Estudo sobre a redução aluminotérmica de Ta2O5 e TiO2 usando descarga de cátodo oco

In this study it was used two metallic oxides, Ta2O5 and TiO2, in order to obtain metallic powders of Ta and Ti through aluminothermic reduction ignited by plasma. Ta2O5 and TiO2 powders were mixed with Al in a planetary mill, using different milling times. A thermal analysis study (DTA and TG) was carried out, in order to know the temperature to react both the mixtures. Then, these mixtures were submitted to a hollow cathode discharge, where they were reacted using aluminothermic reduction ignited by plasma. The product obtained was characterized by XRD and SEM, where it was proven the possibility of producing these metallic particles, different from the conventional process, where metallic ingots are obtained. It was verified that the aluminothermic reduction ignited by plasma is able to produce metallic powders of Ta and Ti, and a higher efficiency was observed to the process with Ta2O5-Al mixtures. Among different microstructural aspects observed, it can be noted the presence of metallic nanoparticles trapped into an Al2O3 matrix, besides acicular structures (titanium) and dendritic structures (tantalum), which are a product characteristic from a fast cooling

Síntese e caracterização de catalisadores de LaNiO3 não suportados e suportados em Al2O3 e ZrO2 para a reforma a vapor do metano

Ionic oxides with ABO3 structure, where A represents a rare earth element or an alkaline metal and B is a transition metal from group VIII of the periodic table are potential catalysts for oxidation and good candidates for steam reforming reaction. Different methods have been considered for the synthesis of the oxide materials with perovskite structure to produce a high homogeneous material with low amount of impurities and low calcination temperatures. In the current work, oxides with the LaNiO3 formula had been synthesized using the method of the polymeric precursors. The thermal treatment of the materials took place at 300 ºC for 2h. The material supported in alumina and/or zirconia was calcined at 800 ºC temperature for 4h. The samples had been characterized by the following techniques: thermogravimetry; infrared spectroscopy; X-ray diffraction; specific surface area; distribution of particle size; scanning electron microscopy and thermo-programmed reduction. The steam reforming reaction was carried out in a pilot plant using reducing atmosphere in the reactor with a mixture of 10% H2-Argon, a mass about 5g of catalyst, flowing at 50 mL.min-1. The temperature range used was 50 - 1000 oC with a heating rate of 10 oC.min-1. A thermal conductivity detector was used to analyze the gas after the water trapping, in order to permit to quantify the consumption of hydrogen for the lanthanum nickelates (LaNiO3). The results showed that lanthanum nickelate were more efficient when supported in alumina than when supported in zirconia. It was observed that the methane conversion was approximately 100% and the selectivity to hydrogen was about 70%. In all cases were verified low selectivity to CO and CO2

Redução aluminotérmica do óxido de tântalo usando uma tocha de plasma como ignitor

In this work was used a plasma torch of non transferred arc with argon as work gas, using a power supply with maximum DC current of 250 A and voltage of 30 V to activate the plasma and keep it switched on. The flame temperature was characterized by optical emission spectroscopy, through Boltzmann-plot-method. The torch has been used like igniter in the aluminothermic reduction of the mixture tantalum oxide and aluminum, seeking to obtain metallic tantalum. In heating of the reagents only one particle will be considered to study interactions between plasma-particle, seeking to determinate its fusion and residence time. The early powders were characterized by laser granulometry, scanning electron microscopy (SEM) and X-ray diffraction analysis. The final product of this reaction was characterized by SEM and X-ray diffraction. Crystallite size was calculated by the Scherrer equation and microdeformation was determined using Willamsom-Hall graph. With Rietveld method was possible to quantify the percentile in weight of the products obtained in the aluminothermic reaction. Semi-quantitative chemical analysis (EDS) confirmed the presence of metallic tantalum and Al2O3 as products of the reduction. As was waited the particle size of the metallic tantalum produced, presents values in nanometric scale due the short cooling time of those particles during the process