Estudo do aproveitamento do rejeito da mineração de esmeraldas na produção de refratários conformados isolantes

Emerald mining is an important area of the economy in Brazil, country which is in second place among the exporting nations of this gem. Due to the process of extraction, a great amount of reject is generated. Since there is no appropriate destination, the reject is abandoned around the mining industries, contributing to environment degradation. Nowadays, some of the most relevant things to an industry in general are: energy conservation, cost reduction, quality and productivity enhancement. The production of isolating, transformed refractory materials achieves the sustainability dimension when protection of the environment is incorporated to such process. This work investigates the use of emerald mining rejects in the ceramic body of refractory materials, aiming at obtaining a product whose characteristics are compatible with commercial products and, at the same time, allow the use of such rejects to solve the environmental issue caused by its disposal in nature. X-ray fluorescence analysis show that the emerald reject obtained after the flotation to extract molybdenum and mica has 70% of silica and alumina (SiO2+Al2O3) and 21% of a basic oxides and alkaline metals and earthy alkaline mixture (Na2O, K2O, CaO e MgO). Because of the significant amount of silica and alumina present in the reject, four refractory ceramic bodies were prepared. Samples with a rectangular shape and dimensions 100x50x10 mm were pressed in a steel mold at 27,5 MPa and sintered at 1200ºC for 40 min. under environment atmosphere in a resistive oven. The sintered samples were characterized in relation to the chemical composition (FRX), mineralogical composition (DRX), microstructure (MEV) and physical and mechanical properties. The results indicate that the mixture with 45% of reject, 45% of alumina and 10% of kaolin presents a refractory quality of 1420ºC, dimensional linear variation below 2.00%, apparent specific mass of 1,56 g/cm3 and porosity of 46,68%, which demonstrates the potential use of the reject as raw material for the industry of isolating transformed refractory materials

Estudo do potencial refratário de argilas sílico-aluminosas do Rio Grande do Norte

The segment of the structural ceramics industry is one of the most important to the economy of Rio Grande do Norte. The supply chain makes a total of 206 companies that are distributed in 39 counties, concentrated in three regional centers: Seridó Apodi / Assu and great Natal. The ceramic industry in the state is around 80 million pieces per month, with 50,186 million of these tiles, which makes the Rio Grande do Norte one of the largest manufacturers of product in the Country. Different ceramic products can be manufactured by mixing two or more clays and accessory minerals. Mixtures acquire characteristics and form what is called the ceramic body. Refractory masses have a high melting point and thermal shock support. Its composition contains refractory clays with a little iron oxide and material fluxes. A line of semi-refractory ceramic products that stands out for its high added value are the bricks in ivory or red, used in building barbecues, fireplaces, wood stoves and braziers. The aim of this study was to use alumina-clay or silica- alumina-clay to the industrial RN, for the production of refractory bricks semi-refractory burning light. Clay and Kaolin were characterized for their chemical and mineralogical composition, immediately after ceramic bodies were made with different concentrations of the components, they were raised, pressed and sintered. After sintering the resulting products were characterized in terms of mechanical, thermal and dimensional than the characterization by X-ray diffraction and scanning electron microscopy. After obtaining the results, we concluded that the studied clay can be used for the production of semi-refractory bricks

Análise da adição de resíduo oriundo do tratamento de esgotos em massa cerâmica utilizada para fabricação de telhas

Sludge of Wastewater Treatment Plants (WTPs) disposal is a problem for any municipality, for this reason the amount of sludge production is now a key issue in selecting treatment methods. It is necessary to investigate new applications for this waste type, due to the restrictions imposed by the environmental organs. The raw materials used in the Red Ceramic, are generally very heterogeneous, for this reason, such materials can tolerate the presence of different types of wastes. In Rio Grande do Norte, the roof tiles production corresponds to 60,61% from the total of ceramic units produced. Due to the importance of the ceramic industry of roof tiles for the state, allied to the environmental problem of the sludge disposal, this work had for objective to verify the possibility of the incorporation of sewage sludge in ceramic body used for production of roof tiles. In the research, sludge originating from drying beds of WTP of the Central Campus from UFRN and clays originating from a ceramic industry from Goianinha/RN were used. The raw materials were characterized by techniques of: analysis of particles distribution by diffraction to laser; real density; consistence limits; chemical analysis by X-ray fluorescence; mineralogical analysis by X-ray diffraction; organic matter; and solids content. Five batches of roof tiles were manufactured in the approximate dosages of 2%, 4%, 6%, 8% and 10%. To evaluate the properties of each final product, tests of water absorption, impermeability, bending strength, leachability and solubility were accomplished. The roof tiles manufactured with sludge presented characteristics similar to the roof tiles without sludge in relation to the environmental risk. The results showed that it is possible to use approximately up to 4% of sludge in ceramic bodies for production of roof tiles. However, it is observed that the high amount of organic matter (71%) present in the sludge is shown as factor that limits the sludge incorporation in ceramic bodies, worsening the quality of the roof tiles. It is necessary the use of mixtures of different raw materials under point of view of the granulometry and of the other chemical and mineralogical properties for the obtaining of a satisfactory mass to the production of ceramic roof tiles

