Propriedades magnéticas de ortoferritas de lantânio dopadas com estrôncio

Samples of lanthanum Ortoferrites doped with strontium were synthesized in a single phase by the sol-gel method. Two samples were prepared, one by varying the concentration of strontium in lanthanum ortoferrites La1−xSrxFeO3−δ with (0 ≤ x ≤ 0.5), and another batch of samples of type, La1/3Sr2/3FeO3−δ, now varying only the temperature of calcination. Our samples were obtained by Pechini method and sintered in air and oxygen atmospheric. Their crystal structures were determined by x-ray diraction (XRD), scanning electron microscopy (SEM), where we observed that the samples (0 ≤ x ≤ 0.3) have orthorhombic symmetry and the volume of the single cell decreases with the increasing of concentration of strontium. For x = 0.5 it is only observed the simple phase when that is sintered in O2 atmospheric. Their magnetic characteristics were obtained by the Mössbauer spectroscopy and magnetic measurements. The magnetization measurements for samples La1−xSrxFeO3−δ with (0 ≤ x ≤ 0.5) revealed that the magnetization decreases with increasing concentration of strontium, but for the sample x = 0.4 the magnetization shows a high coercive field and a ferrimagnetic behavior, which is attributed to a small amount of strontium hexaferrite. As for the samples La1/3Sr2/3FeO3−δ calcined between 800 oC e 1200 oC. The hysteresis curves revealed two distinct behaviors: an declined antiferromagnetic behavior (Canted) for samples calcined between 800 oC and 1000 oC and a paramagnetic behavior for the samples calcined at 1100 oC e 1200 o C. Thermal hysteresis and sharp peaks around the Néel temperature (TN), over the curves of specific heat as a function of temperature was only observed in calcined samples with 1100 oC and 1200 oC. This eect is attributed to the charge ordering. These results indicate that the charge ordering occurs only in the samples without oxygen deficiency. Magnetic measurements as a function of temperature are also in agreement with this interpretation

Transporte eletrônico e propriedades termodinâmicas de nanobiomoléculas

We use a tight-binding formulation to investigate the transmissivity and the currentvoltage (I_V) characteristics of sequences of double-strand DNA molecules. In order to reveal the relevance of the underlying correlations in the nucleotides distribution, we compare theresults for the genomic DNA sequence with those of arti_cial sequences (the long-range correlated Fibonacci and RudinShapiro one) and a random sequence, which is a kind of prototype of a short-range correlated system. The random sequence is presented here with the same _rst neighbors pair correlations of the human DNA sequence. We found that the long-range character of the correlations is important to the transmissivity spectra, although the I_V curves seem to be mostly inuenced by the short-range correlations. We also analyze in this work the electronic and thermal properties along an _-helix sequence obtained from an _3 peptide which has the uni-dimensional sequence (Leu-Glu-Thr- Leu-Ala-Lys-Ala)3. An ab initio quantum chemical calculation procedure is used to obtain the highest occupied molecular orbital (HOMO) as well as their charge transfer integrals, when the _-helix sequence forms two di_erent variants with (the so-called 5Q variant) and without (the 7Q variant) _brous assemblies that can be observed by transmission electron microscopy. The di_erence between the two structures is that the 5Q (7Q) structure have Ala ! Gln substitution at the 5th (7th) position, respectively. We estimate theoretically the density of states as well as the electronic transmission spectra for the peptides using a tight-binding Hamiltonian model together with the Dyson's equation. Besides, we solve the time dependent Schrodinger equation to compute the spread of an initially localized wave-packet. We also compute the localization length in the _nite _-helix segment and the quantum especi_c heat. Keeping in mind that _brous protein can be associated with diseases, the important di_erences observed in the present vi electronic transport studies encourage us to suggest this method as a molecular diagnostic tool

Propriedades estruturais e optoeletrônicas dos compostos SrSnO3, SrxBa1-xSnO3 e BaSnO3

In this work we present a study for the structural, electronic and optical properties, at ambient conditions of SrSnO3, SrxBa1

