Membrana de alumina anódica: comportamento da microestrutura e estudo das propriedades ópticas após tratamento térmico

Thin commercial aluminum electrolytic and passed through reactions was obtained with anodic alumina membranes nanopores. These materials have applications in areas recognized electronic, biomedical, chemical and biological weapons, especially in obtaining nanostructures using these membranes as a substrate or template for processing nanowires, nanodots and nanofibers for applications noble. Previous studies showed that the membranes that have undergone heat treatment temperature to 1300° C underwent changes in morphology, crystal structure and optical properties. This aim, this thesis, a study of the heat treatment of porous anodic alumina membranes, in order to obtain and to characterize the behavior changes structures during the crystallization process of the membranes, at temperatures ranging between 300 and 1700° C. It was therefore necessary to mount a system formed by a tubular furnace resistive alumina tube and controlled environment, applying flux with special blend of Ag-87% and 13% N2, in which argon had the role of carrying out the oxygen nitrogen system and induce the closing of the pores during the densification of the membrane. The duration of heat treatment ranged from 60 to 15 minutes, at temperatures from 300 to 1700° C respectively. With the heat treatment occurred: a drastic reduction of porosity, grain growth and increased translucency of the membrane. For the characterization of the membranes were analyzed properties: Physical - thermogravimetric, X-ray diffraction, BET surface area; morphological - SEM, EDS through compositional and, optical absorbance, and transmittance in the UV-VIS, and FTIR. The results using the SEM showed that crystallization has occurred, densification and significant changes in membrane structure, as well as obtaining microtube, the BET analysis showed a decrease in specific surface area of the membranes has to 44.381 m2.g-1 to less than 1.8 m2.g-1 and in the analysis of transmittance and absorbance was found a value of 16.5% in the range of 800 nm, characteristic of the near infrared and FTIR have confirmed the molecular groups of the material. Thus, one can say that the membranes were mixed characteristics and properties which qualify for use in gas filtration system, as well as applications in the range of optical wavelength of the infra-red, and as a substrate of nanomaterials. This requires the continuation and deepening of additional study

Alterações morfofisiológicas e moleculares em resposta a estresses abióticos em mamona (Ricinus communis L.)

The use of fossil fuels has been considered one of reason for the increase of pollution in the atmosphere and it may be related to the climate changes. Then, the research of the new sources of fuels will be important. Considering this, the use of biodiesel has been considered not as bad as petrol. The castor bean (Ricinus communis L.) is an important oilseed, which belongs to Euphorbiaceae family, and the oil found in the seed has important characteristics for biodiesel. This plant is considered as “rustic” as it does not need so much water for its development and oil production. Due to this, this plant has been considered to be ideal in semi-arid regions, such as the Northeast of Brazil. The aim of his study is to better understand the responses to abiotic stresses (drought and salinity) from castor bean plants using morphological, physiological and molecular tools. In order to do this, the castor bean plants were subjected to salt stress (50, 100, 150 and 200 mM NaCl) in a controlled environment and drought stress (5, 10, 15 days and 10 days cyclic). After these treatments, these plants were subjected to different analyzes: a) the expansion and retention of water from leaves; b) anatomy using leaves and roots. Based on these results, we found that castor suffered decrease in leaf area with increase drought stress, however restricted water loss, probably by accumulation of compatible solutes in the leaves. The anatomy data showed modifications in the vascular system. These modifications observed suggested that castor bean plant may be resistant to stress as it was verified in 5 days of drought as well as in 100 mM NaCl. In both conditions, these plants were fine. Probably these plants keep some solutes in the cell and then maintain the cell tugor. The data obtained in this study gave a better idea how castor bean plant responds to abiotic stress conditions - drought and salt stress

Membrana de alumina anódica: comportamento da microestrutura e estudo das propriedades ópticas após tratamento térmico

Thin commercial aluminum electrolytic and passed through reactions was obtained with anodic alumina membranes nanopores. These materials have applications in areas recognized electronic, biomedical, chemical and biological weapons, especially in obtaining nanostructures using these membranes as a substrate or template for processing nanowires, nanodots and nanofibers for applications noble. Previous studies showed that the membranes that have undergone heat treatment temperature to 1300° C underwent changes in morphology, crystal structure and optical properties. This aim, this thesis, a study of the heat treatment of porous anodic alumina membranes, in order to obtain and to characterize the behavior changes structures during the crystallization process of the membranes, at temperatures ranging between 300 and 1700° C. It was therefore necessary to mount a system formed by a tubular furnace resistive alumina tube and controlled environment, applying flux with special blend of Ag-87% and 13% N2, in which argon had the role of carrying out the oxygen nitrogen system and induce the closing of the pores during the densification of the membrane. The duration of heat treatment ranged from 60 to 15 minutes, at temperatures from 300 to 1700° C respectively. With the heat treatment occurred: a drastic reduction of porosity, grain growth and increased translucency of the membrane. For the characterization of the membranes were analyzed properties: Physical - thermogravimetric, X-ray diffraction, BET surface area; morphological - SEM, EDS through compositional and, optical absorbance, and transmittance in the UV-VIS, and FTIR. The results using the SEM showed that crystallization has occurred, densification and significant changes in membrane structure, as well as obtaining microtube, the BET analysis showed a decrease in specific surface area of the membranes has to 44.381 m2.g-1 to less than 1.8 m2.g-1 and in the analysis of transmittance and absorbance was found a value of 16.5% in the range of 800 nm, characteristic of the near infrared and FTIR have confirmed the molecular groups of the material. Thus, one can say that the membranes were mixed characteristics and properties which qualify for use in gas filtration system, as well as applications in the range of optical wavelength of the infra-red, and as a substrate of nanomaterials. This requires the continuation and deepening of additional study