Estudos de sinterização da mistura de pós cerâmicos diatomita-titânia

This work is part of an effort of consolidation of a daily search for powder technology at the Department of Physics of the Universidade Federal do Rio Grande do Norte. This work objective the study and development of new ceramic materials from raw materials abundant at the region. For this, were studied ceramic mixtures of powders from diatomite-titania to aiming at a new ceramic material from powder technology. The experimental work involved a characterization of ceramic powders from a diatomite-titania mixture. The powders obtained were pressed and then parameters like variation of mass, linear shrinkage, activation energy and the mechanism of sintering are studied in function of the time and temperature of sintering, beyond microstructural analysis. The obtained results allow us estimate the optimizing of sintering conditions of this material

Estudo de propriedades elétricas em compostos de Bario

Este trabalho tem como objetivo estudar a influência da adição de diversos aditivos tais como óxido de silício (SiO2), óxido de bismuto (BiO2), óxido de cério (CeO2) e óxido de lantânio (La2O3) nas propriedades elétricas e dielétricas do titanato de bário (BaTiO3) policristalino. As amostras de titanato de bário foram compactadas e sinterizadas no Laboratório de Tecnologia dos Pós, do Departamento de Física da Universidade Federal do Rio Grande do Norte. Foram realizadas medidas de resistividade elétrica e constante dielétrica em função da temperatura, bem como ensaios de difração de raios-X e análise microestrutural através da microscopia eletrônica de varredura. A análise dos resultados permitiu avaliar a influência dos aditivos nas propriedades elétricas e dielétricas, e propor a utilização de cerâmicas eletrônicas a base de titanato de bário com propriedades superiores as do material existente atualmente

Síntese e caracterização de pós Ba(x)Sr(1-x)Co0,8Fe0,2O3- através do método de coprecipitação via oxalato

Ceramic powders based on oxides of perovskite-type structure is of fundamental interest nowadays, since they have important ionic-electronic conductivity in the use of materials with technological applications such as gas sensors, oxygen permeation membranes, catalysts and electrolytes for solid oxide fuel cells (SOFC). The main objective of the project is to develop nanostructured ceramic compounds quaternary-based oxide Barium (Br), Strontium (Sr), Cobalt (Co) and Iron (Fe). In this project were synthesized compounds BaxSr(1-x)Co0, 8Fe0,2O3- (x = 0.2, 0.5 and 0.8) through the oxalate co-precipitation method. The synthesized powders were characterized by thermogravimetric analysis and differential thermal analysis (TGADTA), X-ray diffraction (XRD) with the Rietveld refinement using the software MAUD and scanning electron microscopy (SEM). The results showed that the synthesis technique used was suitable for production of nanostructured ceramic solid solutions. The powders obtained had a crystalline phase with perovskite-type structure. The TGA-DTA results showed that the homogeneous phase of interest was obtained temperature above 1034°C. It was also observed that the heating rate of the calcination process did not affect the elimination of impurities present in the ceramic powder. The variation in the addition of barium dopant promoted changes in the average crystallite size in the nanometer range, the composition being BSCF(5582) obtained the lowest value (179.0nm). The results obtained by oxalate co-precipitation method were compared with those synthesis methods in solid state and EDTA-citrate method

