Efeito da coesão semântica sobre a discriminação de itens emocionais em testes de memória de reconhecimento de palavras

Highly emotional itens are best remembered in emotional memory tasks than neutral items. An example of emotional item that benefits declarative memory processes are the taboo words. These words undergo from a conventional prohibition, imposed by tradition or custom. Literature suggests that the strongest recollection these words is due to emotional arousal, as well as, the fact that they form a cohesive semantic group, which is a positive additive effect. However, studies with semantic lists show that cohesion can have a negative effect of interference, impairing memory. We analyzed, in two experiments, the effect of arousal and semantic cohesion of taboo words on recognition tests, comparing with into two other word categories: semantically related and without emotional arousal (semantic category) and neutral, with low semantic relation (objects). Our results indicate that cohesion has interfered whith the performance of the test by increasing the number of false alarms. This effect was strongly observed in the semantic category of words in both experiments, but also in the neutral and taboo words, when both were explicitly considered as semantic categories through the instruction of the test in Experiment 2. Despite the impairment induced by semantic cohesion in both experiments, the taboo words were more discriminated than others, and this result agrees with the indication of the emotional arousal as the main factor for the best recollection of emotional items in memory tests

Uma plataforma de integração de middleware para computação ubíqua

One of the current challenges of Ubiquitous Computing is the development of complex applications, those are more than simple alarms triggered by sensors or simple systems to configure the environment according to user preferences. Those applications are hard to develop since they are composed by services provided by different middleware and it is needed to know the peculiarities of each of them, mainly the communication and context models. This thesis presents OpenCOPI, a platform which integrates various services providers, including context provision middleware. It provides an unified ontology-based context model, as well as an environment that enable easy development of ubiquitous applications via the definition of semantic workflows that contains the abstract description of the application. Those semantic workflows are converted into concrete workflows, called execution plans. An execution plan consists of a workflow instance containing activities that are automated by a set of Web services. OpenCOPI supports the automatic Web service selection and composition, enabling the use of services provided by distinct middleware in an independent and transparent way. Moreover, this platform also supports execution adaptation in case of service failures, user mobility and degradation of services quality. The validation of OpenCOPI is performed through the development of case studies, specifically applications of the oil industry. In addition, this work evaluates the overhead introduced by OpenCOPI and compares it with the provided benefits, and the efficiency of OpenCOPI s selection and adaptation mechanism

O efeito da autocorrelação no desempenho do gráfico T2 de hotelling: caso bivariado

The chart of control of Hotelling T2 has been the main statistical device used in monitoring multivariate processes. Currently the technological development of control systems and automation enabled a high rate of collection of information of the production systems in very short time intervals, causing a dependency between the results of observations. This phenomenon known as auto correlation causes in the statistical control of the multivariate processes a high rate of false alarms, prejudicing in the chart performance. This entails the violation of the assumption of independence and normality of the distribution. In this thesis we considered not only the correlation between two variables, but also the dependence between observations of the same variable, that is, auto correlation. It was studied by simulation, the bi variate case and the effect of auto correlation on the performance of the T2 chart of Hotelling.

As relações entre tectonismo e seqüências deposiconais no rifte potiguar - porção SW do Graben de Umbuzeiro, bacia potiguar emersa

