Influence of deformation conditions and texture on the high temperature flow stress of magnesium AZ31

The evolution of hot working flow stress with strain is examined in torsion, uniaxial compression and channel die compression. The flow stress was found to be strongly dependent on texture and deformation mode. At low strains this dependency accounted for a difference in flow stress of up to a factor of two. At higher strains the influence of texture and deformation mode was less marked. The stresses corresponding to an equivalent strain of 0.5 were modelled using a power law expression with an activation energy of 147 kJ/mol and a strain rate exponent of 0.15. The influence of texture and deformation mode on flow stress is rationalised in terms of the influence of prismatic slip, twinning and dynamic recrystallisation on deformation stress and structure.

Ultrafine grained ferrite formed by interrupted hot torsion deformation of plain carbon steel

A plain carbon steel was deformed using a hot torsion deformation simulator. A schedule known to produce strain-induced ferrite was used with the strain interrupted for increasing intervals of time to determine the effect of an isothermal hold on the final microstructure. Microscopy and electron back-scattered diffraction (EBSD) were used to analyse the changes that occurred in the partially transformed microstructure during the hold and the subsequent applied strain. The strain-induced ferrite coarsened during the hold and this coarsened ferrite was refined during the second deformation. These results were compared to those obtained for a different plain carbon steel deformed in single pass rolling close to the Ar3 temperature.

Effect of deformation schedule on the microstructure and mechanical properties of a thermomechanically processed C-Mn-Si transformation-induced plasticity steel

Thermomechanical processing simulations were performed using a hot-torsion machine, in order to develop a comprehensive understanding of the effect of severe deformation in the recrystallized and nonrecrystallized austenite regions on the microstructural evolution and mechanical properties of the 0.2 wt pct C-1.55 wt pct Mn-1.5 wt pct Si transformation-induced plasticity (TRIP) steel. The deformation schedule affected all constituents (polygonal ferrite, bainite in different morphologies, retained austenite, and martensite) of the multiphased TRIP steel microstructure. The complex relationships between the volume fraction of the retained austenite, the morphology and distribution of all phases present in the microstructure, and the mechanical properties of TRIP steel were revealed. The bainite morphology had a more pronounced effect on the mechanical behavior than the refinement of the microstructure. The improvement of the mechanical properties of TRIP steel was achieved by variation of the volume fraction of the retained austenite rather than the overall refinement of the microstructure.

Influence of grain size on the compressive deformation of wrought Mg-3A1-1Zn

The influence of the grain size on the flow stress of extruded Mg–3Al–1Zn tested in compression is examined. Samples with grain sizes varying between 3 and 23 μm were prepared by altering the extrusion conditions. Compression testing of the extruded bar was carried out at temperatures between ambient and 200 °C. Twinning dominated the deformation at lower temperatures but this gave way to slip dominated flow when the temperature was raised. For tests carried out at intermediate temperatures, a similar transition was observed when the grain size was reduced. The transition was accompanied by a change in flow curve shape and Hall–Petch slope. The peak stresses achieved when twinning dominated the deformation were up to 100 MPa greater than those seen when slip dominated the flow. Critical grain sizes marking the twinning–slip transition were identified and these are described in terms of the deformation conditions.

Generating misorientations in shear deformation structures

Of considerable importance to the generation of ultrafine microstructures is the development of high misorientations. The present work examines the effect of the crystallographic rotation field in simple shear upon the evolution of misorientation during plastic working. A series of Taylor simulations are presented and it is shown that the rotation field is such that small differences in orientation in the region of the main torsion texture components are considerably increased with the application of shear strain. This did not occur in simulations of rolling. The torsion simulations compare favourably with the nature of the misorientations evident in hot worked 1050 Al and Ti-IF steel. It is concluded that shear deformation, by its nature, facilitates the generation of higher misorientations.

Effect of grain size on the deformation and dynamic recrystallization of mg-3AI-1Zn

The influence of grain size on the deformation of extruded Mg-3Al-1Zn tested in tension at temperatures between room temperature and 300°C is investigated. The results enable estimation of the deformation conditions for the transition from slip to twinning dominated flow and for the initiation and completion of dynamic recrystallization. A map illustrating these critical parameters is constructed and it is shown that the operating conditions of the common wrought processes straddle key transitions in microstructure behaviour.

Grain size effect on the warm deformation behaviour of a Ti-IF steel

The effect of grain size on the warm deformation behaviour of a titanium stabilized interstitial free (IF) steel was investigated using hot torsion. The initial work hardening regime is followed by the development of a broad stress peak after which work softening occurs. The hypothetical saturation stress (Estrin–Mecking model) and the stress at final strain were relatively insensitive to grain size. However, the strain to the peak stress was strongly dependent on the grain size at low values of the Zener–Hollomon parameter. A simple phenomenological approach, using a combined Estrin–Mecking model and an Avrami type equation, was used to model the flow curves. The hypothetical saturation stress, the stress at final strain and the strain to peak stress were modelled using three different hyperbolic sine laws. A comparison with independent data from the literature shows that the apparent activation energy of deformation determined in this work (Q=372 kJ/mol) can be used to rationalize the steady-state stress in compression data found in the literature.

