Estudo de duas pseudoligas de Nb-Cu obtidas pela rota da metalurgia do pó

The Nb-Cu pseudoalloys present themselves as potential substitutes for the alloys from a well known system and already commercially applied, as the W-Cu alloys, used in applications such as heat sinks, electrical contacts and coils for the generation of high magnetic fields. Because it is an immiscible system, where there is mutual insolubility and low wettability of the liquid Cu on the Nb surface, the processing route used in this work was the Powder Metallurgy. Two Nb alloys were used, with additions of 10% and 20% in weight of Cu, and times of 20, 30 and 40 hours for the high energy milling of the starting powders. The milling evolution of the powders is presented through the characterization techniques, such as the LASER diffraction for particle size, XRD, SEM, EDS, DSC, dilatometry, TEM and chemical analysis. After the milling, portions of the loads were submitted to the annealing heat treatment. The process used for the samples consolidation was the hot pressing, which has been applied both on some milled powders samples, as on the annealed powders. Subsequent heat treatments were performed in the samples at temperatures of 1000ºC (solid phase) and 1100ºC (in the Cu liquid phase). All sets of consolidated samples, and also the two sets of the heat treated, were analyzed by XRD, SEM, EDS, density and Vickers microhardness. Moreover, other Nb powder samples with 10% and 20% in weight of Cu obtained by simple mechanical mixing, were consolidated, thermally treated and characterized with the same techniques applied to the others, and the results were compared among themselves. Despite the difficulty of consolidation and densification of the two pseudoalloys of the Nb-Cu system of this study, on the route that passes through the HEM, samples were obtained with densities around 90% of the theoretical density. And, on the processing route of which were only mixed, the values reached up to 97%. Therefore, in this work are also emphasized the processes that made possible these results.

Síntese e caracterizações estrutural e magnética das ferritas de cobalto-manganês (Co1-xMnxFe2O4 E Co1,2Fe1,8-xMnxO4)

The cobalt-manganese ferrites (Co1¡xMnxFe2O4 and Co1,2Fe1,8¡xMnxO4) has a mixed structure of spinel type and it has been regarded as one of candidates for petitive wide variety of applications in devices from ultrasonic generation and detection, sensors, transformers, as well as in medical industry. Ferrites cobalt-manganese nanostructured were produced via mechanical alloying with subsequent heat treatment and were characterized by X-ray diffraction, X-ray fluorescence, scanning electron microscopy and magnetization. Samples of Co1¡xMnxFe2O4 and Co1,2Fe1,8¡xMnxO4 were obtained from the precursor powders Fe3O4, Co3O4 and Mn3O4 which were stoichiometrically mixed and ground by 10h and heat treated at 900°C for 2h. The diffraction confirmed the formation of the pure nanocrystalline phases to series Co1,2Fe1,8¡xMnxO4 with an average diameter of about 94nm. It was found that the lattice parameter increases with the substitution of Fe3Å by Mn3Å. The x-ray fluorescence revealed that the portions of metals in samples were close to the nominal stoichiometric compositions. The microstructural features observed in micrographs showed that the particles formed show very different morphology and particle size. The magnetic hysteresis measurements performed at low temperature showed that the saturation magnetization and remanence increased as the concentration of manganese, while the coercive field decreased. The anisotropy constant (Ke f ), was estimated from the data adjustments the law of approaching saturation. It was found that the anisotropy decreases substantially with the substitution of Fe by Mn.

Estudo da influência da adição de níquel em alumina pela rota da metalurgia do pó

Ceramic materials alumina basis have been widely used in structural components, mainly because owning properties such as high hardness, chemical inertness and good wear resistance, however, the low toughness is a factor that compromises its use in many other applications, featuring the addition of nickel as a possible solution to this problem, in this context, this work aims to study the addition of nickel alumina using the route of powder metallurgy processing of the material. The percentage of nickel were added 2, 4 and 6 wt%; and each composition to high energy milling in a planetary mill was performed for 2, 4, 9 and 16h. Subsequently, the samples were compacted at 300 MPa and sintered in a vacuum oven at 1400⁰C for 2h. The samples were characterized as the physical and mechanical properties, observing, in general, an improvement in sinterability of the material with increasing grinding time and nickel content, and mixing with a decrease of porosity and increase of hardness, density values above 80% of theoretical were obtained. The milling time of 4 hours and addition of 2% nickel, particularly if achieved higher hardness (HV 1068.7 +/- 32.6) and density of about 99% theoretical density.

