Polypyrrole-coated electrospun nanofibre membranes for recovery of Au(III) from aqueous solution

In this paper, for the first time, polypyrrole-coated electrospun nanofibre mats have been used as separation membranes to electrolessly recover Au from aqueous [Au(III)Cl₄]− solutions, based on a continuous-flow membrane separation process. With a [Au(III)Cl₄]− solution passing through the nanofibre membrane, the Au(III) ions were converted into elemental Au. The gold recovered was deposited on the nanofibre membranes in the form of Au particles, as confirmed by EDX and XPS measurements. It has been found that the polypyrrole-coated electrospun nanofibres are good candidate membrane material for the recovery of Au, and the recovery efficiency is affected by the membrane thickness, the permeate flux rate and the initial [Au(III)Cl₄]− concentration.

Exposure to As(III) and As(V) changes the Ca²⁺-activation properties of the two major fibre types from the chelae of the freshwater crustacean Cherax destructor

Arsenic is a known carcinogen found in the soil in gold mining regions at concentrations thousands of times greater than gold. Mining releases arsenic into the environment and surrounding water bodies. The main chemical forms of arsenic found in the environment are inorganic arsenite (As(III)) and arsenate (As(V)). Yabbies (Cherax destructor) accumulate arsenic at levels comparable to those in the sediment of their environment but the effect on their physiological function is not known. The effects of arsenic exposure (10 ppm sodium arsenite, AsNaO2 - 5.7 ppm As(III)) and 10 ppm arsenic acid, Na2HAsO4·7H2O - 2.6 ppm As(V)) for 40 days on the contractile function of the two major fibre types from the chelae were determined. After exposure, individual fibres were isolated from the chela, "skinned" (membrane removed) and attached to the force recording apparatus. Contraction was induced in solutions containing increasing [Ca(2+)] until a maximum Ca(2+)-activation was obtained. Submaximal force responses were plotted as a percentage of the maximum Ca(2+)-activated force. As(V) exposure resulted in lower levels of calcium required for activation than As(III) indicating an increased sensitivity to Ca(2+) after long term exposure to arsenate compared to arsenite. Myosin heavy chain and tropomyosin content in individual fibres was also decreased as a result of arsenic exposure. Single fibres exposed to As(V) produced significantly more force than muscle fibres from control animals. Long-term exposure of yabbies to arsenic alters the contractile function of the two major fibre types in the chelae.

Synthesis of a porous sheet-like V₂O₅-CNT nanocomposite using an ice-templating 'bricks-and-mortar' assembly approach as a high-capacity, long cyclelife cathode material for lithium-ion batteries

Tailoring the nanostructures of electrode materials is an effective way to enhance their electrochemical performance for energy storage. Herein, an ice-templating "bricks-and-mortar" assembly approach is reported to make ribbon-like V2O5 nanoparticles and CNTs integrated into a two-dimensional (2D) porous sheet-like V2O5-CNT nanocomposite. The obtained sheet-like V2O5-CNT nanocomposite possesses unique structural characteristics, including a hierarchical porous structure, 2D morphology, large specific surface area and internal conducting networks, which lead to superior electrochemical performances in terms of long-term cyclability and significantly enhanced rate capability when used as a cathode material for LIBs. The sheet-like V2O5-CNT nanocomposite can charge/discharge at high rates of 5C, 10C and 20C, with discharge capacities of approximately 240 mA h g-1, 180 mA h g-1, and 160 mA h g-1, respectively. It also retains 71% of the initial discharge capacity after 300 cycles at a high rate of 5C, with only 0.097% capacity loss per cycle. The rate capability and cycling performance of the sheet-like V2O5-CNT nanocomposite are significantly better than those of commercial V2O5 and most of the reported V2O5 nanocomposite.