Análise de falhas em rolamentos por análise de vibração aplicado a aerogeradores

With the heavy use of bearings in various segments of the industry, there are a large number of necessary interruptions in industrial processes to perform maintenance on these devices, with the case study wind turbines. The growth of the wind energy sector, encouraged to conduct research that helps to solve this problem. To contribute to predictive maintenance has been carried out a signal analysis using techniques which allow detection and location of the problem in order to prevent accidents caused and losses due to unexpected equipment failures, whereas low system rotation complicates the detection of the failure. To work around this problem, there was the indication of standard signals for defects in the bearings, making diagnosis of possible failures. With this diagnosis can be performed predictive maintenance, identifying the failure of the system that were tested, such as the introduction of grains of sand in the bearing, wear on the outer race of the bearing and bearing rust. By processing signals it is possible to construct graphs developing a mapping of defects by different peaks in the frequency band.

Desgaste de polímeros estruturais de engenharia em contato de deslizamento com cilindro metálico

Present work proposed to map and features the wear mechanisms of structural polymers of engineering derived of the sliding contact with a metallic cylindrical spindle submitted to eccentricity due to fluctuations in it is mass and geometric centers. For this it was projected and makes an experimental apparatus from balancing machine where the cylindrical counterbody was supported in two bearings and the polymeric coupon was situated in a holder with freedom of displacement along counterbody. Thus, the experimental tests were standardized using two position of the two bearings (Fixed or Free) and seven different positions along the counterbody, that permit print different conditions to the stiffness from system. Others parameters as applied normal load, sliding velocity and distance were fixed. In this investigation it was used as coupon two structural polymers of wide quotidian use, PTFE (polytetrafluroethylene) and PEEK (poly-ether-ether-ketone) and the AISI 4140 alloy steel as counterbody. Polymeric materials were characterized by thermal analysis (thermogravimetric, differential scanning calorimetry and dynamic-mechanical), hardness and rays-X diffractometry. While the metallic material was submitted at hardness, mechanical resistance tests and metallographic analysis. During the tribological tests were recorded the heating response with thermometers, yonder overall velocity vibration (VGV) and the acceleration using accelerometers. After tests the wear surface of the coupons were analyzed using a Scanning Electronic Microscopy (SEM) to morphological analysis and spectroscopy EDS to microanalysis. Moreover the roughness of the counterbody was characterized before and after the tribological tests. It was observed that the tribological response of the polymers were different in function of their distinct molecular structure. It were identified the predominant wear mechanisms in each polymer. The VGV of the PTFE was smaller than PEEK, in the condition of minimum stiffness, in function of the higher loss coefficient of that polymer. Wear rate of the PTFE was more of a magnitude order higher than PEEK. With the results was possible developed a correlation between the wear rate and parameter (E/ρ)1/2 (Young modulus, E, density, ρ), proportional at longitudinal elastic wave velocity in the material.