Nitriding in cathodic cage of stainless steel AISI 316: influence of sample position

R.R.M. de Sousa et al. Nitriding in cathodic cage of stainless steel AISI 316: Influence of sample position. Vacuum, [s.l.], n.83, 2009. Disponivel em: . Acesso em: 04 out.2010.

Effect of cooling rate on properties of plasma nitrided AISI 1010 steel

In this work, AISI 1010 steel samples were plasma nitrided into 20% N 2 100 Pa and 400 Pa for N 2 and H 2 , respectively), temperatures of 500 and 580 °C, during 2 h. Three different procedures for cooling were accomplished after nitriding. In the first procedure the cooling occurred naturally, that is, the sample was kept on substrate holder. In the second one the sample was pulled off and cooling in a cold surface. Finally, in the third cooling process the sample was pulled off the substrate holder down into special reservoir filled with oil held at ambient temperature. The properties of the AISI 1010 steel samples were characterized by optical and electron microscopy, X-ray diffraction, Mössbauer spectroscopy and microhardness tests. Thermal gradient inside the sample kept on substrate holder during cooling process was measured by three inserted thermocouples at different depths. When samples were cooled rapidly the transformation of ϵ-Fe 2 − 3 N to γ′-Fe 4 N was inhibited. Such effect is indicated by the high concentration of ϵ-Fe compound zone. To get solid state solution of nitrogen in the diffusion zone, instead of precipitates of nitride phases, the cooling rate should be higher than a critical value of about 0.95 °C/s. When this value is reached at any depth of the diffusion zone, two distinct diffusion zones will appear. Temperature gradients were measured inside the samples as a consequence of the plasma treatment. It's suggested the need for standardization of the term “treatment temperature” for plasma treatment because different nitrided layer properties could be reported for the same “treatment temperature”.

Desgaste corrosivo-cavitativo-erosivo de um aço-carbono em meio aquoso com frações de sal (NaCl), CO2 e particulados sólidos (SiO2)

A batch of eighty-four coupons of low carbon steel were investigated at laboratory conditions under a corrosive, cavitative-corrosive (CO2) and corrosive-erosive (SiO2 + CO2) in an aqueous salt solution and two levels of temperature. The following measurements were made on Vickers (HV0,05, HV0,10, HV0,20) Microhardness tests at three levels of subsurface layer. A turbulent flow collided on the cylindrical sample, with and without mechanical stirring and gas bubbling, with and without fluid contamination by solid particles of SiO2, at two temperatures. Surface Roughness and Waviness, under two conditions "as received, after machining" and "after worn out", as well as gravimetric and electrochemical parameter were measured on the two opposite generatrices of each cylindrical sample, on the flow upstream (0°) and downstream (180°) by Profilometry, Mass Variation and Linear Polarization Resistance (LPR). The results of the Microhardness and Surface Texture of all coupons were subjected to statistical comparison, using the software Statgraphics® Centurion XVI, 95% statistical certainty, and significant differences were observed in some arrays of measurements. The corrosive wear rate measured by LPR and mass variation shown to be sensitive to the presence of bubbles and hydrodynamic fluctuations inside the cell, considering the temperature and contamination of corrosive fluid by solid particles. The main results of visual inspection relative to some topologies of the surface damages involving different mechanisms that were seen to give explanation for some fluctuations in wear rates of the steel experimentally investigated