Investigação da estabilidade térmica e das propriedades elétricas do TiO2 em função da dopagem com Ce(SO4)2

The metalic oxides have been studies due to differents applications as materials semiconductor in solar cells, catalysts, full cells and, resistors. Titanium dioxide (TiO2) has a high electric conductivity due to oxygen vacancies. The Ce(SO4)2.2H2O doped samples TiO2 and TiO2 pure was obtained sol-gel process, and characterized by X-ray diffractometry,thermal analysis, and impedance spectroscopy. The X-ray diffraction patterns for TiO2 pure samples shows at 700°C anatase phase is absent, and only the diffraction peaks of rutile phase are observed. However, the cerium doped samples only at 900°C rutile in the phase present with peaks of cerium dioxide (CeO2). The thermal analysis of the TiO2 pure and small concentration cerium doped samples show two steps weight loss corresponding to water of hydration and chemisorbed. To larger concentration cerium doped samples were observed two steps weight loss in the transformation of the doped cerium possible intermediate species and SO3. Finally, two steps weight loss the end products CeO2 and SO3 are formed. Analyse electric properties at different temperatures and concentration cerium doped samples have been investigated by impedance spectroscopy. It was observed that titanium, can be substituted by cerium, changing its electric properties, and increased thermal stability of TiO2 anatase structure

Síntese e caracterização de componentes nanoestruturados de células a combustível de óxidos sólidos

Perovskite-like ceramic materials present the general formula ABO3, where A is a rare earth element or an alkaline metal element, and B is a transition metal. These materials are strong candidates to assume the position of cathode in Solid Oxide Fuel Cells (SOFC), because they present thermal stability at elevated temperatures and interesting chemical and physical properties, such as superconductivity, dieletricity, magnetic resistivity, piezoelectricity, catalytic activity and electrocatalytic and optical properties. In this work the cathodes of Solid Oxide Fuel Cells with the perovskite structure of La1-xSrxMnO3 (x = 0.15, 0.22, 0.30) and the electrolyte composed of zirconia-stabilized-yttria were synthesized by the Pechini method. The obtained resins were thermal treatment at 300 ºC for 2h and the obtained precursors were characterized by thermal analysis by DTA and TG / DTG. The powder precursors were calcined at temperatures from 450 to 1350ºC and were analyzed using XRD, FTIR, laser granulometry, XRF, surface area measurement by BET and SEM methods. The pellets were sintered from the powder to the study of bulk density and thermal expansion

Desenvolvimento de componentes nanométricos para aplicação em células a combustível à base de sólidos estruturados e filmes finos

The present work aims the preparation of filmes of strontium-doped lanthanum manganite (perovskita) yttria-stabilized zirconia (LSM-SDC) films deposited on substrate of YSZ by means of spin coating technique having as principal objective their application to solid oxide fuel cells of intermediate temperature. La0,8Sr0,2MnO3 and Ce0,8Sm0,2O1,9 were obtained by modified Pechini method by use of gelatin which act as polymerization agent. The powders obtained were characterized by Xray fluorescence, X ray diffraction, electronic scanning microscopy and the superficial area by BET method. The results obtained by X-ray fluorescence showed that the route adopted for obtention of powders was effective in the obtention of the compositions with close values to the stoichiometrics. Ethyl cellulose was used as pore-forming agent and mixed with the LSM-SDC powders in weight proportions of 1:24, 2:23 and 1:9. The films were sintered at 1150 °C for 4 h and characterized by X-ray diffraction and scanning electron microscopy technique (SEM) and atomic force. The phases quantification of the precursory powders and of the obtained films was carried through Rietveld method. According with the analysis of SEM, as the content of ethyl cellulose was increased, the pore distribution in films become more uniform and the pore size reduced. The methodology used for the obtention of the films was very efficient, considering a material was obtained with characteristics that were proper to the application as electrolyte/cathode system to solid oxide fuel cells

