Estudo da síntese e sinterização de pós compósitos do sistema Ta-Cu

Ta-Cu bulk composites combine high mechanical resistance of the Ta with high electrical and thermal conductivity of the Cu. These are important characteristics to electrical contacts, microwave absorber and heat skinks. However, the low wettability of Ta under Cu liquid and insolubility mutual these elements come hard sintering this composite. High-energy milling (HEM) produces composite powders with high homogeneity and refines the grain size. This work focus to study Ta-20wt%Cu composite powders prepared by mechanical mixture and HEM with two different conditions of milling in a planetary ball mill and then their sintering using hydrogen plasma furnace and a resistive vacuum furnace. After milling, the powders were pressed in a steel dye at a pressure of 200 MPa. The cylindrical samples pressed were sintered by resistive vacuum furnace at 10-4torr with a sintering temperature at 1100ºC / 60 minutes and with heat rate at 10ºC/min and were sintered by plasma furnace with sintering temperatures at 550, 660 and 800ºC without isotherm under hydrogen atmosphere with heat rate at 80ºC/min. The characterizations of the powders produced were analyzed by scanning electron microscopy (SEM), x-ray diffraction (XRD) and laser granulometry. After the sintering the samples were analyzed by SEM, XRD and density and mass loss tests. The results had shown that to high intense milling condition produced composite particles with shorter milling time and amorphization of both phases after 50 hours of milling. The composite particles can produce denser structure than mixed powders, if heated above the Cu melting point. After the Cu to arrive in the melting point, liquid copper leaves the composite particles and fills the pores

Estudo da moagem de alta energia e sinterização de pós compósitos W-Cu

The Tungsten/copper composites are commonly used for electrical and thermal objectives like heat sinks and lectrical conductors, propitiating an excellent thermal and electrical conductivity. These properties are dependents of the composition, crystallite size and production process. The high energy milling of the powder of W-Cu produces an dispersion high and homogenization levels with crystallite size of W very small in the ductile Cu phase. This work discusses the effect of the HEM in preparation of the W-25Cu composite powders. Three techniques of powder preparation were utilized: milling the dry with powder of thick Cu, milling the dry with powder of fine Cu and milling the wet with powder of thick Cu. The form, size and composition of the particles of the powders milled were observed by scanning electron microscopy (SEM). The X-ray diffraction (XRD) was used to analyse the phases, lattice parameters, size and microstrain of the crystallite. The analyse of the crystalline structure of the W-25Cu powders milled made by Rietveld Method suggests the partial solid solubility of the constituent elements of the Cu in lattice of the W. This analyse shows too that the HEM produces the reduction high on the crystallite size and the increase in the lattice strain of both phases, this is more intense in the phase W

Efeito da moagem de alta energia na microestrutura e nas propriedades magnéticas do compósito wc-10%p.Co

This work a studied the high energy milling effect in microstructure and magnetic properties of the WC-10wt.%Co composite. The composite powders were prepared by mechanical mixed and milled at 2 hours, 100 hours, 200 hours and 300 hours in planetary milling. After this process the composite were compacted in stainless steel die with cylindrical county of 10 mm of diameter, at pressure 200 Mpa and sintered in a resistive furnace in argon atmosphere at 1400 oC for 5 min. The sintered composite were cutted, inlaid, sandpapered, and polished. The microestrutural parameters of the composite was analyzed by X-ray diffraction, scanning electronic microscopy, optical microscopy, hardness, magnetic propriety and Rietveld method analyze. The results shows, with milling time increase the particle size decrease, it possibility minor temperature of sintering. The increase of milling time caused allotropic transformation in cobalt phase and cold welding between particles. The cold welding caused the formation of the particle composite. The X-ray diffraction pattern of composite powders shows the WC peaks intensity decrease with the milling time increase. The X-ray diffraction pattern of the composite sintered samples shows the other phases. The magnetic measurements detected a significant increase in the coercitive field and a decrease in the saturation magnetization with milling time increase. The increase coercitive field it was also verified with decrease grain size with milling time increase. For the composite powders the increase coercitive field it was verified with particle size reduction and saturation magnetization variation is relate with the variation of free cobalt. The Rietveld method analyze shows at milling time increase the mean crystalline size of WC, and Co-cfc phases in composite sintered sample are higher than in composite powders. The mean crystallite size of Co-hc phase in composite powders is higher than in composite sintered sample. The mean lattice strains of WC, Co-hc and Co-cfc phases in composite powders are higher than in composite sintered samples. The cells parameters of the composite powder decrease at milling time increase this effect came from the particle size reduction at milling time increase. In sintered composite the cells parameters is constant with milling time increase