O circuito espacial da indústria de cerâmica vermelha no seridó potiguar

This research has as an empirical universe, the productive territory of red ware in the Seridó region of Rio Grande do Norte. In the last years this territory has gone through a process of appropriation that has been substantially changing the environmental and social dynamism of the place. However, the industry of red ware has been focusing in some areas, mainly, in the county of Parelhas and Carnaúba dos Dantas. From this point of view, the aim of this work consists in analyze the use of these areas by the red ware industry and the transformations occurred with the expansion of the number of industries and the productivity raise, that requires bigger amounts of earthenware and wood, resources that are low in referred territory. As the result of this process, the suitable alternative has been to acquire inputs in other Rio Grande do Norte counties, as well as in Paraíba counties. To reach the proposed objective, the methodology of this work was consisted of bibliographic and empirical research, regarding the occupation that this activity covers in the Seridó region. From the information obtained during the research, it can be stated that the inputs to the production execution in the red ware industry are acquired in the geographic nearby lands. The analysis of the stages of the production(acquisition of raw material, production and commercialization) showed that the activity acts in a continuous area, having as principal consumer market other northeastern states and the state of Pará. The present study revealed that the pottery activity is set as untenable, because of non-stopping use of the argil and wood, resources that are vanishing from the area, which consume causes a many problems such as deforestation and erosion. Besides, the sale of productive lands for the red ware industries makes harder its good use by the familiar agriculturists in the development of agriculture and cattle raising activity, which for many times is the main economic activity of the place. The precariousness reveals in the constant accidents at work, that most of them are neglected by the local authorities, without any penalty to the industries. Therefore, the industry of red ware in Seridó uses the territory as a resource, leaving its environmental problems that my compromise the quality of life of the actual and future generations

Estudo da adição de resíduos de quartzitos para obtenção de grés porcelanato

In States of Paraíba (PB) and Rio Grande do Norte (RN), northeast of Brazil, the most significant deposits of non-metallic industrial minerals are pegmatites, quartzites and granites, which are located in Seridó region. Extraction of clay, quartz, micas and feldspars occurs mainly in the cities of Várzea (PB), OuroBranco (RN) and Parelhas (RN). Mining companies working in the extraction and processing of quartzite generate large volumes of waste containing about 90% SiO2 in their chemical composition coming from quartz that is one of the basic constituents of ceramic mass for the production of ceramic coating. Therefore, this work evaluates the utilization of these wastes on fabrication of high-quality ceramic products, such as porcelain stoneware, in industrial scale. Characterization of raw materials was based on XRF, XRD, GA, TGA and DSC analysis, on samples composed by 57% of feldspar, 37% of argil and 6% of quartzite residues, with 5 different colors (white, gold, pink, green and black). Samples were synthesized in three temperatures, 1150°C, 1200°C and 1250°C, with one hour isotherm and warming-up tax of 10°C/min. After synthesizing, the specimens were submit to physical characterization tests of water absorption, linear shrinkage, apparently porosity, density, flexural strain at three points. The addition of 6% of quartzite residue to ceramic mass provided a final product with technological properties attending technical norms for the production of porcelain stoneware; best results were observed at a temperature of 1200°C. According to the results there was a high iron oxide on black quartzite, being their use in porcelain stoneware discarded by ethic and structural question, because the material fused at 1250°C. All quartzite formulations had low water absorption when synthesized at 1200°C, getting 0.1% to 0.36% without having gone through the atomization process. Besides, flexural strain tests overcame 27 MPa reaching the acceptance limits of the European Directive EN 100, at 1200°C synthesizing. Thus, the use of quartzite residues in ceramic masses poses as great potential for the production of porcelain stoneware.

Estudo do aproveitamento de resíduos PAE no desenvolvimento de materiais cerâmicos

This work presents a new ceramic material obtained through the incorporation of solid waste from the steel industry and known as dedusting powder PAE - in ceramic formulations based on clay, potassium and sodium feldspars, kaolin and talc. Formulations were prepared with ceramic residue levels of 0% (basic mass - MB), 2%, 4% and 8%, subjected to firing at temperatures of 1000 ° C, 1050ºC, 1100ºC and 1150ºC for periods of 15 min. and 120 min. The physicchemical and mechanical properties of these ceramic formulations were determined based on the firing temperature, residence time in the oven and the percentage of waste. Since the physicochemical and mechanical properties of the sintered materials were evaluated by chemical analysis techniques (fluorescence X-rays - FRX), particle size distribution, specific surface area, apparent density, structural analysis by diffraction of X-rays (DRX) and characterization of surface by scanning electron microscopy (SEM). The magnetic response characteristics and the pattern of magnetic ferrites of the samples were analyzed in the assay conditions, having noticed that the saturation magnetic susceptibility depend on the sintering temperature of the material and it is associated with its crystal structure. From the analysis results, it was concluded that the ceramic material with better physical and mechanical properties is obtained when the 8% from PAE residue is added to standard formulation under the burn time of 15 minutes and temperature of 1150ºC.