Through an integrated approach, using litho, chrono and biostratigraphic data, the relative importance of climate variations and tectonics were recognized in rift sediments of the onshore Potiguar Basin, Northeast Brazil. Concepts of sequence stratigraphy were applied as a template to integrate sedimentological and geochemical data (oxygen isotopes), as well as quantitative palynologic methods to address and recognize the main depositional patterns produced in a rift basin. The main objective was to address the relative importance of climate changes and tectonics to the resultant stratigraphic architecture. The results of computer simulations of sedimentary basin fills of rift basins were quite useful to test working hypothesis and mimic the process of filling a half graben during a rift event. The studied section includes a neovalanginian-eobarremian (Lower Cretaceous) rift interval from the Pendência Formation, located in the southwestern portion of Umbuzeiro Graben, in the offshore Potiguar Basin. The depositional setting is interpreted as progradational deltaic system entering a lake from its flexural margin. Sismoestratigraphyc and well logs analyses allowed to interpret two regressive intervals (Green and Yellow Sequences), separated by a broad transgressive interval (Orange Sequence), known as the Livramento Shale. The depositional history encompass three stages: two tectonically active phases, during the deposition of the Green and Yellow Sequences, and a tectonically quiescent phase, during the deposition of the Orange Sequence. Paleoclimatic interpretation, based on quantitative palynology and geochemical data (��18O), suggests a tendency to arid conditions during the tectonically active phases and wet conditions during the tectonically quiescent phase. Stratigraphic modeling and backstripping techniques, supported by paleoclimatic/paleoecologic interpretations provide a powerful methodology to evaluate the tectonic and climatic controls on tectonic lakes

Modelagem semântica de processos industriais com aplicações

The main hypothesis of this thesis is that the deve lopment of industrial automation applications efficiently, you need a good structuri ng of data to be handled. Then, with the aim of structuring knowledge involved in the contex t of industrial processes, this thesis proposes an ontology called OntoAuto that conceptua lly models the elements involved in the description of industrial processes. To validat e the proposed ontology, several applica- tions are presented. In the first, two typical indu strial processes are modeled conceptually: treatment unit DEA (Diethanolamine) and kiln. In th e second application, the ontology is used to perform a semantic filtering alarms, which together with the analysis of correla- tions, provides temporal relationships between alar ms from an industrial process. In the third application, the ontology was used for modeli ng and analysis of construction cost and operation processes. In the fourth application, the ontology is adopted to analyze the reliability and availability of an industrial plant . Both for the application as it involves costs for the area of reliability, it was necessary to create new ontologies, and OntoE- con OntoConf, respectivamentem, importing the knowl edge represented in OntoAuto but adding specific information. The main conclusions of the thesis has been that on tology approaches are well suited for structuring the knowledge of industrial process es and based on them, you can develop various advanced applications in industrial automat ion.

Percepção de cuidadores de crianças acerca da prevenção de acidentes domésticos infantis: análise à luz do modelo de crenças em saúde

This study aimed to analyze the perception of home caregivers of children from zero to five years-old on child domestic accidents and their influence in preventing these events. Exploratory and descriptive study with a qualitative approach, conducted with 20 caregivers attended at the Family Health Unit of Cidade Nova in Natal/Rio Grande do Norte, Brazil. The participants should have age less than 18 years-old, being a caregiver of at least a five year-old child and living in the area ascribed of Family Health Unit in the neighborhood Cidade Nova. Data collection occurred between March and April 2013 and a semistructured interview script was used. This stage was preceded by the acquiescence of the director of health institution where the research was developed, the Health Department of the Municipality of Natal as well as the Ethics Committee in Research of Universidade Federal do Rio Grande do Norte under Opinion nº 219 872 and CAAE nº 12236013.7.0000.5537. It is noted that respondents were asked to formal authorization by the Term of Consent. The data were treated according to the technique of the Collective Subject Discourse and analyzed based on three dimensions of the Health Belief Model, relating to perceptions of susceptibility to infant domestic accidents, self-efficacy to prevent infant and indicia domestic accidents for action of preventing domestic accidents in childhood. The results revealed that all the respondents were women, who, in their majority, they are mothers of the children they care, and predominantly they are aged between 18 and 30 years-old, full high school education and unemployed. Concerning the perception of susceptibility, it was unveiled understanding of deponents on various types of accidents, which are considered preventable. For this purpose, it was highlighted that the constant surveillance of the children is essential, keeping in view their high degree of curiosity and immaturity. On the perceived selfefficacy, the participants reported adopting preventive measures; however, they reported experiencing falls, burns, electric shocks and dog bites. In regard to the meaning attributed to experienced accidents they highlighted their feelings of guilt and despair, particularly about the cases understood as serious. Regarding the last dimension analyzed, related to indications for action, family, friends and television were the main source of information about household accidents and their prevention methods; however, health professionals were rarely cited as issuers of such knowledge. It is concluded that there is a widespread perception of women about prevention of domestic accidents and the weakness in the view of health professionals, including nurses, as disseminators of this information. This suggests the need to strengthen the dialogue on the issue and encouraging the participation of caregivers actively in the prevention of child domestic accidents

