Effect of relaxation on pressure sensitivity index in a Zr-based metallic glass

Shear-banding features of as-cast and annealed Zr_41.2Ti_13.8Cu_12.5Ni₁₀Be_22.5 bulk metallic glass were investigated through Rockwell indentation tests. Isothermal annealing of the as-cast samples was conducted at temperatures below its glass transition temperature, Tg. The exothermal enthalpy during continuous heating below Tg decreases with increasing annealing temperature, indicating the gradual reduction of free-volume upon annealing. The observation on the morphology of shear-banding pattern around the indents implies a reduced shear bands activity in the annealed samples. The included angles (2θ) between two families of shear bands emanating from the edge of Rockwell indent decrease from 88° for the as-cast sample to 79° for the sample annealed at 633 K for 1 h, indicating a pressure sensitive plasticity. By Mohr–Coulomb criterion, the pressure sensitive index can be obtained on the basis of the measured 2θ, which increases with increasing annealing temperature, indicating an increase of “atomistic friction” due to the reduction of the free volume upon annealing.

Indentation study on the pressure sensitivity of a ZR-based bulk metallic glass

Spherical indentation test was conducted on as-cast and annealed Zr_41.2Ti_13.8Cu_12.5Ni₁₀Be_22.5 bulk metallic glass, and the evolution of the morphology of the deformation zone of indents upon annealing was investigated. The DSC traces of the as-cast and annealed samples show that the enthalpy change at the glass transition, ΔH, decreases with the increasing of annealing temperature, indicating the reduction of the free volume upon annealing. The morphology of the indents implies a reduced shear band activity in the annealed samples. The included angles (2θ) between two families of shear bands emanating from the edge of spherical indent in the as-cast and the annealed samples were measured to be in the range of 88-79°, which decrease with the increasing of annealing temperature, indicating pressure sensitive plasticity in the as-cast and annealed samples. By Mohr–Coulomb criterion, the pressure sensitive index, α, can be obtained on the basis of the measured 2θ. The sensitivity index increases with increasing temperature, implying an increase of 'atomistic friction' due to the reduction of the free volume upon annealing.

The effect of humidity and temperature on Wool Comfort Meter assessment of single jersey wool fabrics

The Wool ComfortMeter provides an objective measurement of the fabric-evoked prickle discomfort rating provided by wearers. This work aimed to quantify the sensitivity of the Wool ComfortMeter over a range of different temperature and humidity conditions to determine the recommended test conditions for its operation. The design was: three temperatures (notionally 20, 25 and 30°C) at three relative humidities (RHs, notionally 50, 65 and 80%) each with two replicates, using six different wool single jersey knits (mean fibre diameter 19.5–27.0 µm). As it was difficult to achieve exactly some of the extreme combinations of temperature and RH, some combinations were repeated, providing a total of 23 different assessment conditions. Data were analysed using restricted maximum likelihood mixed model analysis. The best fixed model included RH, RH2, temperature and the interaction of temperature and RH, accounting for 95% of the variation in Wool ComfortMeter readings. Wool ComfortMeter values were almost constant at 55–60% RH. Generally, the Wool ComfortMeter value reduced with increasing RH > 60% at temperatures of 25°C and 28.5°C as the regain of the fabric increased. However, at 20°C little change was detected as RH was increased from 50 to 80% as there were only small changes in fabric regain. The observed effects were in a good agreement with existing knowledge on the effect of regain on the mechanical properties of wool fibre. Wool ComfortMeter is best operated under standard conditions for textile testing of 65% RH and 20°C.

Personality and plasticity: consistent responses within-, but not across-temperature situations in crabs

Recent research suggests that repeated assays of behaviour, conducted both within and across situations, could reveal important insights into two traditionally distinct areas of study: animal personality and individual differences in behavioural plasticity. However, at present relatively few studies present such data, and few consider how changing abiotic conditions affect behavioural plasticity. Individual differences in metabolic rate have been suggested as a proximate mechanism promoting personality, leading one to speculate that individual differences in metabolic sensitivity to temperature may affect behavioural responses in ectotherms. At present, only one study (out of two) has tested for and shown individual differences in behavioural responses to temperature. Here, we repeatedly assayed the behaviour of a marine crab across a narrow range of temperatures to test for individual differences in responses to temperature. We observed large inter-individual differences in behaviour that were consistent over time at a given temperature (evidence for personality), and individual differences in responses to temperature (evidence for plasticity). This study adds to the very scant literature on ectotherm behavioural sensitivity to temperature, and suggests the phenomenon might be widespread. We speculate about the role of metabolism as a proximate mechanism that might explain these individual differences in plasticity and make suggestions for future research to test this hypothesis. © Koninklijke Brill NV, Leiden, The Netherlands.

