Efeito da adição de grafite expandido por microondas nas propriedades térmicas, elétricas e mecânicas de nanocompósitos de matriz epóxi

Epoxy based nanocomposites with 1 wt % and 3 wt % of nanographite were processed by high shear mixing. The nanographite was obtained by chemical (acid intercalation), thermal (microwave expansion) and mechanical (ultrasonic exfoliation) treatments. The mechanical, electrical and thermal behavior of the nanocomposites was determined and evaluated as a function of the percentage of reinforcement. According to the experimental results, the electrical conductivity of epoxy was not altered by the addition of nanographite in the contents evaluated. However, based on the mechanical tests, nanocomposites with addition of 1 wt.% and 3 wt.% of nanographite showed increase in tensile strength of 16,62 % and 3,20 %, respectively, compared to the neat polymer. The smaller increase in mechanical strength of the nanocomposite with 3 wt.% of nanographite was related to the formation of agglomerates. The addition of 1 wt.% and 3 wt.% of nanographite also resulted in a decrease of 6,25 % and 17,60 %, respectively, in the relative density of the material. Thus, the specific strength of the nanocomposites was approximately 33,33 % greater when compared to the neat polymer. The addition of 1 wt.% and 3 wt.% of nanographite in the material increased the mean values of thermal conductivity in 28,33 % and 132,62 %, respectively, combined with a reduction of 26,11 % and 49,80 % in volumetric thermal capacity, respectively. In summary, it has been determined that an addition of nanographite of the order of 1 wt.% and 3 wt.% produced notable elevations in specific strength and thermal conductivity of epoxy

Análise de viabilidade técnica de utilização da Fibra de bananeira com resina sintética em Compósitos

This paper aims to present the feasibility of using a composite using discarded material from the cultivation of banana tree (pseudostem), which is fibrillated together with synthetic resin replacing glass fiber to be used in structural elements that do not demand large mechanical stress such as reservoirs, troughs, domes, sewage pipes etc.. For this, there were studies about the mechanical properties of a composite made with polyester resin and fiber of banana tree (Musa sp, musac), in which the splints were removed from the pseudostem, being made fibrillation by hand, with the aid of a brush steel, followed by natural drying. After treatment for cleaning and removal of wax, the fiber was cut into pieces of approximately 60 mm to 100 mm, for, together with synthetic resin, make cards of a features fiber composite with random orientation relative to the weight of the resin. We used three different percentages of fiber (3%, 6% and 9%), in order to make a comparative study between them and what would be the one with the best performance. Were manufactured specimens of each material and then subjected to uniaxial tensile tests, three point bending, moisture absorption and thermal characteristics. The results show that, in general, the use of banana tree fiber is feasible simply by an improvement in the production process (machining of the procedure) and greater care in the manufacture of parts

Obtenção e caracterização de um compósito de poliuretano de mamona e pó de vidro para aplicações em insolantes térmicos

Thermal insulation is used to protect the heated or cooled surfaces by the low thermal conductivity materials. The rigid ricin polyurethane foams (PURM) are used for thermal insulation and depend on the type and concentration of blowing agent. Obtaining PURM occurs by the use of polyol, silicone, catalyst and blowing agent are pre -mixed, reacting with the isocyanate. The glass is reusable, returnable and recyclable heat insulating material, whose time of heat dissipation determines the degree of relaxation of its structure; and viscosity determines the conditions for fusion, operating temperatures, annealing, etc. The production of PURM composites with waste glass powder (PV) represents economical and renewable actions of manufacturing of thermal insulating materials. Based on these aspects, the study aimed to produce and characterize the PURM composites with PV, whose the mass percentages were 5, 10, 20, 30, 40 and 50 wt%. PURM was obtained commercially, while the PV was recycled from the tailings of the stoning process of a glassmaking; when the refining process was applied to obtain micrometer particles. The PURM + PV composites were studied taking into account the standard sample of pure PURM and the influence of the percentage of PV in this PURM matrix. The results of the chemical, physical and morphological characterization were discussed taking into account the difference in the microstructural morphology of the PURM+PV composites and the pure PURM, as well the results of the physicochemical, mechanical e thermophysical tests by values obtained of density, hardness, compressive strength, specific heat, thermal conductivity and diffusivity. In general, the structure of pure PURM showed large, elongated and regular pores, while PURM+PV composites showed irregular, small and rounded pores with shapeless cells. This may have contributed to reducing their mechanical strength, especially for PURM - PV50. The hardness and density were found to have a proportional relationship with the PV content on PURM matrix. The specific heat, thermal diffusivity and thermal conductivity showed proportional relationship to each other. So, this has been realized that the increasing the PV content on PURM matrix resulted in the rise of diffusivity and thermal conductivity and the decrease of the specific heat. However, the values obtained by the PURM composites were similar the values of pure PURM, mainly the PURM-PV5 and PURM-PV10. Therefore, these composites can be applied like thermal insulator; furthermore, their use could reduce the production costs and to preserve the environment

Hidrofobização, caracterização e aplicação da vermiculita para remoção de óleo insolúvel em água

Among the various layered silicates, vermiculite has been used as one of the adsorbent material by presenting the ion exchange capacity which facilitates the removal of organic compounds which are potential pollutants in relation to the water surface. The importance of the modification of clay minerals by hydrophobization with carnauba wax establishes the increase in oil removal capacity in aqueous medium, it contributes to a better environment for life in ecosystems. The vermiculite when expanded decreases its hydrophobicity requiring the use of a hydrophobizing leaving - the organoclay. In this work were used in the process of modifying the particle sizes of vermiculite -18+16, -16 +20 and -20 +35 #. Samples of vermiculite hydrophobized with carnauba wax and clay mineral without hydrophobizing were characterized with physicochemical analyzes and analytical. Techniques were used: thermal analysis (thermogravimetry and derivative thermogravimetry), infrared spectroscopy, scanning electron microscopy, fluorescence rays - x adsorption tests. The TG / DTG was used to evaluate the thermal behavior of expanded vermiculite and carnauba wax and samples hidrofobizadas with percentages of 5, 10 and 15 % by weight of hydrophobizing. The results of FTIR confirmed increase of the characteristic signs of carnauba wax in samples hidrofobizadas as the greatest amount of hydrophobizing the clay mineral used in hydrophobization. Thermogravimetry and FTIR show based on the results that coating the surface of the vermiculite occur homogeneously. The data obtained by the technique of x-ray fluorescence with loss on ignition confirmed the results of thermogravimetric analysis in relation to the percentage of wax incorporated. The fluorescence indicates through information provided by the analysis shows that the material covered - is homogeneous. The mev inspection was used to texture and morphology of the clay mineral with and without carnauba wax. The scanning electron microscopy confirms the deposition of wax evenly over the surface of the mineral as indicated by the other techniques. To verify the adsorption capacity of the clay without hydrophobizing hydrophobized and used a fixed volume of water to 1 ½ liters in each experiment with 3 g to 50 g of oil sample. The results show that better extraction of oil for the material processed corresponds to 260 % relative to the weight of the sample coated and greater than 80 % of the oil drop in the system