Effect of cooling rate on properties of plasma nitrided AISI 1010 steel

In this work, AISI 1010 steel samples were plasma nitrided into 20% N 2 100 Pa and 400 Pa for N 2 and H 2 , respectively), temperatures of 500 and 580 °C, during 2 h. Three different procedures for cooling were accomplished after nitriding. In the first procedure the cooling occurred naturally, that is, the sample was kept on substrate holder. In the second one the sample was pulled off and cooling in a cold surface. Finally, in the third cooling process the sample was pulled off the substrate holder down into special reservoir filled with oil held at ambient temperature. The properties of the AISI 1010 steel samples were characterized by optical and electron microscopy, X-ray diffraction, Mössbauer spectroscopy and microhardness tests. Thermal gradient inside the sample kept on substrate holder during cooling process was measured by three inserted thermocouples at different depths. When samples were cooled rapidly the transformation of ϵ-Fe 2 − 3 N to γ′-Fe 4 N was inhibited. Such effect is indicated by the high concentration of ϵ-Fe compound zone. To get solid state solution of nitrogen in the diffusion zone, instead of precipitates of nitride phases, the cooling rate should be higher than a critical value of about 0.95 °C/s. When this value is reached at any depth of the diffusion zone, two distinct diffusion zones will appear. Temperature gradients were measured inside the samples as a consequence of the plasma treatment. It's suggested the need for standardization of the term “treatment temperature” for plasma treatment because different nitrided layer properties could be reported for the same “treatment temperature”.

Estudo da síntese e propriedade magnética de ferritas de manganês/cobalto dopadas com níquel

For the chemical method of synthesis of co-precipitation were produced ferrite powders manganese-cobalt equal stoichiometric formula Mn (1-x) Co (x) Fe2O4, for 0 < x < 1, first reagent element using as the hydroxide ammonium and second time using sodium hydroxide. The obtained powders were calcined at 400 ° C, 650 ° C, 900 ° C and 1150 ° C in a conventional oven type furnace with an air atmosphere for a period of 240 minutes. Other samples were calcined at a temperature of 900 ° C in a controlled atmosphere of argon, to evaluate the possible influence of the atmosphere on the final results the structure and morphology. The samples were also calcined in a microwave oven at 400 ° C and 650 ° C for a period of 45 minutes possible to evaluate the performance of this type of heat treatment furnace. It was successfully tested the ability of this group include isomorphic ferrite with the inclusion of nickel cations in order to evaluate the occurrence of disorder in the crystalline structures and their changes in magnetic characteristics.To identify the structural, morphological, chemical composition and proportions, as well as their magnetic characteristics were performed characterization tests of X-ray diffraction (XRD), scanning electron microscopy (SEM), transmission electron microscopy (TEM), energy dispersive spectroscopy (EDX), thermogravimetric (TG), vibrating sample magnetometry (MAV) and Mössbauer spectroscopy. These tests revealed the occurrence of distortion in the crystal lattice, changes in magnetic response, occurrence of nanosized particles and superparamagnetism

Síntese e caracterização estrutural e magnética da ferrita de cálcio

The calcium ferrite (Ca2Fe2O5) has a perovskite-type structure with oxygen deficiency and is used as a chemical catalyst. With the advent of nanoscience and nanotechnology, methods of preparation, physical and chemical characterizations, and the technological applications of nanoparticles have attracted great scientific interest. Calcium nanostructured ferrites were produced via high-energy milling, with subsequent heat treatment. The milling products were characterized by X-ray diffraction, magnetization and Mössbauer spectroscopy. Samples of the type Ca2Fe2O5 were obtained from the CaCO3 and Fe2O3 powder precursors, which were mixed stoichiometrically and milled for 10h and thermally treated at 700ºC, 900ºC and 1100ºC. The Mössbauer spectra of the treated samples were adjusted three subespectros: calcium ferrite (octahedral and tetrahedral sites) and a paramagnetic component, related to very small particles of calcium ferrite, which are in a superparamagnetic state. For samples beats in an atmosphere of methyl alcohol, there is a significant increase in area associated with the paramagnetic component. Hysteresis curves obtained are characteristic of a weak ferromagnetic-like material

Superparamagnetismo em Jacobsitas sintéticas

In this experimental study sintetic samples of Jacobsites (MnFe2O4) were synthesized by the Pechini method and calcined within ambient atmosphere and afterwards in the vacuum from 400 to 700ºC, the range of calcination temperatures. The X-Ray Diffraction (XRD) and the Scanning Electronic Microscopy (SEM) analysis have shown that the samples treated at 400ºC temperature are composed by a simple type of spinel phase, with a crystallite size of 8:8nm for the sample calcined in ambient atmosphere and 20; 1nm for the sample treated in the vacuum, showing that the cristallite average size can be manipulated by the atmosphere control. The hysteresis loops for the sample calcined at 400ºC in ambient atmosphere reveal features of superparamagnetic behavior with magnetization 29:3emu=g at the maximum field of 1:2T. The sample calcined in 400oC under vacuum show magnetization = 67emu=g at the maximum field of 1:5T. The sample treated at 500oC, under ambient atmosphere, has shown besides the spinel phase, secondary phases of hematite (Fe2O3) and bixbyite (FeMnO3). The hysteresis loops demonstrate a sharp drop of the magnetization compared to the previous sample. The analysis has revealed that for the samples treated in higher temperatures (600ºC and 700ºC) its observed the absence of the spinel phase and the maintenance of the bixbyite and hematite. The hysteresis loops for those samples in accordance to the external magnetic field are straight lines crossing the origin, consistent with the antiferromagnetic behavior of the phases.The Mössbauer espectroscopy show to the sample calcined at 400ºC within ambiente atmosphere two sextet and one doublet. The two sextets are assigned to the hyperfine fields related to the magnetic deployment in the nuclei of Fe3+ ions, at the tetraedric and octaedric sites. The doublet is assigned to superparamagnetic behavior of the particles with smaller diameter than dc . Now the sample calcined at 400ºC under vacuum only show two sextet

