Desempenho mecânico de compósitos híbridos de fibras naturais e poliéster não saturado

With the objective to promote sustainable development, the fibres found in nature in abundance, which are biodegradable, of low cost in comparison to synthetic fibres are being used in the manufacture of composites. The mechanical behavior of the curauá and pineapple leaf fibre (PALF) composites in different proportions, 25% x 75% (P1), 50% x 50% (P2) e 75% x 25% (P3) were respectively studied, being initially treated with a 2% aqueous solution of sodium hydroxide. Mechanical analyses indicated that with respect to studies of traction, for the combination of P1 and P3, better results of 22.17 MPa and 16.98 MPa, were obtained respectively, which are higher than that of the combination P2. The results of the same pattern were obtained for analysis of bending resistance where P1 is 1.21% and P3 represents 0.96%. In the case of resistance to bending, best results were obtained for the combination P1 at 49.07 MPa. However, when Young's modulus values were calculated, the values were different to the pattern of the results of other tests, where the combination P2 with the value of 4.06 GPa is greater than the other combinations. This shows that the PALF had a greater influence in relation to curauá fibre. The analysis of the results generally shows that in combinations of two vegetable fibers of cellulosic origin, the fiber which shows higher percentage (75%) is the best option than to the composition of 50%/50%. In the meantime, according to the results obtained in this study, in the case where the application should withstand bending loads, the better composition would be 50%/50%

Estudo da flamabilidade e resistência à chama de compósito de poliéster insaturado e fibra da folha do abacaxizeiro (PALF)

In the present research work, composites were prepared using pine apple leaf fibres (PALF) as reinforcement with unsaturated polyester resin as matrix, incorporating with fire retardant at different compositions. The PALF was obtained from the decortication of pine apple leaves obtained from Ramada 4 from Ielmo Marinho in the State of Rio Grande do Norte. The unsaturated polyester resin and the catalyzer were bought from the local establishment. The fire retardant, aluminium tri-hydroxide - Al(OH)3 was donated by Alcoa Alumínio S.A and was used in the proportions of 20%, 40% and 60% w/w. Initially the fibres were treated with 2% NaOH for 1 hour, to remove any impurities present on the fibre surface, such as wax, fat, pectin and pectate, in order to have a better adsorption of the fibres with the matrix as well as the flame retardant. The fibre mat was prepared in a mat preparator by immersion, developed in the Textile Engineering Laboratory, at the UFRN. The composites (300x300x3 mm) were prepared by compression molding and the samples (150x25x3 mm) for analysis of the properties were cut randomly using a laser cutter. Some of the cut samples were used to measure the smoke emission and fire resistance using UL94 standard. Mechanical tension-extension and flexural properties were carried in CTGás RN and the Laboratório de Metais e Ensaios Mecânicos Engenharia de Materiais UFRN , as well as SEM studies were carried out at Núcleo de Estudos em Petróleo e Gás Natural - UFRN . From the observed results, it was noted that, there was no marked influence of the fire retardant on the mechanical properties. Also in the water absorption test, the quantity of water absorbed was less in the sample with higher concentration of fire retardant. It was also observed that the increase in the proportion of the fire retardant increased the time of burning, may be due to the compactness of the composite due to the presence of fire retardant as a filling material even though it was meant to reduce the rate of inflammability of the composite

Compósito reforçado com sisal para aplicação na moda

The objective of this research is the fabrication of a composite reinforced with dyed sisal fiber and polyester matrix for application in the fields such as, fashion, clothing, interior textiles; fashion accessories are some of the examples. For the fabrication of the composite, the sisal fibers were subjected to processes such as: chemical treatment with sodium hydroxide (NaOH) in the removal of impurities; bleaching for removing the yellowish color of the natural fiber and dyeing with direct dyes to confer the colors blue, green and orange. The search for new technologies ecologically correct has become a major concern in recent decades. Studies show that composite polymer reinforced by natural fibers is suitable for a large number of applications, and its use is advantageous in terms of economic and ecological. The dyed fibers were cut to a length of 30 mm, is used in the confection of webs. For this purpose, a web preparer by immersion, developed in the Laboratory of Chemical Textile of UFRN. The composite sheets measuring 300 x 300 x3 mm were molded by compression, with unsaturated orthophthalic polyester as matrix, and the samples in sizes 150 x 25 x 3 mm were cut with the aid of a laser machine, to be subjected to traction and flexion. The mechanical properties of traction and flexion in three points were performed in the Laboratory of metal and mechanical tests of Materials Engineering of UFRN. The resulting samples from the tests were evaluated in scanning electron microscope (SEM) at CTGas RN. On the basis of the analysis of the results from the mechanical tests, it was observed that the composite had good mechanical behavior, both in traction as in flexion. Furthermore, it was observed that in the water absorption test, the samples had a different percentage among themselves, this occurred due to the variation of density found in the fibre webs. The images of the SEM showed the failures from the manufacturing process and the adhesion of fibre/matrix. When the samples were prepared with the dyed fibers to be applied in fashion, the results were positive, and it can be concluded that the main objective of this work was achieved