Estudo da influência da adição de níquel em alumina pela rota da metalurgia do pó

Ceramic materials alumina basis have been widely used in structural components, mainly because owning properties such as high hardness, chemical inertness and good wear resistance, however, the low toughness is a factor that compromises its use in many other applications, featuring the addition of nickel as a possible solution to this problem, in this context, this work aims to study the addition of nickel alumina using the route of powder metallurgy processing of the material. The percentage of nickel were added 2, 4 and 6 wt%; and each composition to high energy milling in a planetary mill was performed for 2, 4, 9 and 16h. Subsequently, the samples were compacted at 300 MPa and sintered in a vacuum oven at 1400⁰C for 2h. The samples were characterized as the physical and mechanical properties, observing, in general, an improvement in sinterability of the material with increasing grinding time and nickel content, and mixing with a decrease of porosity and increase of hardness, density values above 80% of theoretical were obtained. The milling time of 4 hours and addition of 2% nickel, particularly if achieved higher hardness (HV 1068.7 +/- 32.6) and density of about 99% theoretical density.

Efeito da adição de WC e Co na sinterização e propriedades mecânicas da alumina

Composites based on alumina (Al2O3), tungsten carbide (WC) and cobalt (Co) exhibit specific properties such as low density, high oxidation resistance, high melting point and high chemical inertia. That composite shows to be a promising material for application in various fields of engineering. In this work, the mechanical properties of the composite (Al2O3 – WC – Co), particularly density and hardness, were evaluated according to the effects of the variables of powder processing parameters, green compact and sintered. Powder composites with the composition of 80 wt% Al2O3, 18 wt% WC and 2 wt% Co were processed by high energy ball milling in a planetary mill for 50 hours as well as mixed by manual mixing in a glass vessel with the same proportion. Samples were collected (2, 10, 20, 30, 40 and 50 hours) during the milling process. Then, the powders were compacted in a cylindrical die with 5 mm in diameter in a uniaxial press with pressures of 200 and 400 MPa. The sintering was in two stages: first, the solid phase sintering was performed at 1126 and 1300 °C for 1 hour with a heating rate of 10 °C/min in a resistive furnace under argon atmosphere for green samples compacted in 200 and 400 MPa; the second sintering was performed on dilatometer in solid phase at 1300 °C for green sample compacted in 200 MPa, another sintering also was performed on dilatometer, this time in liquid phase at 1550 °C for green samples compacted in 200 and 400 MPa, with the same parameters used in resistive furnace. The raw materials were characterized by X – ray diffraction (XRD), X – ray fluorescence (XRF), scanning electron microscopy (SEM), energy dispersive spectroscopy (EDS) and laser particlemeter. The sintered samples were subjected to microhardness testing. The results showed that high energy milling achieved to the objectives regarding the particle size and the dispersion of composite phases. However, the hardness did not achieve to significant results, this is an indication that the composite has low fracture toughness.

Efeito da adição de WC e Co na sinterização e propriedades mecânicas da alumina

Composites based on alumina (Al2O3), tungsten carbide (WC) and cobalt (Co) exhibit specific properties such as low density, high oxidation resistance, high melting point and high chemical inertia. That composite shows to be a promising material for application in various fields of engineering. In this work, the mechanical properties of the composite (Al2O3 – WC – Co), particularly density and hardness, were evaluated according to the effects of the variables of powder processing parameters, green compact and sintered. Powder composites with the composition of 80 wt% Al2O3, 18 wt% WC and 2 wt% Co were processed by high energy ball milling in a planetary mill for 50 hours as well as mixed by manual mixing in a glass vessel with the same proportion. Samples were collected (2, 10, 20, 30, 40 and 50 hours) during the milling process. Then, the powders were compacted in a cylindrical die with 5 mm in diameter in a uniaxial press with pressures of 200 and 400 MPa. The sintering was in two stages: first, the solid phase sintering was performed at 1126 and 1300 °C for 1 hour with a heating rate of 10 °C/min in a resistive furnace under argon atmosphere for green samples compacted in 200 and 400 MPa; the second sintering was performed on dilatometer in solid phase at 1300 °C for green sample compacted in 200 MPa, another sintering also was performed on dilatometer, this time in liquid phase at 1550 °C for green samples compacted in 200 and 400 MPa, with the same parameters used in resistive furnace. The raw materials were characterized by X – ray diffraction (XRD), X – ray fluorescence (XRF), scanning electron microscopy (SEM), energy dispersive spectroscopy (EDS) and laser particlemeter. The sintered samples were subjected to microhardness testing. The results showed that high energy milling achieved to the objectives regarding the particle size and the dispersion of composite phases. However, the hardness did not achieve to significant results, this is an indication that the composite has low fracture toughness.

