Estudo da influência da temperatura de brasagem nas uniões zircônia/aço inox 304 utilizando metalização mecânica

Metal-Ceramic (M/C) Zirconia-stainless steel interfaces have been processed through brazing techniques due to the excellent combination of properties such as high temperature stability, high corrosion resistance and good mechanical properties. However, some M/C interfaces show some defects, like porosity and cracks results in the degradation of the interfaces, leading even to its total rupture. Most of time, those defects are associated with an improper brazing parameters selection to the M/C system. In this work, ZrO2 Y-TZP and ZrO2 Mg - PSZ were joint with the stainless steel grade 304 by brazing using a eutectic silver-copper (Ag28Cu) interlayer alloy with different thermal cycles. Ceramic surfaces were previous mechanically metallized with titanium to improve adhesion of the system. The effect of temperature on the M/C interface was studied. SEM-EDS and 3 point flexural bend test were performed to evaluate morphology, chemical composition and mechanical resistance of the M/C interfaces. Lower thermal cycle temperatures produced better results of mechanical resistance, and more regular/ homogeneous reaction layers between braze alloy and metal-ceramic surfaces. Also was proved the AgCu braze alloy activation in situ by titanium

Propriedades físicas de bicamadas magnéticas

The magnetic order of bylayers composed by a ferromagnetic film (F) coupled with an antiferromagnetic film (AF) is studied. Piles of coupled monolayers describe the films and the interfilm coupling is described by an exchange interaction between the magnetic moments at the interface. The F has a cubic anisotropy while the AF has a uniaxial anisotropy. We analyze the effects of an external do magnetic field applied parallel to the interface. We consider the intralayer coupling is strong enough to keep parallel all moments of the monolayer an then they are described by one vector proportional to the magnetization of the layer. The interlayer coupling is represented by an exchange interaction between these vectors. The magnetic energy of the system is the sum of the exchange. Anisotropy and Zeeman energies and the equilibrium configuration is one that gives the absolute minimum of the total energy. The magnetization of the system is calculated and the influence of the external do field combined with the interfilm coupling and the unidirectional anisotropy is studied. Special attention is given to the region near of the transition fields. The torque equation is used to study dynamical behavior of these systems. We consider small oscillations around the equilibrium position and we negleet nonlinear terms to obtain the natural frequencies of the system. The dependence of the frequencies with the external do field and their behavior in the phase transition region is analized

Estudo de titanatos nanoestruturados obtidos por tratamento hidrotérmico de óxido de titânio em meio alcalino