Estudo comparativo das propriedades mecânicas em compósitos da fibra modal e poliester

In the present work, three composites with distinct reinforcements (polyester, modal e polyester + modal), all if a unsaturated orthophthalic polyester resin as matrix were used, in order to conduct a comparative study by mechanical tests and water absorption. The fibre mats were prepared in a mat preparatory by immersion developed in the Textile Engineering Laboratory. The composites were manufactured using a closed mould process by compression using an unsaturated orthophthalic polyester resin as matrix and 1% MEK (methyl ethyl ketone peroxide) as an initiator. In each composite twelve samples with the dimensions of 150x25x3 mm were cut randomly for the mechanical analysis (tension x extension, three points bending and water absorption and Scanning Electron Micsroscopy). The mechanical tests were carried out in the Laboratório de Metais e Ensaios Mecânicos UFRN . All the analyses were carried out according to the ASTM norms. The resultant samples from the mechanical analysis were subjected for the Scanning Electron Microscopy analysis. Based on the results obtained, it was observed that the reinforced composite with two fibres (modal + polyester) presented better results in comparison to the other two composites both in the tension/extension as well on the three point bending tests. In the water absorption test, it was possible to observe an equilibrium in the water absorption by the modal and polyester composite, due to the union of the two fibres. In the SEM images, the regions of rupture in the composites as well as the adsorption between the fiber and the matrix could be observed

Influência da umidade nas propriedades mecânicas dos compósitos poliméricos híbridos (sisal/ vidro)

This study aims to evaluate the mechanical properties of polymer matrix composites reinforced with sisal fabric bidirectional tissue (Agave sisalana,) and E-glass fibers, containing the following configuration: a polymer matrix hybrid composite (Polyester Resin orthophalic) reinforced with three (3) layers of glass fibers and alternating-2 (two) layers of bidirectional sisal fabric, and finally a composite of polymer matrix reinforced with five (5) layers of glass fiber mat-type E. For this purpose as first step, the preparation of by sisal, since they are not on the market. The composites were made by manual lamination (Hand lay-up) and evaluated for tensile properties and three point bending both in the dry, and wet conditions aswele as immersed in oil. Macroscopic and microscopic characteristics of the materialsweve awalysed, after the completion of the mechanical tests. After the studies, it was proven that the sisal fiber decreases the tensile stiffness of the material above 50% for both situations studied the tensile strength of the material decreases by approximately 40% for the cases mentioned, and when compared to the specific strength stiffness values drop to 14.6% and 29.02% respectively for the dry state only. Constants for bending the values were are to approximately 50% to 25% for strength and stiffness of the material for the cases dry, wet and immersed in oil. Under the influence of tension fluids do not interfere in the stiffness of the material for the bending tests, the same does not occur with the resistance, and these values are modified only in the cases stiffness and flexural strength

Tubulações de PRFV com adição de areia quartzosa visando sua aplicação na indústria do petróleo

