Pigmentos a base de Cobalto para aplicação em revestimentos cerâmicos

Ceramic pigments that own mainly the spinel structure AB2O4 are becoming a matter of great scientific and technological interest due to the ability of accommodate different cations in its structure, allowing different dopings and thus obtaining different colors. Studies on ceramic pigments currently are being directed to the development of stable and pigments obtained at low temperatures and with greater reproducibility. This work aims at the use of inorganic pigments for applications in ceramic tiles, investigating the influence of doping and calcination temperature on the coloring pigments and ceramic glazes. the based pigments of CoCr2O4, CoAl2O4, Co0,8Zn0,2Cr2O4 and Co0,8Zn0,2Al2O4 were synthesized by a chemical route using commercial gelatin as organic precursor. The materials were characterized by thermogravimetric analysis (TG), X-ray diffraction (XRD), infrared spectroscopy (FTIR) spectroscopy scanning electron microscopy (SEM) in the UVVisible region and colorimetry. The results confirmed the feasibility of synthesis used, the route presented pigments crystal structures and the desired phases were obtained from 500 °C with increased crystallinity and the crystallite size. The pigments have hues ranging from green to violet according to their doping and calcination temperatures.

Desenvolvimento de estruturas integradas de filtros e antenas para aplicações em sistemas de comunicações sem fio

This paper presents a study of the integration of filters and microstrip antennas, yielding devices named as filtennas for applications in wireless communications systems. The design of these structures is given from the observation of filtennas based integration between horn antennas and frequency selective surfaces (FSS), used in the band X. The choice of microstrip line structures for the development of a new configuration filtennas justifies the wide application of these transmission lines, in recent decades, always resulting in the production of circuit structures with planar light-weight, compact size, low cost, easy to construct and particularly easy to integrate with other microwave circuits. In addition, the antenna structure considered for the composition of filtennas consists of a planar monopole microstrip to microstrip filters integrated in the feed line of the antenna. In particular, are considered elliptical monopole microstrip (operating in UWB UWB) microstrip filters and (in structures with associated sections in series and / or coupled). In addition, the monopole microstrip has a proper bandwidth and omnidirectional radiation pattern, such that its integration with microstrip filters results in decreased bandwidth, but with slight changes in the radiation pattern. The methods used in the analysis of monopoles, and filters were filtennas finite elements and moments by using commercial software Ansoft Designer and HFSS Ansoft, respectively. Specifically, we analyze the main characteristics of filtennas, such as radiation pattern, gain and bandwidth. Were designed, constructed and measures, several structures filtennas, for validation of the simulated results. Were also used computational tools (CAD) in the process of building prototypes of planar monopoles, filters and filtennas. The prototypes were constructed on substrates of glass-fiber (FR4). Measurements were performed at the Laboratory for Telecommunications UFRN. Comparisons were made between simulated and measured, and found good agreement in the cases considered

Caracterização de água de lavagem de filtros em estações de tratamento de água de filtração direta

The water supply and treatment is considered as a great benefit considering that, if done efficiently, provides public health. However, considering the WTP (Water Treatment Plant) is an industry, with its inputs and waste generation, they must be constantly evaluated and monitored to verify the best and most appropriate way to process and dispose their waste, minimizing therefore the potential impacts to the environment. By volume, the most significant waste is the rapid filter backwash water. It is very common the disposal of this waste without treatment in water sources, which are used, for the most part, as a water supply source of a downstream population. This study evaluated quantitative and qualitative parameters in filter backwash water in three WTP - Itaitinga, Maranguape and Pacatuba, located in Ceará State, northeast of Brazil. It was found that the Maranguape WTP, in terms of treatment capacity, is the larger. The Itaitinga WTP is the one that consumes more water during filters washing. The Pacatuba WTP exhibited higher concentration of total suspended and settleable solids, COD and aluminum in the filters backwash water. It is noteworthy that the settleable solids and total suspended solids in all three WTP are above the effluent discharge standard recommended by Resolution 154/2002 of SEMACE (State Superintendent of Environment of Ceará). It was concluded that the filter backwash water from the study WTP exceeded the allowed values for legislation to be disposed directly into surface water bodies. It is suggested as an alternative to treat and recycle the filter backwashing water the construction of sludge settling ponds.

