Ilmenite FeTiO3 nanoflowers and their pseudocapacitance

Pronounced and stable pseudocapacitance has been found in flowerlike FeTiO3 nanostructures that were synthesized from ball-milled ilmenite (natural mineral) under mild hydrothermal conditions. Each nanoflower is composed of many thin petals with a thickness of 5–20 nm and a width of 100–200 nm. The formation of these flowerlike nanostructures is attributed to a dissolution–precipitation mechanism involving an intermediate sodium-containing phase. Electrochemical properties of the obtained FeTiO3 nanostructures are evaluated in aqueous electrolytes. The capacitance of 122 ± 14.5 F/g is measured in 1 M KOH aqueous electrolyte at the current rate of 500 mA/g, and 50 ± 6 F/g is retained at 5 A/g. The material has good long-term cycling stability. According to our data, FeTiO3 nanostructures show functionality as an electrode material for supercapacitors.

Gamma-irradiated carbon nanotube yarn as substrate for high-performance fiber supercapacitors

As an electrical double layer capacitor, dry-spun carbon nanotube yarn possesses relatively low specific capacitance. This can be significantly increased as a result of the pseudocapacitance of functional groups on the carbon nanotubes developed by oxidation using a gamma irradiation treatment in the presence of air. When coated with high-performance polyaniline nanowires, the gamma-irradiated carbon nanotube yarn acts as a high-strength reinforcement and a high-efficiency current collector in two-ply yarn supercapacitors for transporting charges generated along the long electrodes. The resulting supercapacitors demonstrate excellent electrochemical performance, cycle stability, and resistance to folding-unfolding that are required in wearable electronic textiles.