Novos monômeros obtidos a partir do metacrilato de glicidila, bisfenol A e 4, 4 isopropilidenodicicloexanol : síntese, caracterização estrutural e propriedades de compósitos para utilização em resinas de restauração dental

Nowadays, composite resins are the direct restorative materials more important in dental clinical performance, due to their versatility and aesthetic excellence. Bis-GMA (2,2-bis[4(2-hydroxy-3-metacryloxypropoxy)phenil]propane) is the base monomer more frequently used in restorative composite resins. However, this monomer presents some disadvantages, such as high viscosity and two aromatic rings in its structure that can promote allergic reactions to the humans. In this work, the main purpose was to synthesize new monomers from glycidyl methacrylate to use in dental restorative materials. Structural characterization of the monomers was carried out through FTIR and NMR 1H, and eight composites were produced from the new monomers, by addition of silane-treated alumino silicate particles (inorganic filler) and a photocuring system (camphorquinone and ethyl 4-dimethylaminebenzoate). The composites were analyzed by environmental scanning electronic microscopy and the water sorption and solubility, compressive strength and elastic modulus were determined. A commercial composite resin [Z100 (3M)] was used to comparison effect. The new composites presented general characteristics similar to the commercial ones; however, they didn t present the properties expected. This behavior was attributed to the lower degree of monomer reaction and to the granulometry and size distribution of the mineral filler in the polymeric matrix

Novos monômeros obtidos a partir do metacrilato de glicidila, bisfenol A e 4, 4 isopropilidenodicicloexanol : síntese, caracterização estrutural e propriedades de compósitos para utilização em resinas de restauração dental

Nowadays, composite resins are the direct restorative materials more important in dental clinical performance, due to their versatility and aesthetic excellence. Bis-GMA (2,2-bis[4(2-hydroxy-3-metacryloxypropoxy)phenil]propane) is the base monomer more frequently used in restorative composite resins. However, this monomer presents some disadvantages, such as high viscosity and two aromatic rings in its structure that can promote allergic reactions to the humans. In this work, the main purpose was to synthesize new monomers from glycidyl methacrylate to use in dental restorative materials. Structural characterization of the monomers was carried out through FTIR and NMR 1H, and eight composites were produced from the new monomers, by addition of silane-treated alumino silicate particles (inorganic filler) and a photocuring system (camphorquinone and ethyl 4-dimethylaminebenzoate). The composites were analyzed by environmental scanning electronic microscopy and the water sorption and solubility, compressive strength and elastic modulus were determined. A commercial composite resin [Z100 (3M)] was used to comparison effect. The new composites presented general characteristics similar to the commercial ones; however, they didn t present the properties expected. This behavior was attributed to the lower degree of monomer reaction and to the granulometry and size distribution of the mineral filler in the polymeric matrix

Influência do pré-aquecimento na adaptação marginal de dois materiais seladores de fóssulas e fissuras, analisada através de tomografia de coerência ótica

Among the non-invasive techniques employed in the prevention of caries highlights the sealing pits and fissures which is a conservative maneuver, in order to obliterate them to protect them from attack acid bacteria. Influenced by the studies of pre-heating composite resin, which has experienced great improvement in some of their physical properties, this study aimed to evaluate in vitro the superficial and internal marginal adaptation of different materials and sealants in pre-heating or not. A total of 40 extracted human third molars (n=10) that had their occlusal surfaces prepared to receive sealant. We tested two types of sealing materials: resin sealant (Fluoroshield) and low-viscosity resin (Permaflo), where 50% of previously received heated material and the other half received sealant material at room temperature. All samples were subjected to thermal cycling and pH, simulating a cariogenic oral environment, and later were analyzed appliance OCT (optical coherence tomography). The images obtained alterations were recorded and analyzed statistically. Change was considered as the emergence of bubbles, gaps and cracks in the sealant. Comparisons of the same material, assessing the fact that it is not sealed or preheated material, as well as comparisons between different materials subjected to the same temperature were carried out. The nonparametric Tukey test was used (p < 0,05). The results showed that there was statistically significant difference between both the materials analyzed, as between the situations in which the sealant material was submitted (preheated or not). On the issue of marginal adaptation and internal surface, seen through Optical coherence tomography, may suggest that there is a difference between the use of one type or another of the sealing material analyzed, with superiority attributed to resin Permaflo compared to sealant Fluroshield, telling is the same for the different techniques used

Avaliação da eficiência da técnica de obturação pela compressão hidrùlica vertical após instrumentação automatizada