Caracterização de compósitos Nb-20%cu obtidos por moagem de alta energia e sinterizados por fase líquida

In this work, was studied the formation of a composite of the refractory metal niobium with copper, through the process of high-energy milling and liquid phase sintering. The HEM can be used to synthesize composite powders with high homogeneity and fine size particle distribution. It may also produce the solid solubility in immiscible systems such as Nb-Cu, or extend the solubility of systems with limited solubility. Therefore, in the immiscible system Cu-Nb, the high-energy milling was successfully used to obtain the composite powder particles. Initially, the formation of composite particles during the HEM and the effect of preparation technique on the microstructure of the material was evaluated. Four loads of Nb and Cu powders containing 20%wt Cu were synthesized by MAE in a planetary type ball mill under different periods of grinding. The influence of grinding time on the metal particles is evaluated during the process by the withdrawal of samples at intermediate times of milling. After compaction under different forces, the samples were sintered in a vacuum furnace. The liquid phase sintering of these samples prepared by HEM produced a homogeneous and fine grained. The composite particles forming the sintered samples are the addition of a hard phase (Nb) with a high melting point, and a ductile phase (Cu) with low melting point and high thermal and electrical conductivities. Based on these properties, the Nb-Cu system is a potential material for many applications, such as electrical contacts, welding electrodes, coils for generating high magnetic fields, heat sinks and microwave absorbers, which are coupled to electronic devices. The characterization techniques used in this study, were laser granulometry, used to evaluate the homogeneity and particle size, and the X-ray diffraction, in the phase identification and to analyze the crystalline structure of the powders during milling. The morphology and dispersion of the phases in the composite powder particles, as well the microstructures of the sintered samples, were observed by scanning electron microscopy (SEM). Subsequently, the sintered samples are evaluated for density and densification. And finally, they were characterized by techniques of measuring the electrical conductivity and microhardness, whose properties are analyzed as a function of the parameters for obtaining the composite

Comportamento da adição do carbeto de nióbio (nBC) na matriz metálica do aço ferrítico 15kH2mfa

The 15Kh2MFA steel is a kind of Cr-Mo-V family steels and can be used in turbines for energy generation, pressure vessels, nuclear reactors or applications where the range of temperature that the material works is between 250 to 450°C. To improve the properties of these steels increasing the service temperature and the thermal stability is add a second particle phase. These particles can be oxides, carbides, nitrites or even solid solution of some chemical elements. On this way, this work aim to study the effect of addition of 3wt% of niobium carbide in the metallic matrix of 15Kh2MFA steel. Powder metallurgy was the route employed to produce this metallic matrix composite. Two different milling conditions were performed. Condition 1: milling of pure 15Kh2MFA steel and condition 2: milling of 15Kh2MFA steel with addition of niobium carbide. A high energy milling was carried out during 5 hours. Then, these two powders were sintered in a vacuum furnace (10-4torr) at 1150 and 1250°C during 60 minutes. After sintering the samples were normalized at 950°C per 3 minutes followed by air cooling to obtain a desired microstructure. Results show that the addition of niobium carbide helps to mill faster the particles during the milling when compared with that steel without carbide. At the sintering, the niobium carbide helps to sinter increasing the density of the samples reaching a maximum density of 7.86g/cm³, better than the melted steel as received that was 7,81g/cm³. In spite this good densification, after normalizing, the niobium carbide don t contributed to increase the microhardness. The best microhardness obtained to the steel with niobium carbide was 156HV and to pure 15Kh2MFA steel was 212HV. It happened due when the niobium carbide is added to the steel a pearlitic structure was formed, and the steel without niobium carbide submitted to the same conditions reached a bainitic structure

