29 resultados para Canto rico em titânio
Resumo:
Recent years have seen a significant growth in surface modifications in titanium implants, resulting in shorter healing times in regions with low bone density. Among the different techniques, subtraction by chemical agents to increase oxidation has been applied for surface treatment of dental implants. However, this technique is generally unable to remove undesirable oxides, formed spontaneously during machining of titanium parts, raising costs due to additional decontamination stages. In order to solve this problem, the present study used plasma as an energy source to both remove these oxides and oxidize the titanium surface. In this respect, Ti disks were treated by hollow cathode discharge, using a variable DC power supply and vacuum system. Samples were previously submitted to a cleaning process using an atmosphere of Ar, H2 and a mixture of both, for 20 and 60 min. The most efficient cleaning condition was used for oxidation in a mixture of argon (60%) and oxygen (40%) until reaching a pressure of 2.2 mbar for 60 min at 500°C. Surfaces were characterized by scanning electron microscopy (SEM), X-ray diffraction (XRD), atomic force microscopy (AFM), adhesion and cell proliferation. SEM showed less cell spreading and a larger number of projections orfilopodia in the treated samples compared to the control sample. AFM revealed surface defects in the treated samples, with varied geometry between peaks and valleys. Biological assays showed no significant difference in cell adhesion between treated surfaces and the control. With respect to cell proliferation, the treated surface exhibited improved performance when compared to the control sample. We concluded that the process was efficient in removing primary oxides as well as in oxidizing titanium surfaces
Resumo:
This laboratory study involves the participation of a group with professionals from different areas that had contributed to the construction of a multidisciplinary knowledge, about biological response of titanium surfaces modified through thermochemical treatment by plasma. Thus, the crystalline phase was previously characterized in relation to the topography, roughness, molhability and nitrogen concentration in the samples surface. It s indispensable that materials implanted can influence in a good cellular response as well as promotes a bacteria action. Surfaces modified by plasma were exposed to different cultures such as: cellular (human osteoblastic) and bacteria (Staphylococcus epidermidis ATCC35984 and Pseudomonas aeruginosa ATCC 27853) in order to evaluate the biological response. It was evaluated the adhesion, proliferation, morphology and cellular preference of human ostheoblastic cells (HOST), as well as the formation of a biofilm and bacteria proliferation. It was still analyzed the bacteria selectivity ability in relation to the surfaces. The software Image Pro Plus was used to the counting of cells and bacteria adhered to the surface of disks. The results were submitted to the variance analysis (ANOVA), and then, by the Kruskal-Wallis test, using GraphPad Instat ® software, version 3.5 to Windows. The nitrided samples in spite of show a higher roughness and molhability showed a smaller bacteria growing and higher cellular proliferation, when compared to non treated samples, indicating that the treated material present a high efficiency to biomedical implants
Resumo:
The participation of women of more than 60 years of age in the social ritual of the creation of the Reserva de Desenvolvimento Sustentável Estadual ( Sustainable Development State Reserve ) at Ponta do Tubarão, in the state of Rio Grande do Norte, is the central object of this research. This work is an attempt to analyze the oral discourse of these women, to understand the historical participation in this ritual, pointing out the actions for dehistoricization that, in the Western world, take women out of the community scene making their roles less important or invisible as agents of social construction. The reflections that take place in this research, using as a starting point, the example of a traditional fishing community on the Brazilian coast, and denounce the mechanisms of male domination that try to silence their hábitus, such as: the discourse of power (that is responsible for the permanent division of sexual structures) and of the correspondent social and cultural division. The present research respects the oral discourse of the Elderly Women as a significant practice of community life in Diogo Lopes in Macau, Rio Grande do Norte. The creation of the community of RDSE in Ponta do Tubarão as an instrument for political and social management is also accepted here as a process conducted by various social actors that react to developmental threats that have interfered with and are still trying to interfere with the equilibrium of the regional ecosystem. The methodology used in the research is supported in the oral discourse of these women as social representations of a focus group, on which the method of the Análise do Discurso do Sujeito Coletivo (DSC) ( Collective Subject Discourse Analysis ) is applied
