, such as the grain size, inter-and intragranular porosity, amount of grain boundary and the aspects of the dynamics of domain walls at high frequencies.

Encapsulação de nanopartículas de magnetita em matriz de poli(metacrilato de metilacoácido metacrílico) por processo de polimerização em miniemulsão

Magnetic particles are systems with potential use in drug delivery systems, ferrofluids, and effluent treatment. In many situations, such as in biomedical applications, it is necessary to cover magnetic particles with an organic material, as polymers. In this work, magnetic particles were obtained through covering magnetite particles with poly(methyl methacrylate‐comethacrylic acid) via miniemulsion polymerization process. The resultant materials were characterized X‐ray diffraction (XRD), Fourier Transform infrared spectroscopy (FTIR), thermogravimetric analysis (TGA), zeta potential (��) measurements and vibrating sample magnetometry (VSM). XRD results showed magnetite as the predominant cristalline phase in all samples and that cristallites had nanometric dimensions. Thermogravimetric analysis revealed an increase in polymer thermal stability as a result of magnetite encapsulation. TGA results showed also that the encapsulation efficiency was directly related to nanoparticles s hidrofobicity degree. VSM measurements showed that magnetic polymeric particles were superparamagnetic, so that they may be potentially used for magnetic (bio)separation

Desenvolvimento de sistema magnético polimérico contendo antimicrobianos para tratamento de infecções por Helicobacter pylori

Helicobacter pylori is the main cause of gastritis, gastroduodenal ulcer disease and gastric cancer. The most recommended treatment for eradication of this bacteria often leads to side effects and patient poor compliance, which induce treatment failure. Magnetic drug targeting is a very efficient method that overcomes these drawbacks through association of the drug with a magnetic compound. Such approach may allow such systems to be placed slowed down to a specific target area by an external magnetic field. This work reports a study of the synthesis and characterization of polymeric magnetic particles loaded with the currently used antimicrobial agents for the treatment of Helicobacter pylori infections, aiming the production of magnetic drug delivery system by oral route. Optical microscopy, scanning electron microscopy, transmission electron microscopy, x-ray powder diffraction, nitrogen adsorption/desorption isotherms and vibrating sample magnetometry revealed that the magnetite particles, produced by the co-precipitation method, consisted of a large number of aggregated nanometer-size crystallites (about 6 nm), creating superparamagnetic micrometer with high magnetic susceptibility particles with an average diameter of 6.8 ± 0.2 μm. Also, the polymeric magnetic particles produced by spray drying had a core-shell structure based on magnetite microparticles, amoxicillin and clarithromycin and coated with Eudragit® S100. The system presented an average diameter of 14.2 ± 0.2 μm. The amount of magnetite present in the system may be tailored by suitably controlling the suspension used to feed the spray dryer. In the present work it was 2.9% (w/w). The magnetic system produced may prove to be very promising for eradication of Helicobacter pylori infections

Estudo geológico e geofísico da falha de carnaubais, Bacia Potiguar-RN, e implicações neotectônicas