Nanopartíulas de magnetita com oxacilina obtida por moagem de alta energia para aplicações biomédicas

The drug targeting has been the subject of extensive studies in order to develop site-specific treatments that minimize side effects and become more effective anticancer therapy. Despite considerable interest in this class, drugs like antibiotics also have limitations, and have been neglected. Using new pharmaceutical technologies, the use of magnetic vectors appear as promising candidate for drug delivery systems in several studies. Small magnetic particles bound to the drug of interest can be modulated according to the orientation of a magnet outside the body, locating and holding in a specific site. In this work, we propose the use of High Energy Milling (HEM) for synthesis of a magnetic vector with characteristics suitable for biomedical applications by intravenous administration, and for the formation of an oxacillin-carrier complex to obtain a system for treating infections caused by Staphylococcus aureus. The results of the variation of milling time showed that the size and structural properties of the formed material change with increasing milling time, and in 60 hours we found the sample closest to the ideal conditions of the material. The vector-drug system was studied in terms of structural stability and antimicrobial activity after the milling process, which revealed the integrity of the oxacillin molecule and its bactericidal action on cultures of Staphylococcus aureus ATCC

Análise do efeito do tempo da moagem de alta energia no tamanho de cristalito e microdeformação da rede cristalina do WC-Co

Hard metals are the composite developed in 1923 by Karl Schröter, with wide application because high hardness, wear resistance and toughness. It is compound by a brittle phase WC and a ductile phase Co. Mechanical properties of hardmetals are strongly dependent on the microstructure of the WC Co, and additionally affected by the microstructure of WC powders before sintering. An important feature is that the toughness and the hardness increase simultaneously with the refining of WC. Therefore, development of nanostructured WC Co hardmetal has been extensively studied. There are many methods to manufacture WC-Co hard metals, including spraying conversion process, co-precipitation, displacement reaction process, mechanochemical synthesis and high energy ball milling. High energy ball milling is a simple and efficient way of manufacturing the fine powder with nanostructure. In this process, the continuous impacts on the powders promote pronounced changes and the brittle phase is refined until nanometric scale, bring into ductile matrix, and this ductile phase is deformed, re-welded and hardened. The goal of this work was investigate the effects of highenergy milling time in the micro structural changes in the WC-Co particulate composite, particularly in the refinement of the crystallite size and lattice strain. The starting powders were WC (average particle size D50 0.87 μm) supplied by Wolfram, Berglau-u. Hutten - GMBH and Co (average particle size D50 0.93 μm) supplied by H.C.Starck. Mixing 90% WC and 10% Co in planetary ball milling at 2, 10, 20, 50, 70, 100 and 150 hours, BPR 15:1, 400 rpm. The starting powders and the milled particulate composite samples were characterized by X-ray Diffraction (XRD) and Scanning Electron Microscopy (SEM) to identify phases and morphology. The crystallite size and lattice strain were measured by Rietveld s method. This procedure allowed obtaining more precise information about the influence of each one in the microstructure. The results show that high energy milling is efficient manufacturing process of WC-Co composite, and the milling time have great influence in the microstructure of the final particles, crushing and dispersing the finely WC nanometric order in the Co particles

