Efeito de adições poliméricas na aderência de pastas de cimento a tubos metálicos após ciclagem térmica

Thermal recovery methods, especially steam injection, have been used to produce heavy oils. However, these methods imply that the metallic casing-cement sheath interface is submitted to thermal cycling. As a consequence, cracking may develop due to the thermal expansion mismatch of such materials, which allows the flow of oil and gas through the cement sheath, with environmental and economical consequences. It is therefore important to anticipate interfacial discontinuities that may arise upon Thermal recovery. The present study reports a simple alternative method to measure the shear strength of casing-sheath interfaces using pushthrough geometry, applied to polymer-containing hardened cement slurries. Polyurethane and recycled tire rubber were added to Portland-bases slurries to improve the fracture energy of intrinsically brittle cement. Samples consisting of metallic casing sections surrounded by hardened polymer-cement composites were prepared and mechanically tested. The effect of thermal cycles was investigated to simulate temperature conditions encountered in steam injection recovery. The results showed that the addition of polyurethane significantly improved the shear strength of the casing-sheath interface. The strength values obtained adding 10% BWOC of polyurethane to a Portland-base slurry more than doubled with respect to that of polyurethane-free slurries. Therefore, the use of polyurethane significantly contributes to reduce the damage caused by thermal cycling to cement sheath, improving the safety conditions of oil wells and the recovery of heavy oils

Viabilidade de utilização de um compósito a partir de resíduos para a construção de casas populares

Conselho Nacional de Desenvolvimento Científico e Tecnológico

Estudo térmico e de materiais na construção de casas populares com blocos confeccionados a partir de um composto a base de cimento, gesso, eps e raspa de pneu

We built an experimental house on an UFRN´s land using blocks made by a composite consisting of cement, plaster, EPS, crushed rubber and sand. Several blocks were made from various compositions and we made preliminary tests of mechanical and thermal resistance, choosing the most appropriate proportion. PET bottles were used inside the block to provide thermal resistance. In this work, a second function was given to the bottles: to serve as a docking between the blocks, because the ends of the cylinders came out of each block on top as well as at the bottom, with the bottom cut, allowing to fit of the extremities of the upper cylinder of a block in the lower holes of the other one, which were formed by the cutting already mentioned. Minimum compression tests were performed according to ABNT standards for walls closing blocks (fence). With that house built, we did studies of thermal performance in order to ascertain conditions of comfort, checking external and internal temperatures in the walls and in the ambient, among other variables, such as wind speed and relative humidity. The resulting blocks provided adequate thermal insulation to the environment, where the walls presented differences up to 11.7 ºC between the outer and inner faces, getting the maximum temperature inside the house around 31 °C, within the so-called thermal comfort zone for warm climates. At the end of the experiments it was evident the effectiveness of that construction in order to provide thermal comfort in the internal environment of the house, as well as we could confirm the viability of building houses from recyclable materials, reducing the constructive costs, becoming a suitable alternative for low- incoming families. Moreover, besides the low cost, the proposal represents an alternative use of various recyclable materials, therefore considered an ecological solution

Viabilidade técnica da fabricação de compósito utilizando fibra de pneu na fabricação de blocos intertravados

This work aims to demonstrate the feasibility of a ceramic composite containing fiber in the rubber manufacturing interlocking blocks. Gravel, sand, cement, rubber and fiber: the processes of manufacture and assembly of blocks produced and the various formulations studied with different proportions between the constituent elements were addressed. Mechanical properties were determined for the different formulations, compressive strength, diametral compressive strength, water absorption and apparent density, obeying the rules related to each property. It was concluded that the addition of rubber fiber gave the concrete studied resistance lower than conventional concrete which can be verified on the microstructural analysis obtained by SEM, which revealed the presence of pores and the low adhesion between the fiber and the matrix compression (tire fiber / cement paste). The composite of more viable tire BCPB1 (1/2) fiber can be used in places requests as light squares, pavements, roads and other cycle as well as in the manufacture of the curb and gutter, by having compressive strength in about 20 MPa

