Comportamento da adição do carbeto de nióbio (nBC) na matriz metálica do aço ferrítico 15kH2mfa

The 15Kh2MFA steel is a kind of Cr-Mo-V family steels and can be used in turbines for energy generation, pressure vessels, nuclear reactors or applications where the range of temperature that the material works is between 250 to 450°C. To improve the properties of these steels increasing the service temperature and the thermal stability is add a second particle phase. These particles can be oxides, carbides, nitrites or even solid solution of some chemical elements. On this way, this work aim to study the effect of addition of 3wt% of niobium carbide in the metallic matrix of 15Kh2MFA steel. Powder metallurgy was the route employed to produce this metallic matrix composite. Two different milling conditions were performed. Condition 1: milling of pure 15Kh2MFA steel and condition 2: milling of 15Kh2MFA steel with addition of niobium carbide. A high energy milling was carried out during 5 hours. Then, these two powders were sintered in a vacuum furnace (10-4torr) at 1150 and 1250°C during 60 minutes. After sintering the samples were normalized at 950°C per 3 minutes followed by air cooling to obtain a desired microstructure. Results show that the addition of niobium carbide helps to mill faster the particles during the milling when compared with that steel without carbide. At the sintering, the niobium carbide helps to sinter increasing the density of the samples reaching a maximum density of 7.86g/cm³, better than the melted steel as received that was 7,81g/cm³. In spite this good densification, after normalizing, the niobium carbide don t contributed to increase the microhardness. The best microhardness obtained to the steel with niobium carbide was 156HV and to pure 15Kh2MFA steel was 212HV. It happened due when the niobium carbide is added to the steel a pearlitic structure was formed, and the steel without niobium carbide submitted to the same conditions reached a bainitic structure

Avaliação do comportamento reológico de pastas de cimento para poços de petróleo com adição de plastificantes

The isolation of adjacent zones encountered during oilwell drilling is carried out by Portland-based cement slurries. The slurries are pumped into the annular positions between the well and the casing. Their rheological behavior is a very important component for the cementing process. Nowadays, several alternative materials are used in oilwell cementing, with goal the modification and the improvement of their properties, mainly the increase of the fluidity. And this can be reached by using plasticizers additives able to account for different oilwell conditions, yielding compatible cement slurries and allowing enough time for the complete cementing operation. If the rheological properties of the slurry are properly characterized, the load loss and flow regime can be correctly predicted. However, this experimental characterization is difficult. Rheological models capable of describing the cement slurry behavior must be capable of predicting the slurry cement deformation within reasonable accuracy. The aim of this study was to characterize rheologically the slurries prepared with a especial class of Portland cement, water and plasticizers based on lignosulfonate, melamine and polycarboxylate at temperatures varying from 27°C to 72°C. The tests were carried out according to the practical recommendations of the API RP 10B guidelines. The results revealed a great efficiency and the dispersive power of the polycarboxylate, for all temperatures tested. This additive promoted high fluidity of the slurries, with no sedimentation. High lignosulfonate and melamine concentrations did not reduce the rheological parameters (plastic viscosity and yield stress) of the slurries. It was verified that these additives were not compatible with the type of cement used. The evaluated rheological models were capable of describing the behavior of the slurries only within concentration and temperature ranges specific for each type of additive

Representações sociais do comportamento agressivo do homem sob a ótica da mulher em situação de violência

We aim to understand the social representations of man's aggressive behavior from the perspective of women in situations of domestic violence. This is a descriptive, exploratory and representational study, whose methodological approach falls into the qualitative category. We chose as a scenario for research, by the Reference Center for Citizen Women (CRMC), Natal / RN. The criteria for selection of participants were women who lived/live in situations of domestic violence, with affective or relationship bonding with the assailant, in psychological and emotional positions appropriated to the reality; that are being protected or assisted by the service listed above; whose aggressor is male. We adopted as data collection instruments: questionnaire, Drawing-Story (DE) and a field diary. For analysis of textual data, we decided to use the ALCESTE software conjugated to editing analyze and initial reading. Were investigated 20 women victims of domestic violence, whose author of the attacks was the husband/partner. We identified, from the respondents, that 70% (n = 14) of men with aggressive behavior also had a family history of violence and fragile family relationships. About the physical and emotional condition of the assailant at the time of violence, 50% (n = 10) of these men, regardless the use of alcohol, had often quarrelsome and/or nervous behavior, impatient and unpredictable humor facing a setback, worry or annoyance. Regarding the nature of violence, we observed that women were victims of all types of violence, however, the psychological prevailed in 100% of cases. The corpus "Men" has three classes, whose focuses are, respectively: resignation, denounce and violence/aggression, being possible categorizing them as well: Category 1: The imprisonment of women; Category 2: Violence and its meanings; Category 3: Breaking the violent cycle. We show that the social representations of man s aggressive behavior, from the women in situations of violence, are anchored in the social roles of men in family and society, becoming a dominant model of masculinity. It is aimed, on one hand, from the reproduction of what is already known and/or experienced by male aggressors in the family, as repetitions of behavior. And on the other, present themselves as a state of illness, addiction or psychopathy