Resumo:
This dissertation is about an Education which is made concrete through orality and gestuality of the elderly joking masters of the territory of Mato Grande/RN and proposes a reflection about the exchange between these two knowledges and school education. Thus, it presents the following objectives: identifying the joking elderly in the region; recording their life experiences related to the jokes of the tradition and the way they realize such references at present; besides investigating and recording educative practices which consider the elderly s jokes at the present education. The investigation is supported by the metaphor in the making of a quilt as a methodological resource in the actions of measurement, choice of patches, sewing and binding off. The mapping of the territory of Mato Grande/RN has enabled the identification of seventeen joking elderly people. It considers and records their experiences with the popular amusements and from them, it discusses the ways through which the oral tradition in Mato Grande may be recognized in four categories/actions, namely, narrating, singing, dancing and getting old, which are analyzed under the studies by authors like Benjamin, Zumthor, Almeida, Porpino, among others. Finally, it also focuses the relation between the elderly, the knowledge of the tradition and the systemized education. It describes and articulates educative actions able to connect the knowledge by the joking elderly people and the knowledges taught at school, possibilities of concretization of a rebinding of knowledges which might bring orality and writing, the new and the old, science and tradition close to each other
Resumo:
Plasma DC hollow cathode has been used for film deposition by sputtering with release of neutral atoms from the cathode. The DC Plasma Ar-H2 hollow cathode currently used in the industry has proven to be effective in cleaning surfaces and thin film deposition when compared to argon plasma. When we wish to avoid the effects of ion bombardment on the substrate discharge, it uses the post-discharge region. Were generated by discharge plasma of argon and hydrogen hollow cathode deposition of thin films of titanium on glass substrate. The optical emission spectroscopy was used for the post-discharge diagnosis. The films formed were analyzed by mechanical profilometry technique. It was observed that in the spectrum of the excitation lines of argon occurred species. There are variations in the rate of deposition of titanium on the glass substrate for different process parameters such as deposition time, distance and discharge working gases. It was noted an increase in intensity of the lines of argon compared with the lines of titanium. Deposition with argon and hydrogen in glass sample observed a higher rate deposition of titanium as more closer the sample was in the discharge
Resumo:
Coordenação de Aperfeiçoamento de Pessoal de Nível Superior
Resumo:
The objective of this work is to identify, to chart and to explain the evolution of the soil occupation and the envirionment vulnerability of the areas of Canto do Amaro and Alto da Pedra, in the city of Mossoró-RN, having as base analyzes it multiweather of images of orbital remote sensors, the accomplishment of extensive integrated works of field to a Geographic Information System (GIS). With the use of inserted techniques of it analyzes space inserted in a (GIS), and related with the interpretation and analyzes of products that comes from the Remote Sensoriamento (RS.), make possible resulted significant to reach the objectives of this works. Having as support for the management of the information, the data set gotten of the most varied sources and stored in digital environment, it comes to constitute the geographic data base of this research. The previous knowledge of the spectral behavior of the natural or artificial targets, and the use of algorithms of Processing of Digital images (DIP), it facilitates the interpretation task sufficiently and searchs of new information on the spectral level. Use as background these data, was generated a varied thematic cartography was: Maps of Geology, Geomorfológicals Units soils, Vegetation and Use and Occupation of the soil. The crossing in environment SIG, of the above-mentioned maps, generated the maps of Natural and Vulnerability envirionmental of the petroliferous fields of I Canto do Amaro and Alto da Pedra-RN, working in an ambient centered in the management of waters and solid residuos, as well as the analysis of the spatial data, making possible then a more complex analysis of the studied area
