Red marine algae of the genus Gracilaria synthesize sulfated polysaccharides (PS) bioactive. But many of these PS were not properly assessed, as is the case of PS synthesized by edible seaweed Gracilaria birdiae. Previous studies showed that sulfated galactans this alga has anti-inflammatory effect. In this work, a galactan (GB) of G. birdiae was obtained and evaluated by different tests. GB showed anticoagulant activity in APTT assay. GB showed no toxicity to normal cells (3T3), but inhibited the survival of cells of adenocarcinoma of the cervix (HeLa) and human pancreatic cancer (Panc-1) 80% (1.5 mg / ml). GB was not able to hijack the OH radical or the superoxide radical. However, showed activity electron donor in two different tests and presented iron chelator activity (70% and 1.0 mg / ml) and Copper (70% at 0.5 mg / ml). The presence of a higher GB promotes formation of crystals of calcium oxalate dihydrate small size, which is less aggressive, because GB is able to interact with and stabilize the crystal that form. Furthermore, GB (2.0 mg / mL) was not cytotoxic to human renal cells (HEK-293). The data lead us to propose that GB has a great potential for the treatment of urolithiasis

Effect of cooling rate on properties of plasma nitrided AISI 1010 steel

In this work, AISI 1010 steel samples were plasma nitrided into 20% N 2 100 Pa and 400 Pa for N 2 and H 2 , respectively), temperatures of 500 and 580 °C, during 2 h. Three different procedures for cooling were accomplished after nitriding. In the first procedure the cooling occurred naturally, that is, the sample was kept on substrate holder. In the second one the sample was pulled off and cooling in a cold surface. Finally, in the third cooling process the sample was pulled off the substrate holder down into special reservoir filled with oil held at ambient temperature. The properties of the AISI 1010 steel samples were characterized by optical and electron microscopy, X-ray diffraction, Mössbauer spectroscopy and microhardness tests. Thermal gradient inside the sample kept on substrate holder during cooling process was measured by three inserted thermocouples at different depths. When samples were cooled rapidly the transformation of ϵ-Fe 2 − 3 N to γ′-Fe 4 N was inhibited. Such effect is indicated by the high concentration of ϵ-Fe compound zone. To get solid state solution of nitrogen in the diffusion zone, instead of precipitates of nitride phases, the cooling rate should be higher than a critical value of about 0.95 °C/s. When this value is reached at any depth of the diffusion zone, two distinct diffusion zones will appear. Temperature gradients were measured inside the samples as a consequence of the plasma treatment. It's suggested the need for standardization of the term “treatment temperature” for plasma treatment because different nitrided layer properties could be reported for the same “treatment temperature”.