TiTanate NanoTubes (TTNT) were synthesized by hydrothermal alkali treatment of TiO2 anatase followed by repeated washings with distinct degrees of proton exchange. TTNT samples with different sodium contents were characterized, as synthesized and after heattreatment (200-800ºC), by X-ray diffraction, scanning and transmission electron microscopy, electron diffraction, thermal analysis, nitrogen adsorption and spectroscopic techniques like FTIR and UV-Vis diffuse reflectance. It was demonstrated that TTNTs consist of trititanate structure with general formula NaxH2−xTi3O7·nH2O, retaining interlayer water in its multiwalled structure. The removal of sodium reduces the amount of water and contracts the interlayer space leading, combined with other factors, to increased specific surface area and mesopore volume. TTNTs are mesoporous materials with two main contributions: pores smaller than 10 nm due to the inner volume of nanotubes and larger pores within 5-60 nm attributed to the interparticles space. Chemical composition and crystal structure of TTNTs do not depend on the average crystal size of the precursor TiO2-anatase, but this parameter affects significantly the morphology and textural properties of the nanostructured product. Such dependence has been rationalized using a dissolution-recrystallization mechanism, which takes into account the dissolution rate of the starting anatase and its influence on the relative rates of growth and curving of intermediate nanosheets. The thermal stability of TTNT is defined by the sodium content and in a lower extent by the crystallinity of the starting anatase. It has been demonstrated that after losing interlayer water within the range 100-200ºC, TTNT transforms, at least partially, into an intermediate hexatitanate NaxH2−xTi6O13 still retaining the nanotubular morphology. Further thermal transformation of the nanostructured tri- and hexatitanates occurs at higher or lower temperature and follows different routes depending on the sodium content in the structure. At high sodium load (water washed samples) they sinter and grow towards bigger crystals of Na2Ti3O7 and Na2Ti6O13 in the form of rods and ribbons. In contrast, protonated TTNTs evolve to nanotubes of TiO2(B), which easily convert to anatase nanorods above 400ºC. Besides hydroxyls and Lewis acidity typical of titanium oxides, TTNTs show a small contribution of protonic acidity capable of coordinating with pyridine at 150ºC, which is lost after calcination and conversion into anatase. The isoeletric point of TTNTs was measured within the range 2.5-4.0, indicating behavior of a weak acid. Despite displaying semiconductor characteristics exhibiting typical absorption in the UV-Vis spectrum with estimated bandgap energy slightly higher than that of its TiO2 precursor, TTNTs showed very low performance in the photocatalytic degradation of cationic and anionic dyes. It was concluded that the basic reason resides in its layered titanate structure, which in comparison with the TiO2 form would be more prone to the so undesired electron-hole pair recombination, thus inhibiting the photooxidation reactions. After calcination of the protonated TTNT into anatase nanorods, the photocatalytic activity improved but not to the same level as that exhibited by its precursor anatase

Síntese, caracterização, propriedades e aplicação dos sistemas Mg- Al, Zn-Al e Mg-Fe

The Layered Double Hydroxides has become extremely promising materials due to its range of applications, easily obtained in the laboratory and reusability after calcination, so the knowledge regarding their properties is of utmost importance. In this study were synthesized layered double hydroxides of two systems, Mg-Al and Zn-Al, and such materials were analyzed with X-ray diffraction and, from these data, we determined the volume density, planar atomic density, size crystallite, lattice parameters, interplanar spacing and interlayer space available. Such materials were also subjected to thermogravimetric analysis reasons for heating 5, 10, 20 and 25 ° C / min to determine kinetic parameters for the formation of metaphases HTD and HTB based on theoretical models Ozawa, Flynn-Wall Starink and Model Free Kinetics. In addition, the layered double hydroxides synthesized in this working ratios were calcined heating 2.5 ° C / min and 20 ° C / min, and tested for adsorption of nitrate anion in aqueous solution batch system at time intervals 5 min, 15 min, 30 min, 1h, 2h and 4h. Such calcined materials were also subjected to exposure to the atmosphere and at intervals of 1 week, 2 weeks and 1 month were analyzed by infrared spectroscopy to study the kinetics of regeneration determining structural called "memory effect"

Propriedades fisicas do monocristal fe/mgo(100) e estudo da expansao termica da superficie da ag(100)

In this work we have developed a way to grow Fe/MgO(100) monocrystals by magnetron sputtering DC. We investigated the growing in a temperature range among 100 oC and 300 oC. Structural and magneto-crystalline properties were studied by different experimental techniques. Thickness and surface roughness of the films were investigated by atomic force microscopy, while magneto-crystalline properties were investigated by magneto-optical Kerr effect and ferromagnetic resonance. Our results show that as we increase the deposition temperature, the magneto-crystalline anisotropy of the films also increases, following the equation of Avrami. The best temperature value to make a film is 300 oC. As the main result, we built a base of magnetoresistence devices and as an aplication, we present measurements of Fe/Cr/Fe trilayer coupling. In a second work we investigated the temperature dependence of the first three interlayer spacings of Ag(100) surface using low energy electron diffraction. A linear expansion model of crystal surface was used and the values of Debye temperatures of the first two layers and thermal expansion coefficient were determinated. A relaxation of 1% was found for Ag(100) surface and these results are matched with faces (110) and (111) of the silver. iv