Estudo da obtenção de cerâmica composta de alumina e beta alumina sódica utilizando-se resíduo cerâmico de velas de ignição e pó químico de extintores de incêndio

Ceramic materials the alumina base are large industrial applications. They are required for these products, specific characteristics obtained by following strict criteria during the manufacturing process. However, after life, not always these products are reused by a suitable waste management process. In ceramist context, advance research aimed at the reuse of waste aimed at obtaining ceramics and composite materials, with marked reduction of conventional raw materials. Aiming to generate scientific, technological and environmental contribution, this work studied to obtain a composite of alumina ceramic (Al2O3) and sodium beta alumina (NaAl11O17 ), and as starting materials the residue of the ceramic insulator of spark plugs, as a source alumina (Al2O3) powder and unusable sodium bicarbonate (NaHCO3) of fire extinguishers, as a source of sodium oxide (Na2O). The final ceramic product was obtained from a conventional mixture of sodium aluminum oxide in appropriate molar proportions. Sample spark plugs were obtained, discarded by lifetime, specific to a manufacturer, which, after passing through mechanical stress (grinding, magnetic purification, washing, drying and grinding the high energy), which resulted in residue powder with ceramic content of 84.34 % alumina (Al2O3), found by FRX chemical analysis, the phases present and identified by DRX. The dry chemical fire extinguisher, baking soda-based (NaHCO3) with expired, was obtained through direct collection of the waste generated during maintenance. Subjected to heat treatment at 120 °C , the NaHCO3 powder was decomposed in sodium oxide ( Na2O), which, subjected to chemical analysis (FRX) and mineralogical (DRX) revealed a content of 86.62 % sodium oxide (Na2O) . In the following steps the experimental procedure, chemical formulations were made on a molar basis of the starting material (1:9, 1:10 and 1:11 de Na2O/ Al2O3) inclusion of additives, milling parameters, sieve analysis, dilatometry, conformation of specimens, sintering in firing steps at 800 °C , 1000 °C and 1.200 °C with varying stays 30 , 60 and 120 minutes in each of the levels. The characterization of the final product was made by the following physical tests: water absorption, porosity, linear shrinkage, mineralogical analysis by DRX and microstructural analysis by MEV. A higher formation of sodium beta alumina (NaAl11O17), in sintered specimens in levels of 1.200 °C and 120 minutes, despite the prevailing coexistence of alpha phase alumina (Al2O3). From the results obtained opens up prospects for the reuse of waste studied in this work, the potter context and in other technological areas.

Estudo da obtenção de cerâmica composta de alumina e beta alumina sódica utilizando-se resíduo cerâmico de velas de ignição e pó químico de extintores de incêndio