Síntese e caracterização estrutural e magnética da ferrita de cálcio

The calcium ferrite (Ca2Fe2O5) has a perovskite-type structure with oxygen deficiency and is used as a chemical catalyst. With the advent of nanoscience and nanotechnology, methods of preparation, physical and chemical characterizations, and the technological applications of nanoparticles have attracted great scientific interest. Calcium nanostructured ferrites were produced via high-energy milling, with subsequent heat treatment. The milling products were characterized by X-ray diffraction, magnetization and Mössbauer spectroscopy. Samples of the type Ca2Fe2O5 were obtained from the CaCO3 and Fe2O3 powder precursors, which were mixed stoichiometrically and milled for 10h and thermally treated at 700ºC, 900ºC and 1100ºC. The Mössbauer spectra of the treated samples were adjusted three subespectros: calcium ferrite (octahedral and tetrahedral sites) and a paramagnetic component, related to very small particles of calcium ferrite, which are in a superparamagnetic state. For samples beats in an atmosphere of methyl alcohol, there is a significant increase in area associated with the paramagnetic component. Hysteresis curves obtained are characteristic of a weak ferromagnetic-like material

Estudo de um compósito Nb-15%pCu obtidos por moagem de alta energia e sinterizados por fase líquida

There is great difficulty in forming a composite refractory metal niobium with copper. This is due to the fact that Nb-Cu system is almost mutually immiscible and may be neglected solubility between them. These properties hinder or prevent obtaining homogeneous and high-density structures, conventionally prepared. This study aims to analyze the use of high-energy milling process (MAE) to implement these natural difficulties, with regard to the densification of the sintered bodies. The MAE and the press were used in the preparation of powders, to obtain a fine and homogeneous distribution of the grain size. Four loads Nb and Cu powders containing 15% by weight of Cu were then milled for MAE in a planetary type ball mill under various milling times and speeds. The results obtained by MAE were analyzed by scanning electron microscopy (SEM), according to the parameters of time and grinding speed. The samples were compacted under pressure of 200 MPa, were then sintered in liquid phase in a vacuum furnace at temperatures of 1100 ° C / 60 min and 1200 ° C / 60 min. Then it was used to characterize diffraction of X-rays to identify the phases. The microstructures of the sintered samples were observed and evaluated using scanning electron microscopy (SEM). Vickers Microhardness tests were performed, obtaining higher values for the sintered bodies in the largest of the post milling times and the larger grinding speeds. It was found that the liquid phase sintering of the samples that were processed by MAE produced at the end of a homogeneous and densified structure in 77,4% relative to the value of the theoretical density of the composite

Efeito da moagem de alta energia na densificação e microestrutura do compósito AI2O3-Cu

The Cu-Al2O3 composite ceramic combines the phase of alumina, which is extremely hard and durable, yet very brittle, to metallic copper phase high ductility and high fracture toughness. These characteristics make this material a strong candidate for use as a cutting tool. Al2O3-Cu composite powders nanocrystalline and high homogeneity can be produced by high energy milling, as well as dense and better mechanical structures can be obtained by liquid phase sintering. This work investigates the effect of high-energy milling the dispersion phase Al2O3, Cu, and the influence of the content of Cu in the formation of Cu-Al2O3 composite particles. A planetary mill Pulverisatte 7 high energy was used to perform the experiments grinding. Al2O3 powder and Cu in the proportion of 5, 10 and 15% by weight of Cu were placed in a container for grinding with balls of hard metal and ethyl alcohol. A mass ratio of balls to powder of 1:5 was used. All powders were milled to 100 hours, and powder samples were collected after 2, 10, 20, 50 and 70 hours of grinding. Composite powders with compact cylindrical shape of 8 mm diameter were pressed and sintered in uniaxial matrix resistive furnace to 1200, 1300 to 1350 °C for 60 minutes under an atmosphere of argon and hydrogen. The heating rate used was 10°C/min. The powders and structures of the sintered bodies were characterized by XRD, SEM and EDS. Analysis TG, DSC and particle size were also used to characterize the milled powders, as well as dilatometry was used to observe the contraction of the sintered bodies. The density of the green and sintered bodies was measured using the geometric method (mass / volume). Vickers microhardness with a load of 500 g for 10 s were performed on sintered structures. The Cu-Al2O3 composite with 5% copper density reached 61% of theoretical density and a hardness of 129 HV when sintered at 1300 ° C for 1h. In contrast, lower densities (59 and 51% of the theoretical density) and hardness (110 HV and 105) were achieved when the copper content increases to 10 and 15%.