Study of porcelain-zirconia composites for dental applications

Materiais compósitos restauradores representam um dos mais bem sucedidos biomateriais na pesquisa moderna, na substituição do tecido biológico em aparência e função. Nesta linha, a porcelana feldspática tem sido largamente usada em odontologia devido suas interessantes qualidades como estabilidade de cor, propriedades estéticas, elevada durabilidade mecânica, biocompatibilidade, baixa condutividade térmica e elevada resistência ao desgaste. Entretanto, este material é frágil e pode falhar em ambiente oral devido ao micro-vazamento, baixa resistência à tração, descolagem ou fratura. Assim, para melhorar as propriedades mecânicas da porcelana, a zircônia parcialmente estabilizada com Ítria (Y-TZP) pode ser uma boa alternativa para fortalecer e produzir infraestruturas totalmente cerâmicas (coroas e próteses parciais fixas). Portanto, este estudo tem por objetivo avaliar as propriedades mecânicas e características microestruturais da porcelana reforçada com zircônia (3Y-TZP) em diferentes conteúdos e as variáveis que afetam as propriedades mecânicas destes materiais. O estudo de caracterização revelou que a zircônia comercial apresenta melhores resultados quando comparada com a zircônia sintetizada pelo CPM. Assim, os estudos seguintes utilizaram a zircônia comercial para todos os testes requeridos. As partículas de zircônia apresentam elevadas propriedades mecânicas quando comparadas a zircônia aglomerada. Os diferentes conteúdos revelam que as propriedades mecânicas dos compósitos aumentam com o aumento do conteúdo volumétrico até 30% vol.% (198,5Mpa), ou seja, maior resistência à flexão quando comparada com os outros compósitos. Do mesmo modo, a resistência ao desgaste para os compósitos com (30%, vol.% de zircônia) apresenta valores superiores quando comparado aos demais compósitos. Na adesão cerâmico-cerâmico a porcelana exibe elevada adesão para a superfície de zircônia porosa quando comparada a superfície rugosa. Os furos superficiais (PZ) e aplicação de compósitos com camada intermediária (RZI) na zircônia causam separadamente uma melhoria da resistência ao cisalhamento da zircônia-porcelana quando comparados as amostras convencionais de zircônia-porcelana (RZ), embora não sejam estatisticamente significativas (p>0.05). A presença de uma camada intermediaria produz um aumento significativo na força de ligação (~55%) em relação as amostras convencionais (RZ). Portanto, a correta a correta configuração e tratamento superficial podem produzir subestruturas com qualidade e força de ligação adequadas aos requisitos odontológicos.

Estudo da incorporação de cinza e chamote gerado pela cerâmica vermelha ao próprio processo industrial

The ceramics industry generates waste at various stages of that process, defective products, waste from burning solid fuels, among others. This waste is dumped in landfills, garbage dumps or directly on roads, which has a negative environmental impact. This paper presents a study to incorporate the waste of algaroba wood and chamote (scrap pieces of ceramic already sintered), in to the ceramic material for making sealing blocks. The methodological procedures consist in the characterization of chemical and mineralogical residues, raw materials, and physical-mechanical of the formulations of mixes with clay, silt and waste. By pressing test pieces were produced using a pressure of 200 kgf/cm², varying compositions in the range of 0%, 5%, 10% and 15% by weight of residue. The sintering was performed in a muffle furnace, with the temperature levels of 850 ° C, 900 ° C, 950 ° C, 1000 ° C and 1050 ° C. The evaluated physical and mechanical properties were: Water Absorption, Linear Shrinkage Burning, Apparent Porosity, Apparent Density and Mechanical Resistance to Flexion. Analysis was carried out by Scanning Electron Microscopy on fracture surfaces of the specimens. Evaluation of linear shrinkage property drying and firing , water absorption and mechanical resistance to compression of the sealing blocks 5% wood ash residue, sintered at 900 °C hold temperature in the laboratory the products manufactured on an industrial scale. The main results, it was found on the viability of using the residues of algaroba wood and to confer refractory properties of the ceramic product. The main results, it was concluded feasibility of using the ash residues algaroba wood to impart refractory properties to the ceramic product and the residue of chamote, being derived from the own ceramic product not interfere with the properties, when used in a percentage of up to 5%.Since the residue of chamote being derived from the ceramic product itself had no effect on the properties. Studies in the laboratory have shown that the incorporation of up to 5% of these residues may be adopted as an alternative technology to reduce the environmental impact caused by the industrial sector, without compromising the final properties of the material, since the results on an industrial scale showed absorption values 11.66 and 11.74 of water and waste products respectively, within the parameters of NBR - 15,270, since the mechanical strength was 1.25 MPa and 0.94 MPa respectively for products with and without residue, lower than the minimum required by the technical standard that is 1.5 MPa.

