3 resultados para Dental unit water lines
em Universidade Federal do Rio Grande do Norte(UFRN)
Resumo:
Nowadays, composite resins are the direct restorative materials more important in dental clinical performance, due to their versatility and aesthetic excellence. Bis-GMA (2,2-bis[4(2-hydroxy-3-metacryloxypropoxy)phenil]propane) is the base monomer more frequently used in restorative composite resins. However, this monomer presents some disadvantages, such as high viscosity and two aromatic rings in its structure that can promote allergic reactions to the humans. In this work, the main purpose was to synthesize new monomers from glycidyl methacrylate to use in dental restorative materials. Structural characterization of the monomers was carried out through FTIR and NMR 1H, and eight composites were produced from the new monomers, by addition of silane-treated alumino silicate particles (inorganic filler) and a photocuring system (camphorquinone and ethyl 4-dimethylaminebenzoate). The composites were analyzed by environmental scanning electronic microscopy and the water sorption and solubility, compressive strength and elastic modulus were determined. A commercial composite resin [Z100 (3M)] was used to comparison effect. The new composites presented general characteristics similar to the commercial ones; however, they didn t present the properties expected. This behavior was attributed to the lower degree of monomer reaction and to the granulometry and size distribution of the mineral filler in the polymeric matrix
Resumo:
The aim of this study was to evaluate the compressive strength of microhybrid (FiltekTM Z250) and nanofilled (FiltekTM Supreme XT) composite resins photo-activated with two different light guide tips, fiber optic and polymer, coupled with one LED. The power density was 653 mW cm−2 when using the fiber optic light tip and 596 mW cm−2 with the polymer. After storage in distilled water at 37 ± 2 "C for seven days, the samples were subjected to mechanical testing of compressive strength in an EMIC universal mechanical testing machine with a load cell of 5 kN and speed of 0.5 mm min−1. The statistical analysis was performed using ANOVA with a confidence interval of 95% and Tamhane’s test. The results showed that the mean values of compressive strength were not influenced by the different light tips (p > 0.05). However, a statistical difference was observed (p < 0.001) between the microhybrid composite resin photo-activated with the fiber optic light tip and the nanofilled composite resin. Based on these results, it can be concluded that microhybrid composite resin photo-activated with the fiber optic light tip showed better results than nanofilled, regardless of the tip used, and the type of the light tip did not influence the compressive strength of either composite. Thus, the presented results suggest that both the fiber optic and polymer light guide tips provide adequate compressive strength to be used to make restorations. However, the fiber optic light tip associated with microhybrid composite resin may be an interesting option for restorations mainly in posterior teeth.
Resumo:
Nowadays, composite resins are the direct restorative materials more important in dental clinical performance, due to their versatility and aesthetic excellence. Bis-GMA (2,2-bis[4(2-hydroxy-3-metacryloxypropoxy)phenil]propane) is the base monomer more frequently used in restorative composite resins. However, this monomer presents some disadvantages, such as high viscosity and two aromatic rings in its structure that can promote allergic reactions to the humans. In this work, the main purpose was to synthesize new monomers from glycidyl methacrylate to use in dental restorative materials. Structural characterization of the monomers was carried out through FTIR and NMR 1H, and eight composites were produced from the new monomers, by addition of silane-treated alumino silicate particles (inorganic filler) and a photocuring system (camphorquinone and ethyl 4-dimethylaminebenzoate). The composites were analyzed by environmental scanning electronic microscopy and the water sorption and solubility, compressive strength and elastic modulus were determined. A commercial composite resin [Z100 (3M)] was used to comparison effect. The new composites presented general characteristics similar to the commercial ones; however, they didn t present the properties expected. This behavior was attributed to the lower degree of monomer reaction and to the granulometry and size distribution of the mineral filler in the polymeric matrix