Avaliação das propriedades das fibras de algodões coloridos naturalmente e ecologicamente corretas cultivados nos assentamentos do município de Guamaré/RN

In this work evaluate the technical characteristics of the fibers grown in settlements Guamaré, colored cotton seeds were donated existing in the Germplasm Bank of Embrapa Cotton. We sought through the breeding program, raising the resistance, fineness, length and uniformity of cotton fibers, as well as stabilize the staining of fibers in the BRS Topaz, BRS Brown and BRS Green shades and raise their productivity in the field. First, the individual selections to test progeny seeds, and thereafter the hybridization method followed by family selection to obtain variations in the color tones were performed. The BRS Topaz, BRS Brown and BRS Green varieties were produced, analyzed and compared with existing cottons in the region which is the White cotton. The properties amount of impurities and neps, length, length uniformity, short fiber content, fineness and tensile strength of the fibers were sized in Classifiber, NATI, Pressley and Micronaire devices. 10 trials each with 10 tests for all four fiber types were carried out. The White and Topaz fibers showed greater length (32-34mm) and greater resistance (7.94 lb/mg and 7.97 lb/mg respectively) and showed finesse with lower micronaire index 3,71μg/inch and 3, 73μg/inch and a low rate of short fibers. The results were very promising for the use of genetically improved cotton in the manufacturing of fabric and yarn in the textile industry. The fibers were brown colored cotton used in the manufacture of a composite fiber with thermoplastic resin

Obtenção e caracterização de um compósito polimérico de matriz poliéster e reforço/carga de tecido plano de algodão

He was obtained and studied the feasibility of using TPA (Tissue Cotton Plan) screen type, for bagging, with a weight of 207.9 g / m2 in a composite of orthophthalic crystal polyester resin matrix. The process for obtaining the composite was tested against the maximum number of layers that could be used without compromising the processability and manufacturing of CPs in compression mold. Five configurations / formulations were selected and tested at 1, 4, 8, 10 and 12 layers of cotton tissue - TPA. TPA was not subjected to chemical treatment, only by passing a mechanical washing process. The composite in its various configurations / formulations was characterized to determine its physical properties. The properties of the composite were higher viability resistance to bending, approaching the matrix and impact resistance, superiority in relation to the polyester resin. Another property that has shown good result compared to other composite has water absorption. Analyzing all the properties set the settings / formulations with higher viability were TA8 and TA10, by combining good processability and higher mechanical strength, with lower loss compared to polyester resin matrix. The composite showed lower mechanical behavior of the resin matrix for all the formulations studied except the impact resistance. The SEM showed a good adhesion between the layers of TPA and polyester resin matrix, without the presence of micro voids in the matrix confirming the efficient manufacturing process of the samples for characterization. The composite proposed proved to be viable for the fabrication of structures with low requests from mechanical stresses, and as demonstrated for the manufacture of solar and wind prototypes, and packaging, shelving, decorative items, crafts and shelves, with good visual appearance.

Obtenção e caracterização de um compósito polimérico de matriz poliéster e reforço/carga de tecido plano de algodão

He was obtained and studied the feasibility of using TPA (Tissue Cotton Plan) screen type, for bagging, with a weight of 207.9 g / m2 in a composite of orthophthalic crystal polyester resin matrix. The process for obtaining the composite was tested against the maximum number of layers that could be used without compromising the processability and manufacturing of CPs in compression mold. Five configurations / formulations were selected and tested at 1, 4, 8, 10 and 12 layers of cotton tissue - TPA. TPA was not subjected to chemical treatment, only by passing a mechanical washing process. The composite in its various configurations / formulations was characterized to determine its physical properties. The properties of the composite were higher viability resistance to bending, approaching the matrix and impact resistance, superiority in relation to the polyester resin. Another property that has shown good result compared to other composite has water absorption. Analyzing all the properties set the settings / formulations with higher viability were TA8 and TA10, by combining good processability and higher mechanical strength, with lower loss compared to polyester resin matrix. The composite showed lower mechanical behavior of the resin matrix for all the formulations studied except the impact resistance. The SEM showed a good adhesion between the layers of TPA and polyester resin matrix, without the presence of micro voids in the matrix confirming the efficient manufacturing process of the samples for characterization. The composite proposed proved to be viable for the fabrication of structures with low requests from mechanical stresses, and as demonstrated for the manufacture of solar and wind prototypes, and packaging, shelving, decorative items, crafts and shelves, with good visual appearance.