Estudo da participação das espécies fortemente oxidantes produzidas durante a oxidação eletroquímica de corantes usando eletrodo de diamante dopado com boro: função das propriedades eletroquímicas do eletrodo e condições experimentais

The textile industry is one of the most polluting in the world (AHMEDCHEKKAT et al. 2011), generating wastewater with high organic loading. Among the pollutants present in these effluents are dyes, substances with complex structures, toxic and carcinogenic characteristics, besides having a strong staining. Improper disposal of these substances to the environment, without performing a pre-treatment can cause major environmental impacts. The objective this thesis to use a technique of electrochemical oxidation of boron doped diamond anode, BDD, for the treatment of a synthetic dye and a textile real effluent. In addition to studying the behavior of different electrolytes (HClO4, H3PO4, NaCl and Na2SO4) and current densities (15, 60, 90 and 120 mA.cm-2 ), and compare the methods with Rhodamine B (RhB) photolysis, electrolysis and photoelectrocatalytic using H3PO4 and Na2SO4. Electrochemical oxidation studies were performed in different ratio sp3 /sp2 of BDD with solution of RhB. To achieve these objectives, analysis of pH, conductivity, UV-visible, TOC, HPLC and GC-MS were developed. Based on the results with the Rhodamine B, it was observed that in all cases occurred at mineralization, independent of electrolyte and current density, but these parameters affect the speed and efficiency of mineralization. The radiation of light was favorable during the electrolysis of RhB with phosphate and sulfate. Regarding the oxidation in BDD anode with different ratio sp3 /sp2 (165, 176, 206, 220, 262 e 329), with lower carbon-sp3 had a longer favoring the electrochemical conversion of RhB, instead of combustion. The greater the carbon content on the anodes BDD took the biggest favor of direct electrochemical oxidation

Densificação e microestrutura de um compósito Mo-Cu preparado a partir de um pó de heptamolibidato de amônia e cobre

The Cu-Mo system is a composite used in the electrical industry as material for electrical contact and resistance welding electrode as well as the heat sink and microwave absorber in microelectronic devices. The use of this material in such applications is due to the excellent properties of thermal and electrical conductivity and the possibility of adjustment of its coefficient of thermal expansion to meet those of materials used as substrates in the semiconductor micoreletrônic industry. Powder metallurgy through the processes of milling, pressing shaping and sintering is a viable technique for consolidation of such material. However, the mutual insolubility of both phases and the low wettability of liquid Cu on Mo impede its densification. However, the mutual insolubility of both phases and the low wettability of liquid Cu on Mo impede its densification. The mechanical alloying is a technique for preparation of powders used to produce nanocrystalline composite powder with amorphous phase or extended solid solution, which increases the sinterability immiscible systems such as the Mo-Cu. This paper investigates the influence of ammonium heptamolybdate (HMA) and the mechanical alloying in the preparation of a composite powder HMA-20% Cu and the effect of this preparation on densification and structure of MoCu composite produced. HMA and Cu powders in the proportion of 20% by weight of Cu were prepared by the techniques of mechanical mixing and mechanical alloying in a planetary mill. These were milled for 50 hours. To observe the evolution of the characteristics of the particles, powder samples were taken after 2, 10, 15, 20, 30 and 40 hours of milling. Cylindrical samples 5 to 8 mm in diameter and 3 to 4 mm thickness were obtained by pressing at 200 MPa to the mixed powders so as to ground. These samples were sintered at 1200 ° C for 60 minutes under an atmosphere of H2. To determine the effect of heating rate on the structure of the material during the decomposition and reduction of HMA, rates of 2, 5 and 10 ° C / min were used .. The post and the structures of the sintered samples were characterized by SEM and EDS. The density of the green and sintered bodies was measured using the geometric method (weight / volume). Vickers microhardness with a load of 1 N for 15 s were performed on sintered structures. The density of the sintered structures 10 ° C / min. reached 99% of theoretical density, how the density of sintered structures to 2 ° C / min. reached only 90% of the theoretical density

Efeito da moagem de alta energia na densificação e microestrutura do compósito AI2O3-Cu