Ceramic materials the alumina base are large industrial applications. They are required for these products, specific characteristics obtained by following strict criteria during the manufacturing process. However, after life, not always these products are reused by a suitable waste management process. In ceramist context, advance research aimed at the reuse of waste aimed at obtaining ceramics and composite materials, with marked reduction of conventional raw materials. Aiming to generate scientific, technological and environmental contribution, this work studied to obtain a composite of alumina ceramic (Al2O3) and sodium beta alumina (NaAl11O17 ), and as starting materials the residue of the ceramic insulator of spark plugs, as a source alumina (Al2O3) powder and unusable sodium bicarbonate (NaHCO3) of fire extinguishers, as a source of sodium oxide (Na2O). The final ceramic product was obtained from a conventional mixture of sodium aluminum oxide in appropriate molar proportions. Sample spark plugs were obtained, discarded by lifetime, specific to a manufacturer, which, after passing through mechanical stress (grinding, magnetic purification, washing, drying and grinding the high energy), which resulted in residue powder with ceramic content of 84.34 % alumina (Al2O3), found by FRX chemical analysis, the phases present and identified by DRX. The dry chemical fire extinguisher, baking soda-based (NaHCO3) with expired, was obtained through direct collection of the waste generated during maintenance. Subjected to heat treatment at 120 °C , the NaHCO3 powder was decomposed in sodium oxide ( Na2O), which, subjected to chemical analysis (FRX) and mineralogical (DRX) revealed a content of 86.62 % sodium oxide (Na2O) . In the following steps the experimental procedure, chemical formulations were made on a molar basis of the starting material (1:9, 1:10 and 1:11 de Na2O/ Al2O3) inclusion of additives, milling parameters, sieve analysis, dilatometry, conformation of specimens, sintering in firing steps at 800 °C , 1000 °C and 1.200 °C with varying stays 30 , 60 and 120 minutes in each of the levels. The characterization of the final product was made by the following physical tests: water absorption, porosity, linear shrinkage, mineralogical analysis by DRX and microstructural analysis by MEV. A higher formation of sodium beta alumina (NaAl11O17), in sintered specimens in levels of 1.200 °C and 120 minutes, despite the prevailing coexistence of alpha phase alumina (Al2O3). From the results obtained opens up prospects for the reuse of waste studied in this work, the potter context and in other technological areas.

Estudo da síntese e sinterização de pós compósitos do sistema Ta-Cu

Ta-Cu bulk composites combine high mechanical resistance of the Ta with high electrical and thermal conductivity of the Cu. These are important characteristics to electrical contacts, microwave absorber and heat skinks. However, the low wettability of Ta under Cu liquid and insolubility mutual these elements come hard sintering this composite. High-energy milling (HEM) produces composite powders with high homogeneity and refines the grain size. This work focus to study Ta-20wt%Cu composite powders prepared by mechanical mixture and HEM with two different conditions of milling in a planetary ball mill and then their sintering using hydrogen plasma furnace and a resistive vacuum furnace. After milling, the powders were pressed in a steel dye at a pressure of 200 MPa. The cylindrical samples pressed were sintered by resistive vacuum furnace at 10-4torr with a sintering temperature at 1100ºC / 60 minutes and with heat rate at 10ºC/min and were sintered by plasma furnace with sintering temperatures at 550, 660 and 800ºC without isotherm under hydrogen atmosphere with heat rate at 80ºC/min. The characterizations of the powders produced were analyzed by scanning electron microscopy (SEM), x-ray diffraction (XRD) and laser granulometry. After the sintering the samples were analyzed by SEM, XRD and density and mass loss tests. The results had shown that to high intense milling condition produced composite particles with shorter milling time and amorphization of both phases after 50 hours of milling. The composite particles can produce denser structure than mixed powders, if heated above the Cu melting point. After the Cu to arrive in the melting point, liquid copper leaves the composite particles and fills the pores

Comportamento da adição do carbeto de nióbio (nBC) na matriz metálica do aço ferrítico 15kH2mfa

The 15Kh2MFA steel is a kind of Cr-Mo-V family steels and can be used in turbines for energy generation, pressure vessels, nuclear reactors or applications where the range of temperature that the material works is between 250 to 450°C. To improve the properties of these steels increasing the service temperature and the thermal stability is add a second particle phase. These particles can be oxides, carbides, nitrites or even solid solution of some chemical elements. On this way, this work aim to study the effect of addition of 3wt% of niobium carbide in the metallic matrix of 15Kh2MFA steel. Powder metallurgy was the route employed to produce this metallic matrix composite. Two different milling conditions were performed. Condition 1: milling of pure 15Kh2MFA steel and condition 2: milling of 15Kh2MFA steel with addition of niobium carbide. A high energy milling was carried out during 5 hours. Then, these two powders were sintered in a vacuum furnace (10-4torr) at 1150 and 1250°C during 60 minutes. After sintering the samples were normalized at 950°C per 3 minutes followed by air cooling to obtain a desired microstructure. Results show that the addition of niobium carbide helps to mill faster the particles during the milling when compared with that steel without carbide. At the sintering, the niobium carbide helps to sinter increasing the density of the samples reaching a maximum density of 7.86g/cm³, better than the melted steel as received that was 7,81g/cm³. In spite this good densification, after normalizing, the niobium carbide don t contributed to increase the microhardness. The best microhardness obtained to the steel with niobium carbide was 156HV and to pure 15Kh2MFA steel was 212HV. It happened due when the niobium carbide is added to the steel a pearlitic structure was formed, and the steel without niobium carbide submitted to the same conditions reached a bainitic structure