Resumo:
The present experiment used cell culture to analyze the adhesion capacity of mouse mesenchymal bone marrow cells and rat periodontal ligament to different titanium surfaces. Grade II ASTM F86 titanium discs 15mm in diameter and 1.5mm thick were used and received 2 distinct surface treatments (polished and cathodic cage plasma nitriding). The cells were isolated from the mouse bone marrow and rat periodontal ligament and cultured in α-MEM basic culture medium containing antibiotics and supplemented with 10% FBS and 5% CO2, for 72 hours at 37ºC in a humidified atmosphere. Subculture cells were cultured in a 24-well plate with a density of 1 x 104 cells per well. The titanium discs were distributed in accordance with the groups, including positive controls without titanium discs. After a 24-hour culture, the cells were counted in a Neubauer chamber. The results show that both the mouse mesenchymal bone marrow cells and rat periodontal ligament cells had better adhesion to the control surface. The number of bone marrow cells adhered to the polished Ti surface was not statistically significant when compared to the same type of cell adhered to the Ti surface treated by cathodic cage plasma nitriding. However a significant difference was found between the control and polished Ti groups. In relation to periodontal ligament cell adhesion, a significant difference was only found between the control and plasma-treated Ti surfaces. When comparing equal surfaces with different cells, no statistically significant difference was observed. We can therefore conclude that titanium is a good material for mesenchymal cell adhesion and that different material surface treatments can influence this process
Resumo:
In the last years, many scientific researches in implantology have been focused on alternatives that would provide higher speed and quality in the process of osseointegration. Different treatment methods can be used to modify the topographic and chemical properties of titanium surface in order to optimize the tissue-implant reactions by a positive tissue response. This study aimed to evaluate the adhesion and proliferation of mesenchymal cells from human periodontal ligament on two different titanium surfaces, using cell culture techniques. Grade II titanium discs received different surface treatments, forming two distinct groups: polished and cathodic cage plasma nitriding. Human periodontal ligament mesenchymal cells were cultured on titanium discs in 24-well cell culture plates, at a density of 2 x 104 cells per well, including wells with no discs as positive control. Data obtained by counting the cells that adhered to the titanium surfaces (polished group and cathodic cage group) and to the plastic surface (control group), in the 24, 48 and 72-hour periods after plating, were used to analyze cell adhesion and proliferation and to obtain the cell growing curve in the different groups. The data were submitted to nonparametric analysis and the differences between groups were compared by Kruskal-Wallis and Friedman statistical tests. No statistically significant differences were found in the cells counts between the groups (p>0.05). It was concluded that both treatments produced surfaces compatible with the adhesion and proliferation of human periodontal ligament mesenchymal cells
Resumo:
TiTanate NanoTubes (TTNT) were synthesized by hydrothermal alkali treatment of TiO2 anatase followed by repeated washings with distinct degrees of proton exchange. TTNT samples with different sodium contents were characterized, as synthesized and after heattreatment (200-800ºC), by X-ray diffraction, scanning and transmission electron microscopy, electron diffraction, thermal analysis, nitrogen adsorption and spectroscopic techniques like FTIR and UV-Vis diffuse reflectance. It was demonstrated that TTNTs consist of trititanate structure with general formula NaxH2−xTi3O7·nH2O, retaining interlayer water in its multiwalled structure. The removal of sodium reduces the amount of water and contracts the interlayer space leading, combined with other factors, to increased specific surface area and mesopore volume. TTNTs are mesoporous materials with two main contributions: pores smaller than 10 nm due to the inner volume of nanotubes and larger pores within 