The Cu-Al2O3 composite ceramic combines the phase of alumina, which is extremely hard and durable, yet very brittle, to metallic copper phase high ductility and high fracture toughness. These characteristics make this material a strong candidate for use as a cutting tool. Al2O3-Cu composite powders nanocrystalline and high homogeneity can be produced by high energy milling, as well as dense and better mechanical structures can be obtained by liquid phase sintering. This work investigates the effect of high-energy milling the dispersion phase Al2O3, Cu, and the influence of the content of Cu in the formation of Cu-Al2O3 composite particles. A planetary mill Pulverisatte 7 high energy was used to perform the experiments grinding. Al2O3 powder and Cu in the proportion of 5, 10 and 15% by weight of Cu were placed in a container for grinding with balls of hard metal and ethyl alcohol. A mass ratio of balls to powder of 1:5 was used. All powders were milled to 100 hours, and powder samples were collected after 2, 10, 20, 50 and 70 hours of grinding. Composite powders with compact cylindrical shape of 8 mm diameter were pressed and sintered in uniaxial matrix resistive furnace to 1200, 1300 to 1350 °C for 60 minutes under an atmosphere of argon and hydrogen. The heating rate used was 10°C/min. The powders and structures of the sintered bodies were characterized by XRD, SEM and EDS. Analysis TG, DSC and particle size were also used to characterize the milled powders, as well as dilatometry was used to observe the contraction of the sintered bodies. The density of the green and sintered bodies was measured using the geometric method (mass / volume). Vickers microhardness with a load of 500 g for 10 s were performed on sintered structures. The Cu-Al2O3 composite with 5% copper density reached 61% of theoretical density and a hardness of 129 HV when sintered at 1300 ° C for 1h. In contrast, lower densities (59 and 51% of the theoretical density) and hardness (110 HV and 105) were achieved when the copper content increases to 10 and 15%.

Geoquímica de elementos maiores e traços de granitoides neoproterozoicos da província Borborema e sua correlação com propriedades físicas de rochas

This paper discusses the correlation of thermal conductivity, density and magnetic susceptibility with composition of major and trace elements of Neoproterozoic igneous bodies from Borborema Province, Northeastern Brazil. These properties were used as potential markers among the studied magmatic suites. For the correlation between petrophysical and geochemical properties it was considered a set of 195 chemical analyzes of granitoid rocks, separated by the degree of acidity in basic, intermediate and acidic. Major (SiO2, Al2O3, Fe2O3, MgO, CaO, Na2O, K2O and TiO2) and some trace elements (Rb, Sr, Ba, Zr, Th and U) that are usually linked to the formation of the most common minerals of igneous rocks were used. The results show that SiO2 has the best positive correlation with the thermal conductivity, while Al2O3, CaO, Fe2O3, MgO and TiO2 exhibit negative correlation for the same property. The correlation with density is opposite to that one for these oxides with the thermal conductivity. The magnetic susceptibility did not correlate with the elements studied. The results for thermal conductivity and density indicate a tendency of SiO2 and oxides with higher affinity with mafic minerals (Al2O3, CaO, Fe2O3, TiO2 and MgO) in controlling these petrophysical parameters. The set of samples was divided into five different magmatic suites based on their lithogeochemical aspects into: i) peralkaline / alkaline; ii) alkaline; iii) calc-alkaline; iv) high potassium calcium alkaline; and v) shoshonitic. Data analysis showed that the thermal conductivity and density presented good results in the individualization of these suites, notably between peralkaline / alkaline, alkaline suites, calc-alkaline and shoshonitic. However, the high-K calc-alkaline suite overlapped with the other. In contrast, the magnetic susceptibility did not show effective results for separating the five chemical suites.

