Texture changes during uniaxial compression of Mg-3AI-1Zn

The mechanical anisotropy of wrought Mg alloys is very high. For example the yield stress of extruded Mg-3Al-1Zn tested in tension can be as high as twice that obtained in compression [1]. To solve the problems this creates for product design it is necessary to understand the sensitivity of texture to processing parameters. Uniaxial compression tests at different temperatures were performed on cylindrical samples of an extruded Mg-3Al-1Zn bar. The texture
during this deformation changes from a situation where all crystal c-axes are nearly perpendicular to the sample axis to one where the c-axes are all nearly parallel to this axis. Compression was stopped at different strains to examine the rate of this texture change. Textures were examined using EBSD measurements. It was found that different mechanisms operate depending on the temperature of deformation and that a variety of textures can be created. Also it was seen that an annealing treatment performed after compression has an influence on the texture. Afterwards the samples were subjected to another uniaxial compression test to examine the influence of texture on room temperature properties.

Orientation dependence of the deformation microstructure in a Fe-30Ni-Nb model austenitic steel subjected to hot uniaxial compression

The present work was aimed at a detailed investigation of the orientation dependence of the microstructure characteristics in a Fe-30Ni-Nb austenitic model steel subjected to hot uniaxial compression at 1198 K (925 °C) at a strain rate of 1 s−1 to several strain levels up to 1.0. The quantification of the substructure evolution as a function of strain was performed for the stable 〈011〉 oriented grains. Other grain orientations were also investigated in detail at a strain of 0.2. The 〈110〉 oriented grains contained self-screening arrays of “microbands” (MBs) aligned with high Schmid factor {111} slip planes. The MB crystallographic alignment was largely maintained up to a strain of 1.0, which suggests that the corresponding boundaries kept continuously rearranging themselves during straining and did not follow the sample shape change. The mean MB spacing decreased and misorientation angle increased with strain towards saturation, indicating the operation of the “repolygonization” dynamic recovery mechanism. The non-〈011〉 oriented grains displayed a strong tendency to split during deformation into deformation bands having alternating orientations and being mutually rotated by large angles. The bands were separated by transition regions comprising arrays of closely spaced, extended sub-boundaries collectively accommodating large misorientations across very small distances.