Comparative study on thermodynamical and electrochemical behavior of Al88Ni6La6 and Al86Ni6La6Cu2 amorphous alloys

Two amorphous ribbons with the compositions of Al₈₈Ni₆La₆ and Al₈₆Ni₆La₆Cu₂ were made using the meltspun method, and their thermal response and electrochemical behavior were studied comparatively. Differential scanning calorimetry (DSC) and electrochemical polarization measurements indicated that Al₈₆Ni₆La₆Cu₂ exhibited slightly higher crystallization temperature (T_x), lower melting point (T₁) and better corrosion resistance in 0.01 mol · L⁻¹ NaCl alkaline solution. These results demonstrated that Cu (2%) addition could slightly promote the glass forming ability, but it could greatly improve the corrosion resistance of Al₈₈Ni₆La₆ alloy in 0.01 mol · L⁻¹ NaCl alkaline solution.

Extrusion properties of a Zr-based bulk metallic glass

The extrusion behavior of Zr_41.2Ti_13.8Cu_12.5Ni₁₀Be_22.5 metallic glasses in the supercooled liquid region was investigated. Good extrusion formability was observed under low strain rates at temperatures higher than 395 °C. The metallic glasses were fully extruded without crystallization and failure within the range of T=395–415 °C under strain rates from 5×10⁻³ s⁻¹ to 5×10⁻² s⁻¹, and the deformation behavior of the metallic glasses during the extrusion was found to be in a Newtonian viscous flow mode by a strain rate sensitivity of 1.0.

Compressive deformation and damage of Mg-based metallic glass interpenetrating phase composite containing 30-70 vol% titanium

Mg-based metallic glass interpenetrating phase composites (IPCs) containing 30-70 vol% titanium was fabricated in this study. The effects of reinforced phase volume fraction and interspace on the mechanical properties were investigated systematically. With increasing the volume fraction of titanium, the fracture strength and strain increased up to 1860 MPa and 44%, respectively. The results showed that the critical volume fraction (around 40%) of Ti metal should be required for significantly improving plasticity of IPC. Decreasing the interspace of the titanium phase could lead to enhancement of yield and fracture strength. The deformation behavior and strengthening mechanisms were discussed in detail.

Conjugated polymer−titania nanoparticle hybrid films : random lasing action and ultrasensitive detection of explosive vapors

We have first demonstrated that a random laser action generated by a hybrid film composed of a semiconducting organic polymer (SOP) and TiO₂ nanoparticles can be used to detect 2,4,6-trinitrotoluene (TNT) vapors. The hybrid film was fabricated by spin-casting SOP solution dispersed with nanosized TiO₂ particles on quartz glass. The SOP in the hybrid film functioned as both the gain medium and the sensory transducer. A random lasing action was observed with a certain pump power when the size (diameter of 50 nm) and concentration (8.9 - 10¹²/cm³) of TiO₂ nanoparticles were optimized. Measurements of fluorescence quenching behavior of the hybrid film in TNT vapor atmosphere (10 ppb) showed that attenuated lasing in optically pumped hybrid film displayed a sensitivity to vapors of explosives more than 20 times higher than was observed from spontaneous emission. This phenomenon has been explained with the four-level laser model. Since the sensory transducer used in the hybrid polymer/nanoparticles system could be replaced by other functional materials, the concept developed could be extended to more general domains of chemical or environment detection.

Effect of the degree of crystallinity on the electrochemical behavior of Mg65Cu25Y10 and Mg70Zn25Ca5 bulk metallic glasses

The effect of varying the percent crystallinity on the electrochemical behavior of Mg65Cu25Y10 and Mg70Zn25Ca5 bulk metallic glasses was studied. The alloys were heat-treated to achieve desired microstructures ranging from fully amorphous to fully crystalline, providing a systematic basis for subsequent testing. Potentiodynamic experiments in 0.01 M sodium chloride (NaCl) were used, whereby both the amorphous and partially crystallized samples were observed to have more noble corrosion potentials and lower anodic kinetics. However, this was accompanied by more rapid cathodic kinetics relative to their fully crystalline counterparts, meaning that corrosion rates were not significantly lower in the amorphous state. To describe the electrochemical response as a function of the degree of crystallinity, differential scanning calorimetry (DSC), scanning electron microscopy, x-ray diffraction (XRD), and electrical conductivity measurements were undertaken, where it was found that crystallinity alone is not necessarily the controlling factor and microchemistry that evolves upon devitrification, plays a key role in the electrochemical response of these materials.