Revestimentos a base de Ta/Al2O3 produzidos por aspersão térmica sobre substrato metálico

Metal substrates were coated by thermal spraying plasma torch, they were positioned at a distance of 4 and 5 cm from the nozzle exit of the plasma jet. The starting materials were used for deposition of tantalum oxide powder and aluminium. These two materials were mixed and ground into high-energy mill, then immersed in the torch for the production of alumina coating infused with particles of tantalum with nano and micrometric size. The spraying equipment used is a plasma torch arc not transferred, which operating in the range of 250 A and 80 V, was able to produce enough heat to ignite aluminothermic between Ta2O5 and aluminum. Upon reaching the plasma jet, the mixing powders react with the heat of the blaze, which provides sufficient energy for melting aluminum particles. This energy is transferred through mechanisms of self-propagating to the oxide, beginning a reduction reaction, which then hits on the surface of the substrate and forms a coating on which a composite is formed by a junction metal - ceramic (Ta +Al2O3). The phases and quantification of each were obtained respectively by X-ray diffraction and the Rietveld method. Morphology by scanning electron microscopy and chemical analysis by energy dispersive spectroscopy EDS. It was also performed measurements of the substrate roughness, Vickers microhardness measurements in sprays and determination of the electron temperature of the plasma jet by optical emission spectroscopy EEO. The results confirmed the expectation generated around the end product of spraying the mixture Ta2O5 + Al, both in the formation of nano-sized particles and in their final form. The electron excitation temperature was consistent with the purpose of work, in addition, the thermodynamic temperature was efficient for the reduction process of Ta2O5. The electron excitation temperature showed values of 3000, 4500 and 8000 K for flows10, 20 and 30 l / min respectively, these values were taken at the nozzle exit of the plasma jet. The thermodynamic temperature around 1200 ° C, was effective in the reduction process of Ta2O5

Desenvolvimento e caracterização de nanocompósito de resina epóxi com nanopartículas de sílica para revestimento de dutos para transporte de petróleo

The use of polymer based coatings is a promising approach to reduce the corrosion problem in carbon steel pipes used for the transport of oil and gas in the oil industry. However, conventional polymer coatings offer limited properties, which often cannot meet design requirements for this type of application, particularly in regard to use temperature and wear resistance. Polymer nanocomposites are known to exhibit superior properties and, therefore, offer great potential for this type of application. Nevertheless, the degree of enhancement of a particular property is greatly dependent upon the matrix/nanoparticle material system used, the matrix/nanoparticle interfacial bonding and also the state of dispersion of the nanoparticle in the polymer matrix. The objective of the present research is to develop and characterize polymer based nanocomposites to be used as coatings in metallic pipelines for the transportation of oil and natural gas. Epoxy/SiO2 nanocomposites with nanoparticle contents of 2, 4, and 8 wt % were processed using a high-energy mill. Modifications of the SiO2 nanoparticles‟ surfaces with two different silane agents were carried out and their effect on the material properties were investigated. The state of dispersion of the materials processed was studied using Scanning and Transmission Electron Microscopy (SEM and TEM) micrographs. Thermogravimetric analysis (TG) were also conducted to determine the thermal stability of the nanocomposites. In addition, the processed nanocomposites were characterized by dynamic mechanical analysis (DMA) to investigate the effect of nanoparticles content and silane treatment on the viscoelastic properties and on the glass transition temperature. Finally, wear tests of the pin-on-disc type were carried out to determine the effects of the nanoparticles and the silane treatments studied. According to the results, the addition of SiO2 nanoparticles treated with silane increased the thermal stability, the storage modulus and Tg of the epoxy resin and decreased wear rate. This confirms that the interaction between the nanoparticles and the polymer chains plays a critical role on the properties of the nanocomposites

