Desgaste de polímeros estruturais de engenharia em contato de deslizamento com cilindro metálico

Present work proposed to map and features the wear mechanisms of structural polymers of engineering derived of the sliding contact with a metallic cylindrical spindle submitted to eccentricity due to fluctuations in it is mass and geometric centers. For this it was projected and makes an experimental apparatus from balancing machine where the cylindrical counterbody was supported in two bearings and the polymeric coupon was situated in a holder with freedom of displacement along counterbody. Thus, the experimental tests were standardized using two position of the two bearings (Fixed or Free) and seven different positions along the counterbody, that permit print different conditions to the stiffness from system. Others parameters as applied normal load, sliding velocity and distance were fixed. In this investigation it was used as coupon two structural polymers of wide quotidian use, PTFE (polytetrafluroethylene) and PEEK (poly-ether-ether-ketone) and the AISI 4140 alloy steel as counterbody. Polymeric materials were characterized by thermal analysis (thermogravimetric, differential scanning calorimetry and dynamic-mechanical), hardness and rays-X diffractometry. While the metallic material was submitted at hardness, mechanical resistance tests and metallographic analysis. During the tribological tests were recorded the heating response with thermometers, yonder overall velocity vibration (VGV) and the acceleration using accelerometers. After tests the wear surface of the coupons were analyzed using a Scanning Electronic Microscopy (SEM) to morphological analysis and spectroscopy EDS to microanalysis. Moreover the roughness of the counterbody was characterized before and after the tribological tests. It was observed that the tribological response of the polymers were different in function of their distinct molecular structure. It were identified the predominant wear mechanisms in each polymer. The VGV of the PTFE was smaller than PEEK, in the condition of minimum stiffness, in function of the higher loss coefficient of that polymer. Wear rate of the PTFE was more of a magnitude order higher than PEEK. With the results was possible developed a correlation between the wear rate and parameter (E/ρ)1/2 (Young modulus, E, density, ρ), proportional at longitudinal elastic wave velocity in the material.

Avaliação por pig de perfilagem de danos superfciais nos materiais das paredes de dutos de petróleo

The modern technology of materials and structural integrity of pipelines requests the use of inspection tools named inspection pigs to detect, localize and measure the length, width and depth dimensions of the thickness losses of walls of buried and underwater pipelines in service. These tools run them internally, performing and recording measurements, with performance that varies according to the pig s technology. It has been developed recently an instrumented pig technology, called feller pig. This work aims to indicate factors that influence the feller pig technology performance in the detection and in the accuracy of measurement of the length, width and depth dimensions of the thickness losses on the internal surface of an oil pipeline wall under normal conditions of oil pipe inspection with pig. In this work, is made a collection of factors and an analyses of the technology based on the available literature, as well as an experiment to observe the technology and the factors operating. In the experiment, a feeler pig is used in a pipeline built in carbon steel and in operation that flows petroleum, in witch are observed areas with internal thickness losses occurred naturally. Some of these areas and their dimensions taken by automated ultra-sound scanner are compared with the ones indicated by the feller pig. Based on the data collection, on the analysis and on the experiment, the influence of factors object of this research is discussed. It is concluded that, among these, there are factors related to pipe fabrication tolerances, to wear of pig components, to internal adhesive wear of pipeline, to other pipeline damages and to technology characteristics. Finally, actions are suggested to know better, improve and define the applicability of this technology

Mecanismos de desgaste, história térmica e ciclo de vida de componentes de um motor de combustão interna de aeromodelo

We developed an assay methodology that considered the temperature variation and the scanning electron microscopy as a method to quantify and characterize respectively the consumption evolution in three 46 LA machines, with internal combustion and two-stroke engines, 7.64 cm3 cylinder capacity, 23.0 millimeters diameter and 18.4 millimeters course, RPM service from 2.000 to 16.000 rpm, 1.2 HP power, and 272 grams weight. The investigated engines components were: (1) head of the engine (Al-Si alloy), (2) piston (Al-Si alloy) and (3) piston pin (AISI 52100 steel). The assays were carried out on a desktop; engines 1 and 2 were assayed with no load, whereas in two assays of engine 3 we added a fan with wind speed that varied from 8.10 m/s to 11.92 m/s, in order to identify and compare the engine dynamic behavior as related to the engines assayed with no load. The temperatures of the engine s surface and surroundings were measured by two type K thermopairs connected to the assay device and registered in a microcomputer with data recording and parameters control and monitoring software, throughout the assays. The consumed surface of the components was analyzed by scanning electron microscopy (SEM) and microanalysis-EDS. The study was complemented with shape deformation and mass measurement assays. The temperature variation was associated with the oxides morphology and the consumption mechanisms were discussed based on the relation between the thermal mechanical effects and the responses of the materials characterization