The segment of Carnaubais Fault located in the southeasthern portion of Guamaré Graben (Potiguar Basin) was studied. Several structures were detected and some of them strongly suggest that the last movements in Carnaubais Fault are of Neotectonic age. The study comprises an integrated interpretation of geologic, geomorphologic and geophysical data (gravimetry, magnetometry, resistivity, and self potential methods). According to the size of the studied areas, two approaches were used in this research. The first approach is of a regional nature and was conducted in an area, hereafter named Regional Area, having approximately 6,000 km2 and localized in the northern portion of Rio Grande do Norte state, around Macau city. The second approach comprises detailled studies of two small areas inside the Regional Area: the Camurupim and São Bento areas. Gravimetric and topographic data were used in the Regional Area. A separation into regional and residual components were conducted both on gravimetric and topographic data. The interpretation of the residual component of the gravimetric data allows a precise mapping of the borders of the Guamaré Graben. The regional component features of the topographic data are controlled by the pair of conjugate faults composed by the Carnaubais Fault (NE direction) and the Afonso Bezerra Fault (NW direction). On the other hand, the residual component of the topographic data shows that river valleis of NW direction are sharply interrupted where they intersect Carnaubais Fault. This fact is interpreted as an evidency that the last significant moviments occured in the Carnaubais Fault. Geologic, geomorphologic and geophysical data (magnetometry, resistivity, and self potential methods) were used in the Camurupim Area. The geologic mapping allows to identify five lithophacies unities. The first two unities (from base to top) were interpreted as composing a marine (or transitional) depositional sequency while the other were interpreted is composing a continental depositional sequence. The two sequences are clearly separated of an erosional discordance. The unities grouped in the marine sequence are composed by calcarenites (Unity A) and mudstones (Unity B). Unity A was deposited in a shalow plataform while Unity B, in a tidal flat. The unities grouped in the continental sequence are composed of conglomerate (Unity C) and sandstones (Unities D and E). Unities C and D are fluvial deposits while unity E is an eolian deposit. Unities A and B can be stratigraphycally correlated with Guamaré Formation. Unities C and D present three possible correlations. They may be correlated with Tibau Formation; or with Barreiras Formation; or with a clastic sediment deposit, commonly found in some rivers of Rio Grande do Norte state, and statigraphycally positioned above Barreiras Formation. Based on the decrease of the grain sizes from base to top both on unities C and D, it is proposed that these unities are correlated with the clastic sediment above mentioned. In this case, these unities would have, at least, Pleistocenic age. Finally, it is proposed that Unity E represent an eolian deposit that sufferred recent changes (at least in the Quaternary). The integrated interpretation of hydrographic, morphologic and geophysical data from Camurupim Area shows that Carnaubais Fault is locally composed by a system of several paralel subvertical faults. The fault presenting the larger vertical slip controls the valley of Camurupim river and separates the area in two blocks; in the nothern block the top of the Jandaira limestone is deeper than in the southern block. In addition, at least one of the faults in the northern block is cutting the whole sedimentary section. Because unities C , D, and/or E may be of Quaternary age, tectonic moviments possibly occured in Carnaubais Fault during this period. Detailled geologic mapping were conducted in beachrocks found in São Bento Area. This area is located at the intersection of the coast line with the Carnaubais Fault. The detected structures in the beachrocks are very similar to those caused by fragile deformations. The structures mapped in the beachrocks are consistent with a stress field with maximun compressional stress in E-W direction and extensional stress in the N-S direction. Since the Carnaubais Fault has a NE direction, it is optimally positioned to suffer tectonic movements under the action of such stress field. In addition, the shape of the coastal line appear to be controlled by the Carnaubais Fault. Furthemore, the observed structures in Camurupim Área are consistent with this stress field. These facts are interpreted as evidences that Carnaubais Fault and beachrocks suffered coupled tectonic movements. These moviments are of Neotectonic age because the beachrocks present ages less than 16,000 years

analise da dispersao de ondas de superficie na provincia borborema, Nordeste do Brasil

The Borborema Province, Northeastern Brazil, had its internal structure investigated by different geophysical methods like gravity, magnetics and seismics. Additionally, many geological studies were also carried out to define the structural domains of this province. Despite the plethora of studies, there are still many important open aspects about its evolution. Here, we study the velocity structure of S-wave in the crust using dispersion of surface waves. The dispersion of surface waves allows an estimate of the average thickness of the crust across the region between the stations. The inversion of the velocity structure was carried out using the inter-station dispersion of surface waves of Rayleigh and Love types. The teleseismic events are mainly from the edges of the South and North American plates. The period of data collection occurred between 2007 and 2010 and we selected 7 events with magnitude above 5.0 MW and up to 40 km depth. The difference between the events back-azimuths and the interstation path was not greater than 10. We also know the depth of the Moho, results from Receiver Functions (Novo Barbosa, 2008), and use those as constrains in inversion. Even using different parameterizations of models for the inversion, our results were very similar the mean profiles velocity structure of S-wave. In pairs of stations located in the Cear´a Central Domain Borborema the province, there are ranges of depths for which the velocities of S are very close. Most of the results in the profile near the Moho complicate their interpretation at that depth, coinciding with the geology of the region, where there are many shear zones. In particular, the profile that have the route Potiguar Bacia in inter-station, had low velocities in the crust. We combine these results to the results of gravimetry and magnetometry (Oliveira, 2008) and receptor function (Novo Barbosa, 2008). We finally, the first results on the behavior of the velocity structure of S-wave with depth in the Province Borborema

Produção e estudo de multicamadas magnéticas em substrato flexível

Magnetic multilayers are the support for the production of spintronic devices, representing great possibilities for miniaturized electronics industry. having the control to produce devices as well as their physical properties from simple multilayer films to highly complex at the atomic scale is a fundamental need for progress in this area, in recent years has highlighted the production of organic and flexible spintronic devices. Because of this trend, the objective of this work was to produce magnetic multilayers deposited on flexible substrate using magnetron sputtering dc technique. Three sets of samples were prepared. The first set composed of the trilayer type CoFe=Cu(t)=CoFe with different thickness of the metallic spacer. The second set consists of two multilayer subgroups, CoFe=Cu in the presence of IrMn layer as a buffer and the next multilayer as cap layer. The third set consisting of non-magnetostrictive multilayer permalloy (Py=Ta and Py=Ag) on flexible substrate and glass. The magnetic properties, were investigated by magnetometry measurements, ferromagnetic resonance and magnetoimpedance (MI), measurements were carried out at room temperature with the magnetic field always applied on the sample plane. For structural analysis, the diffraction X-ray was used. The results of the trilayer showed a high uniaxial anisotropy field for the sample with a spacer of 4.2 nm. For the multilayer in the presence of IrMn layer as the buffer, the study of static and dynamic magnetic properties showed isotropic behavior. For the multilayer in the presence of IrMn layer as a cap, the results of static magnetic properties of the magnetic behavior exhibited a spin valve structure type. However there was a disagreement with results of ferromagnetic resonance measurements, which was justified by the contribution of the unstable and stable grain to the rotatable anisotropy and Exchange bias in ferromagneticantiferromagnetic interface. The third serie of samples showed similar results behavior for the MI Ag multilayers spacer in both substrates. There are also significant MI changes with the Ta spacer, possible associated with the compressive stress on the flexible substrate sample.