Fillers are often added in composites to enhance performance and/or to reduce cost. Fiberglass pipes must meet performance requirements and industrial sand is frequently added for the pipe to be cost competitive. The sand is added to increase pipe wall thickness, thus increase pipe stiffness. The main goal of the present work is to conduct an experimental investigation between pipes fabricated with and without de addition of sand, to be used in the petroleum industry. Pipes were built using E-glass fibers, polyester resin and siliceous sand. The fabrication process used hand lay up and filament winding and was divided in two different parts: the liner and the structural wall. All tested pipes had the same liner, but different structural wall composition, which is the layer where siliceous sand may be added or not. The comparative investigation was developed considering the results of longitudinal tensile tests, hoop tensile tests, hydrostatic pressure leak tests and parallel-plate loading stiffness tests. SEM was used to analyze if the sand caused any damage to the glass fibers, during the fabrication process, because of the fiber-sand contact. The procedure was also used to verify the composite conditions after the hydrostatic pressure leak test. The results proved that the addition of siliceous sand reduced the leak pressure in about 17 %. In the other hand, this loss in pressure was compensated by a stiffness increment of more than 380 %. MEV analyses show that it is possible to find damage on the fiber-sand contact, but on a very small amount. On most cases, the contact occurs without damage evidences. In summary, the addition of sand filler represented a 27.8 % of cost reduction, when compared to a pipe designed with glass fiber and resin only. This cost reduction combined to the good mechanical tests results make siliceous sand filler suitable for fiberglass pressure pipes

Remoção de óleo da água de produção por flotação em coluna utilizando tensoativos de origem vegetal

In the petroleum industry, water is always present in the reservoir formation together with petroleum and natural gas and this fact provokes the production of water with petroleum, resulting in a great environmental impact. Several methods can be applied for treatment of oily waters, such as: gravitational vases, granulated media filtration systems, flotation process, centrifugation process and the use of hydrocyclones, which can also be used in a combined way. However, the flotation process has showed a great efficiency as compared with other methods, because these methods do not remove great part of the emulsified oil. In this work was investigated the use of surfactants derived from vegetable oils, OSS and OGS, as collectors, using the flotation process in a glass column with a porous plate filter in its base for the input of the gaseous steam. For this purpose, oil/water emulsions were prepared using mechanical stirring, with concentrations around 300 ppm. The air flow rate was set at 700 cm3/min and the porous plate filter used for the generation of the air bubbles has pore size varying from 16 to 40 Pm. The column operated at constant volume (1500mL). A new methodology has been developed to collect the samples, where, instead of collecting the water phase, it was collected the oil phase removed by the process in the top of the flotation column. It has been observed that it is necessary to find an optimum surfactant concentration to achieve enhanced removal efficiency. Being for OSS 1.275 mmol/L and for OGS 0.840 mmol/L, with removal efficiencies of 93% and 99%, respectively, using synthetic solutions. For the produced water, the removal in these concentrations was 75% for OSS and 65% for OGS. It is possible to remove oil from water in a flotation process using surfactants of high HLB, fact that is against the own definition of HLB (Hydrophile-Lipophile Balance). The interfacial tension is an important factor in the oil removal process using a flotation process, because it has direct interference in the coalescence of the oil drops. The spreading of the oil of the air bubble should be considered in the process, and for the optimum surfactant concentrations it reached a maximum value. The removal kinetics for the flotation process using surfactants in the optimum concentration has been adjusted according to a first order model, for synthetic water as for the produced water.

Otimização do processo de recuperação do cromo de efluentes de curtumes por microemulsões no extrator Morris

The tanning industries are those which transform animal hide or skin into leather. Due to the complexity of the transformation process, greater quantities of chemicals are being used which results in the generation of effluents with residual solids. The chromium in the residual waters generated by tanning tend to be a serious problem to the environment, therefore the recovery of this metal could result in the reduction of manufacturing costs. This metal is usually found in a trivalent form which can be converted into a hexavalent compound under acidic conditions and in the presence of organic matter. The present study was carried out with the objective to recover chromium through an extraction/re-extraction process using micro emulsions. Micro emulsions are transparent and thermodynamically stable system composed of two immiscible liquids, one forming the continuous phase and the other dispersed into micro bubbles, established by an interfacial membrane formed by surface active and co-surface active molecules. The process of recovering the chromium was carried out in two stages. The first, an extraction process, where the chromium was extracted in the micro emulsion phase and the aqueous phase in excess was separated. In the second stage, a concentrated acid was added to the micro emulsion phase rich in chromium in order to obtain a Winsor II system, where the water that formed in the micro emulsion phase separates into a new micro emulsion phase with a higher concentration of chromium, due to the lowering of the hydrophiles as well as the ionisation of the system. During the experimental procedure, a study was initiated with a synthetic solution of chromium sulphate passing onto the effluent. A Morris extractor was used in the extraction process. Tests were carried out according to the plan and the results were analysed by statistical methods in order to optimise the main parameters that influence the process: the total rate of flow (Q), stirring speed (w) and solvent rate (r). The results, after optimization, demonstrated that the best percentuals in relation to the chromium extraction (99 %) were obtained in the following operational conditions: Q= 2,0 l/h, w= 425 rpm and r= 0,375. The re-extraction was carried out at room temperature (28 °C), 40 °C and 50°C using hydrochloric acid (8 and 10 M) and sulphuric acid (8 M) as re-extracting agents. The results obtained demonstrate that the process was efficient enough in relation to the chromium extraction, reaching to re-extraction percentage higher than 95 %.

