Falhas e complicações com o uso de prótese parcial removível inferior de extremidade livre bilateral

Aim: To determine the frequency and type of complications related to removable partial denture (RPD) less, Kennedy Class I, over time . Materials and Methods: This observational study consisted of a sample of 65 users PPR lower arches in Kennedy Class I and dentures, rehabilitated in the Department of Dentistry, Federal University of Rio Grande do Norte (UFRN). Patients were followed through periodic controls during periods of 60 days, 6 months and 1 year from installation. After the first year of control had other returns annually. The occurrence of complications or prosthetic failure was observed and recorded in a specific clinical record over 39 months. The patterns of failures observed were classified in the following situations: occurrence of traumatic ulcers after 2 months of installation, lack of retention, fracture or caries in the rest, fracture or dislocation of the artificial teeth, the larger connector fracture, fracture clip fracture support, poor support (need to reline the denture) and prosthesis fracture. Results: The incidence of complications was low frequency, being higher in the second year of use of the prosthesis. Among the complications that occurred more is the loss of retention (31.57%). Failures more severe and difficult to solve as the fracture elements of the metal structure of the PPR had low occurrence and were represented by only one case of the larger connector (5.3%) fractures. Conclusion: Removable partial dentures mandibular free end opposing of the conventional dentures have a low complication rate after 39 months of use when subjected to periodic controls

Passividade na interface prótese/pilar intermediário de infraestrutura implantossuportadas confeccionadas pela tecnologia CAD/CAM e método convencional

The objective of this research was to evaluate the passivity and strain induced in infrastructures screwed on abutments, made by CAD/CAM technology, and to compare these samples with parts manufactured by conventional casting. Using CAD/CAM technology, 4 samples were made from zirconia (Zircad) and 4 samples were manufactured from cobaltchrome (CoCrcad). The control groups were 4 specimens of cobalt-chrome, made by onepiece casting (CoCrci), for a total of 12 infrastructures. To evaluate the passivity, the infraestructures were installed on the abutments. One end was tightened and the vertical gap between the infrastructure and the prosthetic abutment was measured with scanning electron microscopy (250×). The mean strain in these infrastructures was analyzed via the photoelasticity test. A significant difference (p = 0.000) in passivity was observed between the control (CoCrci) and sample groups (CoCrcad and CoCrci). CoCrcad exhibited the best value of passivity (48.76 ± 13.45 μm) and CoCrci the worst (187.55 ± 103.63 μm), Zircad presented an intermediate value (103.81 ± 43.15 μm). When compared to the other groups, CoCrci showed the highest mean strain around the implants (17.19 ± 7.22 kPa). It was concluded that the zirconia infrastructure made by CAD / CAM showed a higher vertical marginal misfit than those made in cobalt-chromium alloy with the same methodology, however, the tension generated in the implants was similar. The CAD/CAM technology is more accurate for passivity and mean strain of infrastructure screwed on abutments than conventional manufacturing techniques