Estudo de duas pseudoligas de Nb-Cu obtidas pela rota da metalurgia do pó

The Nb-Cu pseudoalloys present themselves as potential substitutes for the alloys from a well known system and already commercially applied, as the W-Cu alloys, used in applications such as heat sinks, electrical contacts and coils for the generation of high magnetic fields. Because it is an immiscible system, where there is mutual insolubility and low wettability of the liquid Cu on the Nb surface, the processing route used in this work was the Powder Metallurgy. Two Nb alloys were used, with additions of 10% and 20% in weight of Cu, and times of 20, 30 and 40 hours for the high energy milling of the starting powders. The milling evolution of the powders is presented through the characterization techniques, such as the LASER diffraction for particle size, XRD, SEM, EDS, DSC, dilatometry, TEM and chemical analysis. After the milling, portions of the loads were submitted to the annealing heat treatment. The process used for the samples consolidation was the hot pressing, which has been applied both on some milled powders samples, as on the annealed powders. Subsequent heat treatments were performed in the samples at temperatures of 1000ºC (solid phase) and 1100ºC (in the Cu liquid phase). All sets of consolidated samples, and also the two sets of the heat treated, were analyzed by XRD, SEM, EDS, density and Vickers microhardness. Moreover, other Nb powder samples with 10% and 20% in weight of Cu obtained by simple mechanical mixing, were consolidated, thermally treated and characterized with the same techniques applied to the others, and the results were compared among themselves. Despite the difficulty of consolidation and densification of the two pseudoalloys of the Nb-Cu system of this study, on the route that passes through the HEM, samples were obtained with densities around 90% of the theoretical density. And, on the processing route of which were only mixed, the values reached up to 97%. Therefore, in this work are also emphasized the processes that made possible these results.

Estudo da influência da adição de níquel em alumina pela rota da metalurgia do pó

Ceramic materials alumina basis have been widely used in structural components, mainly because owning properties such as high hardness, chemical inertness and good wear resistance, however, the low toughness is a factor that compromises its use in many other applications, featuring the addition of nickel as a possible solution to this problem, in this context, this work aims to study the addition of nickel alumina using the route of powder metallurgy processing of the material. The percentage of nickel were added 2, 4 and 6 wt%; and each composition to high energy milling in a planetary mill was performed for 2, 4, 9 and 16h. Subsequently, the samples were compacted at 300 MPa and sintered in a vacuum oven at 1400⁰C for 2h. The samples were characterized as the physical and mechanical properties, observing, in general, an improvement in sinterability of the material with increasing grinding time and nickel content, and mixing with a decrease of porosity and increase of hardness, density values above 80% of theoretical were obtained. The milling time of 4 hours and addition of 2% nickel, particularly if achieved higher hardness (HV 1068.7 +/- 32.6) and density of about 99% theoretical density.

Estudo da influência da adição de níquel em alumina pela rota da metalurgia do pó

Ceramic materials alumina basis have been widely used in structural components, mainly because owning properties such as high hardness, chemical inertness and good wear resistance, however, the low toughness is a factor that compromises its use in many other applications, featuring the addition of nickel as a possible solution to this problem, in this context, this work aims to study the addition of nickel alumina using the route of powder metallurgy processing of the material. The percentage of nickel were added 2, 4 and 6 wt%; and each composition to high energy milling in a planetary mill was performed for 2, 4, 9 and 16h. Subsequently, the samples were compacted at 300 MPa and sintered in a vacuum oven at 1400⁰C for 2h. The samples were characterized as the physical and mechanical properties, observing, in general, an improvement in sinterability of the material with increasing grinding time and nickel content, and mixing with a decrease of porosity and increase of hardness, density values above 80% of theoretical were obtained. The milling time of 4 hours and addition of 2% nickel, particularly if achieved higher hardness (HV 1068.7 +/- 32.6) and density of about 99% theoretical density.