Estudo de duas pseudoligas de Nb-Cu obtidas pela rota da metalurgia do pó

The Nb-Cu pseudoalloys present themselves as potential substitutes for the alloys from a well known system and already commercially applied, as the W-Cu alloys, used in applications such as heat sinks, electrical contacts and coils for the generation of high magnetic fields. Because it is an immiscible system, where there is mutual insolubility and low wettability of the liquid Cu on the Nb surface, the processing route used in this work was the Powder Metallurgy. Two Nb alloys were used, with additions of 10% and 20% in weight of Cu, and times of 20, 30 and 40 hours for the high energy milling of the starting powders. The milling evolution of the powders is presented through the characterization techniques, such as the LASER diffraction for particle size, XRD, SEM, EDS, DSC, dilatometry, TEM and chemical analysis. After the milling, portions of the loads were submitted to the annealing heat treatment. The process used for the samples consolidation was the hot pressing, which has been applied both on some milled powders samples, as on the annealed powders. Subsequent heat treatments were performed in the samples at temperatures of 1000ºC (solid phase) and 1100ºC (in the Cu liquid phase). All sets of consolidated samples, and also the two sets of the heat treated, were analyzed by XRD, SEM, EDS, density and Vickers microhardness. Moreover, other Nb powder samples with 10% and 20% in weight of Cu obtained by simple mechanical mixing, were consolidated, thermally treated and characterized with the same techniques applied to the others, and the results were compared among themselves. Despite the difficulty of consolidation and densification of the two pseudoalloys of the Nb-Cu system of this study, on the route that passes through the HEM, samples were obtained with densities around 90% of the theoretical density. And, on the processing route of which were only mixed, the values reached up to 97%. Therefore, in this work are also emphasized the processes that made possible these results.

Uso de resíduos de queima de casca de café e argila da região sul da Bahia na obtenção de isolador elétrico cerâmico

The electrical ceramic insulators industry, uses noble raw materials such as siliceous and aluminous clays of white burning, in order to provide plasticity of the mass and contribute to electrical and mechanical properties required of the product, and feldspar with the flux function In literature references the composition of the masses indicates that the clay participates in percentage between 20 and 32, and feldspar 8 to 35, these materials have significant cost. In this research was performed the total replacement of commercial clay, for white burning clay from Santa Luzia region in southern Bahia and partial replacement of feldspar by ash residue of husk conilon coffee burning, from extreme south of Bahia. The objective of replacement these raw materials is to aver its technical feasibility and call attention for the embryo pole of ceramic industry for the existing in the south and extreme south of Bahia, which has significant reserves of noble raw materials such as clay white burning, kaolin, quartz and feldspar, and generates significant volume of gray husk conilon coffee as alternate flux. Clay Santa Luzia is prima noble material whose current commercial application is the production of white roofing. The residue of coffee husk ash is discarded near of production sites and is harmful to the environment. Phase diagrams and statistic design of experiments, were used for optimization and cost savings in research. The results confirmed the expectations of obtaining electrical ceramic insulators, with white burning clay of Santa Luzia and partial replacement up to 35.4% of feldspar, by treaty residue of conilon ash coffee husk burning. The statistic design that showed best results was for formulation with percentages of: clay 26.4 to 30.4%; kaolin 14.85 to 17.1%; feldspar 12.92 to 16.96%; R2 residue 7.08 to 9.2% and Quartz 32.5 to 38.75%, relative to the total mass of the mixture. The best results indicated; 0.2 to 1.4% apparent porosity , water absorption 0.1 to 0.7%, flexural strength 35 to 45MPa , dielectric strength 35-41 kV/cm , the transverse resistivity 8x109 2.5x1010 Ω.cm and for the dielectric constant ε/ε0 7 to 10.4, specification parameters for manufacturing ceramic electrical insulators of low and medium voltage.