Tratamento superficial de argilas com cera de carnaúba e microemulsão de óleo de coco

Adsorption is a process that has become indispensable due to pollution caused by industrial activity. More economically viable adsorbents are being tested to replace the high cost of materials used. The clays can be used as adsorbents and are low cost materials, natural properties feasible for the application in the adsorption process, structural modifications are performed with ease promoting selective adsorption in these materials. The objective of this study was to synthesize and characterize adsorbents used in the adsorption of organic compounds. The adsorbents were characterized by the techniques of XRD, SEM, FTIR and TG. The results show that the studied materials have affinity to organic compounds and can be applied as adsorbents. The materials studied are viable and can be applied in the treatment of effluents contaminated in industrial scale.

Desenvolvimento de um painel sanduíche com carga de particulado oriundo de resíduo lignocelulósico para aplicação em produtos na área de equipamentos de proteção

This work aims to study and investigate the use of a hybrid composite polymer formed with blanket aramid (Kevlar 29) fiber blanket flax fiber and particulate dry endocarp of coconut (Cocos nucifera Linn), using as matrix an epoxy resin based thermoset for use in areas of protective equipment. Besides such material is used an aluminum plate, joined to the composite by means of glue based on epoxy and araldite commercial. The manufacturing process adopted was manual lamination (Hand Lay Up) to manufacture the hybrid composite. After the composite is prepared, an aluminum plate is subjected to pressure and glued to cure the adhesive. Layers of veil will also be used to separate the particulate from the linen blanket layer without disturbing the alignment of the fibers of the blankets. To characterize the mechanical and physical behavior was manufactured a plate of 800 x 600 mm of the hybrid composite, which were removed specimens for tests of water absorption to saturation; density; impact test (Charpy) and two test specimens for ballistic testing 220 mm x 200 mm to make a comparative study between the dry state and saturated water absorption and thus see the ballistic performance of these two conditions. The test was applied to make a comparative study of fracture in these two conditions, caused by penetrating ballistic missile (38 and 380). To test the impact (Charpy) will analyze the absorbed energy, fracture appearance and lateral contraction, also in dry condition and saturation of absorbed water, thereby analyzing situations where the impact load is relevant, such as bumps and shocks produced by stone, metal or wooden bars among others. The proposed configuration, along with the tests, has the purpose, application in the fields of equipment against ballistic impact, such as helmets; bullet proof vests; shields; protective packaging and other items to be identified in this research.

Fabricação e caracterização de um compósito hibrido com resíduo lignocelulósico

This work aims to manufacture and characterize a hybrid plastic composite with the matrix isophthalic polyester resin base and having as reinforcing glass fiber and the dry endocarp of coconut (Coco nucifera Linn) in the form of particles as filler. The composite was made industrially in Tecniplas Industry and Trade LTDA. in the form of plate, and was manufactured process made by the manual lamination (Hand Lay Up). From the plate they were prepared test specimens for testing density, water absorption, uniaxial traction in dry and wet states, and testing of bending, as well as studies on the behavior of the generated fractures, macroscopic and microscopic, in mechanical tests through. All tests were performed in order to find the most viable applications the hybrid composite manufactured. The tensile and bending tests were analyzed last tensile properties, elasticity and deformation module. After the studies, it is observed that the percentage moisture absorbed was 3.03%. The presence of moisture in the tensile test meant a decrease of 19.77% from last stand, and 5.26% in the elastic modulus. For bending tests gave an average value of 69.13 MPa flexural strength. The results show the application of hybrid composite studied in lightweight structures, indoors, which require low / medium performance traction demands, and which involve flexural requests.

Obtenção e caracterização de um compósito polimérico de matriz poliéster e reforço/carga de tecido plano de algodão