Mecanismos de desgaste de poliuretano em ensaios de microabrasão

Wear mechanisms and thermal history of two non-conforming sliding surfaces was investigated in laboratory. A micro-abrasion testing setup was used but the traditional rotative sphere method was substituted by a cylindrical surface of revolution which included seven sharp angles varying between 15o to 180o. The micro-abrasion tests lead to the investigation on the polyurethane response at different contact pressures. For these turned counterfaces with and without heat treatment. Normal load and sliding speeds were changed. The sliding distance was fixed at 5 km in each test. The room and contact temperatures were measured during the tests. The polyurethane was characterized using tensile testing, hardness Shore A measurement, Thermogravimetric Analysis (TGA), Differential Scanning Calorimetry (DSC) and Thermomechanical Analyze (TMA). The Vickers micro-hardness of the steel was measured before and after the heat treatment and the metallographic characterization was also carried out. Worn surface of polyurethane was analysed using Scanning Electron Microscope (SEM) and EDS (Electron Diffraction Scanning) microanalyses. Single pass scratch testing in polyurethane using indenters with different contact angles was also carried out. The scar morphology of the wear, the wear mechanism and the thermal response were analyzed in order to correlate the conditions imposed by the pressure-velocity pair to the materials in contact. Eight different wear mechanisms were identified on the polyurethane surface. It was found correlation between the temperature variation and the wear scar morphology.

Desgaste corrosivo-cavitativo-erosivo de um aço-carbono em meio aquoso com frações de sal (NaCl), CO2 e particulados sólidos (SiO2)

A batch of eighty-four coupons of low carbon steel were investigated at laboratory conditions under a corrosive, cavitative-corrosive (CO2) and corrosive-erosive (SiO2 + CO2) in an aqueous salt solution and two levels of temperature. The following measurements were made on Vickers (HV0,05, HV0,10, HV0,20) Microhardness tests at three levels of subsurface layer. A turbulent flow collided on the cylindrical sample, with and without mechanical stirring and gas bubbling, with and without fluid contamination by solid particles of SiO2, at two temperatures. Surface Roughness and Waviness, under two conditions "as received, after machining" and "after worn out", as well as gravimetric and electrochemical parameter were measured on the two opposite generatrices of each cylindrical sample, on the flow upstream (0°) and downstream (180°) by Profilometry, Mass Variation and Linear Polarization Resistance (LPR). The results of the Microhardness and Surface Texture of all coupons were subjected to statistical comparison, using the software Statgraphics® Centurion XVI, 95% statistical certainty, and significant differences were observed in some arrays of measurements. The corrosive wear rate measured by LPR and mass variation shown to be sensitive to the presence of bubbles and hydrodynamic fluctuations inside the cell, considering the temperature and contamination of corrosive fluid by solid particles. The main results of visual inspection relative to some topologies of the surface damages involving different mechanisms that were seen to give explanation for some fluctuations in wear rates of the steel experimentally investigated

Estudo comparativo da queima rápida com a queima tradicional nas propriedades de materiais cerâmicos de base argilos

Dutra, R. P. S.; Varela,M. L.; Nascimento, R. M. ; Gomes, U. U. ; Martinelli1, A. E. ; Paskocimas, C. A. Estudo comparativo da queima rápida com a queima tradicional nas propriedades de materiais cerâmicos de base argilosa. Cerâmica [online]. 2009, vol.55, n.333, pp. 100-105. ISSN 0366-6913. doi:Disponivem em: . Acesso em: 04 out. 2010.