Estimação de potência em tempo real utilizando a transformada wavelet

The goal of the power monitoring in electrical power systems is to promote the reliablility as well as the quality of electrical power.Therefore, this dissertation proposes a new theory of power based on wavelet transform for real-time estimation of RMS voltages and currents, and some power amounts, such as active power, reactive power, apparent power, and power factor. The appropriate estimation the of RMS and power values is important for many applications, such as: design and analysis of power systems, compensation devices for improving power quality, and instruments for energy measuring. Simulation and experimental results obtained through the proposed MaximalOverlap Discrete Wavelet Transform-based method were compared with the IEEE Standard 1459-2010 and the commercial oscilloscope, respectively, presenting equivalent results. The proposed method presented good performance for compact mother wavelet, which is in accordance with real-time applications.

Estudo sobre a relação entre a atividade geomagnética e cintilações de sinais de GPS em Natal-RN (Brasil)

To identify the relationship between GPS scintillation in Natal-RN (Brazil) and geomagnetic disturbances of any intensities and variations, this work made analysis of the ionospheric behavior and magnetic indexes (Dst , AE and Bz of the interplanetary magnetic field) concerning to different periods of the solar cycle between 2000 and 2014. Part of the data of this research originated at the UFRN observatory, from a GEC Plessey board connected to an ANP -C 114 antenna, modified by Cornell University’s Space group Plasma Physics in order to operate the ScintMon, a GPS monitoring program. This study, therefore, found several cases of inhibited scintillations after the main phase of magnetic storms, a fact that, along with others, corroborated with categorization of Aarons (1991) and models of disturbed dynamo (according to Bonelli, 2008) and over-shielding penetration, defended by Kelley et al. (1979) and Abdu (2011) [4]. In addition to these findings, different morphologies were noted in such disruptions in the GPS signal in accordance with previous magnetic activities. It also found a moderate relationship (R2 = 0.52) between the Dst rate (concerning to specific time) and the average of S4 through a polynomial function. This finding therefore, corroborating Ilma et al. (2012) [17], is an important evidence that the scintillation GPS are not directly controlled by magnetic induction of storms. Completing this work, this relation did show itself as a way of partial predicting of scintillations.

Estudo da variabilidade da deriva vertical do plasma ionosférico sobre a região de Natal/RN, Fortaleza/CE e Cachoeira Paulista/SP para alguns casos de tempestades magnéticas de abril a setembro de 2000

In this work are presented the results of research on the variation of vertical plasma drift from the F layer that commonly occurs during the period close to the going down of the sun (between 21UT - 22UT), and consisting of an increase in the F layer in time of day and a drop at night on the cities of Natal / RN (The 33.7º, 5.6º S), Fortaleza / CE (38.45º O, 3.9º S) and Cachoeira Paulista / SP (45.0ºO, 22.7º S ). Thus, data was used (ionograms) virtual height t ( h' ) as a function of the frequency F for the layer of the ionosphere. These data were collected through ionossonda type CADI (Canadian Advanced Digital Ionosonde) to the cities of Natal and Fortaleza, and the Digisonde DPS to the town of Cachoeira Paulista. They considered only the data available 2000 maximum solar year. With the virtual height ( h' ) data reduced in the frequencies of 6MHz and 5MHz, the next step was to calculate. The results showed that the variability of the vertical drift rate F ionospheric layer periods of magnetic storms is related both to the penetration of the electric fields as the disturbance dynamo electric fields.