Influência espaço-temporal e fisiológica na absorção de nutrientes e elementos tóxicos por Eichhornia crassipes visando o uso adequado da sua biomassa: o caso do Rio Apodi/Mossoró - RN

This study aims to determine the amount of nutrients and toxic elements in aquatic macrophytes of species Eichhornia crassipes present in River Apodi/Mossoró - RN and check some of the possibilities of using the biomass produced, based on the influence of space - temporal and physiological absorption of nutrients by plants. For this, was determined: Leaf area, Leaf wet mass, Leaf dry mass, Real humidity, Apparent humidity, Ash, Total nitrogen, Crude protein, Calcium, Magnesium, Potassium, Total phosphorus, Sodium, Iron, Copper, Manganese, Zinc, Nickel, Cobalt, Aluminum, Cadmium, Lead and Total chromium at different times, 2 sampling points and 2 parts of plants (leaves and roots). The results show that the levels of nutrients, protein and toxic elements present in plant tissue of Eichhornia crassipes are influenced by spatial, temporal and physiological variability. In general, because the maximum values in the dry matter for total nitrogen (4.4088 g/100g), crude protein (27.5549 g/100g), total phosphorus (0.642 g/100 g), calcium (1.444 g/100g), magnesium (0.732 g/100 g), potassium (7.51 g/100 g), copper (4.4279 mg/100g), manganese (322.668 mg/100g), sodium (1.39 g/100g), iron (194.169 mg/100g) and zinc (3.5836 mg/100g), there was the possibility of using biomass of Eichhornia crassipes for various purposes such as in food animal, products production for human consumption, organic fertilizers, fabrication of brick low cost, and crafts. For all these applications requires a control of the levels of substances in plant tissue. Based on the levels of nutrients and crude protein, the younger plants (0 Month) would be best to have their biomass used. Moreover, one factor that contributes to the use of larger plants (6 Months), the levels of toxic elements which have significantly small or below the detection limit. Therefore, further studies quantifying the biomass produced/m2 at 0 and 6 months are needed for a more correct choice for the best time of harvest

Determinação da composição química do molusco anadara notabilis encontrado em Galinhos no Rio Grande do Norte

Tendo em vista a grande biodiversidade existente no litoral brasileiro, onde muitas espécies ainda são pouco conhecidas, inclusive sob o aspecto nutricional, e considerando que os moluscos bivalves se constituem em um recurso natural de boa aceitação pela população mundial, escolheu-se o molusco bivalve Anadara notabilis, por não ter sido encontrado na literatura nenhuma informação nutricional ou toxicológica sobre ele e devido seu tamanho ser bem maior que outras espécies de moluscos mais popularmente encontrados nessa região. Foram determinados neste trabalho teores de umidade, cinzas, proteínas, macro e microminerais, além de íons metálicos de importância toxicológica. Todas as determinações seguiram as Normas Analíticas do Instituto Adolfo Lutz. A determinação de proteína foi realizada pelo método de Kjeldahl. Todos os íons metálicos foram determinados por espectroscopia de emissão ótica com plasma indutivamente acoplado (ICP-OES) descrito pela metodologia USEPA 6010C. Os resultados mostraram que a Anadara notabilis pode ser introduzida na alimentação dos seres humanos, tendo em vista sua riqueza mineral. Merecem destaque entre os macronutrientes o magnésio e o fósforo que apresentaram os respectivos valores em mg/kg 918,7 e 586,7. Com relação aos micronutrientes destacam-se o ferro presente com 586,7 mg/kg e o Zinco com 12,31 mg/kg. Não foi encontrado índice elevado de metais contaminantes para este molusco, o que impediria seu consumo, apenas o cromo esta 0,7 mg/kg acima do valor estabelecido pela legislação brasileira. Os resultados obtidos certamente serão muito úteis em futuras pesquisas nutricionais e para construção de uma tabela brasileira de composição química de alimentos

Determinação da composição química do molusco Anadara notabilis encontrado em Galinhos no Rio Grande do Norte

