Influência da desordem estrutural nas propriedades magnéticas de filmes finos de Co2FeAl

Thin films of Co2FeAl (CFA) and trilayers with CFA/M/CFA, where M is Au or Ag, produced by magnetron sputtering onto glass and oriented (MgO (100)) substrates were investigated. The structural, magnetic static and magnetic dynamics properties were analyzed by distinct experimental techniques. Through X-ray diffraction was observed an A2 phase for the samples (completely disordered), where the atoms are randomly located in the lattice. The static magnetic behavior, in some samples, reveal a plateau behavior generated by a biphasic system. The magnetoimpedance measurements were performed by varying the angle between the external magnetic field and current with respect of anisotropy direction. For this reason, the MI results show a asymmetric magnetoimpedance (AMI) behavior. For the single and trilayers samples with 500 nm-thick, the AMI effect is more evident in comparison with samples with 1000 nm-thick. Therefore, in this work was stablished a route to produce Heusler alloy samples with A2 phase in thin film geometry onto amorphous and oriented substrates, and due to structural disorder was possible to study the hysteretic and MI asymmetric effects.

Produção e estudo de multicamadas magnéticas em substrato flexível

Magnetic multilayers are the support for the production of spintronic devices, representing great possibilities for miniaturized electronics industry. having the control to produce devices as well as their physical properties from simple multilayer films to highly complex at the atomic scale is a fundamental need for progress in this area, in recent years has highlighted the production of organic and flexible spintronic devices. Because of this trend, the objective of this work was to produce magnetic multilayers deposited on flexible substrate using magnetron sputtering dc technique. Three sets of samples were prepared. The first set composed of the trilayer type CoFe=Cu(t)=CoFe with different thickness of the metallic spacer. The second set consists of two multilayer subgroups, CoFe=Cu in the presence of IrMn layer as a buffer and the next multilayer as cap layer. The third set consisting of non-magnetostrictive multilayer permalloy (Py=Ta and Py=Ag) on flexible substrate and glass. The magnetic properties, were investigated by magnetometry measurements, ferromagnetic resonance and magnetoimpedance (MI), measurements were carried out at room temperature with the magnetic field always applied on the sample plane. For structural analysis, the diffraction X-ray was used. The results of the trilayer showed a high uniaxial anisotropy field for the sample with a spacer of 4.2 nm. For the multilayer in the presence of IrMn layer as the buffer, the study of static and dynamic magnetic properties showed isotropic behavior. For the multilayer in the presence of IrMn layer as a cap, the results of static magnetic properties of the magnetic behavior exhibited a spin valve structure type. However there was a disagreement with results of ferromagnetic resonance measurements, which was justified by the contribution of the unstable and stable grain to the rotatable anisotropy and Exchange bias in ferromagneticantiferromagnetic interface. The third serie of samples showed similar results behavior for the MI Ag multilayers spacer in both substrates. There are also significant MI changes with the Ta spacer, possible associated with the compressive stress on the flexible substrate sample.