Avaliação de catalisadores a base de carbeto e nitreto de molibdênio na obtenção de lactitol via hidrogenação da lactose

Seeking a greater appreciation of cheese whey was developed to process the hydrogenation of lactose for the production of lactitol, a polyol with high added value, using the catalyst Ni / activated carbon (15% and 20% nickel), the nitride Mo2N, the bimetallic carbide Ni-Mo/ activated carbon and carbide Mo2C. After synthesis, the prepared catalysts were analyzed by MEV, XRD, laser granulometry and B.E.T. The reactor used in catalytic hydrogenation of lactose was the type of bed mud with a pressure (68 atm), temperature (120 oC) and stirring speed (500 rpm) remained constant during the experiments. The system operated in batch mode for the solid and liquid and semi-continuous to gas. Besides the nature of the catalyst, we studied the influence of pH of reaction medium for Mo2C carbide as well as evaluating the character of the protein inhibitor and chloride ions on the activity of catalysts Ni (20%)/Activated Carbon and bimetallic carbide Ni-Mo/Activated Carbon. The decrease in protein levels was performed by coagulation with chitosan and adsorption of chloride ions was performed by ion exchange resins. In the process of protein adsorption and chloride ions, the maximum percentage extracted was about 74% and 79% respectively. The micrographs of the powders of Mo2C and Mo2N presented in the form of homogeneous clusters, whereas for the catalysts supported on activated carbon, microporous structure proved impregnated with small particles indicating the presence of metal. The results showed high conversion of lactose to lactitol 90% for the catalyst Ni (20%)/Activated Carbon at pH 6 and 46% for the carbide Mo2C pH 8 (after addition of NH4OH) using the commercial lactose. Monitoring the evolution of the constituents present in the reaction medium was made by liquid chromatography. A kinetic model of heterogeneous Langmuir Hinshelwood type was developed which showed that the estimated constants based catalysts promoted carbide and nitride with a certain speed the adsorption, desorption and production of lactitol

Recuperação e purificação de ramnolipídeos produzidos por pseudomonas aeruginosa P029-GVIIA utilizando melaço de cana como substrato

Biosurfactants are molecules produced by microorganisms mainly bacteria as Pseudomonas and Bacillus. Among the biosurfactants, rhamnolipids play an important role due to their tensoactive as well as emulsifying properties. Besides can be produced in a well consolidated way the production costs of biosurfactants are quite expansive mainly if downstream processing is goning to be considered. Actually, attention has been given to identification of biosurfactants as well as optimization of its fermentative processes including downstream ones. This work deals with the development of strategies to recovery and purification of rhamnolipids produced by Pseudomonas aeruginosa P029-GVIIA using sugar-cane molasses as substrate. Broth free of cells was used in order to investigate the best strategies to recovery and purification produced by this system. Between the studied acids (HCl and H2SO4) for the acid precipitation step, HCl was the best one as has been showed by the experimental design 24. Extraction has been carried out using petroleum ether and quantification has been done using the thioglycolic acid method. Adsorption studies were carried out with activated carbon in a batch mode using a 24 experimental design as well as combined with an hydrophobic resin Streamline Phenyl aiming to separate the produced biosurfactant. Biosurfactant partial identification was carried out using High Performance Liquid Chromatography (HPLC). Experiments in batch mode showed that adsorption has been controlled mainly by pH and temperature. It was observed a reduction of 41.4% for the liquid phase and the solid phase it was possible to adsorb up to 15 mg of rhamnolipd/g of activated carbon. The kinetics of adsorption has been well fitted to a pseudo-first order reaction with velocity constant (k1) of 1.93 x 10-2 min-1. Experiments in packed bed ranging concentration on eluent (acetone) has been shown the highest recovery factor of 98% when pure acetone has been used. The combined effect if using activated carbon with an hydrophobic resin Streamline Phenyl has been shown successful for the rhamnolipids purification. It has been possible to purify a fraction of the crude broth with 98% of purity when the eluted of activated carbon packed bed was used with pure acetone

Ensaios de tratabilidade aplicados a determinação de parâmetros para dimensionamento de processos de tratamento de água de manancial eutrofizado