Given the large existing biodiversity in the Brazilian coast, where many species are still little known, even under the nutritional aspect, and considering that bivalve molluscs are constituted by a natural resource of well accepted by the population, chose the bivalve Anadara notabilis, it was not found in the literature any nutritional or toxicological information about it and because its size is much larger than other species of mollusks commonly found in this region. Were studied moisture, ash, protein, macro and micro minerals, and metal ions of toxicological significance. All analytical determinations followed the standards of the Institute Adolfo Lutz. The protein determination was performed by the Kjeldahl method. All metal ions were determined by optical emission spectroscopy with inductively coupled plasma (ICP-OES) method described by USEPA 6010C. The results showed that Anadara notabilis can be introduced into food for human beings, in view of its mineral wealth. Noteworthy among the macronutrients phosphorus and magnesium showed that their values in mg / kg 918.7 and 586.7. With regard to micronutrients stand out with this iron 586.7 mg / kg and zinc with 12.31 mg / kg. Was not found high content of metal contaminants to this mollusc, which would prevent their use, only this chromium 0.7 mg / kg above the value established by Brazilian legislation. The results will certainly be very useful in future studies of nutrition and to build a table of chemical composition of Brazilian foods

Tratamento eletroquímico de água produzida sintética para remoção de hidrocarbonetos policíclicos aromáticos

The aim of this work is the treatment of produced water from oil by using electrochemical technology. Produced water is a major waste generated during the process of exploration and production in the oil industry. Several approaches are being studied aiming at the treatment of this effluent; among them can be cited the biological process and chemical treatments such as advanced oxidation process and electrochemical treatments (electrooxidation, electroflotation, electrocoagulation, electrocoagulation). This work studies the application of electrochemical technology in the treatment of the synthetic produced water effluent through the action of the electron, in order to remove or transform the toxic and harmful substances from the environment by redox reactions in less toxic substances. For this reason, we used a synthetic wastewater, containing a mixture H2SO4 0,5M and 16 HPAs, which are: naphthalene, acenaphthylene, acenaphthene, fluorene, phenanthrene, anthracene, fluoranthene, pyrene, benzo (a) anthracene, chrysene, benzo(b)fluoranthene, benzo(k) fluoranthene, benzo(a)pyrene, indeno(1,2,3-cd)pyrene, dibenzo(a, h)anthracene, benzo(g, h, i)perylene. Bulk electrochemical oxidation experiments were performed using a batch electrochemical reactor containing a pair of parallel electrodes, coupled with a power supply using a magnetic stirrer for favoring the transfer mass control. As anodic material was used, a Dimensionally Stable Anode (DSA) of Ti/Pt, while as cathode was used a Ti electrode. Several samples were collected at specific times and after that, the analysis of these samples were carried out by using Gas Chromatography Coupled to Mass Spectrometry (GC - MS) in order to determine the percentage of removal. The results showed that it was possible to achieve the removal of HPAs about 80% (in some cases, more than 80%). In addition, as an indicator of the economic feasibility of electrochemical treatment the energy consumption was analyzed for each hour of electrolysis, and based on the value kWh charged by ANEEL, the costs were estimated. Thus, the treatment costs of this research were quite attractive

Deposição de filmes de ZrO2 modificados sobre substratos metálicos

This work makes use of the Pechini process for synthesis of the solutions and the dip-coating process for the addition of zirconium oxide films pure and doped cerium metal substrates. The metals with ceramic substrates were subjected to severe conditions of salinity. The x-ray fluorescence of the substrate showed a great diversity of chemical elements. The x-ray diffraction of the samples showed the phase of iron substrate because the thickness of nano-thin film. Tests using an LPR probe showed that the film presents with zirconia corrosion independent of film thickness. The substrates of ZrO2-doped ceria showed low chemical attack of the salt in films with less than 15 dives. The results imply that ultrathin films are shown in protecting metallic substrates

Determinação do teor de cálcio através da termogravimetria, em medicamentos utilizados no tratamento da osteoporose: um estudo comparativo