Capacidade de carga de misturas de solo laterítico e desbastes de pneus

Government efforts have found some obstacles in achieving a better infrastructure regarding environmental preservation requirements. There is a need to develop new techniques that leave the big exploitation of environmental resources. This study measures the evaluation of the behavior of a composite formed by lateritic soil mix and tire buffings. In this way, a road embankment model was developed to assess the bearing capacity of the composite. This study measured the load capacity of the composites with 0%, 10%, 20% and 40% rubber mixed with the soil, by weight, iron plate loading tests on a simulated embankment in a metal box of 1.40 x 1.40 x 0.80 m. After four compaction layers of the composite, a plate test was performed, and then stress-settlement curves were obtained for the material. The embankments with 20% and 40% rubber content was difficult to compact. There was a significant reduction in the load capacity of the soil-plate system with increasing rubber content. The composite with the lowest loss of bearing capacity in relation to the reference soil was the one with a χ = 10%. In the load capacity tests, another aspect noted was the bearing capacity in terms of CBR. The results also show a gradual decrease in bearing capacity in the composites as with the rubber incorporation content increases. As in the plate load tests, the composite that had the lower bearing capacity loss was also that with 10% content.

Acidentes por quedas em um grupo específico de idosos

Este estudo objetivou conhecer a incidência do evento queda e identificar a presença de seus principais fatores de risco. Estudo exploratório, realizado de março a novembro/2009, com aplicação de um formulário sobre quedas em um grupo de idosos. Os dados foram analisados por cálculo de frequências, média e desvio-padrão. Participaram 62 idosos, 41,9% relataram queda nos últimos seis meses, a maioria mulheres. Identificou-se ocorrência de agravos concomitantes: visão regular, audição boa, polifarmácia, IMC normal, forte força de preensão palmar e condições dos pés adequadas. Na maioria dos que caiu, o desequilíbrio foi apontado como principal motivo. A queda ocorreu mais no período da manhã, em local de piso áspero e seco, sem degraus, rampas ou tapetes, iluminação adequada e o tipo de calçado mais utilizado foi chinelo de borracha. Percebe-se a alta ocorrência das quedas na população idosa, fato que fundamenta a necessidade de avaliação das condições de risco envolvidas

Análise de falhas em martelos oscilantes dos desfibradores da indústria sucroalcooleira da Região Norte-Nordeste

The failure of materials is always an unwelcome event for several reasons: human lives are put in danger, economic losses, and interference in the availability of products and services. Although the causes of failures and behaviour of materials can be known, the prevention of such a condition is difficult to be guaranteed. Among the failures, wear abrasion by the low voltage is the kind of failure that occurs in more equipment and parts industry. The Plants Sucroalcooleiras suffer significant losses because of such attrition, this fact that motivated their choice for the development of this work. For both, were considered failures in the swing hammers desfibradores stopped soon after the exchange provided in accordance with tonnage of cane processed, then were analyzed by the level of wear testing of rubber wheel defined by the standard ASTM G65-91.The failures were classified as to the origin of the cause and mechanism, moreover, were prepared with samples of welding procedures according to ASME code, sec. IX as well, using the technique of thermal spraying to analyze the performance of these materials produced in laboratories, and compares them with the solder used in the plant. It was observed that the bodies-of-proof prepared by the procedure described as welding, and the thermal spraying the results of losing weight have been minimized significantly compared to the preparations in the plant. This is because the use of techniques more appropriate and more controlled conditions of the parameters of welding. As for the thermal spraying, this technique has presented a satisfactory result, but requires the use of these coatings in the best condition for real affirmation of the results

Análise do comportamento reológico de pastas de cimento contendo resíduos de pneu para poços de petróleo

