Tratamento de borra de petróleo com sistemas microemulsionados

During the storage of oil, sludge is formed in the bottoms of tanks, due to decantation, since the sludge is composed of a large quantity of oil (heavy petroleum fractions), water and solids. The oil sludge is a complex viscous mixture which is considered as a hazardous waste. It is then necessary to develop methods and technologies that optimize the cleaning process, oil extraction and applications in industry. Therefore, this study aimed to determine the composition of the oil sludge, to obtain and characterize microemulsion systems (MES), and to study their applications in the treatment of sludge. In this context, the Soxhlet extraction of crude oil sludge and aged sludge was carried out, and allowing to quantify the oil (43.9 % and 84.7 % - 13 ºAPI), water (38.7 % and 9.15 %) and solid (17.3 % and 6.15 %) contents, respectively. The residues were characterized using the techniques of X-ray fluorescence (XRF), Xray diffraction (XRD) and transmission Infrared (FT-IR). The XRF technique determined the presence of iron and sulfur in higher proportions, confirming by XRD the presence of the following minerals: Pyrite (FeS2), Pyrrhotite (FeS) and Magnetite (Fe3O4). The FT-IR showed the presence of heavy oil fractions. In parallel, twelve MES were prepared, combining the following constituents: two nonionic surfactants (Unitol L90 and Renex 110 - S), three cosurfactants (butanol, sec-butanol and isoamyl alcohol - C), three aqueous phase (tap water - ADT, acidic solution 6 % HCl, and saline solution - 3.5 % NaCl - AP) and an oil phase (kerosene - OP). From the obtained systems, a common point was chosen belonging to the microemulsion region (25 % [C+S] 5 % OP and AP 70 %), which was characterized at room temperature (25°C) by viscosity (Haake Rheometer Mars), particle diameter (Zeta Plus) and thermal stability. Mixtures with this composition were applied to oil sludge solubilization under agitation at a ratio of 1:4, by varying time and temperature. The efficiencies of solubilization were obtained excluding the solids, which ranged between 73.5 % and 95 %. Thus, two particular systems were selected for use in storage tanks, with efficiencies of oil sludge solubilization over 90 %, which proved the effectiveness of the MES. The factorial design delimited within the domain showed how the MES constituents affect the solubilization of aged oil sludge, as predictive models. The MES A was chosen as the best system, which solubilized a high amount of aged crude oil sludge (~ 151.7 g / L per MES)

Síntese e caracterização de PSFC (Pr0,5Sr0,5Fe1-xCuxO3-δ, sendo x=0,2 e x=0,4) para aplicação como catodo de células a combustível de óxido sólido

The PSFC (Pr0.5Sr0.5Fe1-xCuxO3-δ) is a new mixed oxide perovskite and has been studied and evaluated the cathode materials for intermediate temperature solid oxide fuel cells (IT-SOFCs), mainly due to its good compatibility with the electrolyte (CGO) and its high ionic conductivity and electronic in intermediate temperature. In this work, PSFC powders with two different compositions (Pr0,5Sr0,5Fe0,8Cu0,2O3- PSFC5582 and Pr0,5Sr0,5Fe0,6Cu0,4O3-PSFC5564) were synthesized by the citrate method using a new route. The powders obtained were characterized by thermal analysis (Differential Scanning Calorimetry and Thermogravimetry), and the material calcined at 800, 900 and 1000 °C for 5h were analyzed by X-ray diffractometry (XRD), with the Rietveld refinement of the diffraction data and dilatometry. PSFC5582 composite films were obtained by screen printing of powder calcined at 1000 °C. The films were deposited on substrate ceria doped with gadolinia (CGO) and then sintered at 1050 °C for 2h. The electrochemical performance of the electrodes was evaluated by impedance spectroscopy and the interface electrode/electrolyte was observed by scanning electron microscopy (SEM). The specific resistance area (ASR) was 0.44 Ω.cm² at 800 °C, slightly lower than those reported in the literature for cathodes containing cobalt. The thermal expansion coefficients of both the PSFC compositions were obtained and varied between 13 and 15 x 10-6 °C-1 , in a temperature range of 200 to 650 °C, demonstrating the good thermal compatibility of cathodes with Ce0,9Gd0,1O1,95 electrolytes (CET = 12 x 10-6 °C).