Avaliação da conformidade dos blocos cerâmicos produzidos em algumas cerâmicas no Rio Grande do Norte

The final quality of the works accomplished by the building construction industry depends directly on the quality of the materials supplied and used during all their phases of execution. The federal government participation and several state programs have established conditions to stimulate and require the increment of the quality level in the building construction industry´s product chain. These programs aim at the product conformity to the technical standards. Within this context, the evaluation program of the ceramic product conformity in Rio Grande do Norte state is assessing the conformity degree to Brazilian Technical Standards of ceramic bricks and tiles made in the ceramic production area in the state. In this work, is determine the degree of conformity of the sealing ceramic bricks made by some companies in different areas of the state, such as Assú, São Gonçalo do Amarante, Apodi, Parelhas, São José do Mipibu e Macaíba. Using the technical standards as a point of reference, we attempted to reproduce in the laboratory the experimental procedures to the analysis execution, according to the specifications. It was possible to determine that none of the evaluated samples are in strict conformity with the current technical standards, what reflects the real situation of the products available on the market.

Estudo do aproveitamento de resíduos PAE no desenvolvimento de materiais cerâmicos

This work presents a new ceramic material obtained through the incorporation of solid waste from the steel industry and known as dedusting powder PAE - in ceramic formulations based on clay, potassium and sodium feldspars, kaolin and talc. Formulations were prepared with ceramic residue levels of 0% (basic mass - MB), 2%, 4% and 8%, subjected to firing at temperatures of 1000 ° C, 1050ºC, 1100ºC and 1150ºC for periods of 15 min. and 120 min. The physicchemical and mechanical properties of these ceramic formulations were determined based on the firing temperature, residence time in the oven and the percentage of waste. Since the physicochemical and mechanical properties of the sintered materials were evaluated by chemical analysis techniques (fluorescence X-rays - FRX), particle size distribution, specific surface area, apparent density, structural analysis by diffraction of X-rays (DRX) and characterization of surface by scanning electron microscopy (SEM). The magnetic response characteristics and the pattern of magnetic ferrites of the samples were analyzed in the assay conditions, having noticed that the saturation magnetic susceptibility depend on the sintering temperature of the material and it is associated with its crystal structure. From the analysis results, it was concluded that the ceramic material with better physical and mechanical properties is obtained when the 8% from PAE residue is added to standard formulation under the burn time of 15 minutes and temperature of 1150ºC.

Estudo comparativo da queima rápida com a queima tradicional nas propriedades de materiais cerâmicos de base argilos

Dutra, R. P. S.; Varela,M. L.; Nascimento, R. M. ; Gomes, U. U. ; Martinelli1, A. E. ; Paskocimas, C. A. Estudo comparativo da queima rápida com a queima tradicional nas propriedades de materiais cerâmicos de base argilosa. Cerâmica [online]. 2009, vol.55, n.333, pp. 100-105. ISSN 0366-6913. doi:Disponivem em: . Acesso em: 04 out. 2010.

Avaliação da conformidade de blocos cerâmicos para alvenaria de vedação produzidas na Região Integrada de Desenvolvimento da Grande Teresina

This research presents an outlook of the industries of red ceramic in the region next to the city of Teresina and an analysis of the ceramic products producted in this pole. The microregion investigated possesses 13 boroughs where were identified 32 ceramic in operation, being that 24 are located in Teresina, the ceramic region more important of Piauí, 1 is located in the city of Miguel Leão and 7 is located in Timon city that belongs to the state of Maranhão. The majority of ceramics are pulverized in these two cities, Teresina and Timon , responsible by a largely production independent of distance between fabric and consumer market. Furthermore, there is an artisanal production realized in other boroughs, mainly manual conformation bricks, where are producted diverse types of handicraft and ceramics utilitarian. The objective of this research is to evalue the conformity of ceramic blocks for brick of obstruction made by red ceramic industry of microregion at studying, verifying their pontentialities and adequacy in terms of production. In this research universe made a search of ceramic industries related to the Foundation CEPRO (Foundation Center of Research Social and Economic of Piauí). For the analysis of the ceramic products , were colected 60 crude bricks sample in three industries for their characterization, and 39 burned bricks sample for the Evaluation of Conformity. The results of the characterization made reached a accetptable standard in all formulations and temperature studied. The burned samples were applied to the geometric, physical and mechanical assays according to the ABNT standards (Brazilian Association of Technical Standards). The results of the physical assays showed that all the samples are at the same band recommended by standard. However, through the geometric assays just two industries did not present results according to the standard, due to lack of control in their process such as in their equipments. Taking into account the mechanical properties, only one industry investigated was not according to the standard