He was obtained and studied the feasibility of using TPA (Tissue Cotton Plan) screen type, for bagging, with a weight of 207.9 g / m2 in a composite of orthophthalic crystal polyester resin matrix. The process for obtaining the composite was tested against the maximum number of layers that could be used without compromising the processability and manufacturing of CPs in compression mold. Five configurations / formulations were selected and tested at 1, 4, 8, 10 and 12 layers of cotton tissue - TPA. TPA was not subjected to chemical treatment, only by passing a mechanical washing process. The composite in its various configurations / formulations was characterized to determine its physical properties. The properties of the composite were higher viability resistance to bending, approaching the matrix and impact resistance, superiority in relation to the polyester resin. Another property that has shown good result compared to other composite has water absorption. Analyzing all the properties set the settings / formulations with higher viability were TA8 and TA10, by combining good processability and higher mechanical strength, with lower loss compared to polyester resin matrix. The composite showed lower mechanical behavior of the resin matrix for all the formulations studied except the impact resistance. The SEM showed a good adhesion between the layers of TPA and polyester resin matrix, without the presence of micro voids in the matrix confirming the efficient manufacturing process of the samples for characterization. The composite proposed proved to be viable for the fabrication of structures with low requests from mechanical stresses, and as demonstrated for the manufacture of solar and wind prototypes, and packaging, shelving, decorative items, crafts and shelves, with good visual appearance.

Obtenção e caracterização de um compósito polimérico de matriz poliéster e reforço/carga de tecido plano de algodão

He was obtained and studied the feasibility of using TPA (Tissue Cotton Plan) screen type, for bagging, with a weight of 207.9 g / m2 in a composite of orthophthalic crystal polyester resin matrix. The process for obtaining the composite was tested against the maximum number of layers that could be used without compromising the processability and manufacturing of CPs in compression mold. Five configurations / formulations were selected and tested at 1, 4, 8, 10 and 12 layers of cotton tissue - TPA. TPA was not subjected to chemical treatment, only by passing a mechanical washing process. The composite in its various configurations / formulations was characterized to determine its physical properties. The properties of the composite were higher viability resistance to bending, approaching the matrix and impact resistance, superiority in relation to the polyester resin. Another property that has shown good result compared to other composite has water absorption. Analyzing all the properties set the settings / formulations with higher viability were TA8 and TA10, by combining good processability and higher mechanical strength, with lower loss compared to polyester resin matrix. The composite showed lower mechanical behavior of the resin matrix for all the formulations studied except the impact resistance. The SEM showed a good adhesion between the layers of TPA and polyester resin matrix, without the presence of micro voids in the matrix confirming the efficient manufacturing process of the samples for characterization. The composite proposed proved to be viable for the fabrication of structures with low requests from mechanical stresses, and as demonstrated for the manufacture of solar and wind prototypes, and packaging, shelving, decorative items, crafts and shelves, with good visual appearance.

Efeito da adição de WC e Co na sinterização e propriedades mecânicas da alumina

Composites based on alumina (Al2O3), tungsten carbide (WC) and cobalt (Co) exhibit specific properties such as low density, high oxidation resistance, high melting point and high chemical inertia. That composite shows to be a promising material for application in various fields of engineering. In this work, the mechanical properties of the composite (Al2O3 – WC – Co), particularly density and hardness, were evaluated according to the effects of the variables of powder processing parameters, green compact and sintered. Powder composites with the composition of 80 wt% Al2O3, 18 wt% WC and 2 wt% Co were processed by high energy ball milling in a planetary mill for 50 hours as well as mixed by manual mixing in a glass vessel with the same proportion. Samples were collected (2, 10, 20, 30, 40 and 50 hours) during the milling process. Then, the powders were compacted in a cylindrical die with 5 mm in diameter in a uniaxial press with pressures of 200 and 400 MPa. The sintering was in two stages: first, the solid phase sintering was performed at 1126 and 1300 °C for 1 hour with a heating rate of 10 °C/min in a resistive furnace under argon atmosphere for green samples compacted in 200 and 400 MPa; the second sintering was performed on dilatometer in solid phase at 1300 °C for green sample compacted in 200 MPa, another sintering also was performed on dilatometer, this time in liquid phase at 1550 °C for green samples compacted in 200 and 400 MPa, with the same parameters used in resistive furnace. The raw materials were characterized by X – ray diffraction (XRD), X – ray fluorescence (XRF), scanning electron microscopy (SEM), energy dispersive spectroscopy (EDS) and laser particlemeter. The sintered samples were subjected to microhardness testing. The results showed that high energy milling achieved to the objectives regarding the particle size and the dispersion of composite phases. However, the hardness did not achieve to significant results, this is an indication that the composite has low fracture toughness.

