Desgaste de polímeros estruturais de engenharia em contato de deslizamento com cilindro metálico

Present work proposed to map and features the wear mechanisms of structural polymers of engineering derived of the sliding contact with a metallic cylindrical spindle submitted to eccentricity due to fluctuations in it is mass and geometric centers. For this it was projected and makes an experimental apparatus from balancing machine where the cylindrical counterbody was supported in two bearings and the polymeric coupon was situated in a holder with freedom of displacement along counterbody. Thus, the experimental tests were standardized using two position of the two bearings (Fixed or Free) and seven different positions along the counterbody, that permit print different conditions to the stiffness from system. Others parameters as applied normal load, sliding velocity and distance were fixed. In this investigation it was used as coupon two structural polymers of wide quotidian use, PTFE (polytetrafluroethylene) and PEEK (poly-ether-ether-ketone) and the AISI 4140 alloy steel as counterbody. Polymeric materials were characterized by thermal analysis (thermogravimetric, differential scanning calorimetry and dynamic-mechanical), hardness and rays-X diffractometry. While the metallic material was submitted at hardness, mechanical resistance tests and metallographic analysis. During the tribological tests were recorded the heating response with thermometers, yonder overall velocity vibration (VGV) and the acceleration using accelerometers. After tests the wear surface of the coupons were analyzed using a Scanning Electronic Microscopy (SEM) to morphological analysis and spectroscopy EDS to microanalysis. Moreover the roughness of the counterbody was characterized before and after the tribological tests. It was observed that the tribological response of the polymers were different in function of their distinct molecular structure. It were identified the predominant wear mechanisms in each polymer. The VGV of the PTFE was smaller than PEEK, in the condition of minimum stiffness, in function of the higher loss coefficient of that polymer. Wear rate of the PTFE was more of a magnitude order higher than PEEK. With the results was possible developed a correlation between the wear rate and parameter (E/ρ)1/2 (Young modulus, E, density, ρ), proportional at longitudinal elastic wave velocity in the material.

Estudo comparativo das propriedades mecânicas em compósitos da fibra modal e poliester

In the present work, three composites with distinct reinforcements (polyester, modal e polyester + modal), all if a unsaturated orthophthalic polyester resin as matrix were used, in order to conduct a comparative study by mechanical tests and water absorption. The fibre mats were prepared in a mat preparatory by immersion developed in the Textile Engineering Laboratory. The composites were manufactured using a closed mould process by compression using an unsaturated orthophthalic polyester resin as matrix and 1% MEK (methyl ethyl ketone peroxide) as an initiator. In each composite twelve samples with the dimensions of 150x25x3 mm were cut randomly for the mechanical analysis (tension x extension, three points bending and water absorption and Scanning Electron Micsroscopy). The mechanical tests were carried out in the Laboratório de Metais e Ensaios Mecânicos UFRN . All the analyses were carried out according to the ASTM norms. The resultant samples from the mechanical analysis were subjected for the Scanning Electron Microscopy analysis. Based on the results obtained, it was observed that the reinforced composite with two fibres (modal + polyester) presented better results in comparison to the other two composites both in the tension/extension as well on the three point bending tests. In the water absorption test, it was possible to observe an equilibrium in the water absorption by the modal and polyester composite, due to the union of the two fibres. In the SEM images, the regions of rupture in the composites as well as the adsorption between the fiber and the matrix could be observed

Fabricação de eco-composito com a fibra de lã canina

The Sustainability has been evidence in the world today; organizations have sought to be more and more into this philosophy in their processes, whether products or attendance. In the present work were manufactured eco-composites with animal fiber (dog wool) that is currently discarded into the environment without any use. The fibers were characterized and made matting (non-woven). The phases of the project were consisted to develop methods and to convert these fibers (booster) blended with polyester resin (matrix) in different proportions (10%, 20% and 30%) at the composite. Were studied fiber characteristics, mechanical properties of the composites, water absorption and scanning electron microscopy. Initially, the fibers were treated with solution of sodium hydroxide of 0.05 mols, and then taken to matting preparing at the textile engineering laboratory - UFRN. The composites were made by compression molding, using an orthophthalic polyester resin as matrix and 1% MEK (methyl ethyl ketone peroxide) as initiator (catalyst). To evaluate the mechanical tests (tensile and flexural) and water absorption were made twelve specimens with dimensions 150x25x3 mm were cut randomly. According to the standard method, tensile tests (ASTM 3039) bending tests (ASTM D790) were performed at the mechanical testing of metals at laboratory UFRN. The results of these tests showed that the composite reinforced with 30% had a better behavior when exposed to tension charge; while on the three points bending test showed that the composite reinforced with 10% had a better behavior. In the water absorption test it was possible to see that the highest absorption happened on the composite reinforced with 30%. In the micrographs, it was possible to see the regions of rupture and behavior of the composite (booster / matrix)

Xilanas de sabugo de milho como agente antioxidante, citotóxico, anticoagulante e imunomodulador

Prospecting pharmacological active polysaccharides from agricultural byproducts, such as corncobs, is an underexplored practice in the scientific community. Thus, this work aims to expand knowledge about pharmacological activities of polysaccharides extracted from corncobs. From corn cob flour a extract was obtained by ultrasound waves in an alkaline medium, and the end of the process the product was termed PECC (polysaccharidic extract from corncobs). This extract was physicochemical characterized and evaluated by in vitro assays as an antioxidant, cytotoxic, anticoagulant and imunomodulator agent. Results indicated significant activity metal chelating by PECC, and the use of PECC in cell culture cells showed no toxic effects to normal cell lines, but toxic action against HeLa tumor cells due promoting cell death by apoptosis. In addition, other pharmacological effects were observed, the PECC decreased nitric oxide (NO) production by activated macrophages, and prolonged blood clotting time through APTT assay. Then methanolic, ethanolic and ketone fractions were obtained from fractionation of PECC polysaccharides. Five methanolic fractions, six ethanolic fractions and two ketones were obtained; and all fractions were evaluated for antioxidant, cytotoxic, anticoagulant, immunomodulatory activities. E1.4 fraction exhibited significant metal chelating effect, a toxic action to induce apoptosis in HeLa cells, decreased NO production by activated macrophages, and extended blood clotting time. These results showed that the PECC pharmacological active polysaccharides would be present in the fraction E1.4. From fractionation of E1.4 polysaccharide six subfractions with different sizes were obtained: <3; 3-10; 10-30; 30-50; 50-100 and >100 KDa. About 80% of E1.4 polysaccharides had lower size to 10 KDa, and all the subfractions showed over 61% sugar in their chemical compositions. These subfractions exhibited different monosaccharide compositions, but xylose was presented in all of them. The subfractions exhibited distinct pharmacological effects in in vitro assays. Smaller subfractions (<30 KDa) had highest metal chelating activity and greater toxic action in tumor cells. The intermediate fractions (between 30-100 KDa) decreased more NO production of activated macrophages, for other side, the larger size (>100 KDa) modulated a greater number of inflammatory cytokines, and the had greatest anticoagulant effect. Therefore, when analyzing all the results together it is evident that the PECC pharmacological polysaccharides are heteroxylans, and were concentrated in E1.4 fraction, and heteroxilanas pharmacological effects depends on their molecular size. Thus, corncobs could be used as source from molecules with biotechnology potential