Caracterização morfológica e microestrutural da perovskita BaCexPr1-xO3 sintetizada a partir do método de complexação combinando EDTA/Citrato

In this study, binary perovskite (BaCexO3) were doped with praseodymium (Pr) to obtainment of the ternary material BaCexPr1-xO3. This material was synthesized by the complexation method combining EDTA/Citrate with the stoichiometric ratio of the element Praseodymium ranging from x = 0.1 to x = 0.9 in order to determine the influence of this rare earth element on the morphology and microstructure of the final powder. At first the material was synthesized based on the route proposed by literature (Santos, 2010), and then characterized by SEM and XRD, besides being refined by the Rietveld method. In the material that had lowest residual parameter, S, and lowest average size of crystal, pH variation of synthesis solution was made in order to identify the influence of this parameter on the morphology and microscopy of the final powder. The results show that addition of praseodymium did not directly influence the crystallographic and lattice parameters, keeping even the same orthorhombic structure of the binary material BaCexO3, according to Yamanaka et al (2003). Material type BaCe0,2Pr0,8O3 had lowest residual parameter (S=1.4) and lowest average size of crystallite (26.4 nm), being used as reference in the pH variation of synthesis solution for 9, 7, 5 and 3, respectively. Variation of this parameter showed that when the synthesis solution pH was decreased to below 11, there was an increase in the average size of crystals, for pH 9, about 58.3%, for pH 7 (30.3 %), for pH 2 (2.3%) and for pH 3 (42%), indicating that the value initially used and quoted by Santos (2010) was the most coherent

Síntese e caracterização de membranas zeolíticas tipo mfi e aplicação em separação de aromáticos

The synthesis of MFI-type zeolite membranes was carried by the process in situ or hydrothermal crystallization. We studied the homogenization time of the room temperature and gel filtration just before the crystallization step performed out in an oven, thus obtaining a more uniform zeolite film. The powder synthesized zeolite (structure type MFI, Silicalite) was characterized by several complementary techniques such as Xray diffraction (XRD), scanning electron microscopy (SEM), thermal analysis, temperature programmed desorption (TPD), Fourier Transform infrared spectroscopy (FTIR) and textural analysis by nitrogen adsorption (specific surface area). For the purpose of evaluating the quality of the layer supported on the ceramic support, N2 permeation tests were carried starting from room temperature to 600 °C, where values were observed values more appropriate permeation from 200 °C. With the data obtained, it was made into a graph of temperature versus permeation function, the curve of surface diffusion was found. For scanning electron microscopy, we observed the formation of homogeneous crystals and the zeolite film showed no fissures or cracks, indicating that the process of synthesis and subsequent treatments not damaged the zeolite layer on the support. Carried permeation studies were found values ranging from 3.64x10-6 to 3.78x10-6, 4.71x10-6 to 5.02x10-6, to pressures 20 and 25 psi, respectively. And the mixture xylenes/N2 values were between 5.39x10-6 to 5.67x10-6 and 8.13x10-6 to 8.36x10-6, also for pressures of 20 and 25 psi. The values found for the separation factor were 15.22 at 400 °C in the first experiment and 1.64 for the second experiment at a temperature of 150 °C. It is concluded that the Silicalite membrane was successfully synthesized and that it is effective in the separation of binary mixtures of xylenes