Graphene nanodots-encaged porous gold electrode fabricated via ion beam sputtering deposition for electrochemical analysis of heavy metal ions

All rights reserved. A graphene nanodots-encaged porous gold electrode via ion beam sputtering deposition (IBSD) for electrochemical sensing is presented. The electrodes were fabricated using Au target, and a composite target of Al and graphene, which were simultaneously sputtered onto glass substrates by Ar ion beam, followed with hydrochloric acid corrosion. The as-prepared graphene nanodots-encaged porous gold electrodes were then used for the analysis of heavy metal ions, e.g. Cu2+ and Pb2+ by Osteryoung square wave voltammetry (OSWV). These porous electrodes exhibited enhanced detection range for the heavy metal ions due to the entrapped graphene nanodots in 3-D porous structure. In addition, it was also found that when the thickness of porous electrode reached 40 nm the detection sensitivity came into saturation. The linear detection range is 0.009-4 μM for Cu2+ and 0.006-2.5 μM for Pb2+. Good reusability and repeatability were also observed. The formation mechanism and 3-D structure of the porous electrode were also investigated using scanning electron microscope (SEM), transmission electron microscope (TEM) and X-ray photoelectron spectra (XPS). This graphene entrapped 3-D porous structure may envision promising applications in sensing devices.

A novel graphene nanodots inlaid porous gold electrode for electrochemically controlled drug release

A uniform graphene nanodots inlaid porous gold electrode was prepared via ion beam sputtering deposition (IBSD) and mild corrosion chemistry. HRTEM, SEM, AFM and XPS analyses revealed the successful fabrication of graphene nanodots inlaid porous gold electrode. The as-prepared porous electrode was used as π-orbital-rich drug loading platform to fabricate an electrochemically controlled drug release system with high performance. π-orbital-rich drugs with amino mioety, like doxorubicin (DOX) and tetracycline (TC), were loaded into the graphene nanodots inlaid porous gold electrode via non-covalent π-π stacking interaction. The amino groups in DOX and TC can be easily protonated at acidic medium to become positively-charged NH3(+), which allow these drug molecules to be desorbed from the porous electrode surface via electrostatic repulsion when positive potential is applied at the electrode. The drug loading and release experiment indicated that this graphene nanodots inlaid porous gold electrode can be used to conveniently and efficiently control the drug release electrochemically. Not only did our work provide a benign method to electrochemically controlled drug release via electrostatic repulsion process, it also enlighten the promising practical applications of micro electrode as a drug carrier for precisely and efficiently controlled drug release via embedding in the body.

Graphene nanodots encaged 3-D gold substrate as enzyme loading platform for the fabrication of high performance biosensors

Herein, a uniform three-dimensional (3-D) graphene nanodots-encaged porous gold electrode was prepared via ion beam sputtering deposition (IBSD) and mild corrosion chemistry for efficient enzyme electrode fabrication. Enzymes, like glucose oxidase and catalase, were modified with pyrene functionalities and then loaded into the graphene nanodots encaged porous gold electrode via non-covalent π-π stacking interaction between pyrene and graphene. The fabricated enzyme electrodes showed profound reusability and repeatability, high sensitivity, inherent selectivity and enhanced detection range. As for glucose analysis a broad linear range from 0.05 to 100 mM was obtained and the linear range for hydrogen peroxide was 0.005 to 4 mM. Detection limits of 30 μM for glucose and 1 μM for hydrogen peroxide were achieved (S/N = 3), respectively. These electrodes can be applied to analyze the clinical samples with reliable results. The formation mechanism and 3-D structure of the porous electrode were investigated using high resolution transmission electron microscope (HRTEM), atomic force microscopy (AFM), scanning electron microscope (SEM) and electrochemical impedance spectroscopy (EIS). Most importantly, various other ideal biosensors can be fabricated using the same porous electrode and the same enzyme modification methodology.

Superhydrophobic modification of polyimide films based on gold-coated porous silver nanostructures and self-assembled monolayers

We present a facile and effective method for controlling the surface hydrophobicity of polyimide films from sticky to superhydrophobic properties by tailoring their topographies. Nanostructured silver layers were produced on polyimide films by treatment with aqueous KOH and AgNO3, followed by thermal treatment at 200 degrees C or higher temperatures. Further modification of the gold-coated silver layers with n-dodecanethiol led to hydrophobic surfaces. Different morphologies of the silver layers at the micro- and nano-meter scales, which result in the variety of hydrophobicity, can be tailored by controlling the thermal treatment temperature. Surfaces prepared at 320 degrees C showed a sticky property that water drops did not slide off even when the sample was held upside down. Superhydrophobic surfaces were obtained when the temperature was above 340 degrees C. A remarkable superhydrophobicity, as evidenced by a very large water contact angle of 162 degrees and a very small sliding angle of 7 degrees, was achieved by heating the modified polyimide films at 360 degrees C. This is also the first example for superhydrophobic modification of polyimide films.