Síntese, caracterização e cinética da decomposição térmica dos materiais cerâmicos PrMO3 (M = Ni ou Co)

In this work have been studied the preparation, characterization and kinetic study of decomposition of the polymerizing agent used in the synthesis under non-isothermal condition ceramics PrMO3 of general formula (M = Co and Ni). These materials were obtained starting from the respective metal nitrates, as a cations source, and making use of gelatin as polymerizing agent. The powders were calcined at temperatures of 500°C, 700°C and 900°C and characterized by X-ray Diffraction (XRD), Thermogravimetric Analysis (TG / DTG/ DTA), Infrared Spectroscopy (FTIR), Temperature Programmed Reduction (TPR) and Scanning Electron Microscopy (SEM). The perovskite phase was detected in all the X-rays patterns. In the infrared spectroscopy observed the oxide formation as the calcination temperature increases with the appearance of the band metal - oxygen. The images of SEM revealed uniform distribution for the PrCoO3 and particles agglomerated as consequence of particle size for PrNiO3. From the data of thermal analysis, the kinetics of decomposition of organic matter was employed using the kinetics methods called Model Free Kinetics and Flynn and Wall, in the heating ratios 10, 20 and 30° C.min-1 between room temperature and 700°C. Finally, been obtained the values of activation energy for the region of greatest decomposition of organic matter in samples that were determined by the degree of conversion (α)

Adição de cascalho de perfuração da bacia potiguar em argilas para uso em materiais cerâmicos: influência da concentração e temperatura de queima.

One of waste produced on large scale during the well drilling is the gravel drilling. There are techniques for the treatment of the same, but there isn t consensus on what are the best in terms of economic and environmental. One alternative for disposal of this waste and objective of this paper is the incorporation and immobilization of gravel clay matrix to assess their technological properties. The Raw Materials used were characterized by the following techniques: Chemical Analysis by X-ray fluorescence (XRF), mineralogical analysis by X-ray Diffraction (XRD), Grain Size Analysis (FA) and Thermal Analysis by Thermogravimetry (TG) and thermodiferential (DTA). After characterizing, samples were formulated in the following percentages: 0, 5, 10, 15, 25, 50, 75, 100% (weight) of gravel drilling, then the pieces were pressed, dried (110 ° C) and sintered at temperatures of 850, 950 and 1050 ° C. After sintering, samples were tested for water absorption, linear shrinkage, flexural strength, porosity, density, XRD and test color. The results concluded that the incorporation of gravel drilling is a viable possibility for solid masonry bricks and ceramic blocks manufacture at concentrations and firing temperature described here. Residue incorporation reduces an environmental problem, the cost of raw materials for manufacture of ceramic products

Síntese e caracterização de espinélios a base de Cu, Fe e Cr para pigmentos cerâmicos

Inorganic pigment comprises a host lattice, which is part of the chromophore component (usually a transition metal cation) and possible components modifiers, which stabilize, add or restate the properties pigments. Among the materials with spinel, ferrites, and the chromite stand out, because they have broad technological importance in the area of materials, applicability, pigments, catalytic hydrogenation, thin film, ceramic tiles, among others. The present work, pigments containing CuFe2O4, CuCr2O4,e CuFeCrO4, were synthesized by a method that makes use of gelatin as organic precursor using their application to ceramic pigments. The pigments were characterized by X-ray diffraction (XRD), Infrared spectroscopy, scanning electron microscopy (SEM) spectroscopy in the UV-visible and Colorimetry. The results confirmed the feasibility of the synthetic route used, with respect to powders synthesized, there is the formation of spinel phase from 500°C, with an increase in crystallinity and the formation of other phases. The pigments were shown to be crystalline and the desired phases were obtained. The copper chromite have hues ranging from green to black according to the calcination temperature, while the copper chromite doped with iron had brownish. The ferrites showed copper color and darker brown to black, which may indicate an interesting factor because of the importance of black pigment

Influência do uso de combustíveis alternativos na síntese por combustão via microondas para a produção de materiais cerâmicos com estrutura espinélio