5-60 nm attributed to the interparticles space. Chemical composition and crystal structure of TTNTs do not depend on the average crystal size of the precursor TiO2-anatase, but this parameter affects significantly the morphology and textural properties of the nanostructured product. Such dependence has been rationalized using a dissolution-recrystallization mechanism, which takes into account the dissolution rate of the starting anatase and its influence on the relative rates of growth and curving of intermediate nanosheets. The thermal stability of TTNT is defined by the sodium content and in a lower extent by the crystallinity of the starting anatase. It has been demonstrated that after losing interlayer water within the range 100-200ºC, TTNT transforms, at least partially, into an intermediate hexatitanate NaxH2−xTi6O13 still retaining the nanotubular morphology. Further thermal transformation of the nanostructured tri- and hexatitanates occurs at higher or lower temperature and follows different routes depending on the sodium content in the structure. At high sodium load (water washed samples) they sinter and grow towards bigger crystals of Na2Ti3O7 and Na2Ti6O13 in the form of rods and ribbons. In contrast, protonated TTNTs evolve to nanotubes of TiO2(B), which easily convert to anatase nanorods above 400ºC. Besides hydroxyls and Lewis acidity typical of titanium oxides, TTNTs show a small contribution of protonic acidity capable of coordinating with pyridine at 150ºC, which is lost after calcination and conversion into anatase. The isoeletric point of TTNTs was measured within the range 2.5-4.0, indicating behavior of a weak acid. Despite displaying semiconductor characteristics exhibiting typical absorption in the UV-Vis spectrum with estimated bandgap energy slightly higher than that of its TiO2 precursor, TTNTs showed very low performance in the photocatalytic degradation of cationic and anionic dyes. It was concluded that the basic reason resides in its layered titanate structure, which in comparison with the TiO2 form would be more prone to the so undesired electron-hole pair recombination, thus inhibiting the photooxidation reactions. After calcination of the protonated TTNT into anatase nanorods, the photocatalytic activity improved but not to the same level as that exhibited by its precursor anatase
Resumo:
The aim of this work was to study a series of 11 different compositions of Ti-Zr binary alloys resistance to aggressive environment, i. e., their ability to keep their surface properties and mass when exposed to them as a way to evaluate their performance as biomaterials. The first stage was devoted to the fabrication of tablets from these alloys by Plasma-Skull casting method using a Discovery Plasma machine from EDG Equipamentos, Brazil. In a second stage, the chemical composition of each produced tablet was verified. In a third stage, the specimen were submitted to: as-cast microstructure analysis via optical and scanning electron microscopy (OM and SEM), x-ray dispersive system (EDS) chemical analysis via SEM, Vickers hardness tests for mechanical evaluation and corrosion resistence tests in a 0.9% NaCl solution to simulate exposition to human saliva monitored by open circuit potential and polarization curves. From the obtained results, it was possible to infer that specimens A1 (94,07 wt% Ti and 5,93% wt% Zr), A4 (77,81 wt % Ti and 22,19 wt % Zr) and A8 (27,83 wt% Ti and 72,17 wt% Zr), presented best performance regarding to corrosion resistance, homogeneity and hardness which are necessary issues for biomaterials to be applied as orthopedic and odontological prosthesis
Resumo:
The groundwater pollution arising due to fuel leaks gas stations has presented a problem aggravating. Increasingly studies related to environmental problems such accidents and seek to propose some solutions for the treatment of groundwater and soils that are contaminated by gasoline. This study evaluated the use of molecular sieve TiSBA-15 as a catalyst for the reaction of removing of volatile organic compounds, particularly benzene, toluene, ethylbenzene and xylenes, known as BTEX, one of the main pollutants found in groundwater. The catalyst was synthesized by the method post-synthesis techniques and characterized by XSD, TG/DTG, adsorption/desorption of N2, XRF-EDX, for checking the incorporation of titanium and formation of the structure of the catalyst. The reaction occurred with the presence of hydrogen peroxide, H2O2, in aqueous medium to form hydroxyl radicals, which are needed in the process of removal of BTEX compounds. The catalytic reaction was carried out for 5 hours at 60 °C, pH to 3.0, and analyzes of the compounds were made in a gas chromatograph with a flame detection means photoionization static headspace (HS-GC-PID). The catalytic tests have shown the efficacy of using this type of catalyst for the removal of these volatile organic compounds, having a removal rate of 90.60% in the range where the catalyst was studied TiSBA-15(5,0)