Estudo da obtenção de cerâmica composta de alumina e beta alumina sódica utilizando-se resíduo cerâmico de velas de ignição e pó químico de extintores de incêndio

Ceramic materials the alumina base are large industrial applications. They are required for these products, specific characteristics obtained by following strict criteria during the manufacturing process. However, after life, not always these products are reused by a suitable waste management process. In ceramist context, advance research aimed at the reuse of waste aimed at obtaining ceramics and composite materials, with marked reduction of conventional raw materials. Aiming to generate scientific, technological and environmental contribution, this work studied to obtain a composite of alumina ceramic (Al2O3) and sodium beta alumina (NaAl11O17 ), and as starting materials the residue of the ceramic insulator of spark plugs, as a source alumina (Al2O3) powder and unusable sodium bicarbonate (NaHCO3) of fire extinguishers, as a source of sodium oxide (Na2O). The final ceramic product was obtained from a conventional mixture of sodium aluminum oxide in appropriate molar proportions. Sample spark plugs were obtained, discarded by lifetime, specific to a manufacturer, which, after passing through mechanical stress (grinding, magnetic purification, washing, drying and grinding the high energy), which resulted in residue powder with ceramic content of 84.34 % alumina (Al2O3), found by FRX chemical analysis, the phases present and identified by DRX. The dry chemical fire extinguisher, baking soda-based (NaHCO3) with expired, was obtained through direct collection of the waste generated during maintenance. Subjected to heat treatment at 120 °C , the NaHCO3 powder was decomposed in sodium oxide ( Na2O), which, subjected to chemical analysis (FRX) and mineralogical (DRX) revealed a content of 86.62 % sodium oxide (Na2O) . In the following steps the experimental procedure, chemical formulations were made on a molar basis of the starting material (1:9, 1:10 and 1:11 de Na2O/ Al2O3) inclusion of additives, milling parameters, sieve analysis, dilatometry, conformation of specimens, sintering in firing steps at 800 °C , 1000 °C and 1.200 °C with varying stays 30 , 60 and 120 minutes in each of the levels. The characterization of the final product was made by the following physical tests: water absorption, porosity, linear shrinkage, mineralogical analysis by DRX and microstructural analysis by MEV. A higher formation of sodium beta alumina (NaAl11O17), in sintered specimens in levels of 1.200 °C and 120 minutes, despite the prevailing coexistence of alpha phase alumina (Al2O3). From the results obtained opens up prospects for the reuse of waste studied in this work, the potter context and in other technological areas.

Estudo da obtenção de cerâmica composta de alumina e beta alumina sódica utilizando-se resíduo cerâmico de velas de ignição e pó químico de extintores de incêndio

Ceramic materials the alumina base are large industrial applications. They are required for these products, specific characteristics obtained by following strict criteria during the manufacturing process. However, after life, not always these products are reused by a suitable waste management process. In ceramist context, advance research aimed at the reuse of waste aimed at obtaining ceramics and composite materials, with marked reduction of conventional raw materials. Aiming to generate scientific, technological and environmental contribution, this work studied to obtain a composite of alumina ceramic (Al2O3) and sodium beta alumina (NaAl11O17 ), and as starting materials the residue of the ceramic insulator of spark plugs, as a source alumina (Al2O3) powder and unusable sodium bicarbonate (NaHCO3) of fire extinguishers, as a source of sodium oxide (Na2O). The final ceramic product was obtained from a conventional mixture of sodium aluminum oxide in appropriate molar proportions. Sample spark plugs were obtained, discarded by lifetime, specific to a manufacturer, which, after passing through mechanical stress (grinding, magnetic purification, washing, drying and grinding the high energy), which resulted in residue powder with ceramic content of 84.34 % alumina (Al2O3), found by FRX chemical analysis, the phases present and identified by DRX. The dry chemical fire extinguisher, baking soda-based (NaHCO3) with expired, was obtained through direct collection of the waste generated during maintenance. Subjected to heat treatment at 120 °C , the NaHCO3 powder was decomposed in sodium oxide ( Na2O), which, subjected to chemical analysis (FRX) and mineralogical (DRX) revealed a content of 86.62 % sodium oxide (Na2O) . In the following steps the experimental procedure, chemical formulations were made on a molar basis of the starting material (1:9, 1:10 and 1:11 de Na2O/ Al2O3) inclusion of additives, milling parameters, sieve analysis, dilatometry, conformation of specimens, sintering in firing steps at 800 °C , 1000 °C and 1.200 °C with varying stays 30 , 60 and 120 minutes in each of the levels. The characterization of the final product was made by the following physical tests: water absorption, porosity, linear shrinkage, mineralogical analysis by DRX and microstructural analysis by MEV. A higher formation of sodium beta alumina (NaAl11O17), in sintered specimens in levels of 1.200 °C and 120 minutes, despite the prevailing coexistence of alpha phase alumina (Al2O3). From the results obtained opens up prospects for the reuse of waste studied in this work, the potter context and in other technological areas.

