Metodologia númerico-experimental para avaliação da espessura de filmes de nitreto de titânio obtidos por processamento a plasma

In recent decades, changes in the surface properties of materials have been used to improve their tribological characteristics. However, this improvement depends on the process, treatment time and, primarily, the thickness of this surface film layer. Physical vapor deposition (PVD) of titanium nitrate (TiN) has been used to increase the surface hardness of metallic materials. Thus, the aim of the present study was to propose a numerical-experimental method to assess the film thickness (l) of TiN deposited by PVD. To reach this objective, experimental results of hardness (H) assays were combined with a numerical simulation to study the behavior of this property as a function of maximum penetration depth of the indenter (hmax) into the film/substrate conjugate. Two methodologies were adopted to determine film thickness. The first consists of the numerical results of the H x hmax curve with the experimental curve obtained by the instrumental indentation test. This methodology was used successfully in a TiN-coated titanium (Ti) conjugate. A second strategy combined the numerical results of the Hv x hmax curve with Vickers experimental hardness data (Hv). This methodology was applied to a TiN-coated M2 tool steel conjugate. The mechanical properties of the materials studied were also determined in the present study. The thicknesses results obtained for the two conjugates were compatible with their experimental data.

Avaliação do desempenho do aço AISI D2 tratado termicamente e nitretado em plasma com gaiola catódica visando aplicação industrial

In the research, steel samples tool AISI D2, treated thermally, in the conditions: relief of tension, when maximum, seasoned and seasoned was treated thermally in the temperature of revenimento and revenida had been nitrited in plasma with cathodic cage, in atmosphere of 80%N2:20%H2. One used pressure of 2,5 mbar, 400 and 480°C temperatures with treatment time of 3 and 4 hours, with the objective to evaluate its performance in pipes cut tool. It was compared that the performance of the same steel when only thermally treated, both with tension relief. It was evaluated its hardness. Microstructural aspects (the layer thickness, interface, graisn size, etc) and crystalline phases on the surface. Besides, it was verified accomplishment possibility of nitriding simultaneous to annealing treatment. The tempering samples had presented hardness levels of 600 HV, while in nitrited samples these values had been 1100 HV

Avaliação do desempenho do aço AISI D2 tratado termicamente e nitretado em plasma com gaiola catódica visando aplicação industrial

In the research, steel samples tool AISI D2, treated thermally, in the conditions: relief of tension, when maximum, seasoned and seasoned was treated thermally in the temperature of revenimento and revenida had been nitrited in plasma with cathodic cage, in atmosphere of 80%N2:20%H2. One used pressure of 2,5 mbar, 400 and 480°C temperatures with treatment time of 3 and 4 hours, with the objective to evaluate its performance in pipes cut tool. It was compared that the performance of the same steel when only thermally treated, both with tension relief. It was evaluated its hardness. Microstructural aspects (the layer thickness, interface, graisn size, etc) and crystalline phases on the surface. Besides, it was verified accomplishment possibility of nitriding simultaneous to annealing treatment. The tempering samples had presented hardness levels of 600 HV, while in nitrited samples these values had been 1100 HV