The development and study of detectors sensitive to flammable combustible and toxic gases at low cost is a crucial technology challenge to enable marketable versions to the market in general. Solid state sensors are attractive for commercial purposes by the strength and lifetime, because it isn t consumed in the reaction with the gas. In parallel, the use of synthesis techniques more viable for the applicability on an industrial scale are more attractive to produce commercial products. In this context ceramics with spinel structure were obtained by microwave-assisted combustion for application to flammable fuel gas detectors. Additionally, alternatives organic-reducers were employed to study the influence of those in the synthesis process and the differences in performance and properties of the powders obtained. The organic- reducers were characterized by Thermogravimetry (TG) and Derivative Thermogravimetry (DTG). After synthesis, the samples were heat treated and characterized by Fourier Transform Infrared Spectroscopy (FTIR), X-ray Diffraction (XRD), analysis by specific area by BET Method and Scanning Electron Microscopy (SEM). Quantification of phases and structural parameters were carried through Rietveld method. The methodology was effective to obtain Ni-Mn mixed oxides. The fuels influenced in obtaining spinel phase and morphology of the samples, however samples calcined at 950 °C there is just the spinel phase in the material regardless of the organic-reducer. Therefore, differences in performance are expected in technological applications when sample equal in phase but with different morphologies are tested

Síntese de pigmentos cerâmicos inorgânicos nanométricos e encapsulados com estrutura core-shell pela rota dos precursores poliméricos

The present work has as objective the development of ceramic pigments based in iron oxides and cobalt through the polymeric precursor method, as well as study their characteristics and properties using methods of physical, chemical, morphological and optical characterizations.In this work was used iron nitrate, and cobalt citrate as precursor and nanometer silica as a matrix. The synthesis was based on dissolving the citric acid as complexing agent, addition of metal oxides, such as chromophores ions and polymerization with ethylene glycol. The powder obtained has undergone pre-ignition, breakdown and thermal treatments at different calcination temperatures (700 °C, 800 °C, 900 °C, 1000 °C and 1100 °C). Thermogravimetric analyzes were performed (BT) and Differential Thermal Analysis (DTA), in order to evaluate the term decomposition of samples, beyond characterization by techniques such as BET, which classified as microporous materials samples calcined at 700 ° C, 800 º C and 900 º C and non-porous when annealed at 1000 ° C and 1100 º C, X-ray diffraction (XRD), which identified the formation of two crystalline phases, the Cobalt Ferrite (CoFe2O4) and Cristobalite (SiO2), Scanning Electron Microscopy (SEM) revealed the formation of agglomerates of particles slightly rounded;and Analysis of Colorimetry, temperature of 700 °C, 800 °C and 900 °C showed a brown color and 1000 °C and 1100 °C violet

Preparação e caracterização de filmes cerâmicos para cátodos de células a combustível de óxido sólido

Alternative and clean energy generation research has been intensified in last decades. Among the alternatives, fuel cells are one of the most important. There are different types of fuel cells, among which stands out intermediate temperature solid oxide fuel cell (IT-SOFC) matter of the present work. For application as cathode on this type of devices, the ceramic Ba0.5Sr0.5C0.8Fe0.2O3-δ doped with rare earth ions (Nd, Sm) have been quite promising because they show good ionic conductivity and operate at relatively low temperatures (500 - 800°C). In this work, Ba0.5Sr0.5Co0.8Fe0.2O3-δ, (BaSr)0.5Sm0.5Co0.8Fe0.2O3-δ and (BaSr)0.5Nd0.5C0.8Fe0.2O3-δ were obtained by modified Pechini method, making use of gelatin as polymerizing agent. The powders were characterized by X-Ray Diffraction (XRD), Temperature Programmed Reduction (TPR) and Scanning Electron Microscopy (SEM). The perovskite phase was observed in all X-ray patterns for the materials Ba0.5Sr0.5C0.8Fe0.2O3-δ doped with rare earth ions (Nd, Sm). The SEM images showed that the materials have a characteristics porous, with very uniform pore distribution, which are favorable for application as cathodes. Subsequently, screen-printed assymmetrical cells were studied by impedance spectroscopy, to assess the kinetics of the cathode for the reduction reaction of oxygen. The best resistance to the specific area was found for the cathode BSSCF sintered at 1050 °C for 4 hours with around 0.15 Ω.cm2 at 750 °C as well as cathodes BSNCF and BSCF obtained resistances specific area of 0.2 and 0.73 Ω.cm2, respectively, for the same conditions. The polarization curves showed similar behavior to the best cathodes BSSCF and BSNCF, such combination of properties indicates that the film potentially depict good performance as IT-SOFC cathodes

Estudo da molhabilidade de ligas de adição à base de prata sobre insertos cerâmicos para aplicação em brocas perfuração de poços de petróleo

