Utilização de resíduo lignocelulósico na obtenção de chapa de madeira aglomerada homogênea e compósito reforçado com fibra de vidro-E

This research is about the use of the coconut´s endocarp (nucifera linn) and the waste of derivatives of wood and furniture as raw material to technological use. In that sense, the lignocellulosic waste is used for manufacture of homogeneous wood sheet agglomerate (LHWS) and lignocellulosic load which take part of a polymeric composite with fiber glass E (GFRP-WC). In the manufacturing of the homogeneous wood sheet agglomerate (LHWS), it was used mamona´s resin as waste s agglutinating element. The plates were taken up in a hydraulic press engine, heated, with temperature control, where they were manufactured for different percentage of waste wood and coconuts nucífera linn. Physical tests were conducted to determine the absorption of water, density, damp grade (in two hours and twenty-four hours), swelling thickness (in two hours and twenty-four hours), and mechanical tests to evaluate the parallel tensile strength (internal stick) and bending and the static (steady) flexural. The physical test´s results indicate that the LHWS can be classified as bonded wood plate of high-density and with highly water resistant. In the mechanical tests it was possible to establish that LHWS presents different characteristics when submitted to uniaxial tensile and to the static (steady) flexural, since brittle and elasticity module had a variation according to the amount of dry endocarp used to manufacture each trace of LHWS. The GFRP-WC was industrially manufactured by a hand-lay-up process where the fiber glass E was used as reinforcement the lignocellulósic´s waste as load. The matrix was made with ortofitalic unsaturated polyester resin. Physical and mechanical tests were performed in presence of saturated humidity and dry. The results indicated good performance of the GFRP-WC, as traction as in flexion in three points. The presence of water influenced the modules obtained in the flexural and tensile but there were no significant alteration in the properties analyzed. As for the fracture, the analysis showed that the effects are more harmful in the presence of damp, under the action of loading tested, but despite this, the fracture was well defined starting in the external parts and spreading to the internal regions when one when it reaches the hybrid load

Utilização de resíduo lignocelulósico na obtenção de chapa de madeira aglomerada homogênea e compósito reforçado com fibra de vidro-E

This research is about the use of the coconut´s endocarp (nucifera linn) and the waste of derivatives of wood and furniture as raw material to technological use. In that sense, the lignocellulosic waste is used for manufacture of homogeneous wood sheet agglomerate (LHWS) and lignocellulosic load which take part of a polymeric composite with fiber glass E (GFRP-WC). In the manufacturing of the homogeneous wood sheet agglomerate (LHWS), it was used mamona´s resin as waste s agglutinating element. The plates were taken up in a hydraulic press engine, heated, with temperature control, where they were manufactured for different percentage of waste wood and coconuts nucífera linn. Physical tests were conducted to determine the absorption of water, density, damp grade (in two hours and twenty-four hours), swelling thickness (in two hours and twenty-four hours), and mechanical tests to evaluate the parallel tensile strength (internal stick) and bending and the static (steady) flexural. The physical test´s results indicate that the LHWS can be classified as bonded wood plate of high-density and with highly water resistant. In the mechanical tests it was possible to establish that LHWS presents different characteristics when submitted to uniaxial tensile and to the static (steady) flexural, since brittle and elasticity module had a variation according to the amount of dry endocarp used to manufacture each trace of LHWS. The GFRP-WC was industrially manufactured by a hand-lay-up process where the fiber glass E was used as reinforcement the lignocellulósic´s waste as load. The matrix was made with ortofitalic unsaturated polyester resin. Physical and mechanical tests were performed in presence of saturated humidity and dry. The results indicated good performance of the GFRP-WC, as traction as in flexion in three points. The presence of water influenced the modules obtained in the flexural and tensile but there were no significant alteration in the properties analyzed. As for the fracture, the analysis showed that the effects are more harmful in the presence of damp, under the action of loading tested, but despite this, the fracture was well defined starting in the external parts and spreading to the internal regions when one when it reaches the hybrid load

A concepção estrutural como expressão plástica: um olhar tectônico sobre arquitetura em madeira

This work regards to the structural conception as a formal element of design in wood architecture. On this approach, the group of projects studied is formed by some realized works of two important Brazilian architects: Severiano Porto and Marcos Acayaba. The time interval comprises the period from 1971 to 1997, which correspond respectively to the years of the creation of first and the last of the analyzed constructions. The research perspective concerns to the relationship between the parts, the whole and the building techniques adopted in each project. Moreover, the analysis focuses on the structure as the link among the different projectual ideas. Thus, the research method firstly includes a survey of specific bibliographies and documents which refer to the structural conception in wood architecture. Secondly,the buildings are analyzed according to the methods of architectural composition discussed through this work.