The present study utilized the thermogravimetry (TG) and optical emission spectroscopy with inductively coupled plasma - ICP / OES to determine the calcium content in tablets of carbonate, citrate and calcium lactate used in the treatment of osteoporosis. The samples were characterized by IR, SEM, TG / DTG, DTA, DSC and XRD. The thermal analysis evaluated the thermal stability and physical-chemical events and showed that the excipients influence the decomposition of active ingredients. The results of thermogravimetry indicated that the decomposition temperature of the active CaCO3 (T = 630.2 °C) is lower compared to that obtained in samples of the tablets (633.4 to 655.2 °C) except for sample AM 2 (Ti = 613.8 oC). In 500.0 °C in the samples of citrate and calcium lactate, as well as their respective active principles had already been formed calcium carbonate. The use of N2 atmosphere resulted in shifting the initial and final temperature related to the decomposition of CaCO3. In the DTA and DSC curves were observed endo and exothermic events for the samples of tablets and active ingredients studied. The infrared spectra identified the main functional groups in all samples of active ingredients, excipients and tablets studied, such as symmetric and asymmetric stretches of the groups OH, CH, C = O. Analysis by X-ray diffraction showed that all samples are crystalline and that the final residue showed peaks indicative of the presence of calcium hydroxide by the reaction of calcium oxide with moisture of the air. Although the samples AM 1, AM 2, AM 3 and AM 6 in their formulations have TiO2 and SiO2 peaks were not observed in X-ray diffractograms of these compounds. The results obtained by TGA to determine the calcium content of the drugs studied were satisfactory when compared with those obtained by ICP-OES. In the AM 1 tablet was obtained the content of 35.37% and 32.62% for TG by ICP-OES, at 6 AM a percentage of 17.77% and 16.82% and for AM 7 results obtained were 8.93% for both techniques, showing that the thermogravimetry can be used to determine the percentage of calcium in tablets. The technique offers speed, economy in the use of samples and procedures eliminating the use of acid reagents in the process of the sample and efficiency results.

Obtenção e Caracterização Físico-Química do Sistema Compósito PEG-TiO2

Hybrid systems formed from polymers and transition metals have now their physical and chemical properties extensively investigated for use in electronic devices. In this work, Titanium Dioxide (TiO2) from the precursor of titanium tetrabutoxide and the composite system Poly(Ethylene Glycol)-Titanium Dioxide (TiO2-PEG) were synthesized by sol-gel method. The PEG as acquired and TiO2 and composites powders were analyzed by X-Ray Diffraction (XRD), Spectroscopy in the Infrared region with Fourier transform (IRFT), Thermogravimetric Analysis (TGA), Scanning Electron Microscopy (SEM) and Electrochemical Impedance Spectroscopy (EIS). In the XRD analysis were observed in the TiO2 crystal faces of one of its polymorphs - anatase phase, crystal planes in Poly (Ethylene Glycol) with considerable intensity and in the composite systems the mixture of crystal faces of their precursors isolated and reduction of crystallinity. The TG / DTG suggested increasing the thermal instability of PEG in the composite powders as TiO2 is incorporated into the system. Spectral analysis presented in the infrared overlapping bands for the polymer and metal oxide, reducing the intensity of symmetric stretching of ligand groups in the main chain polymer and angular deformations; were observed using SEM micrographs of the morphological changes suffered by composite systems with the variation of the oxide concentration. Analyses by impedance spectroscopy indicated that the increased conductivity in composite occurs in line with the addition of the metal oxide concentration in the composite system

Aplicação de argila branca comercial pura e modificada para adsorção de sulfeto de hidrogênio