Comportamento magnético de compósitos de matriz polimérica com adição de ferritas

Polymer matrix composites offer advantages for many applications due their combination of properties, which includes low density, high specific strength and modulus of elasticity and corrosion resistance. However, the application of non-destructive techniques using magnetic sensors for the evaluation these materials is not possible since the materials are non-magnetizable. Ferrites are materials with excellent magnetic properties, chemical stability and corrosion resistance. Due to these properties, these materials are promising for the development of polymer composites with magnetic properties. In this work, glass fiber / epoxy circular plates were produced with 10 wt% of cobalt or barium ferrite particles. The cobalt ferrite was synthesized by the Pechini method. The commercial barium ferrite was subjected to a milling process to study the effect of particle size on the magnetic properties of the material. The characterization of the ferrites was carried out by x-ray diffraction (XRD), field emission gun scanning electron microscopy (FEG-SEM) and vibrating sample magnetometry (VSM). Circular notches of 1, 5 and 10 mm diameter were introduced in the composite plates using a drill bit for the non-destructive evaluation by the technique of magnetic flux leakage (MFL). The results indicated that the magnetic signals measured in plates with barium ferrite without milling and cobalt ferrite showed good correlation with the presence of notches. The milling process for 12 h and 20 h did not contribute to improve the identification of smaller size notches (1 mm). However, the smaller particle size produced smoother magnetic curves, with fewer discontinuities and improved signal-to-noise ratio. In summary, the results suggest that the proposed approach has great potential for the detection of damage in polymer composites structures

Síntese e caracterização de ferrita ni-zn pelo método dos precursores poliméricos calcinada por energia de microondas

Magnetic ceramics have been widely investigated, especially with respect to intrinsic and extrinsic characteristics of these materials. Among the magnetic ceramic materials of technological interest, there are the ferrites. On the other hand, the thermal treatment of ceramic materials by microwave energy has offered various advantages such as: optimization of production processes, high heat control, low consumption of time and energy among others. In this work were synthesized powders of Ni-Zn ferrite with compositions Ni1- xZnxFe2O4 (0.25 ≤ x ≤ 0.75 mols) by the polymeric precursor route in two heat treatment conditions, conventional oven and microwave energy at 500, 650, 800 and 950°C and its structural, and morphological imaging. The materials were characterized by thermal analysis (TG/ DSC), X-ray diffraction (XRD), absorption spectroscopy in the infrared (FTIR), scanning electron microscopy (SEM), X-ray spectroscopy and energy dispersive (EDS) and vibrating sample magnetometry (VSM). The results of X-ray diffraction confirmed the formation of ferrite with spinel-type cubic structure. The extrinsic characteristics of the powders obtained by microwave calcination and influence significantly the magnetic behavior of ferrites, showing particles ferrimagnéticas characterized as soft magnetic materials (soft), is of great technological interest. The results obtained led the potential application of microwave energy for calcining powders of Ni-Zn ferrite

Estudo da síntese e propriedade magnética de ferritas de manganês/cobalto dopadas com níquel

For the chemical method of synthesis of co-precipitation were produced ferrite powders manganese-cobalt equal stoichiometric formula Mn (1-x) Co (x) Fe2O4, for 0 < x < 1, first reagent element using as the hydroxide ammonium and second time using sodium hydroxide. The obtained powders were calcined at 400 ° C, 650 ° C, 900 ° C and 1150 ° C in a conventional oven type furnace with an air atmosphere for a period of 240 minutes. Other samples were calcined at a temperature of 900 ° C in a controlled atmosphere of argon, to evaluate the possible influence of the atmosphere on the final results the structure and morphology. The samples were also calcined in a microwave oven at 400 ° C and 650 ° C for a period of 45 minutes possible to evaluate the performance of this type of heat treatment furnace. It was successfully tested the ability of this group include isomorphic ferrite with the inclusion of nickel cations in order to evaluate the occurrence of disorder in the crystalline structures and their changes in magnetic characteristics.To identify the structural, morphological, chemical composition and proportions, as well as their magnetic characteristics were performed characterization tests of X-ray diffraction (XRD), scanning electron microscopy (SEM), transmission electron microscopy (TEM), energy dispersive spectroscopy (EDX), thermogravimetric (TG), vibrating sample magnetometry (MAV) and Mössbauer spectroscopy. These tests revealed the occurrence of distortion in the crystal lattice, changes in magnetic response, occurrence of nanosized particles and superparamagnetism