Estudo da incorporação de cinza e chamote gerado pela cerâmica vermelha ao próprio processo industrial

The ceramics industry generates waste at various stages of that process, defective products, waste from burning solid fuels, among others. This waste is dumped in landfills, garbage dumps or directly on roads, which has a negative environmental impact. This paper presents a study to incorporate the waste of algaroba wood and chamote (scrap pieces of ceramic already sintered), in to the ceramic material for making sealing blocks. The methodological procedures consist in the characterization of chemical and mineralogical residues, raw materials, and physical-mechanical of the formulations of mixes with clay, silt and waste. By pressing test pieces were produced using a pressure of 200 kgf/cm², varying compositions in the range of 0%, 5%, 10% and 15% by weight of residue. The sintering was performed in a muffle furnace, with the temperature levels of 850 ° C, 900 ° C, 950 ° C, 1000 ° C and 1050 ° C. The evaluated physical and mechanical properties were: Water Absorption, Linear Shrinkage Burning, Apparent Porosity, Apparent Density and Mechanical Resistance to Flexion. Analysis was carried out by Scanning Electron Microscopy on fracture surfaces of the specimens. Evaluation of linear shrinkage property drying and firing , water absorption and mechanical resistance to compression of the sealing blocks 5% wood ash residue, sintered at 900 °C hold temperature in the laboratory the products manufactured on an industrial scale. The main results, it was found on the viability of using the residues of algaroba wood and to confer refractory properties of the ceramic product. The main results, it was concluded feasibility of using the ash residues algaroba wood to impart refractory properties to the ceramic product and the residue of chamote, being derived from the own ceramic product not interfere with the properties, when used in a percentage of up to 5%.Since the residue of chamote being derived from the ceramic product itself had no effect on the properties. Studies in the laboratory have shown that the incorporation of up to 5% of these residues may be adopted as an alternative technology to reduce the environmental impact caused by the industrial sector, without compromising the final properties of the material, since the results on an industrial scale showed absorption values 11.66 and 11.74 of water and waste products respectively, within the parameters of NBR - 15,270, since the mechanical strength was 1.25 MPa and 0.94 MPa respectively for products with and without residue, lower than the minimum required by the technical standard that is 1.5 MPa.

Estudo da obtenção de cerâmica composta de alumina e beta alumina sódica utilizando-se resíduo cerâmico de velas de ignição e pó químico de extintores de incêndio

Ceramic materials the alumina base are large industrial applications. They are required for these products, specific characteristics obtained by following strict criteria during the manufacturing process. However, after life, not always these products are reused by a suitable waste management process. In ceramist context, advance research aimed at the reuse of waste aimed at obtaining ceramics and composite materials, with marked reduction of conventional raw materials. Aiming to generate scientific, technological and environmental contribution, this work studied to obtain a composite of alumina ceramic (Al2O3) and sodium beta alumina (NaAl11O17 ), and as starting materials the residue of the ceramic insulator of spark plugs, as a source alumina (Al2O3) powder and unusable sodium bicarbonate (NaHCO3) of fire extinguishers, as a source of sodium oxide (Na2O). The final ceramic product was obtained from a conventional mixture of sodium aluminum oxide in appropriate molar proportions. Sample spark plugs were obtained, discarded by lifetime, specific to a manufacturer, which, after passing through mechanical stress (grinding, magnetic purification, washing, drying and grinding the high energy), which resulted in residue powder with ceramic content of 84.34 % alumina (Al2O3), found by FRX chemical analysis, the phases present and identified by DRX. The dry chemical fire extinguisher, baking soda-based (NaHCO3) with expired, was obtained through direct collection of the waste generated during maintenance. Subjected to heat treatment at 120 °C , the NaHCO3 powder was decomposed in sodium oxide ( Na2O), which, subjected to chemical analysis (FRX) and mineralogical (DRX) revealed a content of 86.62 % sodium oxide (Na2O) . In the following steps the experimental procedure, chemical formulations were made on a molar basis of the starting material (1:9, 1:10 and 1:11 de Na2O/ Al2O3) inclusion of additives, milling parameters, sieve analysis, dilatometry, conformation of specimens, sintering in firing steps at 800 °C , 1000 °C and 1.200 °C with varying stays 30 , 60 and 120 minutes in each of the levels. The characterization of the final product was made by the following physical tests: water absorption, porosity, linear shrinkage, mineralogical analysis by DRX and microstructural analysis by MEV. A higher formation of sodium beta alumina (NaAl11O17), in sintered specimens in levels of 1.200 °C and 120 minutes, despite the prevailing coexistence of alpha phase alumina (Al2O3). From the results obtained opens up prospects for the reuse of waste studied in this work, the potter context and in other technological areas.

