Oxide type spinel AB2O4 presents structure adjusted for application in the automobile industry. The spinel of cobalt has many practical applications had its excellent physical and chemical properties such as catalyst in hydrocarbon oxidation reaction. The CeO2 has been used in many of these processes because it assigns to a material with excellent thermal resistance and mechanics, high capacity of oxygen stockage (OSC) among others properties. This work deals with the synthesis, characterization and catalytic application of spinel of cobalt and CeO2 with fluorita structure, obtained for method of Pechini and method of Gel-Combustion. The process of Pechini, the puff was obtained at 300 ºC for 2 h in air. In the process of Gel-Combustion the approximately at 350 ºC material was prepared and burnt for Pyrolysis, both had been calcined at 500 ºC, 700 ºC, 900 ºC and 1050 ºC for 2 h in air. The materials of the calcinations had been characterized by TG/DTA, electronic microscopy of sweepings (MEV), spectroscopy of absorption in the infra-red ray (FTIR) and diffraction of X-rays (DRX). The obtained material reaches the phase oxide at 450 oC for Pechini method and 500 °C for combustion method. The samples were submitted catalytic reaction of n-hexane on superficies of materials. The reactor function in molar ration of 0, 85 mol.h-1.g-1 and temperature of system was 450 °C. The sample obtained for Pechini and support in alumine of superficial area of 178,63 m2.g-1 calcined at 700 ºC, give results of catalytic conversions of 39 % and the sample obtained for method of gel-combustion and support in alumina of 150 mesh calcined at 500 ºC result 13 % of conversion. Both method were selective specie C1

Relevância:

60.00% 60.00%

Publicador:

Resumo:

In this work, the objective in study was the development of a biossensor potencyometric for urea detection, starting from the extracted urease of soy grains. Initially, was made a chemometrics study, through a planning factorial 24, objectified to find great conditions for the extraction of the urease without its properties were affected. Starting from this study, the best conditions were determined for the obtaining of rich extracts in urease, allowing the biossensors making with good characteristics. These were made using a platinum electrode as transducer with the dispersed urease in chitosan head office and reticulated in glutaraldehyde vapor. The biossensors obtained presented a limit of urea detection the same to 0,33 mM and lineal strip between 0,33 and 3 mM of the substratum. The time of answer was considered loud, mainly, in low concentrations of the substratum, where it was taken about 5 minutes by analysis. For high concentrations that time was reduced for not more than one minute. The time of life was limited by the adherence of the enzymatic membrane to the transducer, but it was possible to maintain the biossensor with operation for one month with about 50 accomplished measures. Application of the biossensor for analyses of fertilizers to the urea base presented excellent result for a sample with few interfering, but it was different when the used fertilizer was originating from of a complex sample. Even so the label was not expressed the text of nitrogen it was totally coming of the urea. An evaluation of the kinetic parameters of the catalytic reaction of the biossensor showed coherence with the results exposed in the literature

Relevância:

60.00% 60.00%

Publicador:

Resumo:

The groundwater pollution arising due to fuel leaks gas stations has presented a problem aggravating. Increasingly studies related to environmental problems such accidents and seek to propose some solutions for the treatment of groundwater and soils that are contaminated by gasoline. This study evaluated the use of molecular sieve TiSBA-15 as a catalyst for the reaction of removing of volatile organic compounds, particularly benzene, toluene, ethylbenzene and xylenes, known as BTEX, one of the main pollutants found in groundwater. The catalyst was synthesized by the method post-synthesis techniques and characterized by XSD, TG/DTG, adsorption/desorption of N2, XRF-EDX, for checking the incorporation of titanium and formation of the structure of the catalyst. The reaction occurred with the presence of hydrogen peroxide, H2O2, in aqueous medium to form hydroxyl radicals, which are needed in the process of removal of BTEX compounds. The catalytic reaction was carried out for 5 hours at 60 °C, pH to 3.0, and analyzes of the compounds were made in a gas chromatograph with a flame detection means photoionization static headspace (HS-GC-PID). The catalytic tests have shown the efficacy of using this type of catalyst for the removal of these volatile organic compounds, having a removal rate of 90.60% in the range where the catalyst was studied TiSBA-15(5,0)

Relevância:

60.00% 60.00%

Publicador:

Resumo:

Stimulus encouraging the production and consumption of biodiesel favors the policy of pre-serving the environment, contributing to the reduction of greenhouse gas reducing climate change. The current trend of research in this field focuses on improving these processes with the use of heterogeneous catalysts, seeing has significant advantages such as: low contamination of products, ease of separation of the catalyst from the reaction medium, possibili-ty of reuse of the catalyst, decreased corrosion problems. The objective of this research was to optimize the synthesis of AlSBA-15 for the production of biodiesel through transesterification process via ethyl route. For the optimization of hydrothermal synthesis of type AlSBA-15 catalyst has assembled a 23 factorial experimental matrix with eleven trials. The stoichiometric amounts of starting materials were varied according to different ratios Si / Al which is a factor in the experimental design, in addition to the time and temperature of aging of the synthesis gel. The material showed the best results of characterization (SBET = 591.7 (m2 / g), Vp = 0.83 (cm3 / g), Dp = 5.59 (nm), w = 6.48 (nm) was synthesized at 100 ° C for 24 hours, with a ratio Si / Al = 10.This material was applied as a heterogeneous catalyst in the reaction of ethyl transesterification as raw coconut oil in natura. Coconut oil presented suitable for obtaining biodiesel via ethyl route.The visual aspects and physical-chemical characteristics of the reaction products show that AlSBA-15 catalyst favored the reaction. According to physical-chemical analysis the order of oxidative stability of the product of the transesterification reaction was: catalytic reaction at 1500 ° C> non-catalytic reaction at 100 ° C> 100 ° C catalytic> catalytic reaction at 200 ° C Reaction. The results of oxidative stability and kinematic viscosity shows that the biodiesel produced in the catalytic sandblasting held at 150 ° C which was maintained within the ABNT NBR 7148, ABNT NBR 10441 and EN 14112.

Relevância:

60.00% 60.00%

Publicador:

Resumo:

The need to preserve the environment has led to the search for new materials for efficient disposal of chemical compounds that alter the stability of our natural resources. Among these resources, stands in first place the water, as a precious commodity and scarce, leading to the proper use and reuse. As a result, the World Health Organization has established maximum permissible values in drinking water, such as: 50 mg/L, 0, 1 mg/L and 0, 5 mg/L to at-3, at-2, NH 4, respectively. For these reasons, assesses the implementation of new materials and water treatment processes aiming at the removal of these compounds, such as alumina, in the form of powder or as a support for a catalytic system using inorganic membranes capable of supporting more severe conditions of temperature and pressure by opening new possibilities for applications of membrane reactors; and also for electrochemical treatments with doped diamond bobo electrodes (BDD) as anode and copper as cathode. For such purpose, was conducted the study of adsorption of nitrate in different times to assess the time required to achieve equilibrium by employing three commercial alumina called: acidic, basic and neutral alumina, with subsequent treatment only in the acidic alumina impregnating metals (PdCu/Al2O3) for the catalytic reaction. The materials were previously characterized by XRD, SEM techniques and ABET. Aluminas presented a considerable adsortive capacity of nitrate in the first thirty minutes, equivalent to 50% of removal reaching equilibrium in that time. After treatment, using alumina as catalyst for the reaction in batch reactor (Pd-Cu/Al2O3), the results were more favourable, totalling 64% reduction of ion NO3-at the end of three hours. On the other hand, the results for the catalytic reaction using the catalytic support Pd-Cu/TiO2 in membrane reactor proved to be low. -if, in this way, improve the conditions of catalytic system to optimize the process. Already, for the electrochemical tests using DDB1 electrodes as anode, and Cu, as cathode, there was a fairly significant nitrate reduction, approximately 80% of ion removal during three hours and cost viable applications.

Relevância:

60.00% 60.00%

Publicador:

Resumo:

Oxide type spinel AB2O4 presents structure adjusted for application in the automobile industry. The spinel of cobalt has many practical applications had its excellent physical and chemical properties such as catalyst in hydrocarbon oxidation reaction. The CeO2 has been used in many of these processes because it assigns to a material with excellent thermal resistance and mechanics, high capacity of oxygen stockage (OSC) among others properties. This work deals with the synthesis, characterization and catalytic application of spinel of cobalt and CeO2 with fluorita structure, obtained for method of Pechini and method of Gel-Combustion. The process of Pechini, the puff was obtained at 300 ºC for 2 h in air. In the process of Gel-Combustion the approximately at 350 ºC material was prepared and burnt for Pyrolysis, both had been calcined at 500 ºC, 700 ºC, 900 ºC and 1050 ºC for 2 h in air. The materials of the calcinations had been characterized by TG/DTA, electronic microscopy of sweepings (MEV), spectroscopy of absorption in the infra-red ray (FTIR) and diffraction of X-rays (DRX). The obtained material reaches the phase oxide at 450 oC for Pechini method and 500 °C for combustion method. The samples were submitted catalytic reaction of n-hexane on superficies of materials. The reactor function in molar ration of 0, 85 mol.h-1.g-1 and temperature of system was 450 °C. The sample obtained for Pechini and support in alumine of superficial area of 178,63 m2.g-1 calcined at 700 ºC, give results of catalytic conversions of 39 % and the sample obtained for method of gel-combustion and support in alumina of 150 mesh calcined at 500 ºC result 13 % of conversion. Both method were selective specie C1