Static and metadynamic recrystallization of interstitial free steels during hot deformation

A rapid method was used to identify kinetics of the recrystallization for two IF (Interstitial Free) steels which have different phosphorous and boron contents. The static and metadynamic softening behaviour of the materials for a range of strain rates and temperatures were quantified. The critical strain for initiation of strain independent softening was estimated for the IF steels in respect to the time for 50 percent softening after deformation. The results showed that the strain for the initiation of strain independent softening (often referred to as metadynamic recrystallization) varies with the Zener Hollomon parameter. Classic static recrystallization was observed at strains below the strain independent softening for all processing conditions and the strain rate had a strong effect on the time for strain independent softening. Results also revealed that static and metadynamic recrystallization was delayed owing to the phosphorous and boron alloying elements. Hence, the large strain at above no-recrystallization temperature may be required for the early stage of Finishing Stands Unit (FSU) in hot strip rolling mills to initiate austenite grain refinement of phosphorous and boron added IF steels.

Observation of deformation modes in Mg-3Al-1Zn

Since magnesium alloys are the lightest metallic materials, they are very attractive for automotive and aerospace industries. The main problem of these alloys is limited ductility due to a shortage of independent slip systems. In order to improve the formability in these alloys, an understanding of the deformation modes is required. In the present work, different slip systems were investigated in rolled Mg-3Al-IZn by means of in situ tensile tests in the SEM. These permitted electron backscatter diffraction (EBSD) and electron backscatter diffraction imaging (QBSD) to be carried out during the test. The results show that non-basal slip systems are active at room temperature.

Mapping the hot deformation microstructure of Ni-30Fe alloy

The evolution of structure during the hot working of an austenitic Ni-30%Fe alloy is studied using EBSD analysis of samples tested in torsion. A microstructural map in temperature-strain space that plots grain size, cell size, fracture and dynamic recrystallization is presented.

EBSD analysis of deformation modes in Mg-3A1-1Zn

Wrought magnesium alloys exhibit poor cold formability and the accepted explanation is the shortage of independent slip systems. In order to improve the formability in these alloys, an understanding of the deformation modes is required. In the present work, activation of different slip and twinning systems are investigated in rolled Mg–3Al–1Zn using electron back scattering diffraction. Analysis was performed on deformed surfaces and on metallographically prepared cross-sections following deformation at room temperature. The results reinforce the importance of prismatic slip and c-axis compression double twinning.

Deformation and annealing of (011)[011] oriented A1 single crystals

High purity Al single crystals of the (011)[011] orientation have been deformed in plane strain compression in a channel die. Deformation was carried out at a strain rate of 0.01 s−1 to true strains of 0.5 and 1.0, and at temperatures of 25, 200 and 300 °C. The as-deformed microstructure has been characterized using electron backscattered diffraction (EBSD) and X-ray diffraction (XRD). No recrystallization was detected after deformation, and the deformation texture analysis showed that the stability of the orientation decreased with increasing temperature, contrary to reports for other orientations.

Annealing was carried out for various times at 300 °C. Nucleation of recrystallization exhibited periodicity, with distinct bands of recrystallized grains forming parallel to the transverse direction. This recrystallized microstructure has been examined using EBSD. A model is proposed to account for the origin of the periodicity of nucleation and the retention of rods or cylinders of unrecrystallized material after significant annealing times.

Effect of transformation volume contraction on the toughness of superelastic shape memory alloys

Shape memory alloys (SMAs) exhibit two very important properties: shape memory phenomenon and superelastic deformation due to intrinsic thermoelastic martensitic transformation. To fully exploit the potential of SMAs in developing functional structures or smart structures in mechanical and biomechanical engineering, it is important to understand and quantify the failure mechanisms of SMAs. This paper presents a theoretical study of the effect of phase-transformation-induced volume contraction on the fracture properties of superelastic SMAs. A simple model is employed to account for the forward and reverse phase transformation with pure volume change, which is then applied to numerically study the transformation field near the tip of a tensile crack. The results reveal that during steady-state crack propagation, the transformation zone extends ahead of the crack tip due to forward transformation while partial reverse transformation occurs in the wake. Furthermore, as a result of the volume contraction associated with the austenite-to-martensite transformation, the induced stress-intensity factor is positive. This is in stark contrast with the negative stress-intensity factor achieved in zirconia ceramics, which undergoes volume expansion during phase transformation. The reverse transformation has been found to have a negligible effect on the induced stress-intensity factor. An important implication of the present results is that the phase transformation with volume contraction in SMAs tends to reduce their fracture resistance and increase the brittleness.