In this work were synthesized matrix-based commercial white clay in its composition having large amounts of kaolinite and quartz, with a certain percentage of iron oxide for use as an adsorbent for hydrogen sulfide (H2S). To characterize the effect of initial matrix techniques were used to characterize XRD, FTIR, XRF and TG. The initial clay mineral matrix was placed in contact with 0.1 molar solutions of the salts of Co2+, Ni2+, Cr3+ and a solution 0.1 g / 100ml rhodamine B. During the synthesis process, the solutions were placed in contact with the initial matrix for a period of 48 hours in order to have ion exchange with the clay mineral. To check the amount of exchanged metals, we used the technique of X-ray Fluorescence (XRF). After synthesis was initiated the process of adsorption of H2S, where the arrays were placed in the reactor, then by passing a stream of hydrogen sulfide. The matrix along with the reactor was weighed before and after to measure the amount of gas adsorbed. Based on the gravimetric data the matrix which had the highest performance of the adsorption matrix was exchanged with Ni2+ ions, obtaining a result of 11.13 mg H2S / g matrix, then the matrix coated with rhodamine B which was reached 10.13 mg H2S / g matrix

Análise bromatológica de carnes antes e após o processamento para obtenção de charque

The process of salting and drying in the sun is used to preserve meat since the beginning of civilization. There is evidence that this preservation technique has arisen in Egypt, between 4,000 and 5,000 years ago. In our country, according to literature, was the first industrial product that gave the appearance of beef jerky, beef being produced, where about 70% to 75% of the muscle is composed of water, where it will be around 45% as a final product, according to the law in his article RIISPOA No. 432 provides that the jerky should contain no more than this amount of moisture in the muscular portion, or more than 15% of total ash with tolerance of up to 5% variation . Besides this parameter, proteins, lipids, ash, and minerals were analyzed in samples before and after the manufacturing process to know the content of these nutrients. Since these are considered important in product quality, thus the concentration in these samples, respectively, in the flesh Front (CD and CHD) before and after the manufacturing process for humidity were respectively 75.28% and 47.38% , the protein was 14.17 and 22.20 g / 100 g sample, 6.360 and 4.251 of lipids g/100g of the sample, and the ashes 0.974 9.144 g/100g sample, minerals like calcium and 4.074 30 , 06 ppm, sódio0, 055 and 5.401 g / L, sodium chloride, 0.139 and 13.74 g / L, potassium 237.5 and 166.8 ppm, 1.721 and 3.295 ppm iron, 0.143 and 0.135 ppm phosphorus, zinc and 4.690 6.905 ppm; magnésio14, 63 e13, 75 ppm manganese .017 e0, 007ppm, copper 0.057 and 0.039 ppm in the case of needle-type meat (CPA and CHPA), 68.04% and 44.17%, protein 13 , 72, and 24.42 g/100g of sample, 1.137 in the ash and 12.68 g / 100g of sample, and the minerals calcium 17.11 and 12.89 ppm; sódio0, 123 and 4.871 g / L, sodium chloride 0.312 and 12.39 g / L, potassium 305.3 and 182.1 ppm; ferro1, 817 and 1.513 ppm, 0.273 and 0.139 ppm phosphorus, zinc 6.305 and 4.783 ppm, 27.95 and 15.85 ppm magnesium, manganese and 0.025 0.011 ppm, 0.057 and 0.143 ppm copper and chromium 0.014 and 0.068 ppm

Membranas de quitosana micro e macroporosas : preparo, caracterização e estudos de permeabilidade

Two methodologies were proposed to obtain micro and macroporous chitosan membranes, using two different porogenic agents. The methodologies proved to be effective in control the porosity as well as the pore size. Thus, microporous membranes were obtained through the physical blend of chitosan and polyethylene oxide (PEO) on an 80:20 (m/m) ratio, respectively, followed by the partial PEO solubilization in water at 80 ◦C. Macroporous chitosan membranes with asymmetric morphology were obtained using SiO2 as the porogenic agent. In this case, chiotsan-silica ratios used were 1:1, 1:3 and 1:5 (m/m). Membranes characterization were carried out by SEM (scanning electronic microscopy), X-ray diffraction, Fourier Transform Infrared Spectroscopy (FTIR), Thermal analysis (TG, DTG , DSC and DMTA). Permeability studies were performed using two model drugs: sodium sulfamerazine and sulfametoxipyridazine. By transmission FTIR it was possible to confirm the complete removal of SiO2. The SEM images confirmed the porous formation for both micro and macroporous membranes and also determined their respective sizes. By thermal analysis it was possible to show differences related with water sorption capacity as well as thermal stability for both membranes. DTG and DSC allowed evidencing the PEO presence on microporous membranes. The absorbance x time curves obtained on permeability tests for micro and macroporous membranes showed a linear behavior for both drugs in all range of concentration used. It was also observed, through P versus C curves, an increase in permeability of macroporous membranes according to the increase in porosity and also a decrease on P with increase in drug concentration. The influences of the drug molecular structure, as well as test temperatures were also evaluated