The purpose of this study was to evaluate through radiographic and microscopic analysis the efficiency of the filling techniques by vertical hidraulic compression after the root canal mechanical instrumentation in vitro as well to evaluate the marginal apical leakage through macroscopic and microscopic analysis. Thirty human mandibular molars were used , they were divided on three groups, these were subdivided on six subgroups with five specimens each, come down to 106 root canals filled. Initially, the teeth were instrumented with Profile system series 29 and filled with two ways: single accessory cone or single cone associated with gutta-percha secundary cone, with Fill Canal sealer or Sealer 26. Completed the filling, the teeth were coated with araldit and finger -nail polish except for the apical 2 mm and dried for 3 hours, thep radiographs were taken of the teeth in orto and disto-radiai directions. Next, the coronal seal was carried out with composite resin photopolymerized and with their process of making impermeable. Teeth of positive controls were used without araldit and finger-nail polish whereas the negative controls were used with total coat of araldit and finger-nail polish. The specimens were placed in 2% Methylene Blue dye for 24 hours and thermocycled for 7 days. Afterwards, sections were made of each tooth at mesial and distal roat, after this the teeth were radiographed at buccolíngual direction for a macroscopic analysis and at buccolingual and mesiodistal directions for assessment of the marginal apical leakage. Cross sections were made 3 mm to 3mm since the tooth apice. The sections obtained for each group were observed with a stereomicroscope to evaluate the quality of the root canal filling and the marginal apical leakage. The results showed that: In the four techniques the marginal dye leakage was present in the apical third; in all groups the quality of the root canal filling in the radiography was better at mesial root canal and the single cone technique showed inefficient when only a single distal root canal was present. In the radiographic evaluation the best quality of the root canal filling was observed in the 1A group (single accessory cone + FiIl Canal), as in the mesial root as in the distal root wich Shcwed twe root canals: when the distaI root had only one canal. the best result was showed by 28 group (single accessory cone associated with secundary cone + Fill Canal) In the macroscopic analysis of longitudinal !eaKage (outside surface). less leakage was showed as In the mesial root as in the distal root in the negative control group (3) followed 2A group (single accessory cone + Sealer 26). When the microscopic analysis of tranversal leakage of both roots (inside surface) was carried out. the groups that showed less dye leakage were the negative control (38) followed the 28 group (single acessory cone associated with secundary cone + Sealer 26). The homogeneity o filling was best noted in the 1 A group (.single accessoty cone + Fill Canal). The groups that showed less dye penetration in the tranversal leakage (total area) were negative control (3B) and 2B

Longitudinal Clinical Evaluation of Undercut Areas and Rest Seats of Abutment Teeth in Removable Partial Denture Treatment

PURPOSE: Adequate preparation of abutment teeth for removable partial denture (RPD) rest seats allows appropriate masticatory force transmission, retention, and stability of supporting structures. It follows that careful preparation will be important for the longevity of the rehabilitation. The present study aimed to clinically evaluate rest seats and undercut areas of abutment teeth in RPD wearers after 2 years of use. MATERIALS AND METHODS: A total of 193 occlusal, incisal, and cingulum rest seats were evaluated in terms of shape, rest adaptation, wear, caries, fractures, and surface type (enamel, composite resin, or amalgam). Two hundred and fourteen undercut areas were evaluated in terms of surface type (enamel or restoration) and integrity. This study was approved by the Research Ethics Committee of the Federal University of Rio Grande do Norte, resolution 196/1996, protocol number 11/05. RESULTS: Intact preparations accounted for 92.2% of the total. Application of the Pearson test (p= 0.289) found no statistically significant differences among the materials on which the rest seats were prepared. For the undercut areas, 20.7% of those obtained on restorative material were nonintact. In addition, Fisher's exact test showed a statistically significant difference (p= 0.001) in surface type; enamel surfaces were shown to be 14 times more stable than restored surfaces. CONCLUSIONS: The results of this study suggest that rest seats are stable, regardless of the material on which they are prepared. Retentive areas were shown to be more stable when they were located in enamel.

Longitudinal Clinical Evaluation of Undercut Areas and Rest Seats of Abutment Teeth in Removable Partial Denture Treatment

PURPOSE: Adequate preparation of abutment teeth for removable partial denture (RPD) rest seats allows appropriate masticatory force transmission, retention, and stability of supporting structures. It follows that careful preparation will be important for the longevity of the rehabilitation. The present study aimed to clinically evaluate rest seats and undercut areas of abutment teeth in RPD wearers after 2 years of use. MATERIALS AND METHODS: A total of 193 occlusal, incisal, and cingulum rest seats were evaluated in terms of shape, rest adaptation, wear, caries, fractures, and surface type (enamel, composite resin, or amalgam). Two hundred and fourteen undercut areas were evaluated in terms of surface type (enamel or restoration) and integrity. This study was approved by the Research Ethics Committee of the Federal University of Rio Grande do Norte, resolution 196/1996, protocol number 11/05. RESULTS: Intact preparations accounted for 92.2% of the total. Application of the Pearson test (p= 0.289) found no statistically significant differences among the materials on which the rest seats were prepared. For the undercut areas, 20.7% of those obtained on restorative material were nonintact. In addition, Fisher's exact test showed a statistically significant difference (p= 0.001) in surface type; enamel surfaces were shown to be 14 times more stable than restored surfaces. CONCLUSIONS: The results of this study suggest that rest seats are stable, regardless of the material on which they are prepared. Retentive areas were shown to be more stable when they were located in enamel.