Highly sensitive SnO2 nanofiber chemiresistors with a low optimal operating temperature: synergistic effect of Cu2+/Au co-doping

Metal oxide chemiresistors (MOCs) with a low optimal operating temperature, high sensitivity and fast response/recovery are highly promising for various applications, but remain challenging to realize. Herein, we demonstrate that SnO2 nanofibers after being co-doped with Cu2+ and Au show considerably enhanced sensing performances at an unexpectedly decreased operating temperature. A synergistic effect occurs when the two dopants are introduced together. Co-doping may form a novel strategy to the development of ultrasensitive MOCs working at a low optimal temperature. This journal is © the Partner Organisations 2014.

Sensitivity of the final properties of tailored hot stamping components to the process and material parameters

The final mechanical properties of hot stamped components are affected by many process and material parameters due to the multidisciplinary nature of this thermal-mechanical-metallurgical process. The phase transformation, which depends on the temperature field and history, determines the final microstructure and consequently the final mechanical properties. Tailored hot stamping parts - where the cooling rates are locally chosen to achieve structures with graded properties - has been increasingly adopted in the automotive industry. In this case, the robustness of final part properties is more critical than in the conventional hot stamping parts, where the part is fully quenched. In this study, a wide range of input parameters in a generalized hot stamping model have been investigated, examining the effect on the temperature history and resulting final material properties. A generic thermo-mechanical finite element model of hot stamping was created and a modified phase transformation model, based on Scheil's additive principle, has been applied. The comparison between modeling and experiments shows that the modified phase transformation model coupled with the incubation time provides higher accuracy on the simulation of transformation kinetics history. The robustness of four conditions relevant to tailored hot stamping was investigated: heated tooling (with low and high tool conductance), air cooling, and conventional hot stamping. The results show the high robustness of the conventional hot stamping compared to tailored hot stamping, with respect to the stamped component's final material properties (i.e. phase fraction and hardness). Furthermore, tailored hot stamping showed higher robustness when low conductivity tools are used relative to high conductivity tools.

Seawater temperature effect on metal accumulation and toxicity in the subantarctic Macquarie Island isopod, Exosphaeroma gigas

Very little is currently known of subantarctic nearshore invertebrates' sensitivity to environmental metals and the role of temperature in this relationship. This study investigated Cu and Zn toxicity in the common subantarctic intertidal isopod, Exosphaeroma gigas, and the influence of temperature on Cu toxicity and bioaccumulation kinetics. Adult E. gigas are insensitive to Cu and Zn at concentrations of 3200 and 7400μg/L respectively in non-renewal tests at 5.5°C (ambient subtidal temperature) over 14days. Under renewed exposures over the same temperature and time period the LC50 for copper was 2204μg/L. A 10-fold increase in Cu body burden occurred relative to zinc, indicating E. gigas has different strategies for regulating the two metals. Copper toxicity and time to mortality both increased with elevated temperature. However, temperature did not significantly affect Cu uptake rate and efflux rate constants derived from biodynamic modelling at lower Cu concentrations. These results may be attributable to E. gigas being an intertidal species with physiological mechanisms adapted to fluctuating environmental conditions. Cu concentrations required to elicit a toxicity response indicates that E. gigas would not be directly threatened by current levels of Cu or Zn present in Macquarie Island intertidal habitats, with the associated elevated temperature fluctuations. This study provides evidence that the sensitivity of this subantarctic intertidal species to metal contaminants is not as high as expected, and which has significance for the derivation of relevant guidelines specific to this distinct subpolar region of the world.

Strain sensors with adjustable sensitivity by tailoring the microstructure of graphene aerogel/PDMS nanocomposites

Strain sensors with high elastic limit and high sensitivity are required to meet the rising demand for wearable electronics. Here, we present the fabrication of highly sensitive strain sensors based on nanocomposites consisting of graphene aerogel (GA) and polydimethylsiloxane (PDMS), with the primary focus being to tune the sensitivity of the sensors by tailoring the cellular microstructure through controlling the manufacturing processes. The resultant nanocomposite sensors exhibit a high sensitivity with a gauge factor of up to approximately 61.3. Of significant importance is that the sensitivity of the strain sensors can be readily altered by changing the concentration of the precursor (i.e., an aqueous dispersion of graphene oxide) and the freezing temperature used to process the GA. The results reveal that these two parameters control the cell size and cell-wall thickness of the resultant GA, which may be correlated to the observed variations in the sensitivities of the strain sensors. The higher is the concentration of graphene oxide, then the lower is the sensitivity of the resultant nanocomposite strain sensor. Upon increasing the freezing temperature from −196 to −20 °C, the sensitivity increases and reaches a maximum value of 61.3 at −50 °C and then decreases with a further increase in freezing temperature to −20 °C. Furthermore, the strain sensors offer excellent durability and stability, with their piezoresistivities remaining virtually unchanged even after 10 000 cycles of high-strain loading−unloading. These novel findings pave the way to custom design strain sensors with a desirable piezoresistive behavior.