Efeito da adição de WC e Co na sinterização e propriedades mecânicas da alumina

Composites based on alumina (Al2O3), tungsten carbide (WC) and cobalt (Co) exhibit specific properties such as low density, high oxidation resistance, high melting point and high chemical inertia. That composite shows to be a promising material for application in various fields of engineering. In this work, the mechanical properties of the composite (Al2O3 – WC – Co), particularly density and hardness, were evaluated according to the effects of the variables of powder processing parameters, green compact and sintered. Powder composites with the composition of 80 wt% Al2O3, 18 wt% WC and 2 wt% Co were processed by high energy ball milling in a planetary mill for 50 hours as well as mixed by manual mixing in a glass vessel with the same proportion. Samples were collected (2, 10, 20, 30, 40 and 50 hours) during the milling process. Then, the powders were compacted in a cylindrical die with 5 mm in diameter in a uniaxial press with pressures of 200 and 400 MPa. The sintering was in two stages: first, the solid phase sintering was performed at 1126 and 1300 °C for 1 hour with a heating rate of 10 °C/min in a resistive furnace under argon atmosphere for green samples compacted in 200 and 400 MPa; the second sintering was performed on dilatometer in solid phase at 1300 °C for green sample compacted in 200 MPa, another sintering also was performed on dilatometer, this time in liquid phase at 1550 °C for green samples compacted in 200 and 400 MPa, with the same parameters used in resistive furnace. The raw materials were characterized by X – ray diffraction (XRD), X – ray fluorescence (XRF), scanning electron microscopy (SEM), energy dispersive spectroscopy (EDS) and laser particlemeter. The sintered samples were subjected to microhardness testing. The results showed that high energy milling achieved to the objectives regarding the particle size and the dispersion of composite phases. However, the hardness did not achieve to significant results, this is an indication that the composite has low fracture toughness.

Efeitos da terapia laser de baixa intensidade associada ao exercício aeróbio no reparo de tenotomia do tendão de aquiles de ratos diabéticos

Diabetes Mellitus (DM ) is a complex disease that requires continuous medical care for the reduction of risk factors in addition to glycemic control. The typical hyperglycemia of this disease produces glycosylation of proteins and so the consequence is the accumulation of glycosylation final products in various human tissues, among them, the tendon. The aerobic exercise (AE) and the low level laser therapy (LLLT) have been used to treat tendinopathies in individuals with or without DM. Objective: The aim of this study was to watch the effect of the LLLT and the AE, in association, in partial tenotomy of the tissue repair of the Achilles tendon (AT) of diabetic rats. Methods: 91 animals were utilized and divided in to the following groups: control group (GC), injured control group (GCL), diabetic group (GD), diabetic group LLLT (GD – TLBI), diabetic group trained (GD - EX) and diabetic group trained laser (GD-EX+TLBI). The animals were submitted to intervention with AE, using a protocol with a progressive increase of time (12 to 60 min) and speed of (4 to 9 m/min), and the LLLT (660 nm laser, 10mW, 4 J/cm², single point for 16 seconds, three times for week). It was analyzed morphological, biomechanical and molecular characteristics. For data showing normal distribution was used one-way ANOVA test and post hoc Tukey and data without normal distribution was used Mann Whitney test and post hoc Dunn's. It was accepted p <0.05 for statistical significance Results: The biomechanical tests indicated major improvement in the GC and GD-EX+TLBI groups when compared with the diabetic groups in the following variables: maximum load, strain, absorbed energy, stress, cross section area, elastic modulus and energy density (p<0.05). The analysis through molecular biology indicated that the association of aerobic exercise and LLLT generated an increase of the collagen I gene expression and modulated the expression of the MMP2 and MMP9 (p<0.05). No observed any major improvement in the morphological variable studied. Conclusion: the LLLT associated with aerobic exercise promotes and increase of the mechanical properties, in the control of collagen I gene expression and of the MMP2 and MMP9 of the diabetic rats.