Compressive strength of dental composites photo-activated with different light tips

The aim of this study was to evaluate the compressive strength of microhybrid (FiltekTM Z250) and nanofilled (FiltekTM Supreme XT) composite resins photo-activated with two different light guide tips, fiber optic and polymer, coupled with one LED. The power density was 653 mW cm−2 when using the fiber optic light tip and 596 mW cm−2 with the polymer. After storage in distilled water at 37 ± 2 "C for seven days, the samples were subjected to mechanical testing of compressive strength in an EMIC universal mechanical testing machine with a load cell of 5 kN and speed of 0.5 mm min−1. The statistical analysis was performed using ANOVA with a confidence interval of 95% and Tamhane’s test. The results showed that the mean values of compressive strength were not influenced by the different light tips (p > 0.05). However, a statistical difference was observed (p < 0.001) between the microhybrid composite resin photo-activated with the fiber optic light tip and the nanofilled composite resin. Based on these results, it can be concluded that microhybrid composite resin photo-activated with the fiber optic light tip showed better results than nanofilled, regardless of the tip used, and the type of the light tip did not influence the compressive strength of either composite. Thus, the presented results suggest that both the fiber optic and polymer light guide tips provide adequate compressive strength to be used to make restorations. However, the fiber optic light tip associated with microhybrid composite resin may be an interesting option for restorations mainly in posterior teeth.

Envelhecimento ambiental acelerado em PRF a base de tecidos híbridos kevlar/vidro: propriedades e instabilidade estrutural

There are a number of damaging mechanisms that various materials can suffer in service. However, when working with polymer composite materials, this is something that requires analysis, especially when exposed to adverse environmental conditions. Thus, the objective of the present thesis is the study of the direct influence of environmental aging and the form of hybridization of the reinforcement woven on the structural stability, surfacedegradation and fracture process of polymer composites laminates. For this, the development of two polymer composite laminates was necessary, where one of them was reinforced with a bi-directional woven with hybrid strandsofkevlar-49/glass-Efibers, and the other also with a bi-directionalwoven, however with weft and warpformed of alternating strandsof Kevlar-49 fibers and glass-E fiber The reinforcementwoven are industrially manufactured. Both laminates use a polyester resin as a matrixand are made up of four layers each. All laminates were industrially prepared by the hand lay-up method of manufacturing. To do this, test specimens were manufactured of the respective laminates and submitted to environmental aging accelerated through the aging chamber. They were exposed to alternating cycles of UV radiation and moisture (heated steam) for a standard defined period. At the end of the exposure period the specimens were subjected to mechanical tests of uniaxial tensile and bending in three points and to the characterizationsof the fracture and surface deterioration. In addition, they were submitted to a structural degradation assessment by the measurement of mass variation technique (MMVT) and the measurement of thickness variation technique (MTVT), this last technique being developed in this thesis. At the end of the analysis it was observed that the form of hybridization of the reinforcement woven and the aging process directly influence with losses or gain in mechanical properties, with losses in the structural degradation and in the formation and propagation of damage mechanism of the developedcomposite laminates

Compósito reforçado com sisal para aplicação na moda

The objective of this research is the fabrication of a composite reinforced with dyed sisal fiber and polyester matrix for application in the fields such as, fashion, clothing, interior textiles; fashion accessories are some of the examples. For the fabrication of the composite, the sisal fibers were subjected to processes such as: chemical treatment with sodium hydroxide (NaOH) in the removal of impurities; bleaching for removing the yellowish color of the natural fiber and dyeing with direct dyes to confer the colors blue, green and orange. The search for new technologies ecologically correct has become a major concern in recent decades. Studies show that composite polymer reinforced by natural fibers is suitable for a large number of applications, and its use is advantageous in terms of economic and ecological. The dyed fibers were cut to a length of 30 mm, is used in the confection of webs. For this purpose, a web preparer by immersion, developed in the Laboratory of Chemical Textile of UFRN. The composite sheets measuring 300 x 300 x3 mm were molded by compression, with unsaturated orthophthalic polyester as matrix, and the samples in sizes 150 x 25 x 3 mm were cut with the aid of a laser machine, to be subjected to traction and flexion. The mechanical properties of traction and flexion in three points were performed in the Laboratory of metal and mechanical tests of Materials Engineering of UFRN. The resulting samples from the tests were evaluated in scanning electron microscope (SEM) at CTGas RN. On the basis of the analysis of the results from the mechanical tests, it was observed that the composite had good mechanical behavior, both in traction as in flexion. Furthermore, it was observed that in the water absorption test, the samples had a different percentage among themselves, this occurred due to the variation of density found in the fibre webs. The images of the SEM showed the failures from the manufacturing process and the adhesion of fibre/matrix. When the samples were prepared with the dyed fibers to be applied in fashion, the results were positive, and it can be concluded that the main objective of this work was achieved