O ambientalismo econômico no discurso da reciclagem dos materiais

O modelo civilizatório da sociedade global fundamenta-se na produção à larga escala e no aumento exponencial e diversificado do consumo. Este modelo impacta o meio ambiente já que demanda grandes quantidades de recursos naturais e provoca contaminação ambiental. No leque desta contaminação, a geração de resíduos sólidos surge como uma das principais devido a seus efeitos nocivos serem sentidos de forma imediata pelas pessoas. Em países como o Brasil, uma das soluções requeridas para se minimizar e/ou equacionar a problemática engendrada pelos resíduos sólidos é a reciclagem dos materiais. A justificativa oficial pelo esforço à reciclagem está nas características da atividade já que o uso de materiais reciclados reduz a demanda por recursos naturais em processos produtivos industriais, aumenta o tempo de vida útil dos aterros sanitários (local de destino final dos resíduos), além de gerar emprego e renda para os catadores, sujeitos que sobrevivem da coleta e separação dos materiais recicláveis. A partir de uma ética ambiental, a pergunta que deve ser feita quando nos propomos a analisar as implicações da geração dos resíduos é: por que a sociedade global gera resíduos sólidos de maneira acentuada? Contudo, à luz dos pressupostos mercadológicos do capitalismo, a pergunta que move as discussões acerca da problemática dos resíduos sólidos é: o que fazer com a crescente geração de resíduos sólidos? O presente artigo se propõe a uma reflexão dos elementos justificativos dessa ode à reciclagem. Em nossa perspectiva, a reciclagem fomenta ao que denominamos de ambientalismo econômico, no qual o discurso pró-reciclagem se apropria dos elementos e potencialidades ambientais da atividade da reciclagem para justificar as ações de caráter econômico no que se refere ao que fazer com os resíduos gerados diariamente.

Estudo da sinterização do aço inox 316L reforçado com 3% Carbeto de Tântalo - TaC

The present work shows a contribution to the studies of development and solid sinterization of a metallic matrix composite MMC that has as starter materials 316L stainless steel atomized with water, and two different Tantalum Carbide TaC powders, with averages crystallite sizes of 13.78 nm and 40.66 nm. Aiming the metallic matrix s density and hardness increase was added different nanometric sizes of TaC by dispersion. The 316L stainless steel is an alloy largely used because it s high resistance to corrosion property. Although, its application is limited by the low wear resistance, consequence of its low hardness. Besides this, it shows low sinterability and it cannot be hardened by thermal treatments traditional methods because of the austenitic structure, face centered cubic, stabilized mainly in nickel presence. Steel samples added with TaC 3% wt (each sample with different type of carbide), following a mechanical milling route using conventional mill for 24 hours. Each one of the resulted samples, as well as the pure steel sample, were compacted at 700 MPa, room temperature, without any addictive, uniaxial tension, using a 5 mm diameter cylindrical mold, and quantity calculated to obtain compacted final average height of 5 mm. Subsequently, were sintered in vacuum atmosphere, temperature of 1290ºC, heating rate of 20ºC/min, using different soaking times of 30 and 60 min and cooled at room temperature. The sintered samples were submitted to density and micro-hardness analysis. The TaC reforced samples showed higher density values and an expressive hardness increase. The complementary analysis in optical microscope, scanning electronic microscope and X ray diffractometer, showed that the TaC, processed form, contributed with the hardness increase, by densification, itself hardness and grains growth control at the metallic matrix, segregating itself to the grain boarders

Análise de falhas em martelos oscilantes dos desfibradores da indústria sucroalcooleira da Região Norte-Nordeste

