Extension ladders - synthesis and characterisation of new spacer-bridged tetraorganodistannoxanes

Preliminary results are described on the synthesis and characterization of novel spacer-bridged tetraorganodistannoxanes, {[[R(Cl)Sn]₂(CH₂)₂]O}₄ (n = 5 – 8, 10, 12; R = CH₂SiMe₃) containing particularly long organic spacers. In the solid state, these compounds reveal typical double-ladder structures with eight tin atoms per molecule, whereas in solution a partial and reversible rearrangement takes place to form tetraorganodistannoxanes, {[[R(Cl)Sn]₂(CH₂)_n]O}₂ (n = 5 – 8, 10, 12; R = CH₂SiMe₃), having four tin atoms per molecule.

Characterisation of a synthesised fluorescent ligand (4-acridinol-1-sulphonic acid) using nuclear magnetic resonance spectroscopy

The synthesis and complete characterisation of the fluorescent ligand, 4-acridinol-1-sulphonic acid (the acridine analogue of 8-quinolinol-5-sulfonic acid) is described. Using a judicious array of nuclear magnetic resonance spectroscopy experiments, the structural elucidation and full assignment of all proton and carbon chemical shifts were afforded. The 4-acridinol-1-sulphonic acid was found to behave in a similar manner to 8-quinolinol-5-sulphonic acid, forming fluorescent complexes with magnesium(II) and zinc(II). The uncorrected emission maxima for the metal–acridinol complexes were found to be at around 620 nm compared to 505 nm for the respective quinolinol complexes. Unfortunately, preliminary spectrofluorimetric analytical figures of merit revealed that the detection limits of the new acridinol metal complexes were one and a half orders of magnitude poorer than those attained with the corresponding quinolinol ligand. However, in contrast to 8-quinolinol-5-sulphonic acid, the 4-acridinol-1-sulphonic acid ligand showed considerable selectivity for magnesium(II) and zinc(II) over aluminium(III).

The characterisation of polycyclic aromatic hydrocarbons emissions from burning of different firewood species in Australia

Four kinds of woods used for residential heating in Australia were selected and burned under two burning conditions in a domestic wood heater installed in a laboratory. The selected wood species included pine (Pinus radiata), red gum (Eucalyptus camaldulensis), sugar gum (Eucalyptus cladocalyx) and yellow box (Eucalyptus melliodora). The two different burning conditions represented fast burning and slow burning, with the air inlet of the combustion chamber respectively ‘full open’ and ‘half open’. By sampling and analysing particulate and gaseous emissions from the burning of each load of wood under defined experimental conditions, PAHs emissions and their profiles in the particulate and gaseous phases were obtained. 16 species out of the 18 selected PAHs were detected. Of these, seven species were detected in the gaseous phase and most were lower molecular weight compounds. Similarly, more than 10 species of PAHs were detected in the particulate phase and these were mostly heavier molecular weight compounds. Under both burning conditions, emission levels for total PAHs and total genotoxic PAHs were the highest for pine and lowest for sugar gum, with red gum being the second highest, followed by yellow box. Using the specific sampling method, gaseous PAHs accounted for above 90% mass fraction of total PAHs in comparison to particulate PAHs (10%). The majority of the genotoxic PAHs were present in the particulate phase. PAHs emission levels in slow burning conditions were generally higher than those in fast burning conditions.

Characterisation of galvanneal coatings on strip steel

Galvanneal is a form of zinc-coated sheet steel, where steel is dipped in molten zinc, and then heat treated in a furnace to produce a complex iron-zinc coating. Many industries, such as automotive, use galvanneal for components fabricated from sheet steel. The microstructural properties of galvanneal have a significant influence on how well the sheet metal changes shape on stamping. By means of optical microscopy, scanning electron microscopy, and glow-discharge optical emission spectrometry, we present a study of the microstructure of several galvanneal samples, both stamped and unformed, relating the phases and morphology of the coatings to performance in stamping operations. Samples of galvanneal were subjected to different heat-treatment temperatures. The frequency of defects in stamped components was found to be related to the average alloy content in the coatings, which varied with furnace temperature. An increased average iron content in the coatings was related to increased powdering defects in stamping operations that use galvanneal coated sheet steel.