Estrutura da população de Microcerotermes exiguus ( Isoptera: Termitidae) e sua partuicipação no consumo de madeira em uma área de caatinga, Nordeste, Brasil

Coordenação de Aperfeiçoamento de Pessoal de Nível Superior

Avaliação de efeitos biológicos de antiinflamatórios derivados do ácido propiônico através de modelos experimentais em nível molecular e celular

Derivatives of propionic acid NSAIDs are irreversible inhibitors of cyclooxygenase enzyme widely used. The aim of this study was to evaluate, through different experimental models, biological effects of derivatives of propionic acid (fenoprofen, naproxen, ibuprofen and ketoprofen) in cellular and molecular level. The labeling of blood constituents with technetium-99m (99mTc) and morphological analysis of erythrocytes of blood of rats, as well as growth, survival of cultures of Escherichia coli (E. coli) and the assessment of bacterial plasmid electrophoretic profiles were models used for experimental evaluation of possible biological effects of antiinflammatory drugs. The results show that, in general, anti-inflammatory drugs evaluated were not able to alter the labeling of blood constituents with 99mTc, the morphology of red blood cells from blood of rats, as well as the growth of cultures of E. coli and the electrophoretic profile of plasmid DNA. However, naproxen appears to cytotoxic effect on bacterial cultures, plasmids and genotoxic effects in reducing the action of stannous chloride in cultures of E. coli. The use of experimental fast performance and low cost was important for assessment of biological effects, contributing to a better understanding of the properties of propionic acid derivatives studied. anti-inflammatory, blood constituents, technetium-99m, stannous chloride, Escherichia coli; DNA

Obtenção de antioxidante a partir de derivados do LCC

Cashew-nut-shell-liquid (CNSL) is a phenolic oil that hás been due its their antioxirsion properties for use in fuels. The present work develops a method to the conversion of hidrogenated cardanol, that is the main component of the CNSL, in a compound with similar chacteristics to antioxidants used in products from petroleum. The antioxidants wasd obtained by exhaustive alkylation of the compound with tert-butyl chloride. After completing the optimization of several reaction steps, the product 2,4,6 tri-tert-butyl (pentadecylphenol) was obtained for the first tima. Characteeization and determination of physico-chemical properties were realized too, as well as wasd developed a study for check your application as an oxidative inhibitor by the molecular modeling. Estimation of process evalution was executed as well, where a rapid and practical computational methodology was utilizated in projects of the fine chemistry. The research showed satisfactory results and it could be concluded that the commercialization of this chemical products is feasible

Extração de metais pesados de efluentes da indústria do petróleo utilizando derivados de óleos vegetais como extratantes

The study of a promising alternative for the treatment of produced water from the oil industry envisaging its reuse was the focus of this work. Millions of liters of water are generated per day, containing heavy metals in low concentrations (< 0,15 mg/L for Pb, <0,04 mg/L for Cd, <0,04 mg/L for Ni). The technology applied to extract these metals from aqueous phase was the solvent extraction and the extratants used were vegetable oils originated from coconut oil. They can be used in natural form or as derivatives, known as MAC - Mixture of Carboxílics Acids. The determination of the heavy metal con¬centrations in a complex matrix was made by using the atomic absorption spectrometry technique (AAS). On the bench tests using synthetics aqueous solutions containing metals, vegetable oils showed no power to extract the metals studied. The extractant MAC was selective for the Pb> Cd> Ni, in the concentration of 8% in the same organic phase. In this condition, the lower efficiency of extraction obtained was 92% for the Pb, 69% for the Cd, in the range of pH ranging from 6 to 8. An experimental planning was conducted for continuous tests. The device used was called MDIF Misturador-Decantador à Inversão de Fases and the aqueous phase was produced water from Pólo Indutrial de Guamaré/RN . No correlation between the studied variables (concentration of metal, concentration of extratant and agitation in the mixing chamer) could be obtained, because of possible factors which occurred as: variation in the composition of the studied sample, phenomena of precipitation and complexation of metals in the reservoir of feed, solubility of extratant

Obtenção de novos derivados de ß-naftol e cardanol hidrogenado e avaliação dos seus efeitos antioxidativos em gasolina automotiva