Estudo de um sistema híbrido de destilação solar para polimento de águas produzidas

The oil industry, experiencing a great economic and environmental impact, has increasingly invested in researches aiming a more satisfactory treatment of its largest effluent, i.e., produced water. These are mostly discarded at sea, without reuse and after a basic treatment. Such effluent contains a range of organic compounds with high toxicity and are difficult to remove, such as polycyclic aromatic hydrocarbons, salts, heavy metals, etc.. The main objective of this work was to study the solar distillation of produced water pre-treated to remove salts and other contaminants trough of a hybrid system with a pre-heater. This developed apparatus was called solar system, which consists of a solar heater and a conventional distillation solar still. The first device consisted of a water tank, a solar flat plate collector and a thermal reservoir. The solar distillator is of simple effect, with 1m2 of flat area and 20° of inclination. This dissertation was divided in five steps: measurements in the solar system, i.e. temperatures and distillate flow rate and weather data; modeling and simulation of the system; study of vapor-liquid equilibrium of the synthetic wastewater by the aqueous solution of p-xylene; physical and chemical analyses of samples of the feed, distillate and residue, as well as climatology pertinent variables of Natal-RN. The solar system was tested separately, with the supply water, aqueous NaCl and synthetic oil produced water. Temperature measurements were taken every minute of the thermal reservoir, water tank and distillator (liquid and vapor phases). Data of solar radiation and rainfall were obtained from INPE (National Institute for Space Research). The solar pre-heater demonstrated to be effective for the liquid systems tested. The reservoir fluid had an average temperature of 58°C, which enabled the feed to be pre-heated in the distillator. The temperature profile in the solar distillator showed a similar behavior to daily solar radiation, with temperatures near 70°C. The distillation had an average yield of 2.4 L /day, i.e., an efficiency of 27.2%. Mathematical modeling aided the identification of the most important variables and parameters in the solar system. The study of the vapor-liquid equilibrium from Total Organic Carbon (TOC) analysis indicated heteroazeotropia and the vapor phase resulted more concentrated in p-xylene. The physical-chemical analysis of pH, conductivity, Total Dissolved Solids (TDS), chlorides, cations (including heavy metals) and anions, the effluent distillate showed satisfactory results, which presents a potential for reuse. The climatological study indicates the region of Natal-RN as favorable to the operation of solar systems, but the use of auxiliary heating during periods of higher rainfall and cloud cover is also recommended

Avaliação da capacidade de adsorção do CO2 em zeólita 12X com gases sintéticos e originados da pirólise do lodo de esgoto

This work depicts a study of the adsorption of carbon dioxide on zeolite 13X. The activities were divided into four stages: study batch adsorption capacity of the adsorbent with synthetic CO2 (4%), fixed bed dynamic evaluation with the commercial mixture of gases (4% CO2, 1.11% CO, 1 2% H2, 0.233% CH4, 0.1% C3, 0.0233% C4 argon as inert closing balance), fixed bed dynamic modeling and evaluation of the breakthrough curve of CO2 originated from the pyrolysis of sewage sludge. The sewage sludge and the adsorbent were characterized by analysis TG / DTA, SEM, XRF and BET. Adsorption studies were carried out under the following operating conditions: temperature 40 °C (for the pyrolysis of the sludge T = 600 °C), pressures of 0.55 to 5.05 bar (batch process), flow rate of the gaseous mixture between 50 - 72 ml/min and the adsorbent masses of 10, 15 and 20 g (fixed bed process). The time for the adsorption batch was 7 h and on the fixed bed was around 180 min. The results of this study showed that in batch adsorption process step with zeolite 13X is efficient and the mass of adsorbed CO2 increases with the increases pressure, decreases with temperature increases and rises due the increase of activation temperature adsorbent. In the batch process were evaluated the breakthrough curves, which were compared with adsorption isotherms represented by the models of Langmuir, Freündlich and Toth. All models well adjusted to the experimental points, but the Langmuir model was chosen in view of its use in the dynamic model does not have implications for adsorption (indeterminacy and larger number of parameters such as occurred with others) in solving the equation. In the fixed bed dynamic study with the synthetic gas mixture, 20 g of mass adsorbent showed the maximum adsorption percentage 46.7% at 40 °C temperature and 50 mL/min of flow rate. The model was satisfactorily fitted to the three breakthrough curves and the parameters were: axial dispersion coefficient (0.0165 dm2/min), effective diffusivity inside the particle (dm2/min 0.0884) and external transfer coefficient mass (0.45 dm/min). The breakthrough curve for CO2 in the process of pyrolysis of the sludge showed a fast saturation with traces of aerosols presents in the gas phase into the fixed bed under the reaction process