Efeito da adição de WC e Co na sinterização e propriedades mecânicas da alumina

Composites based on alumina (Al2O3), tungsten carbide (WC) and cobalt (Co) exhibit specific properties such as low density, high oxidation resistance, high melting point and high chemical inertia. That composite shows to be a promising material for application in various fields of engineering. In this work, the mechanical properties of the composite (Al2O3 – WC – Co), particularly density and hardness, were evaluated according to the effects of the variables of powder processing parameters, green compact and sintered. Powder composites with the composition of 80 wt% Al2O3, 18 wt% WC and 2 wt% Co were processed by high energy ball milling in a planetary mill for 50 hours as well as mixed by manual mixing in a glass vessel with the same proportion. Samples were collected (2, 10, 20, 30, 40 and 50 hours) during the milling process. Then, the powders were compacted in a cylindrical die with 5 mm in diameter in a uniaxial press with pressures of 200 and 400 MPa. The sintering was in two stages: first, the solid phase sintering was performed at 1126 and 1300 °C for 1 hour with a heating rate of 10 °C/min in a resistive furnace under argon atmosphere for green samples compacted in 200 and 400 MPa; the second sintering was performed on dilatometer in solid phase at 1300 °C for green sample compacted in 200 MPa, another sintering also was performed on dilatometer, this time in liquid phase at 1550 °C for green samples compacted in 200 and 400 MPa, with the same parameters used in resistive furnace. The raw materials were characterized by X – ray diffraction (XRD), X – ray fluorescence (XRF), scanning electron microscopy (SEM), energy dispersive spectroscopy (EDS) and laser particlemeter. The sintered samples were subjected to microhardness testing. The results showed that high energy milling achieved to the objectives regarding the particle size and the dispersion of composite phases. However, the hardness did not achieve to significant results, this is an indication that the composite has low fracture toughness.

Efeito da adição de WC e Co na sinterização e propriedades mecânicas da alumina

Composites based on alumina (Al2O3), tungsten carbide (WC) and cobalt (Co) exhibit specific properties such as low density, high oxidation resistance, high melting point and high chemical inertia. That composite shows to be a promising material for application in various fields of engineering. In this work, the mechanical properties of the composite (Al2O3 – WC – Co), particularly density and hardness, were evaluated according to the effects of the variables of powder processing parameters, green compact and sintered. Powder composites with the composition of 80 wt% Al2O3, 18 wt% WC and 2 wt% Co were processed by high energy ball milling in a planetary mill for 50 hours as well as mixed by manual mixing in a glass vessel with the same proportion. Samples were collected (2, 10, 20, 30, 40 and 50 hours) during the milling process. Then, the powders were compacted in a cylindrical die with 5 mm in diameter in a uniaxial press with pressures of 200 and 400 MPa. The sintering was in two stages: first, the solid phase sintering was performed at 1126 and 1300 °C for 1 hour with a heating rate of 10 °C/min in a resistive furnace under argon atmosphere for green samples compacted in 200 and 400 MPa; the second sintering was performed on dilatometer in solid phase at 1300 °C for green sample compacted in 200 MPa, another sintering also was performed on dilatometer, this time in liquid phase at 1550 °C for green samples compacted in 200 and 400 MPa, with the same parameters used in resistive furnace. The raw materials were characterized by X – ray diffraction (XRD), X – ray fluorescence (XRF), scanning electron microscopy (SEM), energy dispersive spectroscopy (EDS) and laser particlemeter. The sintered samples were subjected to microhardness testing. The results showed that high energy milling achieved to the objectives regarding the particle size and the dispersion of composite phases. However, the hardness did not achieve to significant results, this is an indication that the composite has low fracture toughness.