Resumo:
The study of polymer blends has been an alternative method in the search field of new materials for obtaining materials with improved properties. In this work blends of poly(methyl methacrylate) (PMMA) and poly(ethylene oxide) (PEO) doped with titanium dioxide (TiO2) were studied. The PEO is a polymer semicrystalline structure varying between, 70 and 84% crystallinity, while the PMMA exhibits behavior amorphous in their structure. The use of TiO2 is related to corrosion-resistant of titanium as well as good heat transfer and other characteristics. The study of these polymer blends doped TiO2 gives the properties junction organic (polymer) and inorganic (oxide) which leads to modification of the properties of the resultant material. The blends were doped TiO2 (POE/PMMA/TiO2) in different proportions of the PMMA with the PEO and TiO2 fixed. The ratios were: 90/10/0,1; 85/15/0, 1; 80/20/0,1, 75/25/0,1 and 70/30/0,1. The resulting material was obtained in powder form and being characterized by Fourier Transformed Infrared (FTIR) Spectroscopy, Scanning Electron Microscopy (SEM), X-Ray Diffraction (XRD), Thermogravimetric Analysis (TGA) and Electrochemical Impedance Spectroscopy (EIS). The infrared spectra (IR) for the blends in different ratios showed a band at 1744 cm-1, characteristic of the C=O stretching, which increases in intensity with increasing PMMA composition, while in the spectrum of pure PEO this band is absent. This may suggest that the interaction is occurring between the polymers. In the micrographs of the blends also observed change in their surfaces with variation of the composition of PMMA, contributing to the change of the electrical properties of the material. The EIS data showed that the material exhibited conductivity of the order of 10-6 S.cm-1. The blend in the ratio B2(85/15/0, 1) showed better conductivity, σ = 1.56 x 10-6 S.cm-1. It was observed that the diffusion coefficient for the blends, B5(70/30/0, 1) was the largest, 1.07 x 10-6 m2.s-1. The XRD data showing that, with the variation in the composition of the PMMA blend crystallinity of the material is decreased reaching a minimum B3(80/20/0,1), and then increases again. Thermal analysis suggests that blends made from the material obtained can be applied at room temperature
Resumo:
The alginates are copolymers of 1→4-linked β-D-mannuronic acid (M) and α-Lguluronic acid (G) residues that are arranjed in a block structure along a linear chain. Titanium dioxide, TiO2, is a ceramic material and can exist in three distinct crystallography forms: anatase, brookite and rutile. composites of organic and inorganic materials have better properties than the components alone. Thus, this study aims to synthesize, characterize and analyze the composite NaAlg-TiO2 in the form of powder and film. The synthesis of composite powders was performed using the sol-gel process and obtain the composite film was performed using the slow evaporation process, then the composites were analyzed by infrared spectroscopy, fluorescence x ray, thermal analysis, attenuated total reflection (ATR), x ray diffraction and impedance spectroscopy. The X ray diffraction patterns of composite powders show that with increasing calcination temperature, there were no complete transition of rutile-anatase crystalline phase, since at all temperatures studied (300, 500, 700, 900 and 1100ºC) were observed peaks of anatase phase. Thermal analysis shows that at 400°C caused the decomposition of sodium alginate in sodium carbonate and above 600°C, we observe an exothermic peak related to the decomposition of sodium carbonate and in the presence of titanium dioxide becomes sodium titanate. The XRD results confirm the formation of sodium carbonate at 700ºC and the formation sodium titanate in the temperature range 900-1100ºC. The sodium titanate influenced the electrical properties of the material, because with increasing temperature there was a decrease in conductivity, probably due to the creation of Ti vacancies, since the sodium can induce the reduction of surface Ti4+ ions into Ti3+ species. The infrared spectra of the composites in the form of powder and film showed a small shift in the bands compared to the spectrum of pure alginate, indicating that these shifts, even small ones, have evidence of miscibility between the polymer and ceramic material