Metal-ceramic interfaces are present in tricone drill bits with hard ceramic inserts for oil well drilling operations. The combination of actions of cutting, crushing and breaking up of rocks results in the degradation of tricone drill bits by wear, total or partial rupture of the drill bit body or the ceramic inserts, thermal shock and corrosion. Also the improper pressfitting of the ceramic inserts on the bit body may cause its total detachment, and promote serious damages to the drill bit. The improvement on the production process of metal-ceramic interfaces can eliminate or minimize some of above-mentioned failures presented in tricone drill bits, optimizing their lifetime and so reducing drilling metric cost. Brazing is a widely established technique to join metal-ceramic materials, and may be an excellent alternative to the common mechanical press fitting process of hard ceramic inserts on the steel bit body for tricone drill bit. Wetting phenomena plays an essential role in the production of metal/ceramic interfaces when a liquid phase is present in the process. In this work, 72Silver-28Copper eutectic based brazing alloys were melted onto zirconia, silicon nitride and tungsten carbide/Co substrates under high vacuum. Contact angle evolution was measured and graphically plotted, and the interfaces produced were analysed by SEM-EDX. The AgCu eutectic alloy did not wet any ceramic substrates, showing high contact angles, and so without chemical interaction between the materials. Better results were found for the systemns containing 3%wt of titanium in the AgCu alloy. The presence os titanium as a solute in the alloy produces wettable cand termodinamically stable compounds, increasing the ceramics wetting beahviour

Efeito da Gália como aditivo de sinterização em eletrólitos cerâmicos à base de céria sintetizados pelo método de complexação de cátions

Fuel cells are considered one of the most promising ways of converting electrical energy due to its high yield and by using hydrogen (as fuel) which is considered one of the most important source of clean energy for the future. Rare earths doped ceria has been widely investigated as an alternative material for the electrolyte of solid oxide fuel cells (SOFCs) due to its high ionic conductivity at low operating temperatures compared with the traditional electrolytes based on stabilized zirconia. This work investigates the effect of gallium oxide (Gallia) as a sintering aid in Eu doped ceria ceramic electrolytes since this effect has already been investigated for Gd, Sm and Y doped ceria electrolytes. The desired goal with the use of a sintering aid is to reduce the sintering temperature aiming to produce dense ceramics. In this study we investigated the effects on densification, microstructure and ionic conduction caused by different molar fraction of the dopants europium (10, 15 and 20%) and gallium oxide (0.3, 0.6 and 0.9%) in samples sintered at 1300, 1350 and 1450 0 C. Samaria (10 and 20%) doped ceria samples sintered between 1350 and 1450 °C were used as reference. Samples were synthesized using the cation complexation method. The ceramics powders were characterized by XRF, XRD and SEM, while the sintered samples were investigated by its relative density, SEM and impedance spectroscopy. It was showed that gallia contents up to 0.6% act as excellent sintering aids in Eu doped ceria. Above this aid content, gallia addition does not promote significant increase in density of the ceramics. In Ga free samples the larger densification were accomplished with Eu 15% molar, effect expressed in the microstructure with higher grain growth although reduced and surrounded by many open pores. Relative densities greater than 95 % were obtained by sintering between 1300 and 1350 °C against the usual range 1500 - 1600 0 C. Samples containing 10% of Sm and 0.9% of Ga reached 96% of theoretical density by sintering at 1350 0 C for 3h, a gain compared to 97% achieved with 20% of Sm and 1% of Ga co-doped cerias sintered at 1450 0 C for 24 h as described in the literature. It is found that the addition of gallia in the Eu doped ceria has a positive effect on the grain conductivity and a negative one in the grain boundary conductivity resulting in a small decrease in the total conductivity which will not compromise its application as sintering aids in ceria based electrolytes. Typical total conductivity values at 600 and 700 °C, around 10 and 30 mS.cm -1 respectively were reached in this study. Samples with 15% of Eu and 0.9 % of Ga sintered at 1300 and 1350 °C showed relative densities greater than 96% and total conductivity (measured at 700 °C) between 20 and 33 mS.cm -1 . The simultaneous sintering of the electrolyte with the anode is one of the goals of research in materials for SOFCs. The results obtained in this study suggest that dense Eu and Ga co-doped ceria electrolytes with good ionic conductivity can be sintered simultaneously with the anode at temperatures below 1350 °C, the usual temperature for firing porous anode materials