Study of porcelain-zirconia composites for dental applications

Materiais compósitos restauradores representam um dos mais bem sucedidos biomateriais na pesquisa moderna, na substituição do tecido biológico em aparência e função. Nesta linha, a porcelana feldspática tem sido largamente usada em odontologia devido suas interessantes qualidades como estabilidade de cor, propriedades estéticas, elevada durabilidade mecânica, biocompatibilidade, baixa condutividade térmica e elevada resistência ao desgaste. Entretanto, este material é frágil e pode falhar em ambiente oral devido ao micro-vazamento, baixa resistência à tração, descolagem ou fratura. Assim, para melhorar as propriedades mecânicas da porcelana, a zircônia parcialmente estabilizada com Ítria (Y-TZP) pode ser uma boa alternativa para fortalecer e produzir infraestruturas totalmente cerâmicas (coroas e próteses parciais fixas). Portanto, este estudo tem por objetivo avaliar as propriedades mecânicas e características microestruturais da porcelana reforçada com zircônia (3Y-TZP) em diferentes conteúdos e as variáveis que afetam as propriedades mecânicas destes materiais. O estudo de caracterização revelou que a zircônia comercial apresenta melhores resultados quando comparada com a zircônia sintetizada pelo CPM. Assim, os estudos seguintes utilizaram a zircônia comercial para todos os testes requeridos. As partículas de zircônia apresentam elevadas propriedades mecânicas quando comparadas a zircônia aglomerada. Os diferentes conteúdos revelam que as propriedades mecânicas dos compósitos aumentam com o aumento do conteúdo volumétrico até 30% vol.% (198,5Mpa), ou seja, maior resistência à flexão quando comparada com os outros compósitos. Do mesmo modo, a resistência ao desgaste para os compósitos com (30%, vol.% de zircônia) apresenta valores superiores quando comparado aos demais compósitos. Na adesão cerâmico-cerâmico a porcelana exibe elevada adesão para a superfície de zircônia porosa quando comparada a superfície rugosa. Os furos superficiais (PZ) e aplicação de compósitos com camada intermediária (RZI) na zircônia causam separadamente uma melhoria da resistência ao cisalhamento da zircônia-porcelana quando comparados as amostras convencionais de zircônia-porcelana (RZ), embora não sejam estatisticamente significativas (p>0.05). A presença de uma camada intermediaria produz um aumento significativo na força de ligação (~55%) em relação as amostras convencionais (RZ). Portanto, a correta a correta configuração e tratamento superficial podem produzir subestruturas com qualidade e força de ligação adequadas aos requisitos odontológicos.

Estudo da influência da temperatura de brasagem nas uniões zircônia/aço inox 304 utilizando metalização mecânica

Metal-Ceramic (M/C) Zirconia-stainless steel interfaces have been processed through brazing techniques due to the excellent combination of properties such as high temperature stability, high corrosion resistance and good mechanical properties. However, some M/C interfaces show some defects, like porosity and cracks results in the degradation of the interfaces, leading even to its total rupture. Most of time, those defects are associated with an improper brazing parameters selection to the M/C system. In this work, ZrO2 Y-TZP and ZrO2 Mg - PSZ were joint with the stainless steel grade 304 by brazing using a eutectic silver-copper (Ag28Cu) interlayer alloy with different thermal cycles. Ceramic surfaces were previous mechanically metallized with titanium to improve adhesion of the system. The effect of temperature on the M/C interface was studied. SEM-EDS and 3 point flexural bend test were performed to evaluate morphology, chemical composition and mechanical resistance of the M/C interfaces. Lower thermal cycle temperatures produced better results of mechanical resistance, and more regular/ homogeneous reaction layers between braze alloy and metal-ceramic surfaces. Also was proved the AgCu braze alloy activation in situ by titanium