Obtenção de pós de Nb a partir da redução aluminotérmica com ignição por plasma

The aluminothermic reduction consists in an exothermic reaction between a metallic oxide and aluminum to produce the metal and the scum. The extracted melted metal of that reaction usually comes mixed with particles of Al2O3 resulting of the reduction, needing of subsequent refine to eliminate the residual impure as well as to eliminate porosities. Seeking to obtain a product in powder form with nanometric size or even submicrometric, the conventional heat source of the reaction aluminothermic , where a resistor is used (ignitor) as ignition source was substituted, for the plasma, that acts more efficient way in each particle of the sample. In that work it was used as metallic oxide the niobium pentoxide (Nb2O5) for the exothermal reaction Nb2O5 + Al. Amounts stoichiometric, substoichiometric and superestoichiometric of aluminum were used. The Nb2O5 powder was mixed with aluminum powder and milled in planetarium of high energy for a period of 6 hours. Those powders were immerged in plasm that acts in a punctual way in each particle, transfering heat, so that the reaction can be initiate and spread integrally for the whole volume of the particle. The mixture of Nb2O5 + Al was characterized through the particle size analysis by laser and X-ray diffraction (DRX) and the obtained product of reaction was characterized using the electronic microscopy of sweeping (MEV) and the formed phases were analyzed by DRX. Niobium powders with inferior sizes to 1 mm were obtained by that method. It is noticed, through the analysis of the obtained results, that is possible to accomplish the aluminothermic reduction process by plasma ignition with final particles with inferior sizes to the original oxide

Caracterização dos sedimentos superficiais de fundo do complexo recifal de Maracajaú

The study carried out in the environment of Maracajaú reef an São Roque channel, had as main objective to analyze the characteristics of sediments active locally expressed in the grains, through collections of sediments in the field, technical processing and data analyzes of sediments. Data processing were made on three main aspects: biotic composition, concentration of calcium carbonate and particle size of the sediment. Differences between the sediments of the reefs and channel were observed. It was emphasized the contribution of algae limestone in the production of carbonate, with some influence of foraminifera near the coast. The particle size distribution presented significant results for the understanding of locally sedimentary deposits. The results showed an environment of carbonate, with predominance of algae limestone, associated to unconsolidated sediments with gross granularity, besides the presence of rhodoliths in all samples.The fragmentation of biotic components and the prevalence of elliptical rhodoliths with little or no branch, indicate an environment of high energy hydrodynamics. This work is a further contribution to the understanding of sedimentology active locally in reef environments, in particular the of Maracajaú reef, by virtue of their complex ecosystem composed of a diversity of wild fauna and flora that still little studied in Brazil comparing to accelerated growth of teeth extractions and usufructs of natural resources causing often irreversible impacts to the environment

A erosão costeira e sua influência sobre a atividade petrolífera: alternativas sustentáveis na mitigação de impactos ambientais

The study area consist in high sensitivity environments located on the northern coast of Rio Grande do Norte, Northeast Brazil. The barrier island are the main geomorphological features on the coastal landscape, being naturally instable and surrounded by industrial activities like oil fields, salt industry, shrimp farms and urban areas sometimes installed parallel to the coast, combined with coast engineering interventions. High energy hydrodynamic process are responsible for the morphological instability of the coast. The study was based on remote sensing data obtained between 1954 and 2007 which consist in orbital images from Landsat, CBERS and Ikonos satellites and aerial photos. With all data integrated on GIS environment it was possible to update thematic maps of geology, geomorphology, vegetation, soil and landuse and development of multitemporal maps pointing areas with erosion and depositions of sediments, defining the critical erosion process on this region. The bigger morphological changes are related to changes on wind patterns during the year, terrestrial and sea breezes during the day, with spits and barrier island migration, opening and closing of channels like the one parallel to the coast on the area of Serra and Macau oil fields. These factors combined with the significant reduction on sediment budgets due to the loss of natural spaces to sediment reworking contribute to the low resilience which tends to be growing on the area of Serra and Macau oil fields. In front of such scenery a detailed monitoring was done in order to find technological possibilities for coastal restoration. A pilot area was defined to start the project of mangrove restore together with beach nourishment in order to minimize the effect of the erosion caused by the channel parallel to the coast, contributing to stabilize the northeast channel as the main one. It s expected that such methodology will aid the coastal environments restoration and the balance between industrial activities and coastal erosion