Otimização do processo de flotação de emulsão óleo/água através do planejamento fatorial completo

In recent decades, the generation of solid and liquid waste has increased substantially due to increased industrial activity that is directly linked to economic growth. For that is the most efficient process, it is inevitable generation of such wastes. In the oil industry, a major waste generated in oil exploration is produced water, which due to its complex composition and the large amount generated, has become a challenge, given the restrictions imposed by environmental laws regarding their disposal, making if necessary create alternatives for reuse or treatment in order to reduce the content of contaminants and reduce the harmful effects to the environment. This water can be present in free form or emulsified with the oil, when in the form of an emulsion of oil-water type, it is necessary to use chemicals to promote the separation and flotation is the treatment method which has proved to be more efficient, for it can remove much of the emulsified oil when compared to other methods. In this context, the object of this work was to study the individual effects and interactions of some physicochemical parameters of operations, based on previous work to a flotation cell used in the separation of synthetic emulsion oil / water in order to optimize the efficiency of the separation process through of the 24 full factorial design with center point. The response variables to evaluate the separation efficiency was the percentage of color and turbidity removal. The independent variables were: concentration of de-emulsifying, oil content in water, salinity and pH, these being fixed, minimum and maximum limits. The analysis of variance for the equation of the empirical model, was statistically significant and useful for predictive purposes the separation efficiency of the floater with R2 > 90%. The results showed that the oil content in water and the interaction between the oil content in water and salinity, showed the highest values of the estimated effects among all the factors investigated, having great and positive influence on the separation efficiency. By analyzing the response surface was determined maximum removal efficiency above 90% for both measured for turbidity as a measure of color when in a saline medium (30 g/L), the high oil concentrations (306 ppm) using low concentrations of de-emulsifying (1,1 ppm) and at pH close to neutral

Obtenção de novos derivados de ß-naftol e cardanol hidrogenado e avaliação dos seus efeitos antioxidativos em gasolina automotiva

The chemical nature of the hidrocarbons found in gasoline directly affects the formation of oxidation complexes known as gums. Such complexes are slightly soluble in gasoline and their formation is delayed with the use of inhibitors, known as antioxidants. In this study, a synthetic compound (βnaphtol) and a natural subproduct (hydrogenated cardanol, derived from cashewnut shell liquid CNSL) have been used in order to generate novel antioxidant substances. These compounds were submitted to chemical reactions including alkylation, nitration and reduction, with the purpose of forming the following derivatives: 6(Nethyl,Nethylamino)βnaphtol (AO1); 6(Nethyl,Ndiethylamino)βnaphtol (AO2); aminoβnaphtol (AO3); 2(Nethyl,Nethylamino)pentadecylphenol (AOC1), 2(Nethyl,Ndiethylamino)pentadecylphenol (AOC2) and aminopentadecylphenol (AOC3). The derivatives were subjected to accelerated oxidative stability assays (Potential Gum and Induction Period) and to storage assays (Washed Gum and ASTM Color) during six months, with naphtha provided by the petroleum refinery RPBC (Refinaria Presidente Bernardes de Cubatão, in Brazil). The results for the derivatives were compared to those for commercial additives [DBPC (2,6ditbutyl4methylpcresol) and PDA (N,N disecbutylpphenylenediamine)], which were also added to the naphtha produced at RPBC at the moment of sampling. From all tested antioxidants, the novel antioxidant AOC1 (derived from hydrogenated cardanol) yielded a better global performance. During the period of time in which the naphtha was stored, an examination of this material was carried out in parallel, using the mass spectrometry technique. This study allowed to monitor the formation of a triolefinic compound, as well as the observation of subsequent formation and rupture of the olefinic constituents. As an eventual result from these experimental investigations, a reaction route leading to gum formation has been suggested