The failure of materials is always an unwelcome event for several reasons: human lives are put in danger, economic losses, and interference in the availability of products and services. Although the causes of failures and behaviour of materials can be known, the prevention of such a condition is difficult to be guaranteed. Among the failures, wear abrasion by the low voltage is the kind of failure that occurs in more equipment and parts industry. The Plants Sucroalcooleiras suffer significant losses because of such attrition, this fact that motivated their choice for the development of this work. For both, were considered failures in the swing hammers desfibradores stopped soon after the exchange provided in accordance with tonnage of cane processed, then were analyzed by the level of wear testing of rubber wheel defined by the standard ASTM G65-91.The failures were classified as to the origin of the cause and mechanism, moreover, were prepared with samples of welding procedures according to ASME code, sec. IX as well, using the technique of thermal spraying to analyze the performance of these materials produced in laboratories, and compares them with the solder used in the plant. It was observed that the bodies-of-proof prepared by the procedure described as welding, and the thermal spraying the results of losing weight have been minimized significantly compared to the preparations in the plant. This is because the use of techniques more appropriate and more controlled conditions of the parameters of welding. As for the thermal spraying, this technique has presented a satisfactory result, but requires the use of these coatings in the best condition for real affirmation of the results

Análise e avaliação dos elementos de penetração no solo de equipamentos rodoviários após revestimento

The main objective is to analyze the abrasive wear resistance to the low stress of the elements that make up the organs of road machinery that are exposed directly to contact with abrasives. These samples were analyzed after these elements are coated superficially by the process of welding electrode coated with (SAER) and the manual process of coating type LVOF thermal spraying. As well, is to provide suggestions for a better recovery and return of these elements, which are reducing costs and avoiding downtime in the fronts of service. The samples were made from a substrate of carbon ABNT 1045 tempered steel, following the same specifications and composition of metals and alloys of constituents was followed the standard governing the dimensions of these samples and in accordance with the corresponding size. The results were evaluated by testing the hardness, abrasion resistance to wear by the low stress and the loss of volume involving the microstructure of coatings analyzed

Estudo da zircônia reforçado com alumina

Ceramics materials have good properties including chemical stability, high hardness and wear resistance. Moreover, due to its fragility, can suffer failure under relatively low levels of tension. Actually zirconia is the material of choice in metal free dental prostheses used in dentistry due its inertia in physiological environment, good bending strength, hardness and fracture toughness. The alumina and mixed tungsten and titanium carbides additions, acting as reinforcement elements in the zirconia matrix, have as their main objective the improvement of mechanical properties of this material. In this work, samples of zirconia, zirconia with 30% wt of alumina and zirconia with 30% wt mixed carbides were analyzed. The samples were sintered by uniaxial hot pressing on 30 MPa pressure, for 1 hour in an argon atmosphere. They were physically characterized by porosity and density measurements, and mechanically by 3-points bending strength and Vickers microhardness. The X-ray diffraction was used for the phase identifications and microstructure was examined by scanning electron microscopy (SEM). The addition of mixed carbides as reinforcement elements in zirconia matrix provides improvements in all properties analyzed in this work. The alumina addition has dropped the zirconia strength, although it caused improvement in other properties

Síntese, caracterização e cinética da decomposição térmica dos materiais cerâmicos PrMO3 (M = Ni ou Co)

In this work have been studied the preparation, characterization and kinetic study of decomposition of the polymerizing agent used in the synthesis under non-isothermal condition ceramics PrMO3 of general formula (M = Co and Ni). These materials were obtained starting from the respective metal nitrates, as a cations source, and making use of gelatin as polymerizing agent. The powders were calcined at temperatures of 500°C, 700°C and 900°C and characterized by X-ray Diffraction (XRD), Thermogravimetric Analysis (TG / DTG/ DTA), Infrared Spectroscopy (FTIR), Temperature Programmed Reduction (TPR) and Scanning Electron Microscopy (SEM). The perovskite phase was detected in all the X-rays patterns. In the infrared spectroscopy observed the oxide formation as the calcination temperature increases with the appearance of the band metal - oxygen. The images of SEM revealed uniform distribution for the PrCoO3 and particles agglomerated as consequence of particle size for PrNiO3. From the data of thermal analysis, the kinetics of decomposition of organic matter was employed using the kinetics methods called Model Free Kinetics and Flynn and Wall, in the heating ratios 10, 20 and 30° C.min-1 between room temperature and 700°C. Finally, been obtained the values of activation energy for the region of greatest decomposition of organic matter in samples that were determined by the degree of conversion (α)

Adição de cascalho de perfuração da bacia potiguar em argilas para uso em materiais cerâmicos: influência da concentração e temperatura de queima.