Estudo da obtenção de cerâmica composta de alumina e beta alumina sódica utilizando-se resíduo cerâmico de velas de ignição e pó químico de extintores de incêndio

Ceramic materials the alumina base are large industrial applications. They are required for these products, specific characteristics obtained by following strict criteria during the manufacturing process. However, after life, not always these products are reused by a suitable waste management process. In ceramist context, advance research aimed at the reuse of waste aimed at obtaining ceramics and composite materials, with marked reduction of conventional raw materials. Aiming to generate scientific, technological and environmental contribution, this work studied to obtain a composite of alumina ceramic (Al2O3) and sodium beta alumina (NaAl11O17 ), and as starting materials the residue of the ceramic insulator of spark plugs, as a source alumina (Al2O3) powder and unusable sodium bicarbonate (NaHCO3) of fire extinguishers, as a source of sodium oxide (Na2O). The final ceramic product was obtained from a conventional mixture of sodium aluminum oxide in appropriate molar proportions. Sample spark plugs were obtained, discarded by lifetime, specific to a manufacturer, which, after passing through mechanical stress (grinding, magnetic purification, washing, drying and grinding the high energy), which resulted in residue powder with ceramic content of 84.34 % alumina (Al2O3), found by FRX chemical analysis, the phases present and identified by DRX. The dry chemical fire extinguisher, baking soda-based (NaHCO3) with expired, was obtained through direct collection of the waste generated during maintenance. Subjected to heat treatment at 120 °C , the NaHCO3 powder was decomposed in sodium oxide ( Na2O), which, subjected to chemical analysis (FRX) and mineralogical (DRX) revealed a content of 86.62 % sodium oxide (Na2O) . In the following steps the experimental procedure, chemical formulations were made on a molar basis of the starting material (1:9, 1:10 and 1:11 de Na2O/ Al2O3) inclusion of additives, milling parameters, sieve analysis, dilatometry, conformation of specimens, sintering in firing steps at 800 °C , 1000 °C and 1.200 °C with varying stays 30 , 60 and 120 minutes in each of the levels. The characterization of the final product was made by the following physical tests: water absorption, porosity, linear shrinkage, mineralogical analysis by DRX and microstructural analysis by MEV. A higher formation of sodium beta alumina (NaAl11O17), in sintered specimens in levels of 1.200 °C and 120 minutes, despite the prevailing coexistence of alpha phase alumina (Al2O3). From the results obtained opens up prospects for the reuse of waste studied in this work, the potter context and in other technological areas.

Desenvolvimento de formulações para produção de grés porcelanato a partir de matérias-primas da região da bacia do Parnaíba

Brazil is a great ceramic raw materials productor because of the its big number of clay deposits, in various areas of the ceramic industry. Although, the majority of the natural reservations are unknown or not studied yet, so there is no scientific technical dates that can guide their usage and industrial application, as well as the racional and optimazed way of usage by the industrial sector. The state of Maranhão has a gigant mineral wealth as esmectite, bentonite, kaolin, clays, feldspates, marine salt, iron and others, but produce only products with small agregated value compared to the porcelanato, one of the most expensives ceramic cover tiles, the reason for that is the low water absorption (lower than 0,5%), beside present amazing tecnicals features, like mechanical resistence. The main objective of the work is to do the characterization of four clays, with the finallity of find an application by the results and develop formulations to produce porcelanato using these raw materials from Timon-MA. For this were made the raw materials characterization using X ray fluorecence; X ray diffraction; Differencial thermal analysis; Dilatometric analysis and Tecnological properties, planing three formulations that were sinterized at six different temperatures: 1150, 1170, 1190, 1210, 1230 and 1250ºC for 7 minutes. After the sinteratization, the samples were submitted to tension resistance analysis. Were attained two formulations with the requested properties to produce porcelanato