Recuperação de fósforo por cristalização de estruvita

This study investigated the influence of the molar ratio, the phosphorus initial concentration, the mixture gradient, mixing time, pH and the secondary nucleation on struvite s crystallization in synthetic water in batch reactors. The study was divided into two stages. The first investigated struvite s crystallization at different Mg:N:P molar ratios and at different initial concentrations of magnesium, nitrogen and phosphorus. It was also evaluated the importance of secondary nucleation on the struvite s crystallization. In the second, five parameters were tested to evaluate their influence on the struvite s crystallization, which were: Mg:N:P molar ratio, initial concentration of phosphate, mixing time, mixture gradient and pH. The best conditions for struvite s crystallization were: Mg:N:P = 1,3:1:1 molar ratio; mixture gradient = 60 rpm, pH = 10.0, mixing time = 5 minutes and high initial concentrations of the constituent ions of struvite. Furthermore, the use of struvite crystals as seed influenced positively on the struvite s crystallization

Avaliação da disponibilidade hídrica e da demanda hídrica no trecho do Rio Piranhas-Açu entre os açudes Coremas-mãe D´água e Armando Ribeiro Gonçalves

Piranhas-Açu basin is a Federal watershed with a drainage area of 43.681,5 km2, sited at Brazilian northeast semi arid, with 60% of your area in Paraiba State and 40% in Rio Grande do Norte State. The main river, Piranhas-Açu, has strategic importance for development of these states, because it s an essential source for many socio-economics activities developed along watercourse. The river s reach between Coremas-Mãe D`água Dam and Armando Ribeiro Gonçalves Dam has many irrigation projects, and supply many riverside cities. All this activities practiced in this river s reach consumes high water volumes. Due the importance of this stream and the necessity of an adequate management, this work aims for an impartial and detailed evaluation of real water supply conditions in this river s reach, by the application of hydrological modeling, including the arrangement of main dams in tributaries, and storage reservoir water balance. The rainfall-discharge model s applied in each sub-basins it was selected the model MODHISA- Hydrological Model of Semi Arid, that is a concentrated model with easy application. The simulation produced 50 years of inflows into the reservoirs, for which, were constructed the guaranties curves; and produced 50 years of synthetic discharge data in relevant points on the river and on its affluents; so it was constructed the permanence curves. Confronting the available discharge with the current and futures volumes of raw water captured in this river s reach, it was verified that de demands have high guaranties. This work concluded that the MODHISA Model is suitable to reproduce the hydrologic characteristics of Piranhas-Açu sub-basins, and showing good results

Aí marcador de especificidade de SN indefinidos: um estudo funcionalista com implicações para o ensino

This body of work aims to describe and analyze the behavior of the Aí specificity marker of indefinite Noun Phrases (NP), one of the many functions this linguistic item is developing in contemporary Brazilian Portuguese. From the Functional Linguistic theory perspective, the North American declivity, this project intends to outline the possible grammaticalization trajectory taken by the Aí specificity marker. It will be followed from its function as a spatial deitic up to its integration of indefinite NP, and the action of the fundamental principles of the theory, such as iconicity and informativity, will be observed on the use of this item. Following this, Aí specificity marker behavior will be described in respect to various linguistic and social factors: type of text where the occurrence is encountered, language modality in which the latter is produced, syntactic function developed by the NP specified by Aí , the existence or lack of material intervening between Aí and the NP nuclear noun, informational status of the NP adjugated to Aí , and finally, sex, education and age of the speaker. The occurrence of conversational implicatures will also be verified (GRICE, 1982) within the contexts of Aí specificity marker use. Reflections on the teaching of grammar will be made, as well as on the possibility and validity of working with noun phrase specificity markers in elementary and high school Portuguese language classes. The data used in this research project stem from Corpus Discurso & Gramática A língua falada e escrita na cidade do Natal (FURTADO DA CUNHA, 1998), and from Corpus Discurso & Gramática A língua falada e escrita na cidade do Rio de Janeiro (VOTRE; OLIVEIRA, 1995)