Determinação de Ba, Cd, Cr, Cu, Ni, Pb, Sn e Zn em Tainha (Mugil brasiliensis) nos estuários potiguares

Heavy metals can cause problems of human poisoning by ingestion of contaminated food, and the environment, a negative impact on the aquatic fauna and flora. And for the presence of these metals have been used for aquatic animals biomonitoramento environment. This research was done in order to assess the environmental impact of industrial and domestic sewage dumped in estuaries potiguares, from measures of heavy metals in mullet. The methods used for these determinations are those in the literature for analysis of food and water. Collections were 20 samples of mullet in several municipality of the state of Rio Grande do Norte, from the estuaries potiguares. Were analyzed the content of humidity, ash and heavy metals. The data were subjected to two methods of exploratory analysis: analysis of the main components (PCA), which provided a multivariate interpretation, showing that the samples are grouped according to similarities in the levels of metals and analysis of hierarchical groupings (HCA), producing similar results. These tests have proved useful for the treatment of the data producing information that would hardly viewed directly in the matrix of data. The analysis of the results shows the high levels of metallic species in samples Mugil brasiliensis collected in Estuaries /Potengi, Piranhas/Açu, Guaraíra / Papeba / Arês and Curimataú

Hidróxidos duplos lamelares de magnésio e alumínio modificados com carbonato e p123 para adsorção de dióxido de carbono

Muitos mecanismos provocados pela ação humana vêm gerando um aumento na queima de combustíveis fósseis e processos químicos (produtos orgânicos, carvão, madeira, óleo diesel, gasolina e outros derivados de petróleo) e, consequentemente, há um aumento na emissão de CO2 na atmosfera. Uma das alternativas para a captura desse poluente é o processo de adsorção, o qual pode ajudar na redução do CO2. As hidrotalcitas ou hidróxidos duplos lamelares (HDL s) estão dentre esses materiais estudados, já que apresentam alta estabilidade e uma boa porosidade, tornando-se assim um promissor adsorvente de gases poluentes. Os HDL s formam um grupo de argilas do tipo aniônico que consiste em camadas positivamente carregadas de óxido de metal (ou hidróxido de metal) com intercamadas de ânions. Foi constatado que ânions que possuem duas cargas negativas, estabilizam muito mais que ânions monovalentes, sendo o carbonato o mais estável dos ânions divalentes. Neste trabalho, foi proposta uma modificação na síntese direta através da co-precipitação a pH constante utilizando sais de cátions divalentes (Mg2+) e trivalentes (Al3+) reportados na literatura. Durante a síntese dos HDL s retirou-se o carbonato, bem como, utilizou-se um copolímero como um template para o alargamento das lamelas. As amostras foram caracterizadas utilizando as técnicas de DRX, TG/DTG, FTIR, MEV/EDX, MET e adsorção e dessorção de N2. Os dados obtidos indicam que a estrutura, mesmo após a modificação, apresentou resultados condizentes com os encontrados na literatura. Dentre as várias aplicações dos HDL s foi realizado o estudo da adsorção do CO2. A capacidade de adsorção do material foi testada de acordo com o tempo de contato entre o adsorvente e o adsorbato, sendo esperado que os materiais tratados com template apresentassem um maior desempenho