Estudo da viabilidade técnica do uso das argilas da região do agreste potiguar para produção de peças cerâmicas: caracterização e formulação

In recent decades, ceramic products have become indispensable to the technological development of humanity, occupying important positions in scientific production and consequently in industrial production. One area of the economy that continues to absorb large amounts of the products of this sector is Construction. Among the branches of the ceramic industry, there are the red ceramic industry which is traditionally the basis of that economic sector. Among the reasons for which the red ceramic industry became popular in the country, and specifically in Rio Grande do Norte, is the abundance of this raw material, easily found throughout the national territory. However, it appears that the red ceramic industry has deficiencies in technology and skilled labor, resulting in the production of ceramic goods with low added value. Among the factors that determine the quality of the ceramic products red has the proper formulation of the ceramic mass, the conformation and the firing temperature. Thus, the overall goal of this work is to study the mineralogical and technological properties, two clays from the region of the Wasteland Potiguar industrial ceramist. Therefore, the raw materials were characterized by analysis of Xray diffraction (XRD) analysis, X-ray fluorescence (XRF), particle size analysis (FA), scanning electron microscopy (SEM), optical microscopy (OM ), plasticity index (PI), thermal gravimetric analysis (TGA) and differential thermal analysis (DTA). The technological properties of the material were analyzed by water absorption tests (AA%) porosity (% PA), the linear shrinkage (RT%), apparent density (MEA), loss on ignition (PF%) and flexural strength three points (TRF)

Influência da formação de pozolanas com adição de metacaulim em concreto de alta resistência

The need to build durable structures and resistant to harsh environments enabled the development of high strength concrete, these activities generate a high cement consumption, which implies factor in CO2 emissions. Often the desired strength is not achieved using only the cement composition. This study aims to evaluate the influence of pozzolans with the addition of metakaolin on the physical mechanics of high strength concrete comparing them with the standard formulation. Assays were performed to characterize the aggregates according to NBR 7211, evaluation of cement and coarse aggregate through the trials of petrography (NBR 15577-3/08) and alkali-aggregate reaction (NBR 15577-05/08). Specimens were fabricated according to NBR 5738-1/04 with additions of 0%, 4%, 6%, 8% and 10% of metakaolin for cement mortars CP V in the formulations. For evaluation of the concrete hardened in fresh state and scattering assays were performed and compressive strength in accordance with the NBR 7223/1992 and NBR 5739-8/94 respectively. The results of the characterization of aggregates showed good characteristics regarding size analysis and petrography, as well as potentially innocuous as the alkali-aggregate reaction. As to the test of resistance to compression, all the formulations with the addition of metakaolin showed higher value at 28 days of disruption compared with the standard formulation. These results present an alternative to reduce CO2 emissions, and improvements in the quality and durability of concrete, because the fine particle size of metakaolin provides an optimal compression of the mass directly influencing the strength and rheology of the dough

Síntese e caracterização do carbeto de molibdênio nanoestruturado para fins catalíticos na reação de oxidação parcial do metano

The nanostructures materials are characterized to have particle size smaller than 100 nm and could reach 1 nm. Due to the extremely reduced dimensions of the grains, the properties of these materials are significantly modified relatively when compared with the conventional materials. In the present work was accomplished a study and characterization of the molybdenum carbide, seeking obtain it with particles size in the nanometers order and evaluate its potential as catalyst in the reaction of partial methane oxidation. The method used for obtaining the molybdenum carbide was starting from the precursor ammonium heptamolybdate of that was developed in split into two oven, in reactor of fixed bed, with at a heating rate of 5ºC/min, in a flow of methane and hydrogen whose flow was of 15L/h with 5% of methane for all of the samples. The studied temperatures were 350, 500, 600, 650, 660, 675 and 700ºC and were conducted for 0, 60, 120 and 180 minutes, and the percent amount and the crystallite size of the intermediate phases were determined by the Rietveld refinement method. The carbide obtained at 660ºC for 3 hours of reaction showed the best results, 24 nm. Certain the best synthesis condition, a passivating study was accomplished, in these conditions, to verify the stability of the carbide when exposed to the air. The molybdenum carbide was characterized by SEM, TEM, elemental analysis, ICP-AES, TG in atmosphere of hydrogen and TPR. Through the elemental analysis and ICP-AES the presence carbon load was verified. TG in atmosphere of hydrogen proved that is necessary the passivating of the molybdenum carbide, because occur oxidation in room temperature. The catalytic test was accomplished in the plant of Fischer-Tropsch of CTGAS, that is composed of a reactor of fixed bed. Already the catalytic test showed that the carbide presents activity for partial oxidation, but the operational conditions should be adjusted to improve the conversion