Desgaste corrosivo-cavitativo-erosivo de um aço-carbono em meio aquoso com frações de sal (NaCl), CO2 e particulados sólidos (SiO2)

A batch of eighty-four coupons of low carbon steel were investigated at laboratory conditions under a corrosive, cavitative-corrosive (CO2) and corrosive-erosive (SiO2 + CO2) in an aqueous salt solution and two levels of temperature. The following measurements were made on Vickers (HV0,05, HV0,10, HV0,20) Microhardness tests at three levels of subsurface layer. A turbulent flow collided on the cylindrical sample, with and without mechanical stirring and gas bubbling, with and without fluid contamination by solid particles of SiO2, at two temperatures. Surface Roughness and Waviness, under two conditions "as received, after machining" and "after worn out", as well as gravimetric and electrochemical parameter were measured on the two opposite generatrices of each cylindrical sample, on the flow upstream (0°) and downstream (180°) by Profilometry, Mass Variation and Linear Polarization Resistance (LPR). The results of the Microhardness and Surface Texture of all coupons were subjected to statistical comparison, using the software Statgraphics® Centurion XVI, 95% statistical certainty, and significant differences were observed in some arrays of measurements. The corrosive wear rate measured by LPR and mass variation shown to be sensitive to the presence of bubbles and hydrodynamic fluctuations inside the cell, considering the temperature and contamination of corrosive fluid by solid particles. The main results of visual inspection relative to some topologies of the surface damages involving different mechanisms that were seen to give explanation for some fluctuations in wear rates of the steel experimentally investigated

Eficácia do cimento de ionômero de vidro como selante oclusal sobre a paralisação de lesões cariosas em dentina

Dental caries consists in a multifactorial and dynamic process. The knowledge of the ionic interactions among dental tissues and dental biofilm make possible its understanding as a process that can be stopped. Recently, the use of sealants have lost its function as preventive agent and passed to be argued as a possible therapeutical agent. This happens by hindering the substratum flow to the lesion inner and, therefore, controls the advance of the process. This study aimed to evaluate glass ionomer cement as a not invasive technique of treatment in occlusal caries without clinical cavitation, but with dentinal involvement. The research was accomplished using a controlled clinical trial with two groups (experimental and control) in 38 subjects (8-18 years) with 51 molars. The teeth of the experimental group were sealed with glass ionomer cement (Vidrion-R, S.S.White, Juiz de Fora, Brazil) and the molars control did not suffer intervention. The experimental group was followed by a year and the control by 8 months due the progression of the carious injury. Both groups were reevaluated to each 4 months with the use of clinical, radiographic and laser fluorescence (DIAGNOdent®) examination. The analysis of the clinical evaluation did not observe a significant difference between experimental and control groups. However, analysis with radiographic and laser fluorescence (DIAGNOdent®) examination observed a significant difference (p> 0,05) between groups, demonstrating a wors condition to the group without intervention. The results suggest that glass ionomer cement as sealant can be efficient to paralyze dentinal caries without clinical cavitation

Extração e análise da fração lipídica da microalga monoraphidium sp., síntese e caracterização do seu biodiesel

The cultivation of microalgae biomass in order to produce biodiesel arises as an extremely promising aspect, in that the microalgae culture includes short cycle of reproduction, smaller areas for planting and residual biomass rich in protein content. The present dissertation evaluates the performance and features, through spectrometry in the region of infrared with transformed Fourier (FTIR) and spectrometry in the region of UVvisible (UV-Vis), of the extracted lipid material (LM) using different techniques of cell wall disruption (mechanical agitation at low and at high spin and agitation associated with cavitation). The technique of gas chromatography (GC) brought to light the success of alkaline transesterification in the conversion of oil into methyl monoesters (MME), which was also analyzed by spectroscopic techniques (FTIR, proton magnetic resonance (1H NMR) and carbon (13C NMR). Through thermogravimetric analysis (TGA) were analyzed the lipid material (LM), biodiesel and the microalgae biomass. The method which provided the best results concerning the efficiency in extraction of the LP of Monoraphidium sp. (12,51%) was by mechanical agitation at high spin (14 000 rpm), for 2 hours being the ideal time, as shown by the t test. The spectroscopic techniques (1H NMR, 13C NMR and FTIR) confirmed that the structure of methyl monoesters and the chromatographic data (CG) revealed a high content of saturated fatty acid esters (about 70%) being the major constituent eicosanoic acid (33,7%), which justifies the high thermal stability of microalgae biodiesel. The TGA also ratified the conversion rate (96%) of LM into MME, pointing out the quantitative results compatible with the values obtained through GC (about 98%) and confirmed the efficiency of the extraction methods used, showing that may be a good technique to confirm the extraction of these materials. The content of LM microalgae obtained (12,51%) indicates good potential for using such material as a raw material for biodiesel production, when compared to oil content which can be obtained from traditional oil for this use, since the productivity of microalgae per hectare is much larger and requires an extremely reduced period to renew its cultivation