One of waste produced on large scale during the well drilling is the gravel drilling. There are techniques for the treatment of the same, but there isn t consensus on what are the best in terms of economic and environmental. One alternative for disposal of this waste and objective of this paper is the incorporation and immobilization of gravel clay matrix to assess their technological properties. The Raw Materials used were characterized by the following techniques: Chemical Analysis by X-ray fluorescence (XRF), mineralogical analysis by X-ray Diffraction (XRD), Grain Size Analysis (FA) and Thermal Analysis by Thermogravimetry (TG) and thermodiferential (DTA). After characterizing, samples were formulated in the following percentages: 0, 5, 10, 15, 25, 50, 75, 100% (weight) of gravel drilling, then the pieces were pressed, dried (110 ° C) and sintered at temperatures of 850, 950 and 1050 ° C. After sintering, samples were tested for water absorption, linear shrinkage, flexural strength, porosity, density, XRD and test color. The results concluded that the incorporation of gravel drilling is a viable possibility for solid masonry bricks and ceramic blocks manufacture at concentrations and firing temperature described here. Residue incorporation reduces an environmental problem, the cost of raw materials for manufacture of ceramic products

Sinterização de aço inoxidável reforçado com partículas nanométricas dispersas de carbeto de nióbio - NbC

Metal powder sintering appears to be promising option to achieve new physical and mechanical properties combining raw material with new processing improvements. It interest over many years and continue to gain wide industrial application. Stainless steel is a widely accepted material because high corrosion resistance. However stainless steels have poor sinterability and poor wear resistance due to their low hardness. Metal matrix composite (MMC) combining soft metallic matrix reinforced with carbides or oxides has attracted considerable attention for researchers to improve density and hardness in the bulk material. This thesis focuses on processing 316L stainless steel by addition of 3% wt niobium carbide to control grain growth and improve densification and hardness. The starting powder were water atomized stainless steel manufactured for Höganäs (D 50 = 95.0 μm) and NbC produced in the UFRN and supplied by Aesar Alpha Johnson Matthey Company with medium crystallite size 16.39 nm and 80.35 nm respectively. Samples with addition up to 3% of each NbC were mixed and mechanically milled by 3 routes. The route1 (R1) milled in planetary by 2 hours. The routes 2 (R2) and 3 (R3) milled in a conventional mill by 24 and 48 hours. Each milled samples and pure sample were cold compacted uniaxially in a cylindrical steel die (Ø 5 .0 mm) at 700 MPa, carried out in a vacuum furnace, heated at 1290°C, heating rate 20°C stand by 30 and 60 minutes. The samples containing NbC present higher densities and hardness than those without reinforcement. The results show that nanosized NbC particles precipitate on grain boundary. Thus, promote densification eliminating pores, control grain growth and increase the hardness values

Influência do uso de combustíveis alternativos na síntese por combustão via microondas para a produção de materiais cerâmicos com estrutura espinélio

The development and study of detectors sensitive to flammable combustible and toxic gases at low cost is a crucial technology challenge to enable marketable versions to the market in general. Solid state sensors are attractive for commercial purposes by the strength and lifetime, because it isn t consumed in the reaction with the gas. In parallel, the use of synthesis techniques more viable for the applicability on an industrial scale are more attractive to produce commercial products. In this context ceramics with spinel structure were obtained by microwave-assisted combustion for application to flammable fuel gas detectors. Additionally, alternatives organic-reducers were employed to study the influence of those in the synthesis process and the differences in performance and properties of the powders obtained. The organic- reducers were characterized by Thermogravimetry (TG) and Derivative Thermogravimetry (DTG). After synthesis, the samples were heat treated and characterized by Fourier Transform Infrared Spectroscopy (FTIR), X-ray Diffraction (XRD), analysis by specific area by BET Method and Scanning Electron Microscopy (SEM). Quantification of phases and structural parameters were carried through Rietveld method. The methodology was effective to obtain Ni-Mn mixed oxides. The fuels influenced in obtaining spinel phase and morphology of the samples, however samples calcined at 950 °C there is just the spinel phase in the material regardless of the organic-reducer. Therefore, differences in performance are expected in technological applications when sample equal in phase but with different morphologies are tested