The low tenacity presented by the Portland cement pastes used in the oil wells cementation has been motivating several researches with attention focused on alternative materials. Additives have been developed to generate flexible pastes with mechanical resistance capable to support the expansions and retractions of the metallic covering of the wells that submit to the steam injection, technique very used to increase the recovery factor in oil reservoirs with high viscosity. A fresh paste with inadequate rheological behavior may commit the cementation process seriously, involving flaws that affect the performance of the paste substantially in the hardened state. This work proposes the elaboration and the rheological analysis of Portland cement pastes with addition of residues of rubber tire in several proportions, with the aim of minimizing the damages provoked in the hem cementing of these wells. By thermogravimetric analysis, the particles of eraser that go by the sieve of 0,5mm (35 mesh) opening and treated superficially with NaOH solution of 1 mol/L presented appropriate thermal resistance for wells that submit to thermal cyclic. The evaluation of the study based on the results of the rheological analysis of the pastes, complemented by the mechanical analysis, thickening, stability, tenor of free water and filtrate loss, being used as parameter a paste reference, without rubber addition. The results showed satisfactory rheology, passive of few corrections; considerable loss of mechanical resistance (traction and compression), compensated by earnings of tenacity, however with established limits for its application in oil wells; satisfactory stability, free water and thickening time

Estudos de Durabilidade Frente ao Ataque Ácido de Compósitos Portland-Polímero para Cimentação de Poços de Petróleo

Portland-polymers composites are promising candidates to be used as cementing material in Northeastern oil wells of Brazil containing heavy oils submitted to steam injection. In this way, it is necessary to evaluate its degradation in the commonly acidizind agents. In addition, to identify how aggressive are the different hostile environments it is an important contribution on the decision of the acidic systems to be used in. It was investigated the performance of the Portland-polymer composites using powdered polyurethane, aqueous polyurethane, rubber tire residues and a biopolymer, those were reinforced with polished carbon steel SAE 1045 to make the electrochemical measurements. HCl 15,0 %, HCl 6,0 % + HF 1,5 % (soft mud acid), HCl 12,0 % + HF 3,0 % (regular mud acid) and HAc 10 % + HF 1,5 % were used as degrading environment and electrolytes. The more aggressive acid solution to the plain Portland hardened cement paste was the regular mud acid, that showed loss of weight around 23.0 %, followed by the soft mud acid, the showed 11.0 %, 15.0 % HCl with 7,0 % and, at last the 10.0 % HAc plus HF 1.5 % with just 1.0 %. The powdered polyurethane-composite and the aqueous polyurethane one showed larger durability, with reduction around 87.0 % on the loss of weight in regular mud acid. The acid attack is superficial and it occurs as an action layer, where the degraded layer is responsible for the decrease on the kinetic of the degrading process. This behavior can be seen mainly on the Portland- aqueous polyurethane composite, because the degraded layer is impregnated with chemically modified polymer. The fact of the acid attack does not have influence on the compressive strength or fratography of the samples, in a general way, confirms that theory. The mechanism of the efficiency of the Portland-polymers composites subjected to acid attack is due to decreased porosity and permeability related with the plain Portland paste, minor quantity of Ca+2, element preferentially leached to the acidic solution, wave effect and to substitute part of the degrading bulk for the polymeric one. The electrolyte HAc 10 % + HF 1,5 % was the least aggressive one to the external corrosion of the casing, showing open circuit potentials around +250 mV compared to -130 mV to the simulated pore solution to the first 24 hours immersion. This behavior has been performed for two months at least. Similar corrosion rates were showed between both of the electrolytes, around 0.01 μA.cm-2. Total impedance values, insipient arcs and big polarization resistance capacitive arcs on the Nyquist plots, indicating passivity process, confirm its efficiency. In this way, Portlandpolymers composites are possible solutions to be succeed applied to oilwell cementing concomitant submitted to steam injection and acidizing operation and the HAc 10,0 % + HF 1,5 % is the less aggressive solution to the external corrosion of the casing