Eutrophication is a growing process present in the water sources located in the northeast of Brazil. Among the main consequences of these changes in trophic levels of a water source, stands out adding complexity to the treatment to achieve water standards. By these considerations, this study aimed to define, on a laboratory scale, products and operational conditions to be applied in the processing steps using raw water from Gargalheiras dam, RN, Brazil. The dam mentioned shows a high number of cyanobacteria, with a concentration of cells / ml higher than that established by Decree No. 518/04 MS. The same source was also considered by the state environmental agency in 2009 as hypereutrophic. The static tests developed in this research simulated direct filtration (laboratory filters) and pre-oxidation with chlorine and powdered activated carbon adsorption. The research included the evaluation of the coagulants aluminum hydrochloride (HCA) and alum (SA). The development of the research investigated the conditions for rapid mixing, the dosages of coagulants and pHs of coagulation by the drawing of diagrams. The interference of filtration rate and particle size of filtering means were evaluated as samples and the time of contact were tested with chlorine and activated carbon. By the results of the characterization of the raw water source it was possible to identify the presence of a high pH (7.34). The true color was significant (29 uH) in relation to the apparent color and turbidity (66 uH and 13.60 NTU), reflecting in the measurement of organic matter: MON (8.41 mg.L-1) and Abs254 (0.065 cm-1). The optimization of quick mix set time of 17", the speed gradient of 700 s-1 in the coagulation with HCA and the time of 20" with speed gradient of 800 s-1 for SA. The smaller particle sizes of sand filtering means helped the treatment and the variation in filtration rate did not affect significantly the efficiency of the process. The evaluation of the processing steps found adjustment in standard color and turbidity of the Decree nº 518/04 MS, taking in consideration the average values found in raw water. In the treatment using the HCA for direct filtration the palatable pattern based on the apparent color can be achieved with a dose of 25 mg L-1. With the addition of pre-oxidation step, the standard result was achieved with a reduced dose for 12 mgHCA.L-1. The turbidity standard for water was obtained by direct filtration when the dose exceeds 25 mg L-1 of HCA. With pre-oxidation step there is the possibility of reducing the dose to 20 mg L-1.The addition of CAP adsorption, promoted drinking water for both parameters, with even lower dosage, 13 mg L-1 of HCA. With coagulation using SA removal required for the parameter of apparent color it was achieved with pre-oxidation and 22 mgSA.L-1. Despite the satisfactory results of treatment with the alum, it was not possible to provide water with turbidity less than 1.00 NTU even with the use of all stages of treatment

Degradação fotocatalítica oxidativa do fenol utilizando carvão obtido da pirólise de diferentes biomassas

The modern industrial progress has been contaminating water with phenolic compounds. These are toxic and carcinogenic substances and it is essential to reduce its concentration in water to a tolerable one, determined by CONAMA, in order to protect the living organisms. In this context, this work focuses on the treatment and characterization of catalysts derived from the bio-coal, by-product of biomass pyrolysis (avelós and wood dust) as well as its evaluation in the phenol photocatalytic degradation reaction. Assays were carried out in a slurry bed reactor, which enables instantaneous measurements of temperature, pH and dissolved oxygen. The experiments were performed in the following operating conditions: temperature of 50 °C, oxygen flow equals to 410 mL min-1 , volume of reagent solution equals to 3.2 L, 400 W UV lamp, at 1 atm pressure, with a 2 hours run. The parameters evaluated were the pH (3.0, 6.9 and 10.7), initial concentration of commercial phenol (250, 500 and 1000 ppm), catalyst concentration (0, 1, 2, and 3 g L-1 ), nature of the catalyst (activated avelós carbon washed with dichloromethane, CAADCM, and CMADCM, activated dust wood carbon washed with dichloromethane). The results of XRF, XRD and BET confirmed the presence of iron and potassium in satisfactory amounts to the CAADCM catalyst and on a reduced amount to CMADCM catalyst, and also the surface area increase of the materials after a chemical and physical activation. The phenol degradation curves indicate that pH has a significant effect on the phenol conversion, showing better results for lowers pH. The optimum concentration of catalyst is observed equals to 1 g L-1 , and the increase of the initial phenol concentration exerts a negative influence in the reaction execution. It was also observed positive effect of the presence of iron and potassium in the catalyst structure: betters conversions were observed for tests conducted with the catalyst CAADCM compared to CMADCM catalyst under the same conditions. The higher conversion was achieved for the test carried out at acid pH (3.0) with an initial concentration of phenol at 250 ppm catalyst in the presence of CAADCM at 1 g L-1 . The liquid samples taken every 15 minutes were analyzed by liquid chromatography identifying and quantifying hydroquinone, p-benzoquinone, catechol and maleic acid. Finally, a reaction mechanism is proposed, cogitating the phenol is transformed into the homogeneous phase and the others react on the catalyst surface. Applying the model of Langmuir-Hinshelwood along with a mass balance it was obtained a system of differential equations that were solved using the Runge-Kutta 4th order method associated with a optimization routine called SWARM (particle swarm) aiming to minimize the least square objective function for obtaining the kinetic and adsorption parameters. Related to the kinetic rate constant, it was obtained a magnitude of 10-3 for the phenol degradation, 10-4 to 10-2 for forming the acids, 10-6 to 10-9 for the mineralization of quinones (hydroquinone, p-benzoquinone and catechol), 10-3 to 10-2 for the mineralization of acids.

Evaluation of degree of conversion and hardness of dental composites photo-activated with different light guide tips

Objective: The aim of this study was to evaluate the degree of conversion and hardness of different composite resins, photo-activated for 40 s with two different light guide tips, fiber optic and polymer. Methods: Five specimens were made for each group evaluated. The percentage of unreacted carbon double bonds (% C═C) was determined from the ratio of absorbance intensities of aliphatic C═C (peak at 1637 cm−1) against internal standard before and after curing of the specimen: aromatic C-C (peak at 1610 cm−1). The Vickers hardness measurements were performed in a universal testing machine. A 50 gf load was used and the indenter with a dwell time of 30 seconds. The degree of conversion and hardness mean values were analyzed separately by ANOVA and Tukey’s test, with a significance level set at 5%. Results: The mean values of degree of conversion for the polymer and fiber optic light guide tip were statistically different (P<.001). The hardness mean values were statistically different among the light guide tips (P<.001), but also there was difference between top and bottom surfaces (P<.001). Conclusions: The results showed that the resins photo-activated with the fiber optic light guide tip promoted higher values for degree of conversion and hardness.