Um espaço pioneiro de modernidade educacional: Grupo Escolar Augusto Severo -Natal/RN -1908-13

Cette recherche a pour but d analyser l Ecole Augusto Severo, située dans la ville de Natal dont la construction date de 1907,étant le premier établissement d enseignement primaire à l état du Rio Grande do Norte, pendant le processus de restructuration de l enseignement républicain. On cherche à comprendre la représentation de ce milieu scolaire, comme équipement urbain, dans le processus de modernisation de la ville et comme modèle éducationnel pour l état entre 1908 et 1913. En se servant des études historiographes sur le processus de modernisation de quelques villes brésiliennes et des innovations de l enseignement public primaire au pays, à la fin du dix-neuvième siècle et pendant la première décennie du vingtième siècle, comme source pour mieux saisir le contexte général et spécifique. On reconstitue les aspects économiques, sociaux et politiques déterminants des interventions publiques réalisées dans cette ville par les gouvernements républicains ayant comme obectif la construction d une ville embellie,hygiénique et civilisée. Située au quartier Ribeira, principal scénario de la modernité de Natal, l Ecole Augusto Severo est mise em relief comme symbole de civilité du paysage urbain de l époque pour le citoyen du Rio Grande do Norte. Elle disposait de services d énergie et d un tram électrique. Il y avait devant, un grand lac arborisé et une station ferroviaire. A côté, il y avait le théâtre Carlos Gomes (actuellement Alberto Maranhão). Par suíte de son imposante architecture, raffiné style éclectique,on reflète l idéal républicain des elites locales, avec une conception d espace symbolique et éducative de surveillance et contrôle, caractéristiques de l école graduée républicaine

Estudo da síntese e sinterização de pós compósitos do sistema Ta-Cu

Ta-Cu bulk composites combine high mechanical resistance of the Ta with high electrical and thermal conductivity of the Cu. These are important characteristics to electrical contacts, microwave absorber and heat skinks. However, the low wettability of Ta under Cu liquid and insolubility mutual these elements come hard sintering this composite. High-energy milling (HEM) produces composite powders with high homogeneity and refines the grain size. This work focus to study Ta-20wt%Cu composite powders prepared by mechanical mixture and HEM with two different conditions of milling in a planetary ball mill and then their sintering using hydrogen plasma furnace and a resistive vacuum furnace. After milling, the powders were pressed in a steel dye at a pressure of 200 MPa. The cylindrical samples pressed were sintered by resistive vacuum furnace at 10-4torr with a sintering temperature at 1100ºC / 60 minutes and with heat rate at 10ºC/min and were sintered by plasma furnace with sintering temperatures at 550, 660 and 800ºC without isotherm under hydrogen atmosphere with heat rate at 80ºC/min. The characterizations of the powders produced were analyzed by scanning electron microscopy (SEM), x-ray diffraction (XRD) and laser granulometry. After the sintering the samples were analyzed by SEM, XRD and density and mass loss tests. The results had shown that to high intense milling condition produced composite particles with shorter milling time and amorphization of both phases after 50 hours of milling. The composite particles can produce denser structure than mixed powders, if heated above the Cu melting point. After the Cu to arrive in the melting point, liquid copper leaves the composite particles and fills the pores