The chemical nature of the hidrocarbons found in gasoline directly affects the formation of oxidation complexes known as gums. Such complexes are slightly soluble in gasoline and their formation is delayed with the use of inhibitors, known as antioxidants. In this study, a synthetic compound (βnaphtol) and a natural subproduct (hydrogenated cardanol, derived from cashewnut shell liquid CNSL) have been used in order to generate novel antioxidant substances. These compounds were submitted to chemical reactions including alkylation, nitration and reduction, with the purpose of forming the following derivatives: 6(Nethyl,Nethylamino)βnaphtol (AO1); 6(Nethyl,Ndiethylamino)βnaphtol (AO2); aminoβnaphtol (AO3); 2(Nethyl,Nethylamino)pentadecylphenol (AOC1), 2(Nethyl,Ndiethylamino)pentadecylphenol (AOC2) and aminopentadecylphenol (AOC3). The derivatives were subjected to accelerated oxidative stability assays (Potential Gum and Induction Period) and to storage assays (Washed Gum and ASTM Color) during six months, with naphtha provided by the petroleum refinery RPBC (Refinaria Presidente Bernardes de Cubatão, in Brazil). The results for the derivatives were compared to those for commercial additives [DBPC (2,6ditbutyl4methylpcresol) and PDA (N,N disecbutylpphenylenediamine)], which were also added to the naphtha produced at RPBC at the moment of sampling. From all tested antioxidants, the novel antioxidant AOC1 (derived from hydrogenated cardanol) yielded a better global performance. During the period of time in which the naphtha was stored, an examination of this material was carried out in parallel, using the mass spectrometry technique. This study allowed to monitor the formation of a triolefinic compound, as well as the observation of subsequent formation and rupture of the olefinic constituents. As an eventual result from these experimental investigations, a reaction route leading to gum formation has been suggested

Aplicação da parafina e do óleo de linhaça como hidrofobizantes da vermiculita, para remoção de derivados de óleo diesel resentes em água produzida sintética

Produced water has lately aroused interest due to their high degree of salinity, suspended oil particles, chemicals added in various manufacturing processes, heavy metals and radioactivity sometimes. Along with oil and due to its high volume production, water production is one of the pollutants of most concern in the process of oil extraction. PAHs due to their ubiquity and their characteristics carcinogenic or mutagenic and teratogenic even have attracted the attention of every scientific society. Formed from the incomplete combustion of organic matter may be natural or anthropogenic. Some materials have been researched with the goal of cleaning up environmental matrices that may be contaminated by hydrocarbons. Among these materials researched various clays have been employed, of which highlights the vermiculite. The family of phyllosilicates, vermiculite for its potential and its high hydrophobic surface area has been a tool widely used in the decontamination of water in processes of oil spills. However, when it loses its capacity expanded hydrophobic having the necessity of using a hidrofobizante to make it organophilic. Among the numerous hidrofobizantes researched and used the linseed oil was the pioneer. In this study sought to evaluate the capacity of removal of PAHs using the vermiculite hydrofobized with linseed oil and wax also, for it was made use of the 24 full factorial design as the main tool for the experiments. We also evaluated the clay grain size (-20 +48 and -48 +80 #), the percentage of hidrofobizante applied (5 and 10%) and salinity of the water produced synthesized in our laboratory (35,000 and 55,000 ppm). The molecular fluorescence spectroscopy due to its sensitivity and speed was used to verify the adsorption capacity of clay, as well as gas chromatography served as an auxiliary technique to identify and quantify the PAHs in solution. In order to characterize the vermiculite was made use of X-ray fluorescence and X-ray diffraction. The infrared and thermogravimetry were essential to note hydrophobization and the amount of coating of clay. According to the fluorescence analysis showed that the test 12 was the best result in about 98% adsorption of fluorescent compounds, however the high salinity, the smallest particle size, the highest percentage of hidrofobizante and the use of linseed oil showed greater efficiency in the removal capacity of these hydrocarbons, in accordance with the trend followed by the analysis of the major factors of the factorial design. To verify the adsorption capacity of clay using a fixed volume of water produced synthetically, used as the test base 12, at their respective levels and factors. Thus, it was observed that after adding about 1 ½ liters of water solution produced synthetically, about 300 times its volume in mass, the vermiculite was able to adsorb 80% of fluorescent species present in solution

Hidróxidos duplos lamelares de magnésio e alumínio modificados com carbonato e p123 para adsorção de dióxido de carbono

Muitos mecanismos provocados pela ação humana vêm gerando um aumento na queima de combustíveis fósseis e processos químicos (produtos orgânicos, carvão, madeira, óleo diesel, gasolina e outros derivados de petróleo) e, consequentemente, há um aumento na emissão de CO2 na atmosfera. Uma das alternativas para a captura desse poluente é o processo de adsorção, o qual pode ajudar na redução do CO2. As hidrotalcitas ou hidróxidos duplos lamelares (HDL s) estão dentre esses materiais estudados, já que apresentam alta estabilidade e uma boa porosidade, tornando-se assim um promissor adsorvente de gases poluentes. Os HDL s formam um grupo de argilas do tipo aniônico que consiste em camadas positivamente carregadas de óxido de metal (ou hidróxido de metal) com intercamadas de ânions. Foi constatado que ânions que possuem duas cargas negativas, estabilizam muito mais que ânions monovalentes, sendo o carbonato o mais estável dos ânions divalentes. Neste trabalho, foi proposta uma modificação na síntese direta através da co-precipitação a pH constante utilizando sais de cátions divalentes (Mg2+) e trivalentes (Al3+) reportados na literatura. Durante a síntese dos HDL s retirou-se o carbonato, bem como, utilizou-se um copolímero como um template para o alargamento das lamelas. As amostras foram caracterizadas utilizando as técnicas de DRX, TG/DTG, FTIR, MEV/EDX, MET e adsorção e dessorção de N2. Os dados obtidos indicam que a estrutura, mesmo após a modificação, apresentou resultados condizentes com os encontrados na literatura. Dentre as várias aplicações dos HDL s foi realizado o estudo da adsorção do CO2. A capacidade de adsorção do material foi testada de acordo com o tempo de contato entre o adsorvente e o adsorbato, sendo esperado que os materiais tratados com template apresentassem um maior desempenho