Viabilidade de uso de um fogão solar para cocção de alimentos com parábola refletora fabricada em compósito que utiliza fibras de Carnaúba e resina Ortoftálica

Presents a composite formed by orthophthalic resin and fiber loading of carnauba straw. The fibers were first dried in direct sun exposure and subsequently ground into fodder for the reduction in size. Various formulations of the composite were preliminarily tested by choosing the one presenting the best processability in applying the mold. The composite produced is used for the manufacture of a parabolic surface subsequently coated with mirror segments, flexible plastic, for reflecting the solar rays incident on it. The reflective parable represents the main element of the solar cooker that works with the concentration of sunlight and has dimensions of 1.14 m in diameter and area of 1.0 m². Manufacturing processes and assembly of solar cooker concentration produced are presented. The results of tests for cooking and baking various foods, including rice, pasta, beans, cake, cassava, shrimp, beef, breaded demonstrating the competitiveness of solar cooker studied with other stoves already manufactured and tested in Brazil are presented and in the world. It was also demonstrated the feasibility of the proposed composite for Prototypes manufacture of solar and other structures that do not require great efforts resistance

Obtenção e caracterização de um compósito de matriz polimérica com carga de bucha vegetal luffa cylindrica

Composite materials arise from the need for lighter materials and with bigger mechanical and thermal resistance. The difficulties of discard, recycling or reuse are currently environmental concerns and, therefore, they are study object of much researches. In this perspective the feasibility of using loofahs (Luffa Cylindrica) for obtainment of a polymeric matrix composite was studied. Six formulations, with 4, 5 and 6 treated layers and untreated, were tested. The loofahs were treated in boiling water to remove lignins, waxes and impurities present in the fibers. After that, they were dried in a direct exposure solar dryer. For the characterization of the composite, thermal (thermal conductivity, thermal capacity, thermal diffusivity and thermal resistivity), mechanical (tensile and bending resistance) and physicochemical (SEM, XRD, density, absorption and degradation) properties were determined. The proposed composite has as advantage the low fiber density, which is around 0.66 g/cm³ (almost half of the polyester resin matrix), resulting in an average composite density of around 1.17g/cm³, 6.0 % lower in relation to the matrix. The treatment carried out in the loofahs increased the mechanical strength of the composite and decreased the humidity absorption. The composite showed lower mechanical behavior than the matrix for all the formulations. The composite also demonstrated itself to be feasible for thermal applications, with a value of thermal conductivity of less than 0.159 W/m.K, ranking it as a good thermal insulator. For all formulations/settings a low adherence between fibers and matrix occurred, with the presence of cracks, showing the fragility due to low impregnation of the fiber by the matrix. This composite can be used to manufacture structures that do not require significant mechanical strength, such as solar prototypes, as ovens and stoves.

Obtenção e caracterização de um compósito de matriz polimérica com carga de bucha vegetal luffa cylindrica

Composite materials arise from the need for lighter materials and with bigger mechanical and thermal resistance. The difficulties of discard, recycling or reuse are currently environmental concerns and, therefore, they are study object of much researches. In this perspective the feasibility of using loofahs (Luffa Cylindrica) for obtainment of a polymeric matrix composite was studied. Six formulations, with 4, 5 and 6 treated layers and untreated, were tested. The loofahs were treated in boiling water to remove lignins, waxes and impurities present in the fibers. After that, they were dried in a direct exposure solar dryer. For the characterization of the composite, thermal (thermal conductivity, thermal capacity, thermal diffusivity and thermal resistivity), mechanical (tensile and bending resistance) and physicochemical (SEM, XRD, density, absorption and degradation) properties were determined. The proposed composite has as advantage the low fiber density, which is around 0.66 g/cm³ (almost half of the polyester resin matrix), resulting in an average composite density of around 1.17g/cm³, 6.0 % lower in relation to the matrix. The treatment carried out in the loofahs increased the mechanical strength of the composite and decreased the humidity absorption. The composite showed lower mechanical behavior than the matrix for all the formulations. The composite also demonstrated itself to be feasible for thermal applications, with a value of thermal conductivity of less than 0.159 W/m.K, ranking it as a good thermal insulator. For all formulations/settings a low adherence between fibers and matrix occurred, with the presence of cracks, showing the fragility due to low impregnation of the fiber by the matrix. This composite can be used to manufacture structures that do not require significant mechanical strength, such as solar prototypes, as ovens and stoves.