Characterisation and application of a bovine U6 promoter for expression of short hairpin RNAs

Background
The use of small interfering RNA (siRNA) molecules in animals to achieve double-stranded RNA-mediated interference (RNAi) has recently emerged as a powerful method of sequence-specific gene knockdown. As DNA-based expression of short hairpin RNA (shRNA) for RNAi may offer some advantages over chemical and in vitro synthesised siRNA, a number of vectors for expression of shRNA have been developed. These often feature polymerase III (pol. III) promoters of either mouse or human origin.
Results
To develop a shRNA expression vector specifically for bovine RNAi applications, we identified and characterised a novel bovine U6 small nuclear RNA (snRNA) promoter from bovine sequence data. This promoter is the putative bovine homologue of the human U6-8 snRNA promoter, and features a number of functional sequence elements that are characteristic of these types of pol. III promoters. A PCR based cloning strategy was used to incorporate this promoter sequence into plasmid vectors along with shRNA sequences for RNAi. The promoter was then used to express shRNAs, which resulted in the efficient knockdown of an exogenous reporter gene and an endogenous bovine gene.
Conclusion
We have mined data from the bovine genome sequencing project to identify a functional bovine U6 promoter and used the promoter sequence to construct a shRNA expression vector. The use of this native bovine promoter in shRNA expression is an important component of our future development of RNAi therapeutic and transgenic applications in bovine species.

Lipid characterisation and distribution in the fillet of the farmed Australian native fish, Murray cod (Maccullochella peelii peelii)

The objective of this study was to determine the distribution pattern of lipids and fatty acids in different tissues of farmed Murray cod (Maccullochella peelii peelii).

Differences in lipid content were found amongst different portions of the fillet, being lowest in the dorsal/cranial portion (P1) and highest in the more ventral/caudal portion (P8) (P < 0.05). The latter also recorded the highest amount of monounsaturated fatty acid (MUFA) and the lowest in polyunsaturated fatty acids (PUFA), arachidonic acid, 20:4n − 6 (ArA), docosahexaenoic acid, 22:6n − 3, (DHA) and the n3/n6 ratio. In general, lipid content in the different fillet portions was inversely correlated to PUFA and directly to MUFA. Contents of saturated fatty acids (SFA) and eicosapentaenoic acid, 20:5n − 3 (EPA) did not show any discernible trends in the different fillet portions, while significant differences in contents of DHA and ArA were observed. This study shows that lipid deposition in Murray cod varies markedly and that different fatty acids are deposited differently throughout the fillet.

Preparation and characterisation of open-cell microporous nickel

In the present study, nickel foams with an open cell microporous structure were fabricated by the so-called space-holding particle sintering method, which included the adding of a particulate polymeric material (PMMA). The average pore size of the nickel foams approximated 10.5 μm; and the porosity ranged from 70 % to 80 %. The porous characteristics of the nickel foams were observed using scanning electron microscopy and the mechanical properties were evaluated using compressive tests. For comparison, nickel foams with an open-cell macroporous structure (pore size approximately 1.3 mm) were also presented. Results indicated that the nickel foams with a microporous structure possess enhanced mechanical properties than those with a macroporous structure.

Preparation and characterisation of new titanium based alloys for orthopaedic and dental applications

Various types of titanium alloys with high strength and low elastic modulus and, at the same time, vanadium and aluminium free have been developed as surgical biomaterials in recent years. Moreover, porous metals are promising hard tissue implants in orthopaedic and dentistry, where they mimic the porous structure and the low elastic modulus of natural bone. In the present study, new biocompatible Ti-based alloy foams with approximate relative densities of 0.4, in which Sn and Nb were added as alloying metals, were synthesised through powder metallurgy method.
The new alloys were prepared by mechanical alloying and subsequently sintered at high temperature using a vacuum furnace. The characteristics and the processability of the ball milled powders and the new porous titanium-based alloys were characterised by X-ray diffraction, optical
microscopy and scanning electron microscopy .The mechanical properties of the new titanium alloys were examined by Vickers microhardness measurements and compression testing.

Precipitate characterisation of an advanced high-strength low-alloy (HSLA) steel using atom probe tomography

