Produção e estudo de multicamadas magnéticas em substrato flexível

Magnetic multilayers are the support for the production of spintronic devices, representing great possibilities for miniaturized electronics industry. having the control to produce devices as well as their physical properties from simple multilayer films to highly complex at the atomic scale is a fundamental need for progress in this area, in recent years has highlighted the production of organic and flexible spintronic devices. Because of this trend, the objective of this work was to produce magnetic multilayers deposited on flexible substrate using magnetron sputtering dc technique. Three sets of samples were prepared. The first set composed of the trilayer type CoFe=Cu(t)=CoFe with different thickness of the metallic spacer. The second set consists of two multilayer subgroups, CoFe=Cu in the presence of IrMn layer as a buffer and the next multilayer as cap layer. The third set consisting of non-magnetostrictive multilayer permalloy (Py=Ta and Py=Ag) on flexible substrate and glass. The magnetic properties, were investigated by magnetometry measurements, ferromagnetic resonance and magnetoimpedance (MI), measurements were carried out at room temperature with the magnetic field always applied on the sample plane. For structural analysis, the diffraction X-ray was used. The results of the trilayer showed a high uniaxial anisotropy field for the sample with a spacer of 4.2 nm. For the multilayer in the presence of IrMn layer as the buffer, the study of static and dynamic magnetic properties showed isotropic behavior. For the multilayer in the presence of IrMn layer as a cap, the results of static magnetic properties of the magnetic behavior exhibited a spin valve structure type. However there was a disagreement with results of ferromagnetic resonance measurements, which was justified by the contribution of the unstable and stable grain to the rotatable anisotropy and Exchange bias in ferromagneticantiferromagnetic interface. The third serie of samples showed similar results behavior for the MI Ag multilayers spacer in both substrates. There are also significant MI changes with the Ta spacer, possible associated with the compressive stress on the flexible substrate sample.

Estudo da viabilização do uso da mistura híbrida ferrocarbonila / ferrita de NI0,5Zn0,5Fe2o4 como material absorvedor de radiação eletromagnética

Were synthesized ferrites of NiZn on systems Ni0,5Zn0,5Fe2O4, the precursors citrate method. The decomposition of the precursors was studied by thermogravimetric analysis and spectroscopy in the infrared region, the temperature of 350°C/3h. The evolution of the phases formed after calcinations at 350ºC/3h, 600, 1000 and 1100ºC/2h was accompanied by X-ray diffraction using the Rietveld refinement method for better identification os structures formed. Was observed for samples calcined at different temperatures increased crystallinity with increasing calcination temperature, being observed for the samples calcined at 900 and 1100 º C/2h was the precipitation of a secondary phase, the phase hematite. The ferrocarbonila of industrial origin was analyzed by X-ray diffraction and Rietveld for the identification of its structure. The carbonyl iron was added NiZn ferrite calcined at 350ºC/3h, 600, 900, 1000 and 1100ºC/2h to the formation of hybrid mixtures. They were then analyzed by Xray diffraction and Rietveld. The NiZn ferrite and ferrocarbonila as well as the hybrid mixtures were subjected to analysis of scanning electron microscopy, magnetic measurements and reflectivity. The magnetic measurements indicated that the ferrite, the ferrocarbonila, as well as hybrid mixtures showed characteristics of soft magnetic material. The addition of ferrocarbonila in all compositions showed an increase in the results of magnetic measurements and reflectivity. Best result was observed in the increase of the magnetization for the hybrid mixture of Ferrocarbonila / ferrite of NiZn calcined at 600ºC/2h. The mixture Ferrocarbonila / ferrite calcined 1000°C/2h presented better absorption of electromagnetic radiation in the microwave

Estudo das características magnéticas e absorvedoras das ferritas de nizn, niznmn, mnzn, nimg, nicuzn e nicuznmg obtidas via método do citrato precursor

Were synthesized systems Ni0,5Zn0,5Fe2O4, i0,2Zn0,5Mn0,3Fe2O4, Mn0,5Zn0,5Fe2O4, Ni0,5Mg0,5Fe2O4, Ni0,2Cu0,3Zn0,5Fe2O4 and Ni0,2Cu0,3Zn0,5Mg0,08Fe2O4, the precursors citrate method. The decomposition of the precursors was studied by thermogravimetric analysis and spectroscopy in the infrared region, the temperature of 350°C/3h. The evolution of the phases formed after calcinations at 350, 500, 900 and 1100ºC/3h was accompanied by X-ray diffraction using the Rietveld refinement to better identify the structures formed. The materials were also analyzed by scanning electron microscopy, magnetic measurements and analysis of the reflectivity of the material. The samples calcined at different temperatures showed an increase of crystallinity with increasing calcination temperature, verifying that for some compositions at temperatures above 500°C precipitates of second phase such as hematite and CuO. The compositions of manganese present in the structure diffusion processes slower due to the ionic radius of manganese is greater than for other ions substitutes, a fact that delays the stabilization of spinel structure and promotes the precipitation of second phase. The compositions presented with copper precipitation CuO phase at a temperature of 900 and 1100ºC/3h This occurs according to the literature because the concentration of copper in the structure is greater than 0.25 mol%. The magnetic measurements revealed features of a soft ferrimagnetic material, resulting in better magnetic properties for the NiZn ferrite and NiCuZnMg at high temperatures. The reflectivity measurements showed greater absorption of electromagnetic radiation in the microwave band for the samples calcined at 1100ºC/3h, which has higher crystallite size and consequently the formation of multi-domain, increasing the magnetization of the material. The results of absorption agreed with the magnetic measurements, indicating among the ferrites studied, those of NiZn and NiCuZnMg as better absorbing the incident radiation.