Hidrocarbonetos policíclicos aromáticos no meio ambiente: diferenciação de fontes em sedimentos e metabólitos em bile de peixes

Many studies on environmental ecosystems quality related to polycyclic aromatic hydrocarbons (PAH) have been carried out routinely due to their ubiquotus presence worldwide and to their potential toxicity after its biotransformation. PAH may be introduced into the environmet by natural and anthropogenic processes from direct runoff and discharges and indirect atmospheric deposition. Sources of naturally occurring PAHs include natural fires, natural oil seepage and recent biological or diagenetic processes. Anthropogenic sources of PAHs, acute or chronic, are combustion of organic matter (petroleum, coal, wood), waste and releases/spills of petroleum and derivatives (river runoff, sewage outfalls, maritime transport, pipelines). Besides the co-existence of multiples sources of PAH in the environmental samples, these compounds are subject to many processes that lead to geochemical fates (physical-chemical transformation, biodegradation and photo-oxidation), which leads to an alteration of their composition. All these facts make the identification of the hydrocarbons sources, if petrogenic, pyrolytic or natural, a challenge. One of the objectives of this study is to establish tools to identify the origin of hydrocarbons in environmental samples. PAH diagnostic ratios and PAH principal component analysis were tested on a critical area: Guanabara Bay sediments. Guanabara Bay is located in a complex urban area of Rio de Janeiro with a high anthropogenic influence, being an endpoint of chronic pollution from the Greater Rio and it was the scenario of an acute event of oil release in January 2000. It were quantified 38 compounds, parental and alkylated PAH, in 21 sediment samples collected in two surveys: 2000 and 2003. The PAH levels varied from 400 to 58439 ng g-1. Both tested techniques for origin identification of hydrocarbons have shown their applicability, being able to discriminate the PAH sources for the majority of the samples analysed. The bay sediments were separated into two big clusters: sediments with a clear pattern of petrogenic introduction of hydrocarbons (from intertidal area) and sediments with combustion characteristics (from subtidal region). Only a minority of the samples could not display a clear contribution of petrogenic or pyrolytic input. The diagnostic ratios that have exhibited high ability to distinguish combustion- and petroleum-derived PAH inputs for Guanabara Bay sediments were Phenanthrene+Anthracene/(Phenanthrene+Anthracene+C1Phenanthrene); Fluorantene/(Fluorantene+Pyrene); Σ (other 3-6 ring PAHs)/ Σ (5 alkylated PAH series). The PCA results prooved to be a useful tool for PAH source identification in the environment, corroborating the diagnostic indexes. In relation to the temporal evaluation carried out in this study, it was not verified significant changes on the class of predominant source of the samples. This result indicates that the hydrocarbons present in the Guanabara Bay sediments are mainly related to the long-term anthropogenic input and not directly related to acute events such as the oil spill of January 2000. This findings were similar to various international estuarine sites. Finally, this work had a complementary objective of evaluating the level of hydrocarbons exposure of the aquatic organisms of Guanabara Bay. It was a preliminary study in which a quantification of 12 individual biliar metabolites of PAH was performed in four demersal fish representing three different families. The analysed metabolites were 1-hydroxynaphtalene, 2-hidroxinaphtalene, 1hydroxyphenanthrene, 9-hydroxyphenanthrene, 2-hydroxyphenanthrene, 1hydroxypyrene, 3-hidroxibiphenil, 3- hydroxyphenanthrene, 1-hydroxychrysene, 9hydroxyfluorene, 4-hydroxyphenanthrene, 3-hydroxybenz(a)pyrene. The metabolites concentrations were found to be high, ranging from 13 to 177 µg g-1, however they were similar to worldwide regions under high anthropogenic input. Besides the metabolites established by the used protocol, it was possible to verified high concentrations of three other compounds not yet reported in the literature. They were related to pyrolytic PAH contribution to Guanabara Bay aquatic biota: 1-hydroxypyrine and 3-hydroxybenz(a)pyrine isomers