Um sistema para simular o comportamento de bancos trifásicos de reguladores de tensão usados em sistemas de distribuição de energia elétrica

Coordenação de Aperfeiçoamento de Pessoal de Nível Superior

Infoestrutura: um sistema em nuvem para prover contexto como serviço no cenário de internet das coisas integrado a ambientes veiculares

Through numerous technological advances in recent years along with the popularization of computer devices, the company is moving towards a paradigm “always connected”. Computer networks are everywhere and the advent of IPv6 paves the way for the explosion of the Internet of Things. This concept enables the sharing of data between computing machines and objects of day-to-day. One of the areas placed under Internet of Things are the Vehicular Networks. However, the information generated individually for a vehicle has no large amount and does not contribute to an improvement in transit, once information has been isolated. This proposal presents the Infostructure, a system that has to facilitate the efforts and reduce costs for development of applications context-aware to high-level semantic for the scenario of Internet of Things, which allows you to manage, store and combine the data in order to generate broader context. To this end we present a reference architecture, which aims to show the major components of the Infostructure. Soon after a prototype is presented which is used to validate our work reaches the level of contextualization desired high level semantic as well as a performance evaluation, which aims to evaluate the behavior of the subsystem responsible for managing contextual information on a large amount of data. After statistical analysis is performed with the results obtained in the evaluation. Finally, the conclusions of the work and some problems such as no assurance as to the integrity of the sensory data coming Infostructure, and future work that takes into account the implementation of other modules so that we can conduct tests in real environments are presented.

Comportamento da adição do carbeto de nióbio (nBC) na matriz metálica do aço ferrítico 15kH2mfa

The 15Kh2MFA steel is a kind of Cr-Mo-V family steels and can be used in turbines for energy generation, pressure vessels, nuclear reactors or applications where the range of temperature that the material works is between 250 to 450°C. To improve the properties of these steels increasing the service temperature and the thermal stability is add a second particle phase. These particles can be oxides, carbides, nitrites or even solid solution of some chemical elements. On this way, this work aim to study the effect of addition of 3wt% of niobium carbide in the metallic matrix of 15Kh2MFA steel. Powder metallurgy was the route employed to produce this metallic matrix composite. Two different milling conditions were performed. Condition 1: milling of pure 15Kh2MFA steel and condition 2: milling of 15Kh2MFA steel with addition of niobium carbide. A high energy milling was carried out during 5 hours. Then, these two powders were sintered in a vacuum furnace (10-4torr) at 1150 and 1250°C during 60 minutes. After sintering the samples were normalized at 950°C per 3 minutes followed by air cooling to obtain a desired microstructure. Results show that the addition of niobium carbide helps to mill faster the particles during the milling when compared with that steel without carbide. At the sintering, the niobium carbide helps to sinter increasing the density of the samples reaching a maximum density of 7.86g/cm³, better than the melted steel as received that was 7,81g/cm³. In spite this good densification, after normalizing, the niobium carbide don t contributed to increase the microhardness. The best microhardness obtained to the steel with niobium carbide was 156HV and to pure 15Kh2MFA steel was 212HV. It happened due when the niobium carbide is added to the steel a pearlitic structure was formed, and the steel without niobium carbide submitted to the same conditions reached a bainitic structure

Avaliação do comportamento reológico de pastas de cimento para poços de petróleo com adição de plastificantes

The isolation of adjacent zones encountered during oilwell drilling is carried out by Portland-based cement slurries. The slurries are pumped into the annular positions between the well and the casing. Their rheological behavior is a very important component for the cementing process. Nowadays, several alternative materials are used in oilwell cementing, with goal the modification and the improvement of their properties, mainly the increase of the fluidity. And this can be reached by using plasticizers additives able to account for different oilwell conditions, yielding compatible cement slurries and allowing enough time for the complete cementing operation. If the rheological properties of the slurry are properly characterized, the load loss and flow regime can be correctly predicted. However, this experimental characterization is difficult. Rheological models capable of describing the cement slurry behavior must be capable of predicting the slurry cement deformation within reasonable accuracy. The aim of this study was to characterize rheologically the slurries prepared with a especial class of Portland cement, water and plasticizers based on lignosulfonate, melamine and polycarboxylate at temperatures varying from 27°C to 72°C. The tests were carried out according to the practical recommendations of the API RP 10B guidelines. The results revealed a great efficiency and the dispersive power of the polycarboxylate, for all temperatures tested. This additive promoted high fluidity of the slurries, with no sedimentation. High lignosulfonate and melamine concentrations did not reduce the rheological parameters (plastic viscosity and yield stress) of the slurries. It was verified that these additives were not compatible with the type of cement used. The evaluated rheological models were capable of describing the behavior of the slurries only within concentration and temperature ranges specific for each type of additive