Propriedades magnéticas de ortoferritas de lantânio dopadas com estrôncio

Samples of lanthanum Ortoferrites doped with strontium were synthesized in a single phase by the sol-gel method. Two samples were prepared, one by varying the concentration of strontium in lanthanum ortoferrites La1−xSrxFeO3−δ with (0 ≤ x ≤ 0.5), and another batch of samples of type, La1/3Sr2/3FeO3−δ, now varying only the temperature of calcination. Our samples were obtained by Pechini method and sintered in air and oxygen atmospheric. Their crystal structures were determined by x-ray diraction (XRD), scanning electron microscopy (SEM), where we observed that the samples (0 ≤ x ≤ 0.3) have orthorhombic symmetry and the volume of the single cell decreases with the increasing of concentration of strontium. For x = 0.5 it is only observed the simple phase when that is sintered in O2 atmospheric. Their magnetic characteristics were obtained by the Mössbauer spectroscopy and magnetic measurements. The magnetization measurements for samples La1−xSrxFeO3−δ with (0 ≤ x ≤ 0.5) revealed that the magnetization decreases with increasing concentration of strontium, but for the sample x = 0.4 the magnetization shows a high coercive field and a ferrimagnetic behavior, which is attributed to a small amount of strontium hexaferrite. As for the samples La1/3Sr2/3FeO3−δ calcined between 800 oC e 1200 oC. The hysteresis curves revealed two distinct behaviors: an declined antiferromagnetic behavior (Canted) for samples calcined between 800 oC and 1000 oC and a paramagnetic behavior for the samples calcined at 1100 oC e 1200 o C. Thermal hysteresis and sharp peaks around the Néel temperature (TN), over the curves of specific heat as a function of temperature was only observed in calcined samples with 1100 oC and 1200 oC. This eect is attributed to the charge ordering. These results indicate that the charge ordering occurs only in the samples without oxygen deficiency. Magnetic measurements as a function of temperature are also in agreement with this interpretation

Ordenamento de cargas e propriedades magnéticas de ortoferritas de lantânio dopadas com estrôncio

Coordenação de Aperfeiçoamento de Pessoal de Nível Superior (CAPES)

Ordenamento de cargas e propriedades magnéticas de ortoferritas de lantânio dopadas com estrôncio

Coordenação de Aperfeiçoamento de Pessoal de Nível Superior (CAPES)

Effect of cooling rate on properties of plasma nitrided AISI 1010 steel

In this work, AISI 1010 steel samples were plasma nitrided into 20% N 2 100 Pa and 400 Pa for N 2 and H 2 , respectively), temperatures of 500 and 580 °C, during 2 h. Three different procedures for cooling were accomplished after nitriding. In the first procedure the cooling occurred naturally, that is, the sample was kept on substrate holder. In the second one the sample was pulled off and cooling in a cold surface. Finally, in the third cooling process the sample was pulled off the substrate holder down into special reservoir filled with oil held at ambient temperature. The properties of the AISI 1010 steel samples were characterized by optical and electron microscopy, X-ray diffraction, Mössbauer spectroscopy and microhardness tests. Thermal gradient inside the sample kept on substrate holder during cooling process was measured by three inserted thermocouples at different depths. When samples were cooled rapidly the transformation of ϵ-Fe 2 − 3 N to γ′-Fe 4 N was inhibited. Such effect is indicated by the high concentration of ϵ-Fe compound zone. To get solid state solution of nitrogen in the diffusion zone, instead of precipitates of nitride phases, the cooling rate should be higher than a critical value of about 0.95 °C/s. When this value is reached at any depth of the diffusion zone, two distinct diffusion zones will appear. Temperature gradients were measured inside the samples as a consequence of the plasma treatment. It's suggested the need for standardization of the term “treatment temperature” for plasma treatment because different nitrided layer properties could be reported for the same “treatment temperature”.

Estudo da síntese e propriedade magnética de ferritas de manganês/cobalto dopadas com níquel

For the chemical method of synthesis of co-precipitation were produced ferrite powders manganese-cobalt equal stoichiometric formula Mn (1-x) Co (x) Fe2O4, for 0 < x < 1, first reagent element using as the hydroxide ammonium and second time using sodium hydroxide. The obtained powders were calcined at 400 ° C, 650 ° C, 900 ° C and 1150 ° C in a conventional oven type furnace with an air atmosphere for a period of 240 minutes. Other samples were calcined at a temperature of 900 ° C in a controlled atmosphere of argon, to evaluate the possible influence of the atmosphere on the final results the structure and morphology. The samples were also calcined in a microwave oven at 400 ° C and 650 ° C for a period of 45 minutes possible to evaluate the performance of this type of heat treatment furnace. It was successfully tested the ability of this group include isomorphic ferrite with the inclusion of nickel cations in order to evaluate the occurrence of disorder in the crystalline structures and their changes in magnetic characteristics.To identify the structural, morphological, chemical composition and proportions, as well as their magnetic characteristics were performed characterization tests of X-ray diffraction (XRD), scanning electron microscopy (SEM), transmission electron microscopy (TEM), energy dispersive spectroscopy (EDX), thermogravimetric (TG), vibrating sample magnetometry (MAV) and Mössbauer spectroscopy. These tests revealed the occurrence of distortion in the crystal lattice, changes in magnetic response, occurrence of nanosized particles and superparamagnetism