Increased fuel economy, combined with the need for the improved safety has generated the development of new hot-rolled high-strength low-alloy (HSLA) and multiphase steels such as dual-phase or transformation-induced plasticity steels with improved ductility without sacrificing strength and crash resistance. However, the modern multiphase steels with good strength-ductility balance showed deteriorated stretch-flangeability due to the stress concentration region between the soft ferrite and hard martensite phases [1]. Ferritic, hot-rolled steels can provide good local elongation and, in turn, good stretch-flangeability [2]. However, conventional HSLA ferritic steels only have a tensile strength of not, vert, similar600 MPa, while steels for the automotive industry are now required to have a high tensile strength of not, vert, similar780 MPa, with excellent elongation and stretch-flangeability [1]. This level of strength and stretch-flangeability can only be achieved by precipitation hardening of the ferrite matrix with very fine precipitates and by ferrite grain refinement. It has been suggested that Mo [3] and Ti [4] should be added to form carbides and decrease the coiling temperature to 650 °C since only a low precipitation temperature can provide the precipitation refinement [4]. These particles appeared to be (Ti, Mo)C, with a cubic lattice and a parameter of 0.433 nm, and they were aligned in rows [4]. It was reported [4] that the formation of these very fine carbides led to an increase in strength of not, vert, similar300 MPa. However, the detailed analysis of these particles has not been performed to date due to their nanoscale size. The aim of this work was to carry out a detailed investigation using atom probe tomography (APT) of precipitates formed in hot-rolled low-carbon steel containing additions Ti and Mo.

The investigated low-carbon steel, containing Fe–0.1C–1.24Mn–0.03Si–0.11Cr–0.11Mo–0.09Ti–0.091Al at.%, was produced by hot rolling. The processing route has been described in detail elsewhere [5] European Patent Application, 1616970 A1, 18.01.2006.[5]. The microstructure was characterised by transmission electron microscopy (TEM) on a Philips CM 20, operated at 200 kV using thin foil and carbon replica techniques. Qualitative energy dispersive X-ray spectroscopy (EDXS) was used to analyse the chemical composition of particles. The atomic level of particle characterisation was performed at the University of Sydney using a local electrode atom probe [6]. APT was carried out using a pulse repetition rate of 200 kHz and a 20% pulse fraction on the sample with temperature of 80 K. The extent of solute-enriched regions (radius of gyration) and the local solute concentrations in these regions were estimated using the maximum separation envelope method with a grid spacing of 0.1 nm [7]. A maximum separation distance between the atoms of interest of dmax = 1 nm was used.

The microstructure of the steel consisted of two types of fine ferrite grains: (i) small recrystallised grains with an average grain size of 1.4 ± 0.2 μm; and (ii) grains with a high dislocation density (5.8 ± 1.4 × 1014 m−2) and an average grain size of 1.9 ± 0.1 μm in thickness and 2.7 ± 0.1 μm in length (Fig. 1a). Some grains with high dislocation density displayed an elongated shape with Widmanstätten side plates and also the formation of cells and subgrains (Fig. 1a). The volume fraction of recrystallised grains was 34 ± 8%.

Nano- and macro-scale characterisation of the mechanical properties of bovine bone

In the present study, nano- and macro-scale characterisations on the mechanical properties of bovine cortical bones have been performed by using nanoindentation and conventional compressive tests. Nanoindentation results showed that the elastic modulus for the osteons and the interstitial lamellae in the longitude direction were 24.7 ± 2.5 GPa and 30.1 ± 2.4 GPa. As it’s difficult to distinguish osteons from interstitial lamellae in the transverse direction, the average elastic modulus for cortical bovine bone in the transverse direction was 19.8 ± 1.6 GPa. Significant differences were found in the modulus values between different microstructures of bone tissue and in different testing direction. It was found that the elastic modulus of bone bovine material in nano-level was higher than that in macro-level. The elastic modulus and
ultimate stress of large bone samples were 12.5 ± 1.9 GPa and 195 ± 19 MPa respectively from the compression test.

Characterisation of proteins in the milk of fur seals

Milk protein composition was investigated throughout the lactation periods of the Australian fur seal (Arctocephalus pusillus doriferus) and Antarctic fur seal (Arctocephalus gazella). The mean protein content of the milk was found to be 10.9% and 10.6% respectively. The concentration of total protein did not change during lactation, although a decline in casein content of the milk in late lactation was apparent. Milk protein concentration during a foraging/suckling cycle of the Antarctic fur seal analysed at the time of arrival on shore, and 24 h and 72 h after arrival was 12.8%, 11.4% and 12.5% respectively. Re-feeding animals at 72 h resulted in a significant increase in milk protein content to 14.9%. Characterisation of milk protein by SDS-PAGE analysis revealed 5 casein and 10 major whey protein bands. Amino-terminal sequencing indicated that the majority of the whey fraction of the milk is β-lactoglobulin (β-LG). The limited amino acid sequence indicated 3 different β-LGs were secreted in the milk. Subsequently, RT-PCR was used to extend the sequence of one of the β-LGs and translation of the 464 bp fragment indicated that it shared 79% sequence identity with feline β-LG II.